钙钛矿结构荧光材料MZrO3:Eu3+,A (M=Ca2+, Ba2+; A=Li+, Na+, K+) 的制备及其发光性质

引用本文: MARÍ B., CEMBRERO-COCA P., SINGH K. C., KAUSHIK R. D., OM Hari. 钙钛矿结构荧光材料MZrO₃:Eu³⁺,A (M=Ca²⁺, Ba²⁺; A=Li⁺, Na⁺, K⁺) 的制备及其发光性质[J]. 物理化学学报, 2013, 29(06): 1357-1362. doi: 10.3866/PKU.WHXB201304032 shu

Citation: MARÍ B., CEMBRERO-COCA P., SINGH K. C., KAUSHIK R. D., OM Hari. Preparation and Luminescence Properties of MZrO₃:Eu³⁺,A (M=Ca²⁺, Ba²⁺; A=Li⁺, Na⁺, K⁺) Phosphors with Perovskite Structure[J]. Acta Physico-Chimica Sinica, 2013, 29(06): 1357-1362. doi: 10.3866/PKU.WHXB201304032 shu

钙钛矿结构荧光材料MZrO₃:Eu³⁺,A (M=Ca²⁺, Ba²⁺; A=Li⁺, Na⁺, K⁺) 的制备及其发光性质

基金项目:
The project was supported by the Spanish vernment through MCINN (MAT2009-14625-C03-03) (MAT2009-14625-C03-03)

European Commission through Nano CISproject (FP7-PEOPLE-2010-IRSES ref. 269279). (FP7-PEOPLE-2010-IRSES ref. 269279)

摘要:

Calcium and barium zirconate powders based upon CaZrO₃:Eu³⁺,A and BaZrO₃:Eu³⁺,A (A=Li⁺, Na⁺, K⁺) were prepared by combustion synthesis method and heating to ~1000℃ to improve crystallinity.The structure and morphology of materials were examined by X-ray diffraction (XRD) and scanningelectron microscopy (SEM). XRD results showed that CaZrO₃:Eu³⁺,A and BaZrO₃:Eu³⁺,A (A=Li⁺, Na⁺, K⁺) perovskites possessed orthorhombic and cubic structures, respectively. The morphologies of all powderswere very similar consisting of small, coagulated, cubical particles with narrow size distributions andsmooth and regular surfaces. The characteristic luminescences of Eu³⁺ ions in CaZrO₃:Eu³⁺,A (A=Li⁺, Na⁺, K⁺) lattices were present with strong emissions at 614 and 625 nm for ⁵D₀→⁷F₂ transitions with other weakeremissions observed at 575, 592, 655, and 701 nm corresponding to ⁵D₀→⁷F_n transitions (where n=0, 1, 3, 4 respectively). In BaZrO₃:Eu³⁺ both the ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transitions at 595 and 613 nm were strong.Photoluminescence intensities of CaZrO₃:Eu³⁺ samples were higher than those of BaZrO₃:Eu³⁺ lattices. Thisremarkable increase of photoluminescence intensity (corresponding to ⁵D₀→⁷F_n transitions) was observedin CaZrO₃:Eu³⁺ and BaZrO₃:Eu³⁺ if co-doped with Li⁺ ions. An additional broad band composed of manypeaks between 440 to 575 nm was observed in BaZrO₃:Eu³⁺,,A samples. The intensity of this band wasgreatest in Li⁺ co-doped samples and lowest for K⁺ doped samples.

关键词:

CaZrO₃:Eu³⁺, A and BaZrO₃:Eu³⁺, A (A=Li⁺, Na⁺, K⁺)
/ Charge compensator
/ Combustionsynthesis
/ Photoluminescence

English

Preparation and Luminescence Properties of MZrO₃:Eu³⁺,A (M=Ca²⁺, Ba²⁺; A=Li⁺, Na⁺, K⁺) Phosphors with Perovskite Structure

1.
1 Institut de Disseny per la Fabricació Automatitzada (IDF)-Departament de Física Aplicada, Universitat Politècnica de València, Camí de Vera s/n, 46022 València, Spain;
2 Department of Chemistry, Maharshi Dayanand University, Rohtak 124001, Haryana, India;
3 Department of Chemistry, Gurukul Kangari University, Haridwar-249404, Uttarakhand, India
Received Date: 27 December 2012
Available Online: 17 May 2013
Fund Project:
The project was supported by the Spanish vernment through MCINN (MAT2009-14625-C03-03)

European Commission through Nano CISproject (FP7-PEOPLE-2010-IRSES ref. 269279).

Abstract:

Calcium and barium zirconate powders based upon CaZrO₃:Eu³⁺,A and BaZrO₃:Eu³⁺,A (A=Li⁺, Na⁺, K⁺) were prepared by combustion synthesis method and heating to ~1000℃ to improve crystallinity. The structure and morphology of materials were examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). XRD results showed that CaZrO₃:Eu³⁺,A and BaZrO₃:Eu³⁺,A (A=Li⁺, Na⁺, K⁺) perovskites possessed orthorhombic and cubic structures, respectively. The morphologies of all powders were very similar consisting of small, coagulated, cubical particles with narrow size distributions and smooth and regular surfaces. The characteristic luminescences of Eu³⁺ ions in CaZrO₃:Eu³⁺,A (A=Li⁺, Na⁺, K⁺) lattices were present with strong emissions at 614 and 625 nm for ⁵D₀→⁷F₂ transitions with other weaker emissions observed at 575, 592, 655, and 701 nm corresponding to ⁵D₀→⁷F_n transitions (where n=0, 1, 3, 4 respectively). In BaZrO₃:Eu³⁺ both the ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transitions at 595 and 613 nm were strong. Photoluminescence intensities of CaZrO₃:Eu³⁺ samples were higher than those of BaZrO₃:Eu³⁺ lattices. This remarkable increase of photoluminescence intensity (corresponding to ⁵D₀→⁷F_n transitions) was observed in CaZrO₃:Eu³⁺ and BaZrO₃:Eu³⁺ if co-doped with Li⁺ ions. An additional broad band composed of many peaks between 440 to 575 nm was observed in BaZrO₃:Eu³⁺,,A samples. The intensity of this band was greatest in Li⁺ co-doped samples and lowest for K⁺ doped samples.

Key words:

CaZrO₃:Eu³⁺, A and BaZrO₃:Eu³⁺, A (A=Li⁺, Na⁺, K⁺)
/ Charge compensator
/ Combustion synthesis
/ Photoluminescence

1. [1]
  
  (1) Pan, Y.; Su, Q.; Xu, H.; Chen, T.; Ge,W.; Yang, C.;Wu, M.J. Solid State Chem. 2003, 174, 69. doi: 10.1016/S0022-4596(03)00175-0
  (1) Pan, Y.; Su, Q.; Xu, H.; Chen, T.; Ge,W.; Yang, C.;Wu, M.J. Solid State Chem. 2003, 174, 69. doi: 10.1016/S0022-4596(03)00175-0
2. [2]
  (2) Boutinaud, P.; Pinel, E.; Dubois, M.; Vink, A. P.; Mahiou, R.J. Lumin. 2005, 111, 69. doi: 10.1016/j.jlumin.2004.06.006(2) Boutinaud, P.; Pinel, E.; Dubois, M.; Vink, A. P.; Mahiou, R.J. Lumin. 2005, 111, 69. doi: 10.1016/j.jlumin.2004.06.006
3. [3]
  (3) Okamoto, S.; amamoto, H.. Appl. Phys. Lett. 2001, 78, 655.doi: 10.1063/1.1343491(3) Okamoto, S.; amamoto, H.. Appl. Phys. Lett. 2001, 78, 655.doi: 10.1063/1.1343491
4. [4]
  (4) Zhang, H. X.; Kam, C. H.; Zhou, Y.; Han, X.; Buddhudu, S.;Xiang, Q.; Lam, Y. L.; Chan, Y. C. Appl. Phys. Lett. 2000, 77,609. doi: 10.1063/1.127060(4) Zhang, H. X.; Kam, C. H.; Zhou, Y.; Han, X.; Buddhudu, S.;Xiang, Q.; Lam, Y. L.; Chan, Y. C. Appl. Phys. Lett. 2000, 77,609. doi: 10.1063/1.127060
5. [5]
  (5) Amami, J.; Hreniak, D.; Guyot, Y.; Zhao,W.; Boulon, G.J. Lumin. 2006, 119-120, 383.(5) Amami, J.; Hreniak, D.; Guyot, Y.; Zhao,W.; Boulon, G.J. Lumin. 2006, 119-120, 383.
6. [6]
  (6) Park, J. K.; Ryu, H.; Park, H. D.; Choi, S. Y. J. Eur. Ceram. Soc.2001, 21, 535. doi: 10.1016/S0955-2219(00)00238-7(6) Park, J. K.; Ryu, H.; Park, H. D.; Choi, S. Y. J. Eur. Ceram. Soc.2001, 21, 535. doi: 10.1016/S0955-2219(00)00238-7
7. [7]
  (7) Pinel, E.; Boutinaud, P.; Mahiou, R. J. Alloy. Compd. 2004, 380,225. doi: 10.1016/j.jallcom.2004.03.048(7) Pinel, E.; Boutinaud, P.; Mahiou, R. J. Alloy. Compd. 2004, 380,225. doi: 10.1016/j.jallcom.2004.03.048
8. [8]
  (8) Zhang, H.W.; Fu, X. Y.; Niu, S. Y.; Xin, Q. J. Lumin. 2008, 128,1348. doi: 10.1016/j.jlumin.2008.01.007(8) Zhang, H.W.; Fu, X. Y.; Niu, S. Y.; Xin, Q. J. Lumin. 2008, 128,1348. doi: 10.1016/j.jlumin.2008.01.007
9. [9]
  (9) Zhang, H.W.; Fu, X. Y.; Niu, S. Y.; Xin, Q. J. Alloy. Compd.2008, 459, 103. doi: 10.1016/j.jallcom.2007.04.259(9) Zhang, H.W.; Fu, X. Y.; Niu, S. Y.; Xin, Q. J. Alloy. Compd.2008, 459, 103. doi: 10.1016/j.jallcom.2007.04.259
10. [10]
  (10) Alarcon, J.; van der Voort, D.; Blasse, G. Mater. Res. Bull. 1992,27, 467. doi: 10.1016/0025-5408(92)90024-T(10) Alarcon, J.; van der Voort, D.; Blasse, G. Mater. Res. Bull. 1992,27, 467. doi: 10.1016/0025-5408(92)90024-T
11. [11]
  (11) Liu, X. H.;Wang, X. D. Opt. Mater. 2007, 30, 626. doi: 10.1016/j.optmat.2007.02.032(11) Liu, X. H.;Wang, X. D. Opt. Mater. 2007, 30, 626. doi: 10.1016/j.optmat.2007.02.032
12. [12]
  (12) Koopmans, H. J. A.; van de Velde, G. M. H.; Gellings, P. J. Acta Crystallogr. C 1983, 39, 1323. doi: 10.1107/S0108270183008392(12) Koopmans, H. J. A.; van de Velde, G. M. H.; Gellings, P. J. Acta Crystallogr. C 1983, 39, 1323. doi: 10.1107/S0108270183008392
13. [13]
  (13) Norton, F. H. Fine Ceramics; McGraw-Hill: New York, 1970.(13) Norton, F. H. Fine Ceramics; McGraw-Hill: New York, 1970.
14. [14]
  (14) Joly, A. G.; Chen,W.; Zhang, J.;Wang, S. J. Lumin. 2007, 126,491. doi: 10.1016/j.jlumin.2006.09.004(14) Joly, A. G.; Chen,W.; Zhang, J.;Wang, S. J. Lumin. 2007, 126,491. doi: 10.1016/j.jlumin.2006.09.004
15. [15]
  (15) Cong, Y.; Li, B.; Lei, B.;Wang, X.; Liu, C.; Liu, J.; Li,W.J. Lumin. 2008, 128, 105. doi: 10.1016/j.jlumin.2007.05.016(15) Cong, Y.; Li, B.; Lei, B.;Wang, X.; Liu, C.; Liu, J.; Li,W.J. Lumin. 2008, 128, 105. doi: 10.1016/j.jlumin.2007.05.016
16. [16]
  (16) Xiao, X.; Yan, B. J. Mater. Lett. 2007, 61, 1649. doi: 10.1016/j.matlet.2006.07.092(16) Xiao, X.; Yan, B. J. Mater. Lett. 2007, 61, 1649. doi: 10.1016/j.matlet.2006.07.092
17. [17]
  (17) Fu, J. J. Electrochemical Solid State Lett. 2000, 3, 350.(17) Fu, J. J. Electrochemical Solid State Lett. 2000, 3, 350.
18. [18]
  (18) Marí, B.; Singh, K. C.; Moya, M.; Singh, I.; Om, H.; Chand, S.Optical Materials 2012, 34,1267. doi: 10.1016/j.optmat.2012.01.032(18) Marí, B.; Singh, K. C.; Moya, M.; Singh, I.; Om, H.; Chand, S.Optical Materials 2012, 34,1267. doi: 10.1016/j.optmat.2012.01.032
19. [19]
  (19) Marí, B.; Singh, K.; Sahal, M.; Khatkar, S.; Taxak, V.; Kumar,M. J. Lumin. 2011, 131, 587. doi: 10.1016/j.jlumin.2010.10.035(19) Marí, B.; Singh, K.; Sahal, M.; Khatkar, S.; Taxak, V.; Kumar,M. J. Lumin. 2011, 131, 587. doi: 10.1016/j.jlumin.2010.10.035
20. [20]
  (20) Park, I. Y.; Kim, D.; Lee, J.; Lee, S. H.; Kim, K. J. Mater. Chem. Phys. 2007, 106, 149. doi: 10.1016/j.matchemphys.2007.05.050(20) Park, I. Y.; Kim, D.; Lee, J.; Lee, S. H.; Kim, K. J. Mater. Chem. Phys. 2007, 106, 149. doi: 10.1016/j.matchemphys.2007.05.050
21. [21]
  (21) Di,W.; Zhao, X.; Lu, S. J. Solid State Chem. 2007, 180, 2478.doi: 10.1016/j.jssc.2007.06.025(21) Di,W.; Zhao, X.; Lu, S. J. Solid State Chem. 2007, 180, 2478.doi: 10.1016/j.jssc.2007.06.025
22. [22]
  (22) Uhlich, D.; Huppertz, P.;Wiechert, D. U.; Justel, T. J. Opt. Mater. 2007, 29, 1505. doi: 10.1016/j.optmat.2006.07.013(22) Uhlich, D.; Huppertz, P.;Wiechert, D. U.; Justel, T. J. Opt. Mater. 2007, 29, 1505. doi: 10.1016/j.optmat.2006.07.013
23. [23]
  (23) Kang, M.; Liao, X.; Kang, Y.; Liu, J.; Sun, R.; Yin, G.; Huang,Z.; Yao, I. J. Mater. Sci. 2009, 44, 2388. doi: 10.1007/s10853-009-3298-x(23) Kang, M.; Liao, X.; Kang, Y.; Liu, J.; Sun, R.; Yin, G.; Huang,Z.; Yao, I. J. Mater. Sci. 2009, 44, 2388. doi: 10.1007/s10853-009-3298-x
24. [24]
  (24) Ekambaram, S.; Patil, K. C. J. Alloy. Compd. 1997, 248, 7.doi: 10.1016/S0925-8388(96)02622-9(24) Ekambaram, S.; Patil, K. C. J. Alloy. Compd. 1997, 248, 7.doi: 10.1016/S0925-8388(96)02622-9
25. [25]
  (25) Guan, L.; Jin, L. T.; Guo, S. Q.; Liu, Y. F.; Li, X.; Guo, Q. L.;Yang, Z. P.; Fu, G. S. J. Rare Earths 2010, 28, 292.doi: 10.1016/S1002-0721(10)60362-6(25) Guan, L.; Jin, L. T.; Guo, S. Q.; Liu, Y. F.; Li, X.; Guo, Q. L.;Yang, Z. P.; Fu, G. S. J. Rare Earths 2010, 28, 292.doi: 10.1016/S1002-0721(10)60362-6
26. [26]
  (26) Liu, X.;Wang, X. Opt. Mater. 2007, 30, 626. doi: 10.1016/j.optmat.2007.02.032(26) Liu, X.;Wang, X. Opt. Mater. 2007, 30, 626. doi: 10.1016/j.optmat.2007.02.032
27. [27]
  (27) Zhang, H.; Fu, X.; Niu, S.; Xin, Q. J. Alloy. Compd. 2008, 459,103. doi: 10.1016/j.jallcom.2007.04.259(27) Zhang, H.; Fu, X.; Niu, S.; Xin, Q. J. Alloy. Compd. 2008, 459,103. doi: 10.1016/j.jallcom.2007.04.259
28. [28]
  (28) Li, X.; Guan, L.; An, J. Y.; Jin, L. T.; Yang, Z. P.; Yang, Y. M.;Li, P. L.; Fu, G. S. Chin. Phys. Lett. 2011, 28, 027805-1.doi: 10.1088/0256-307X/28/2/027805(28) Li, X.; Guan, L.; An, J. Y.; Jin, L. T.; Yang, Z. P.; Yang, Y. M.;Li, P. L.; Fu, G. S. Chin. Phys. Lett. 2011, 28, 027805-1.doi: 10.1088/0256-307X/28/2/027805
29. [29]
  (29) Hannan, A.; Iwasa, K.; Kohgi, M.; Suzuki, T. J. Phys. Soc. Jpn.2000, 69, 2358. doi: 10.1143/JPSJ.69.2358(29) Hannan, A.; Iwasa, K.; Kohgi, M.; Suzuki, T. J. Phys. Soc. Jpn.2000, 69, 2358. doi: 10.1143/JPSJ.69.2358
30. [30]
  (30) Ahmed, M. A.; Ateia, E.; El-Dek, S. I. Mater. Lett. 2003, 57,4256. doi: 10.1016/S0167-577X(03)00300-8(30) Ahmed, M. A.; Ateia, E.; El-Dek, S. I. Mater. Lett. 2003, 57,4256. doi: 10.1016/S0167-577X(03)00300-8
31. [31]
  (31) Zhang, H.W.; Fu, X. Y.; Niu, S. Y.; Xin, Q. J. Solid State Chem.2004, 177, 2649. doi: 10.1016/j.jssc.2004.04.037(31) Zhang, H.W.; Fu, X. Y.; Niu, S. Y.; Xin, Q. J. Solid State Chem.2004, 177, 2649. doi: 10.1016/j.jssc.2004.04.037
32. [32]
  (32) Lu, Z.; Chen, L.; Tang, Y.; Li, Y. J. Alloy. Compd. 2005, 387,L1.(32) Lu, Z.; Chen, L.; Tang, Y.; Li, Y. J. Alloy. Compd. 2005, 387,L1.
33. [33]
  (33) Mao, Z. Y.;Wang, D. J.; Lu, Q. F.; Yu,W. H.; Yuan, Z. H. Chem. Commun. 2009, 346.(33) Mao, Z. Y.;Wang, D. J.; Lu, Q. F.; Yu,W. H.; Yuan, Z. H. Chem. Commun. 2009, 346.
34. [34]
  (34) Shimizu, Y.; Sakagami, S.; to, K.; Nakachi, Y.; Ueda, K.Materials Science and Engineering: B 2009, 161, 100.doi: 10.1016/j.mseb.2008.11.035(34) Shimizu, Y.; Sakagami, S.; to, K.; Nakachi, Y.; Ueda, K.Materials Science and Engineering: B 2009, 161, 100.doi: 10.1016/j.mseb.2008.11.035
35. [35]
  (35) Blasse, G.; Grabmaier, B. C. Luminescent Materials; Springer:Berlin, 1994.(35) Blasse, G.; Grabmaier, B. C. Luminescent Materials; Springer:Berlin, 1994.
36. [36]
  (36) Ryu, H.; Singh, B. K.; Bartwal, K. S.; Brik, M. G.; Kityk, I. V.Acta Mater. 2008, 56, 358. doi: 10.1016/j.actamat.2007.09.041(36) Ryu, H.; Singh, B. K.; Bartwal, K. S.; Brik, M. G.; Kityk, I. V.Acta Mater. 2008, 56, 358. doi: 10.1016/j.actamat.2007.09.041
37. [37]
  (37) Diallo, P. T.; Jeanlouis, K.; Boutinaud, P. J. Alloy. Compd. 2001,323 - 324, 218.(37) Diallo, P. T.; Jeanlouis, K.; Boutinaud, P. J. Alloy. Compd. 2001,323 - 324, 218.
38. [38]
  (38) Tang, J. F.; Yu, X. B.; Yang, L. Z.; Zhou, C. L.; Peng, X. D.Mater. Lett. 2006, 60, 326. doi: 10.1016/j.matlet.2005.08.047(38) Tang, J. F.; Yu, X. B.; Yang, L. Z.; Zhou, C. L.; Peng, X. D.Mater. Lett. 2006, 60, 326. doi: 10.1016/j.matlet.2005.08.047
39. [39]
  (39) Yang, H. K.; Chung, J.W.; Moon, B. K.; Choi, B. C.; Jeong, J.H.; Kim, K. H. J. Phys. D: Appl. Phys. 2009, 42, 085411.doi: 10.1088/0022-3727/42/8/085411
  (39) Yang, H. K.; Chung, J.W.; Moon, B. K.; Choi, B. C.; Jeong, J.H.; Kim, K. H. J. Phys. D: Appl. Phys. 2009, 42, 085411.doi: 10.1088/0022-3727/42/8/085411

扫一扫看文章

计量

PDF下载量: 924
文章访问数: 1642
HTML全文浏览量: 87

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

钙钛矿结构荧光材料MZrO₃:Eu³⁺,A (M=Ca²⁺, Ba²⁺; A=Li⁺, Na⁺, K⁺) 的制备及其发光性质

English

Preparation and Luminescence Properties of MZrO₃:Eu³⁺,A (M=Ca²⁺, Ba²⁺; A=Li⁺, Na⁺, K⁺) Phosphors with Perovskite Structure

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处