GROUP TRANSFER POLYMERIZATION OF ETHYL ACRYLATE WITH LEWIS ACID CATALYST
摘要:
This paper reports the kinetics of group transfer polymerization (GTP)of ethyl acrylate (EA)with zinc iodide catalyst in 1,2-dichloroethane using dimethyl ketene methyl trimethylsilyl acetal (MTS) as initiator at 0℃ and above 0℃. The amount of catalyst used was studied. When zinc iodide catalyst used is more than 10mol% relative to monomer, the rate of polymerization is proportional to the concentration of monomer, whereas zinc iodide catalyst used is less than 10 mol% of the monomer, the rate of polymerization is independent of the monomer concentration.In the GTP of EA an induction period was observed when the zinc iodide contents are less than 10mol%.If the reaction temperature is over 0℃,living species become unstable and diminish,leading to incomplete weight distributions which are not changed as decreasing zinc iodide contents.The polydispersity is about 1.2.
English
GROUP TRANSFER POLYMERIZATION OF ETHYL ACRYLATE WITH LEWIS ACID CATALYST
Abstract:
This paper reports the kinetics of group transfer polymerization (GTP)of ethyl acrylate (EA)with zinc iodide catalyst in 1,2-dichloroethane using dimethyl ketene methyl trimethylsilyl acetal (MTS) as initiator at 0℃ and above 0℃. The amount of catalyst used was studied. When zinc iodide catalyst used is more than 10mol% relative to monomer, the rate of polymerization is proportional to the concentration of monomer, whereas zinc iodide catalyst used is less than 10 mol% of the monomer, the rate of polymerization is independent of the monomer concentration.In the GTP of EA an induction period was observed when the zinc iodide contents are less than 10mol%.If the reaction temperature is over 0℃,living species become unstable and diminish,leading to incomplete weight distributions which are not changed as decreasing zinc iodide contents.The polydispersity is about 1.2.
扫一扫看文章
计量
- PDF下载量: 0
- 文章访问数: 0
- HTML全文浏览量: 0
下载: