刘兰, 聂福德, 曾贵玉, 谯志强. 超音速气流粉碎下NiO纳米棒的低温固相制备[J]. 应用化学,
2010, 27(4): 454-457.
doi:
10.3724/SP.J.1095.2010.90328
Citation: LIU Lan, NIE Fu-De, ZENG Gui-Yu, QIAO Zhi-Qiang. Preparation of NiO Nanorods by a Solid State Reaction at Low Temperatures under an Ultrasonic Airflow[J]. Chinese Journal of Applied Chemistry, 2010, 27(4): 454-457. doi: 10.3724/SP.J.1095.2010.90328
Citation: LIU Lan, NIE Fu-De, ZENG Gui-Yu, QIAO Zhi-Qiang. Preparation of NiO Nanorods by a Solid State Reaction at Low Temperatures under an Ultrasonic Airflow[J]. Chinese Journal of Applied Chemistry, 2010, 27(4): 454-457. doi: 10.3724/SP.J.1095.2010.90328
超音速气流粉碎下NiO纳米棒的低温固相制备
English
Preparation of NiO Nanorods by a Solid State Reaction at Low Temperatures under an Ultrasonic Airflow
Abstract:
The nanoparticles of NiO precursor were prepared by a low temperature solid state reaction under ultrasonic airflow.The precursor was converted into NiO nanorods after annealing at 650~900℃ in a molten salt medium.The structure and morphology of NiO precursor and nanorods were investigated by XRD,SEM and TEM technologies.The results indicated that the prepared precursor was spheric particles with a diameter of about 25 nm,and grew gradually to NiO nanorods with a diameter of about 300 nm and a length of several micrometers along with rising calcinging temperatures.The key factor in the process for the grwoth of NiO nanorods is the molten salt medium.
-
-