Tough Biopolymer IPN Hydrogel Fibers by Bienzymatic Crosslinking Approach

Citation: Xiao-jiu Liu, Ye-min Zhang, Xin-song Li. Tough Biopolymer IPN Hydrogel Fibers by Bienzymatic Crosslinking Approach[J]. Chinese Journal of Polymer Science, 2015, 33(12): 1741-1749. doi: 10.1007/s10118-015-1717-9 shu

Tough Biopolymer IPN Hydrogel Fibers by Bienzymatic Crosslinking Approach

1.
School of Chemistry and Chemical Engineering, Southeast University, Nanjing 210018, China

通讯作者: Xin-song Li,

基金项目:
This work was financially supported by the National Natural Science Foundation of China(Nos.51373034 and 51073036).

摘要: In this report, bienzymatic crosslinking approach was applied to prepare biopolymer hydrogel fibers composed of gelatin and chitosan with an interpenetrating polymer network(IPN) structure. The IPN biopolymer hydrogel fibers were prepared by wet spinning while microbial transglutaminase(mTG) catalyzed the formation of one network of gelatin and horseradish peroxidase(HRP) in the presence of H2O2 induced another network of chitosan grafted with phloretic acid(chitosan-PA) intertwining with the former. The mechanical performances of the hydrogel fibers were measured by an electronic single fiber strength tester. It was found that the mechanical properties of the gelatin/chitosan IPN hydrogel fibers had a significant improvement with the increase of the concentration of gelatin and chitosan, and the IPN fiber has the highest tension of 38.6 cN and elongation of 387.2%. Accelerated degradation in the presence of papin indicated that the gelatin/chitosan-PA IPN hydrogel fibers own controllable degradability. In addition, biological evaluation indicated the IPN hydrogel fibers can support cell adhesion and proliferation. Moreover, hand weaving trail showed the knittablity of the IPN hydrogel fibers. Therefore, the gelatin/chitosan IPN hydrogel fibers prepared by bienzymatic crosslinking approach possess excellent biocompatibility and mechanical strength, which may be desirable candidates for engineering tissue scaffolds.

关键词:

English

Tough Biopolymer IPN Hydrogel Fibers by Bienzymatic Crosslinking Approach

1.
School of Chemistry and Chemical Engineering, Southeast University, Nanjing 210018, China

Corresponding author: Xin-song Li,

Received Date: 28 May 2015
Revised Date: 18 June 2015
Available Online: 05 December 2015
Fund Project:
This work was financially supported by the National Natural Science Foundation of China(Nos.51373034 and 51073036).

Abstract: In this report, bienzymatic crosslinking approach was applied to prepare biopolymer hydrogel fibers composed of gelatin and chitosan with an interpenetrating polymer network(IPN) structure. The IPN biopolymer hydrogel fibers were prepared by wet spinning while microbial transglutaminase(mTG) catalyzed the formation of one network of gelatin and horseradish peroxidase(HRP) in the presence of H2O2 induced another network of chitosan grafted with phloretic acid(chitosan-PA) intertwining with the former. The mechanical performances of the hydrogel fibers were measured by an electronic single fiber strength tester. It was found that the mechanical properties of the gelatin/chitosan IPN hydrogel fibers had a significant improvement with the increase of the concentration of gelatin and chitosan, and the IPN fiber has the highest tension of 38.6 cN and elongation of 387.2%. Accelerated degradation in the presence of papin indicated that the gelatin/chitosan-PA IPN hydrogel fibers own controllable degradability. In addition, biological evaluation indicated the IPN hydrogel fibers can support cell adhesion and proliferation. Moreover, hand weaving trail showed the knittablity of the IPN hydrogel fibers. Therefore, the gelatin/chitosan IPN hydrogel fibers prepared by bienzymatic crosslinking approach possess excellent biocompatibility and mechanical strength, which may be desirable candidates for engineering tissue scaffolds.

Key words:

1. [1]
  Lin, H.Y., Peng, C.W. and Wu, W.W., J. Mater. Sci. Mater. Med., 2014, 25(1):259
2. [2]
  McCullen, S.D., Haslauer, C.M. and Loboa, E.G., J. Mat. Chem., 2010, 20(40):8776
3. [3]
  Chen, V.J. and Ma, P.X., Biomaterials, 2004, 25(11):2065
4. [4]
  Cui, Z.X., Zhao, H.B., Peng, Y.Y., Srithep, Y., Turng, L.S. and Shen, C.Y., Chinese J. Polym. Sci., 2014, 32(7):864
5. [5]
  Nichol, J.W. and Khademhosseini, A., Soft Matter, 2009, 5(7):1312
6. [6]
  Dragan, E.S., Cocarta, A.L. and Dinu, M.V., Chem. Eng. J., 2014, 243:572
7. [7]
  Wen, C., Lu, L.L. and Li, X.S., Macromol. Mater. Eng., 2014, 299(4):504
8. [8]
  Slaughter, B.V., Khurshid, S.S, Fisher, O.Z., Khademhosseini, A. and Peppas, N.A., Adv. Mater., 2009, 21(32-33):3307
9. [9]
  Meyer, M., Baltzer, H. and Schwikal, K., Mater. Sci. Eng., C, 2010, 30(8):1266
10. [10]
  Billiet, T., Vandenhaute, M., Schelfhout, J., Vlierberghe, S.V. and Dubruel, P., Biomaterials, 2012, 33(26):6020
11. [11]
  Williams, C.G., Malik, A.N., Kim, T.K., Manson, P.N. and Elisseeff, J.H., Biomaterials, 2005, 26(11):1211
12. [12]
  Van Tomme, S.R., van Steenbergen, M.J., De Smedt, S.C., van Nostrum, C.F. and Hennink, W.E., Biomaterials, 2005, 26(14):2129
13. [13]
  Hao, J.K. and Weiss, R.A., Polymer, 2013, 54(8):2174
14. [14]
  Zhang, J.Z., Xiao, C.S., Wang, J.C., Zhuang, X.L. and Chen, X.S., Chinese J. Polym. Sci., 2013, 31(12):1697
15. [15]
  Zhang, Y.B., Ding, J.X., Xu, W.G., Wu, J., Chang, F., Zhuang, X.L., Chen, X.S. and Wang, J.C., Chinese J. Polym. Sci., 2014, 32(12):1590
16. [16]
  Song, G.S., Zhang, L., He, C.C., Fang, D.C., Whitten, P.G. and Wang, H.L., Macromolecules, 2013, 46(18):7423
17. [17]
  Kim, K.S., Park, S.J., Yang, J.A, Jeon, J.H., Bhang, S.H., Kim, B.S. and Hahn, S.K., Acta Biomater., 2011, 7(2):666
18. [18]
  Jin, R., Lou, B. and Lin, C., Polym. Int., 2013, 62(3):353
19. [19]
  Lih, E., Lee, J. S., Park, K.M. and Park, K.D., Acta Biomater., 2012, 8(9):3261
20. [20]
  Tran, N.Q., Joung, Y.K., Lih, E. and Park, K.D., Biomacromolecules, 2011, 12(8):2872
21. [21]
  Zhang, Y.M., Fan, Z.P., Xu, C., Liu, X.J. and Li, X.S., Eur. Polym. J., 2015, doi: 10.1016/j.eurpolymj.2014.12.038
22. [22]
  Association for the Advancement of Medical Instrumentation, Biological Evaluation of Medical Devices:Part 5 Tests for In vitro cytotoxicity, AAMI/ISO 10993-5:2009, Arlington, USA, 2009
23. [23]
  Fuchs, S., Kutscher, M., Hertel, T., Winter, G., Pietzsch, M. and Coester, C., J. Microencapsulation, 2010, 27(8):747
24. [24]
  Yung, C.W., Wu, L.Q., Tullman, J.A., Payne, G.F., Bentley, W.E. and Barbari, T.A., J. Biomed. Mater. Res., A., 2007, 83(4):1039

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 1317
HTML全文浏览量: 38

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Tough Biopolymer IPN Hydrogel Fibers by Bienzymatic Crosslinking Approach

通讯作者: Xin-song Li,

English

Tough Biopolymer IPN Hydrogel Fibers by Bienzymatic Crosslinking Approach

Corresponding author: Xin-song Li,

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

Tough Biopolymer IPN Hydrogel Fibers by Bienzymatic Crosslinking Approach

通讯作者: Xin-song Li,

English

Tough Biopolymer IPN Hydrogel Fibers by Bienzymatic Crosslinking Approach

Corresponding author: Xin-song Li,

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南： 你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

文章相关

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs