Table S4.
Lattice variation of LCO-1 and LCO-2 during electrochemical cycling.
Citation:
Xiangkang Jiang, Zhixing Wang, Hong Dong, Xiang Zhang, Jin Hu, Manman Chu, Yanshuai Hong, Lei Xu, Wenjie Peng, Xiqian Yu, Jiexi Wang. Corrigendum to “An in-depth understanding of Al doping homogeneity affecting the performance of LiCoO2 at cut-off voltage over 4.6 V” [Chinese Chemical Letters 35 (2024) 109553][J]. Chinese Chemical Letters,
2026, 37(10): 113195.
doi:
10.1016/j.cclet.2026.113195
Corrigendum to “An in-depth understanding of Al doping homogeneity affecting the performance of LiCoO2 at cut-off voltage over 4.6 V” [Chinese Chemical Letters 35 (2024) 109553]
English
Corrigendum to “An in-depth understanding of Al doping homogeneity affecting the performance of LiCoO2 at cut-off voltage over 4.6 V” [Chinese Chemical Letters 35 (2024) 109553]
-
The authors regret due to an oversight during the Supporting information preparation, the original Table S4 was published with missing numerical data in the table cells. The prior data should be assigned to unit cell variation, but not shrinkage rate of unit cell. To address this, we provide the corrected table, as can be seen below. This correction ensures that all data points are accurately and clearly to the readers.
The authors would like to apologize for any inconvenience caused.
Table S4
DownLoad:
CSV
Sample Unit cell (Å) Shrinkage rate of unit cell (%)# a c V a (%) c (%) V (%) LCO-1 2.816 14.063 96.532 0.7129 4.534 4.023 LCO-2 2.815 14.058 96.539 0.2635 0.2635 3.785 #(max-min)/max during the charging process.
-
Table S4. Lattice variation of LCO-1 and LCO-2 during electrochemical cycling.
Sample Unit cell (Å) Shrinkage rate of unit cell (%)# a c V a (%) c (%) V (%) LCO-1 2.816 14.063 96.532 0.7129 4.534 4.023 LCO-2 2.815 14.058 96.539 0.2635 0.2635 3.785 #(max-min)/max during the charging process. 