引用本文: 杨扬, 丛妍, 肖宇, 付悦, 夏胜强, 董斌. Cd₃Al₂Ge₃O₁₂:Mn²⁺磷光体的发光和长余辉性能[J]. 无机化学学报, 2015, 31(8): 1529-1533. doi: 10.11862/CJIC.2015.207 shu

Citation: YANG Yang, CONG Yan, XIAO Yu, FU Yue, XIA Sheng-Qiang, DONG Bin. Luminescent and Long-Lasting Properties of Cd₃Al₂Ge₃O₁₂:Mn²⁺ Phosphor[J]. Chinese Journal of Inorganic Chemistry, 2015, 31(8): 1529-1533. doi: 10.11862/CJIC.2015.207 shu

Cd₃Al₂Ge₃O₁₂:Mn²⁺磷光体的发光和长余辉性能

杨扬 ^1, ,
丛妍 ^{1,2,
,} ,
肖宇 ^1, ,
付悦 ^1, ,
夏胜强 ^1, ,
董斌 ^{1,2,
,}

1.
1. 大连民族大学物理与材料工程学院, 大连 116600;
2.
2. 辽宁省光电薄膜材料重点实验室, 大连 116600

通讯作者: 丛妍,E-mail:congyan@dlnu.edu.cn;董斌,E-mail:dong@dlnu.edu.cn; 丛妍,E-mail:congyan@dlnu.edu.cn;董斌,E-mail:dong@dlnu.edu.cn

基金项目:
国家自然科学基金(No.61205178,11274057,11474046) (No.61205178,11274057,11474046)

辽宁省博士启动基金(No.20121073) (No.20121073)

大连市金州新区科技计划项目(No.2012-A1-051) (No.2012-A1-051)

中央高校基本科研业务费专项资金(No.DC201502080302,DC201502080203) (No.DC201502080302,DC201502080203)

大连民族学院大学生创新创业训练计划(No.X201413257)资助项目。 (No.X201413257)

摘要: 采用传统的高温固相法合成了Cd₃Al₂Ge₃O₁₂:Mn²⁺长余辉发光材料,利用X射线粉末衍射仪、荧光光谱仪、热释光谱计量仪等手段对粉末样品进行了表征。研究了以Zr⁴⁺离子作为辅助激活剂离子,对发光材料Cd₃Al₂Ge₃O₁₂:Mn²⁺余辉性能的影响。分析结果表明,样品位于500~700 nm的黄光宽带发射峰源于Mn²⁺的⁴T₁(⁴G)→⁶A₁(⁶S)跃迁发射结果。并且观察到了由Cd₃Al₂Ge₃O₁₂基质向激活剂离子Mn²⁺的能量传递。共掺杂Zr⁴⁺离子后样品发射峰位没有明显变化,但是余辉亮度衰减曲线表明适量的Zr⁴⁺离子掺杂可延长Cd₃Al₂Ge₃O₁₂:Mn²⁺的余辉时间。通过对热释光谱的分析,解释了双掺杂荧光粉余辉性能增强的原因,Zr⁴⁺的掺杂在材料中引入了深度更为合适的缺陷陷阱,可有效存储光能,增强余辉的时间和强度。

关键词:

长余辉发光;锰离子;能量传递

English

Luminescent and Long-Lasting Properties of Cd₃Al₂Ge₃O₁₂:Mn²⁺ Phosphor

YANG Yang ^1, ,
CONG Yan ^{1,2,
,} ,
XIAO Yu ^1, ,
FU Yue ^1, ,
XIA Sheng-Qiang ^1, ,
DONG Bin ^{1,2,
,}

1.
1. School of Physics & Materials Engineering, Dalian Nationalities University, Dalian, Liaoning 11660, China;
2.
2. Liaoning Key Laboratory of Optoelectronic Films and Materials, Dalian, Liaoning 11660, China

Corresponding author: 丛妍,E-mail:congyan@dlnu.edu.cn;董斌,E-mail:dong@dlnu.edu.cn; 丛妍,E-mail:congyan@dlnu.edu.cn;董斌,E-mail:dong@dlnu.edu.cn

Received Date: 24 January 2015
Fund Project:
国家自然科学基金(No.61205178,11274057,11474046)

辽宁省博士启动基金(No.20121073)

大连市金州新区科技计划项目(No.2012-A1-051)

中央高校基本科研业务费专项资金(No.DC201502080302,DC201502080203)

大连民族学院大学生创新创业训练计划(No.X201413257)资助项目。

Abstract: Cd₃Al₂Ge₃O₁₂:Mn²⁺ afterglow phosphors were synthesized by the conventional solid-state reaction in this work, and the enhanced afterglow properties were observed with Zr⁴⁺ ions co-doping. The Cd₃Al₂Ge₃O₁₂:Mn²⁺, Zr⁴⁺ phosphors were characterized by using XRD, photoluminescence and thermoluminescence spectroscopy. The emission spectrum shows a broad emission band from 500 to 700 nm which is assigned to the ⁴T₁(⁴G)→⁶A₁(⁶S) transitions of Mn²⁺ ion. An energy transfer from the Cd₃Al₂Ge₃O₁₂ host to Mn²⁺ ions was observed. The center and the profile of the emission remain unchanged when co-doped with Zr⁴⁺ ions, but the introduction of Zr⁴⁺ ions improved the afterglow duration. Thermoluminescence spectra indicated that the introduction of Zr⁴⁺ into the host produces traps with suitable depth, resulting in the enhanced phosphorescence of Mn²⁺.

Key words:

long-lasting luminescence;Mn²⁺ ion;energy transfer

1. [1] LIU Ying-Liang(刘应亮), LEI Bing-Fu(雷炳富), KUANG Jin-Yong(邝金勇), et al. Chinese J. Inorg. Chem.(无机化学学报), 2009,25(8):1323-1329[1] LIU Ying-Liang(刘应亮), LEI Bing-Fu(雷炳富), KUANG Jin-Yong(邝金勇), et al. Chinese J. Inorg. Chem.(无机化学学报), 2009,25(8):1323-1329
2. [2] Lei B, Sha L, Zhang H, et al. Solid State Sci., 2010,12(12):2177-2181[2] Lei B, Sha L, Zhang H, et al. Solid State Sci., 2010,12(12):2177-2181
3. [3] Matsuzawa T, Aoki Y, Takeuchi N. J. Electrochem. Soc., 1996,143(8):2670-2673[3] Matsuzawa T, Aoki Y, Takeuchi N. J. Electrochem. Soc., 1996,143(8):2670-2673
4. [4] LI Cheng-Yu(李成宇), SU Qiang(苏锵), QIU Jiang-Rong(邱建荣). Chinese J. Lumin.(发光学报), 2003,24:19-27[4] LI Cheng-Yu(李成宇), SU Qiang(苏锵), QIU Jiang-Rong(邱建荣). Chinese J. Lumin.(发光学报), 2003,24:19-27
5. [5] SHI Chao-Shu(施朝淑), QI Ze-Ming(戚泽明). Chinese J. Inorg. Chem.(无机化学学报), 2004,19:961-969[5] SHI Chao-Shu(施朝淑), QI Ze-Ming(戚泽明). Chinese J. Inorg. Chem.(无机化学学报), 2004,19:961-969
6. [6] Pan Z, Lu Y, Liu F. Nat. Mater., 2012,11:58-63[6] Pan Z, Lu Y, Liu F. Nat. Mater., 2012,11:58-63
7. [7] Lei B, Liu Y, Zhang J, et al. J. Alloys Compd., 2010,459:247-253[7] Lei B, Liu Y, Zhang J, et al. J. Alloys Compd., 2010,459:247-253
8. [8] Jha Pardeep K, Jha Priyanka A, Kumar P, et al. J. Mater. Sci.:Mater. Electron., 2014,25:664-672[8] Jha Pardeep K, Jha Priyanka A, Kumar P, et al. J. Mater. Sci.:Mater. Electron., 2014,25:664-672
9. [9] Sun Y, Yu H, Liu H, et al. Adv. Mater. Res., 2012,415-417:495-498[9] Sun Y, Yu H, Liu H, et al. Adv. Mater. Res., 2012,415-417:495-498
10. [10] HE Ming-Rui(贺明睿), XIAO Jiu-Lin(肖久林), TIAN Yan-Wen(田彦文), et al. Chinese Rare Earths(稀土), 2009,30(1):10-13[10] HE Ming-Rui(贺明睿), XIAO Jiu-Lin(肖久林), TIAN Yan-Wen(田彦文), et al. Chinese Rare Earths(稀土), 2009,30(1):10-13
11. [11] LIU Xing-Ren(刘行仁), TIAN Jun(田军), WANG Xiao-Jun (王晓君), et al. Chinese J. Lumin.(发光学报), 1994,15(2):83-88[11] LIU Xing-Ren(刘行仁), TIAN Jun(田军), WANG Xiao-Jun (王晓君), et al. Chinese J. Lumin.(发光学报), 1994,15(2):83-88
12. [12] LIU Zheng-Wei(刘正伟). Thesis for the Masterate of Jinan University(暨南大学硕士论文). 2005.[12] LIU Zheng-Wei(刘正伟). Thesis for the Masterate of Jinan University(暨南大学硕士论文). 2005.
13. [13] Nosenko A E, Abramov A P, Kostyk L V, et al. Opt. Spectrasc., 1986,61(5):648-653[13] Nosenko A E, Abramov A P, Kostyk L V, et al. Opt. Spectrasc., 1986,61(5):648-653
14. [14] Zhang T, Su Q. J. Soc. Inf. Disp., 2000,8(1):27-30[14] Zhang T, Su Q. J. Soc. Inf. Disp., 2000,8(1):27-30
15. [15] Ihara M, Igarashi T, Kusunoki I, et al. J. Electrochem. Soc., 2002,149(3):H72-H75[15] Ihara M, Igarashi T, Kusunoki I, et al. J. Electrochem. Soc., 2002,149(3):H72-H75

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 546
HTML全文浏览量: 44

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Cd₃Al₂Ge₃O₁₂:Mn²⁺磷光体的发光和长余辉性能

通讯作者: 丛妍,E-mail:congyan@dlnu.edu.cn;董斌,E-mail:dong@dlnu.edu.cn; 丛妍,E-mail:congyan@dlnu.edu.cn;董斌,E-mail:dong@dlnu.edu.cn

English

Luminescent and Long-Lasting Properties of Cd₃Al₂Ge₃O₁₂:Mn²⁺ Phosphor

Corresponding author: 丛妍,E-mail:congyan@dlnu.edu.cn;董斌,E-mail:dong@dlnu.edu.cn; 丛妍,E-mail:congyan@dlnu.edu.cn;董斌,E-mail:dong@dlnu.edu.cn

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处