Preparation of PLGA Microspheres with Different Porous Morphologies

Citation: Shu-ying Wang, Xu-dong Shi, Zhi-hua Gan, Feng Wang. Preparation of PLGA Microspheres with Different Porous Morphologies[J]. Chinese Journal of Polymer Science, 2015, 33(1): 128-136. doi: 10.1007/s10118-014-1507-9 shu

Preparation of PLGA Microspheres with Different Porous Morphologies

1.
State Key Laboratory of Chemical Resource Engineering, Beijing Key Laboratory of Electrochemical Process and Technology for Materials, Beijing University of Chemical Technology, Beijing 100029, China
2.
Institute of Chemistry, Chinese Academy of Science, Beijing 100190, China
3.
1. Institute of Chemistry, Chinese Academy of Science, Beijing 100190, China
4.
2. State Key Laboratory of Organic-inorganic Composites, Beijing Laboratory of Biomedical Materials, Beijing University of Chemical Technology, Beijing 100029, China
5.
基金项目:
This work was financially supported by the National Natural Science Foundation of China (Nos. 51003109, 51125007 and 51025314).

摘要: Poly(D,L-lactide-co-glycolide) (PLGA) microspheres were prepared by emulsion solvent evaporation method. The influences of inner aqueous phase, organic solvent, PLGA concentration on the morphology of microspheres were studied. The results showed that addition of porogen or surfactants to the inner aqueous phase, types of organic solvents and polymer concentration affected greatly the microsphere morphology. When dichloromethane was adopted as organic solvent, microspheres with porous structure were produced. When ethyl acetate served as organic solvent, two different morphologies were obtained. One was hollow microspheres with thin porous shell under a lower PLGA concentration, another was erythrocyte-like microspheres under a higher PLGA concentration. Three types of microspheres including porous, hollow core with thin porous shell (denoted by hollow in brief) and solid structures were finally selected for in vitro drug release tests. Bovine serum albumin (BSA) was chosen as model drug and encapsulated within the microspheres. The BSA encapsulation efficiency of porous, hollow and solid microspheres was respectively 90.4%, 79.8% and 0. And the ultimate accumulative release was respectively 74.5%, 58.9% and 0. The release rate of porous microspheres was much slower than that of hollow microspheres. The experiment results indicated that microspheres with different porous structures showed great potentials in controlling drug release behavior.

关键词:

English

Preparation of PLGA Microspheres with Different Porous Morphologies

1.
State Key Laboratory of Chemical Resource Engineering, Beijing Key Laboratory of Electrochemical Process and Technology for Materials, Beijing University of Chemical Technology, Beijing 100029, China
2.
Institute of Chemistry, Chinese Academy of Science, Beijing 100190, China
3.
1. Institute of Chemistry, Chinese Academy of Science, Beijing 100190, China
4.
2. State Key Laboratory of Organic-inorganic Composites, Beijing Laboratory of Biomedical Materials, Beijing University of Chemical Technology, Beijing 100029, China
5.
Received Date: 13 May 2014
Revised Date: 02 July 2014
Available Online: 05 January 2015
Fund Project:
This work was financially supported by the National Natural Science Foundation of China (Nos. 51003109, 51125007 and 51025314).

Abstract: Poly(D,L-lactide-co-glycolide) (PLGA) microspheres were prepared by emulsion solvent evaporation method. The influences of inner aqueous phase, organic solvent, PLGA concentration on the morphology of microspheres were studied. The results showed that addition of porogen or surfactants to the inner aqueous phase, types of organic solvents and polymer concentration affected greatly the microsphere morphology. When dichloromethane was adopted as organic solvent, microspheres with porous structure were produced. When ethyl acetate served as organic solvent, two different morphologies were obtained. One was hollow microspheres with thin porous shell under a lower PLGA concentration, another was erythrocyte-like microspheres under a higher PLGA concentration. Three types of microspheres including porous, hollow core with thin porous shell (denoted by hollow in brief) and solid structures were finally selected for in vitro drug release tests. Bovine serum albumin (BSA) was chosen as model drug and encapsulated within the microspheres. The BSA encapsulation efficiency of porous, hollow and solid microspheres was respectively 90.4%, 79.8% and 0. And the ultimate accumulative release was respectively 74.5%, 58.9% and 0. The release rate of porous microspheres was much slower than that of hollow microspheres. The experiment results indicated that microspheres with different porous structures showed great potentials in controlling drug release behavior.

Key words:

1. [1]
  Yu, D., Zhang, Y., Zhou, X., Mao, Z. and Gao,C., Biomacromolecules, 2012, 13: 3272
2. [2]
  Chun, K.W., Yoo, H.S., Yoon, J.J. and Park, T.G., Biotechnol. Prog., 2004, 20: 1797
3. [3]
  Shi, X.D., Sun, L., Jiang, J., Zhang, X., Ding, W. and Gan, Z.H., Macromol. Biosci., 2009, 9: 1211
4. [4]
  Yang, Y.Y., Chung, T.S. and Ng, N.P., Biomaterials, 2001, 22: 231
5. [5]
  Luo, R., Neu, B. and Venkatraman, S.S., Small, 2012, 8: 2585
6. [6]
  O'Donnell, P.B.and McGinity, J.W., Eur. J. Pharm. Biopharm., 1998, 45: 83
7. [7]
  Bae, S.E., Son, J.S., Park, K. and Han, D.K., J. Control. Release, 2009, 133: 37
8. [8]
  Morita, T., Horikiri, Y., Suzuki,T. and Yoshino, H., Eur. J. Pharm. Biopharm., 2001, 51: 45
9. [9]
  Shi, X.D., Sun, L. and Gan, Z.H., Acta Polymerica Sinica (in Chinese), 2011, (8): 866
10. [10]
  Shi, X.D., Jiang, J., Sun, L. and Gan, Z.H., Colloids Surf. B Biointerfaces, 2011, 85: 73
11. [11]
  Sah, H. and Lee, B.J., Macromol. Rapid Commun., 2006, 27: 1845
12. [12]
  Newman, K.D. and McBurney, M.W., Biomaterials, 2004, 25: 5763
13. [13]
  Gabler, F., Frauenschuh, S., Ringe, J., Brochhausen, C., Goetz, P., Kirkpatrick, C.J., Sittinger, M., Schubert, H. and Zehbe, R., Biomol. Eng., 2007, 24: 515
14. [14]
  Wang, Q., Jamal, S., Detamore, M.S. and Berkland, C., J. Biomed. Mater. Res. Part A, 2001, 96A: 520
15. [15]
  Hariharan, S., Bhardwaj, V., Bala, I., Sitterberg, J., Bakowsky, U. and Kumar, M., Pharm. Res., 2006, 23: 184
16. [16]
  Jiang, W.L., Gupta, R.K., Deshpande, M.C. and Schwendeman, S.P., Adv. Drug Deliver. Rev., 2005, 57: 391
17. [17]
  Ke, C.J., Su, T.Y., Chen, H.L., Liu, H.L., Chiang, W.L., Chu, P.C., Xia, Y. and Sung, H.W., Angew. Chem. Int. Ed., 2011, 50: 8086
18. [18]
  Kong, S.D., Zhang, W., Lee, J.H., Brammer, K., Lal, R., Karin, M. and Jin, S., Nano Lett., 2010, 10: 5088
19. [19]
  Chiang, W.L., Ke, C.J., Liao, Z.X., Chen, S.Y., Chen, F.R., Tsai, C.Y., Xia, Y. and Sung, H.W., Small, 2010, 8: 3584
20. [20]
  Jaklenec, A., Wan, E., Murray, M.E. and Mathiowitz, E., Biomaterials, 2008, 29: 185
21. [21]
  Cheung, H.Y., Lau, K.T., Lu, T.P. and Hui, D., Compos. Part B Eng., 2007, 38: 291

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 1365
HTML全文浏览量: 36

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Preparation of PLGA Microspheres with Different Porous Morphologies

English

Preparation of PLGA Microspheres with Different Porous Morphologies

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

Preparation of PLGA Microspheres with Different Porous Morphologies

English

Preparation of PLGA Microspheres with Different Porous Morphologies

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南： 你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

文章相关

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs