t/FeSnO(OH)5: A Novel Supported Pt Catalyst for Catalytic Oxidation of Benzene

YU Han ,  CAO Zhou-Ming ,  WEIXiao-Feng ,  YU Yan

downloadPDF
Citation:  YU Han, CAO Zhou-Ming, YU Yan. t/FeSnO(OH)5: A Novel Supported Pt Catalyst for Catalytic Oxidation of Benzene[J]. Chinese Journal of Structural Chemistry, 2016, 35(6): 889-902. doi: 10.14102/j.cnki.0254-5861.2011-1052 shu

t/FeSnO(OH)5: A Novel Supported Pt Catalyst for Catalytic Oxidation of Benzene

  • a.

    a. Key Laboratory of Eco-materials Advanced Technology (Fuzhou University), Fujian Province University, College of Materials Science and Engineering, Fuzhou University, Fuzhou 350108, China;

  • b.

    b. College of Chemical Engineering, Fuzhou University, Fuzhou 350108, China

    • 通讯作者: YU Yan,
  • 基金项目:

    This project was supported by the National Natural Science Foundation of China (No. 51102047, 51472050) (No. 51102047, 51472050)

    the Natural Science Foundation of Fujian Province (No. 2013J05027)  (No. 2013J05027)

    Young Teachers (No. JA13050) (No. JA13050)

摘要: Pt/FeSnO(OH)5 was synthesized as a novel catalyst for VOCs oxidation. Compared with Pt/γ-Al2O3 during catalytic oxidation of benzene, Pt/FeSnO(OH)5 showed better catalytic activity. After characterization of the catalysts by XRD, SEM, TEM, EDS, XPS, BET, TGA and DTA, we found most Pt could be reduced to metallic state when the hydroxyl catalyst was used as supporter, and the metallic Pt in Pt/FeSnO(OH)5 was more active than the oxidized Pt in Pt/γ-Al2O3 in catalytic oxidation of VOCs. Pt/FeSnO(OH)5 shows both good catalytic activity and high stability, which may be a promising catalyst. This study may also be helpful for the design and fabrication of new catalysts.

English

  • 
    1. [1]

      (1) Li, Z. H.; Yang, K.; Liu, G.; Deng, G. F.; Li, J. Q.; Li, G.; Yue, R. L.; Yang, J.; Chen, Y. F. Effect of reduction treatment on structural properties of TiO2 supported Pt nanoparticles and their catalytic activity for benzene oxidation. Catal. Lett. 2014, 144, 1080-1087.(1) Li, Z. H.; Yang, K.; Liu, G.; Deng, G. F.; Li, J. Q.; Li, G.; Yue, R. L.; Yang, J.; Chen, Y. F. Effect of reduction treatment on structural properties of TiO2 supported Pt nanoparticles and their catalytic activity for benzene oxidation. Catal. Lett. 2014, 144, 1080-1087.

    2. [2]

      (2) Shim, W. G.; Lee, J. W.; Kim, S. C. Analysis of catalytic oxidation of aromatic hydrocarbons over supported palladium catalyst with different pretreatments based on heterogeneous adsorption properties. Appl. Catal. B: Environ. 2008, 84, 133-141.(2) Shim, W. G.; Lee, J. W.; Kim, S. C. Analysis of catalytic oxidation of aromatic hydrocarbons over supported palladium catalyst with different pretreatments based on heterogeneous adsorption properties. Appl. Catal. B: Environ. 2008, 84, 133-141.

    3. [3]

      (3) Wu, J. C. S.; Lin, Z. A.; Pan, J. W.; Rei, M. H. A novel boron nitride supported Pt catalyst for VOC incineration. Appl. Catal. A: Gen. 2001, 219, 117-124.(3) Wu, J. C. S.; Lin, Z. A.; Pan, J. W.; Rei, M. H. A novel boron nitride supported Pt catalyst for VOC incineration. Appl. Catal. A: Gen. 2001, 219, 117-124.

    4. [4]

      (4) Giraudon, J. M.; Elhachimi, A.; Leclercq, G. Catalytic oxidation of chlorobenzene over Pd/perovskites. Appl. Catal. B: Environ. 2008, 84, 251-261.(4) Giraudon, J. M.; Elhachimi, A.; Leclercq, G. Catalytic oxidation of chlorobenzene over Pd/perovskites. Appl. Catal. B: Environ. 2008, 84, 251-261.

    5. [5]

      (5) Diehl, F.; Barbier, J.; Duprez, D.; Guibard, I.; Mabilon, G. Catalytic oxidation of heavy hydrocarbons over Pt/Al2O3: influence of the structure of the molecule on its reactivity. Appl. Catal. B: Environ. 2010, 95, 217-227.(5) Diehl, F.; Barbier, J.; Duprez, D.; Guibard, I.; Mabilon, G. Catalytic oxidation of heavy hydrocarbons over Pt/Al2O3: influence of the structure of the molecule on its reactivity. Appl. Catal. B: Environ. 2010, 95, 217-227.

    6. [6]

      (6) Lin, C. A.; Wu, J. C. S.; Pan, J. W.; Yeh, C. T. Characterization of boron-nitride-supported Pt catalysts for the deep oxidation of benzene. J. Catal. 2002, 210, 39-45.(6) Lin, C. A.; Wu, J. C. S.; Pan, J. W.; Yeh, C. T. Characterization of boron-nitride-supported Pt catalysts for the deep oxidation of benzene. J. Catal. 2002, 210, 39-45.

    7. [7]

      (7) Escandón, L. S.; Ordóñez, S.; Vega, A.; Díez, F. Oxidation of methane over palladium catalysts effect of the support. Chemosphere 2005, 58, 9-17.(7) Escandón, L. S.; Ordóñez, S.; Vega, A.; Díez, F. Oxidation of methane over palladium catalysts effect of the support. Chemosphere 2005, 58, 9-17.

    8. [8]

      (8) Silviya, T.; Georgi, K.; Krasimir, T.; Yuri, K.; Vladislav, K. K. Particle size and support effects on the complete benzene oxidation by Co and Co-Pt catalysts. J. Mater. Sci. 2007, 42, 3315-3320.(8) Silviya, T.; Georgi, K.; Krasimir, T.; Yuri, K.; Vladislav, K. K. Particle size and support effects on the complete benzene oxidation by Co and Co-Pt catalysts. J. Mater. Sci. 2007, 42, 3315-3320.

    9. [9]

      (9) Miller, J. B.; Malatpure, M. Pd catalysts for total oxidation of methane support effects. Appl. Catal. A: Gen. 2015, 495, 54-62.(9) Miller, J. B.; Malatpure, M. Pd catalysts for total oxidation of methane support effects. Appl. Catal. A: Gen. 2015, 495, 54-62.

    10. [10]

      (10) Corro, G.; Cano, C.; Fierro, J. L. G. A study of Pt–Pd-Al2O3 catalysts for methane oxidation resistant to deactivation by sulfur poisoning. J. Mol. Catal. A: Chem. 2010, 315, 35-42.(10) Corro, G.; Cano, C.; Fierro, J. L. G. A study of Pt–Pd-Al2O3 catalysts for methane oxidation resistant to deactivation by sulfur poisoning. J. Mol. Catal. A: Chem. 2010, 315, 35-42.

    11. [11]

      (11) Belopukhov, E. A.; Belyi, A. S.; Smolikov, M. D.; Kir'yanov, D. I.; Gulyaeva, T. I. Benzene hydroisomerization over Pt/MOR/Al2O3 catalysts. Catal. Ind. 2012, 4, 253-260.(11) Belopukhov, E. A.; Belyi, A. S.; Smolikov, M. D.; Kir'yanov, D. I.; Gulyaeva, T. I. Benzene hydroisomerization over Pt/MOR/Al2O3 catalysts. Catal. Ind. 2012, 4, 253-260.

    12. [12]

      (12) Kwon, D. K.; Seo, P. W.; Kim, G. J.; Hong, C. Characteristics of the HCHO oxidation reaction over Pt-TiO2 catalysts at room temperature: the effect of relative humidity on catalytic activity. Appl. Catal. B: Environ. 2015, 163, 436-443.(12) Kwon, D. K.; Seo, P. W.; Kim, G. J.; Hong, C. Characteristics of the HCHO oxidation reaction over Pt-TiO2 catalysts at room temperature: the effect of relative humidity on catalytic activity. Appl. Catal. B: Environ. 2015, 163, 436-443.

    13. [13]

      (13) Huang, H. B.; Leung, D. Y. C.; Ye, D. Q. Effect of reduction treatment on structural properties of TiO2 supported Pt nanoparticles and their catalytic activity for formaldehyde oxidation. J. Mater. Chem. 2011, 21, 9647-9652.(13) Huang, H. B.; Leung, D. Y. C.; Ye, D. Q. Effect of reduction treatment on structural properties of TiO2 supported Pt nanoparticles and their catalytic activity for formaldehyde oxidation. J. Mater. Chem. 2011, 21, 9647-9652.

    14. [14]

      (14) Pires, J.; Carvalho, A.; Carvalho, M. B. Adsorption of volatile organic compounds in Y zeolites and pillared clays. Microporous Mesoporous Mater. 2001, 43, 277-287.(14) Pires, J.; Carvalho, A.; Carvalho, M. B. Adsorption of volatile organic compounds in Y zeolites and pillared clays. Microporous Mesoporous Mater. 2001, 43, 277-287.

    15. [15]

      (15) Postole, G.; Gervasini, A.; Guimon, C.; Auroux, A.; Bonnetot, B. Boron nitride supported metal catalysts: influence of the metal and preparation method. Mater. Sci. Forum. 2006, 518, 203-210.(15) Postole, G.; Gervasini, A.; Guimon, C.; Auroux, A.; Bonnetot, B. Boron nitride supported metal catalysts: influence of the metal and preparation method. Mater. Sci. Forum. 2006, 518, 203-210.

    16. [16]

      (16) Haines, B. M.; Gland, J. L. Deep oxidation of chlorobenzene on the Pt(111) surface. Surf. Sci. 2008, 602, 1892-1897.(16) Haines, B. M.; Gland, J. L. Deep oxidation of chlorobenzene on the Pt(111) surface. Surf. Sci. 2008, 602, 1892-1897.

    17. [17]

      (17) Liu, C. H.; Chen, H. Y.; Ren, Z.; Dardona, S.; Piech, M.; Gao, H. Y.; Gao, P. X. Controlled synthesis and structure tunability of photocatalytically active mesoporous metal-based stannate nanostructures. Appl. Surf. Sci. 2014, 296, 53-60.(17) Liu, C. H.; Chen, H. Y.; Ren, Z.; Dardona, S.; Piech, M.; Gao, H. Y.; Gao, P. X. Controlled synthesis and structure tunability of photocatalytically active mesoporous metal-based stannate nanostructures. Appl. Surf. Sci. 2014, 296, 53-60.

    18. [18]

      (18) Fu, X. L.; Huang, D. W.; Qin, Y.; Li, L. F.; Jiang, X. L.; Chen, S. F. Effects of preparation method on the microstructure and photocatalytic performance of ZnSn(OH)6. Appl. Catal. B: Environ. 2014, 148, 532-542.(18) Fu, X. L.; Huang, D. W.; Qin, Y.; Li, L. F.; Jiang, X. L.; Chen, S. F. Effects of preparation method on the microstructure and photocatalytic performance of ZnSn(OH)6. Appl. Catal. B: Environ. 2014, 148, 532-542.

    19. [19]

      (19) Fu, X. L.; Wang, X. X.; Ding, Z. X.; Leung, D. Y. C.; Zhang, Z. Z.; Long, J. L.; Zhang, W. X.; Li, Z. H.; Fu, X. Z. Hydroxide ZnSn(OH)6: a promising new photocatalyst for benzene degradation. Appl. Catal. B: Environ. 2009, 91, 67-72.(19) Fu, X. L.; Wang, X. X.; Ding, Z. X.; Leung, D. Y. C.; Zhang, Z. Z.; Long, J. L.; Zhang, W. X.; Li, Z. H.; Fu, X. Z. Hydroxide ZnSn(OH)6: a promising new photocatalyst for benzene degradation. Appl. Catal. B: Environ. 2009, 91, 67-72.

    20. [20]

      (20) Wang, Z. J.; Liu, J.; Wang, F.; Chen, S. Y.; Luo, H.; Yu, X. B. Size-controlled synthesis of ZnSnO3 cubic crystallites at low temperatures and their HCHO-Sensing properties. J. Phys. Chem. C 2010, 114, 13577-13582.(20) Wang, Z. J.; Liu, J.; Wang, F.; Chen, S. Y.; Luo, H.; Yu, X. B. Size-controlled synthesis of ZnSnO3 cubic crystallites at low temperatures and their HCHO-Sensing properties. J. Phys. Chem. C 2010, 114, 13577-13582.

    21. [21]

      (21) Jiang, H.; Geng, B. Y.; Kuai, L.; Wang, S. Z. Simultaneous reduction-etching route to Pt/ZnSnO3 hollow polyhedral architectures for methanol electrooxidation in alkaline media with superior performance. Chem. Commun. 2011, 47, 2447-2449.(21) Jiang, H.; Geng, B. Y.; Kuai, L.; Wang, S. Z. Simultaneous reduction-etching route to Pt/ZnSnO3 hollow polyhedral architectures for methanol electrooxidation in alkaline media with superior performance. Chem. Commun. 2011, 47, 2447-2449.

    22. [22]

      (22) Jena, H.; Kutty, K. V. G.; Kutty, T. R. N. Ionic transport and structural investigations on MSn(OH)6 (M = Ba, Ca, Mg, Co, Zn, Fe, Mn) hydroxide perovskites synthesized by wet sonochemical methods. Mater. Chem. Phys. 2004, 88, 167-179.(22) Jena, H.; Kutty, K. V. G.; Kutty, T. R. N. Ionic transport and structural investigations on MSn(OH)6 (M = Ba, Ca, Mg, Co, Zn, Fe, Mn) hydroxide perovskites synthesized by wet sonochemical methods. Mater. Chem. Phys. 2004, 88, 167-179.

    23. [23]

      (23) Kramer, J. W.; Isaacs, S. A.; Manivannan, V. Microwave-assisted metathesis synthesis of Schoenfliesite-type MSn(OH)6 (M = Mg, Ca, Zn, and Sr) materials. J. Mater. Sci. 2009, 44, 3387-3392.(23) Kramer, J. W.; Isaacs, S. A.; Manivannan, V. Microwave-assisted metathesis synthesis of Schoenfliesite-type MSn(OH)6 (M = Mg, Ca, Zn, and Sr) materials. J. Mater. Sci. 2009, 44, 3387-3392.

    24. [24]

      (24) Zhong, S.; Xu, R.; Wang, L.; Xu, H. F.; Zhong, S. L. CuSn(OH)6 submicrospheres: room-temperature synthesis, growth mechanism,and weak antiferromagnetic behavior. Mater. Res. Bull. 2011, 46, 2385-2391.(24) Zhong, S.; Xu, R.; Wang, L.; Xu, H. F.; Zhong, S. L. CuSn(OH)6 submicrospheres: room-temperature synthesis, growth mechanism,and weak antiferromagnetic behavior. Mater. Res. Bull. 2011, 46, 2385-2391.

    25. [25]

      (25) Velu, S.; Suzuki, K.; Okazaki, M.; Osaki, T.; Tomura, S.; Ohashi, F. Synthesis of new Sn-incorporated layered double hydroxides and their thermal evolution to mixed oxides. Chem. Mater. 1999, 11, 2163-2172.(25) Velu, S.; Suzuki, K.; Okazaki, M.; Osaki, T.; Tomura, S.; Ohashi, F. Synthesis of new Sn-incorporated layered double hydroxides and their thermal evolution to mixed oxides. Chem. Mater. 1999, 11, 2163-2172.

    26. [26]

      (26) Pramanik, N. C.; Das, S.; Biswas, P. K. The effect of Sn(IV) on transformation of co-precipitated hydrated In(III) and Sn(IV) hydroxides to indium tin oxide (ITO) powder. Mater. Lett. 2002, 56, 671-679.(26) Pramanik, N. C.; Das, S.; Biswas, P. K. The effect of Sn(IV) on transformation of co-precipitated hydrated In(III) and Sn(IV) hydroxides to indium tin oxide (ITO) powder. Mater. Lett. 2002, 56, 671-679.

    27. [27]

      (27) Han, L. X.; Liu, J.; Wang, Z. J.; Zhang, H.; Luo, H.; Xu, B.; Zou, X.; Zheng, X.; Ye, B.; Yu, X. B. Shape-controlled synthesis of ZnSn(OH)6 crystallites and their HCHO-sensing properties. CrystEngComm. 2012, 14, 3380-3386.(27) Han, L. X.; Liu, J.; Wang, Z. J.; Zhang, H.; Luo, H.; Xu, B.; Zou, X.; Zheng, X.; Ye, B.; Yu, X. B. Shape-controlled synthesis of ZnSn(OH)6 crystallites and their HCHO-sensing properties. CrystEngComm. 2012, 14, 3380-3386.

  • 加载中
WeChat 扫一扫看文章
计量
  • PDF下载量:  0
  • 文章访问数:  1937
  • HTML全文浏览量:  45
文章相关
  • 收稿日期:  2015-11-16
  • 网络出版日期:  2016-04-13
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

/

返回文章

All Rights Reserved by the Chinese Chemical Society   中国化学会 版权所有 京ICP备05002797号

本系统由北京仁和汇智信息技术有限公司开发    技术支持: info@rhhz.net