Rheological Behaviors of a Series of Hyperbranched Polyethers

Citation: Xue-pei Miao, Yan-shuang Guo, Li-fan He, Yan Meng, Xiao-yu Li. Rheological Behaviors of a Series of Hyperbranched Polyethers[J]. Chinese Journal of Polymer Science, 2015, 33(11): 1574-1585. doi: 10.1007/s10118-015-1707-y shu

Rheological Behaviors of a Series of Hyperbranched Polyethers

1.
Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing 100029, China
2.
TA Instruments-Waters LLC (Beijing), 9/F, Tongniu International Manson, Beijing 100026, China
3.
1. Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing 100029, China
4.
2. State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China
5.
基金项目:
This work was financially supported by the National Natural Science Foundation of China (No. 51173012) and The Fundamental Research Funds for the Central Universities at Beijing University of Chemical Technology.

摘要: Hyperbranched polyethers with different structures and molecular weights (MW) were synthesized using the A2+B3 approach by varying monomer ratio, A2 structure, and reaction time. Effects of backbone structure and MW on melt rheological behaviors were investigated by both small amplitude oscillatory shear and steady shear measurements. Master curves were constructed using the time-temperature superposition principle and compared. In the reduced frequency range covered, lgG~lg(aT) always show a slope of 1.0, suggesting a terminal zone behavior; in contrast, unexpected step changes or plateaus are observed on lgG' master curves. Effects of backbone structure and MW on master curves were discussed. The Cox-Merz rule was tested at different temperatures and was found to be applicable when flow instability was absent.

关键词:

English

Rheological Behaviors of a Series of Hyperbranched Polyethers

1.
Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing 100029, China
2.
TA Instruments-Waters LLC (Beijing), 9/F, Tongniu International Manson, Beijing 100026, China
3.
1. Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing 100029, China
4.
2. State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China
5.
Received Date: 18 April 2015
Revised Date: 30 June 2015
Available Online: 05 November 2015
Fund Project:
This work was financially supported by the National Natural Science Foundation of China (No. 51173012) and The Fundamental Research Funds for the Central Universities at Beijing University of Chemical Technology.

Abstract: Hyperbranched polyethers with different structures and molecular weights (MW) were synthesized using the A2+B3 approach by varying monomer ratio, A2 structure, and reaction time. Effects of backbone structure and MW on melt rheological behaviors were investigated by both small amplitude oscillatory shear and steady shear measurements. Master curves were constructed using the time-temperature superposition principle and compared. In the reduced frequency range covered, lgG~lg(aT) always show a slope of 1.0, suggesting a terminal zone behavior; in contrast, unexpected step changes or plateaus are observed on lgG' master curves. Effects of backbone structure and MW on master curves were discussed. The Cox-Merz rule was tested at different temperatures and was found to be applicable when flow instability was absent.

Key words:

1. [1]
  Yan, D., Gao, C. and H. Frey, Hyperbranched polymers: synthesis, properties and application, Angew. Chem. Int. ed, John Wiley Sons, Inc, Hoboken, New Jersey, 2011, p. 2543
2. [2]
  Lv, J., Meng, Y., He, L., Li, X. and Wang, H., Chinese J. Polym. Sci., 2012, 30(4): 493
3. [3]
  Hawker, C.J., Lee, R. and Frchet, J.M.J., J. Am. Chem. Soc., 1991, 113: 4583
4. [4]
  Ma, L., Wang, H., He, L. and Li, X., Chinese J. Polym. Sci., 2011, 29(3): 300
5. [5]
  Kim, Y.H. and Webster, O.W., Macromolecules, 1992, 25: 5561
6. [6]
  Wu, D., Wu, L., Zhao, Y., Deng, Y., Zhang, H., Zhang, H. and Dong, L., Chinese J. Polym. Sci., 2015, 33(3): 444
7. [7]
  Yin, X., Tan, Y., Song, Y. and Zheng, Q., Chinese J. Polym. Sci., 2012, 30(1): 26
8. [8]
  Hsieh, T.T., Tiu, C. and Simon, G.P., Polymer, 2001, 42: 1931
9. [9]
  Choi, J., Chung, J.W., Jang, S.H. and Kwak, S.Y., J. Polym. Sci., Part B: Polym. Phys., 2008, 46: 2079
10. [10]
  Magnusson, H., Malmstrm, E., Hult, A. and Johansson, M., Polymer, 2002, 43: 301
11. [11]
  Kharchenko, S.B. and Kannan, R.M., Macromolecules, 2003, 36: 407
12. [12]
  Kharchenko, S.B., Kannan, R.M., Cernohous, J.J. and Venkataramani, S., Macromolecules, 2003, 36: 399
13. [13]
  Sendijarevic, I. and McHugh, A.J., Macromolecules, 2000, 33: 590
14. [14]
  Wood-Adams, P.M., Dealy, J.M., Degroot, A.W. and Redwine, O.D., Macromolecules, 2000, 33: 7489
15. [15]
  Emrick, T., Chang, H.T. and Frchet, J.M.J., J. Polym. Sci., Part A: Polym. Chem., 2000, 38: 4850
16. [16]
  Emrick, T., Chang, H.T. and Frchet, J.M.J., Macromolecules, 1999, 32: 6380
17. [17]
  Turner, S.R., Voit, B.I. and Mourey, T.H., Macromolecules, 1993, 26: 4617
18. [18]
  Turner, S.R., Walter, F., Voit, B.I. and Mourey, T.H., Macromolecules, 1994, 27: 1611
19. [19]
  Chen, Z.Y. and Cui, S.M., Macromolecules, 1996, 29: 7943
20. [20]
  Mansfield, M.L. and Klushin, L.I., Macromolecules, 1993, 26: 4262
21. [21]
  Mansfield, M.L., Polymer, 1994, 35: 1827
22. [22]
  Hawker, C.J. and Frchet, J.M.J., J. Am. Chem. Soc., 1990, 112: 7638
23. [23]
  Uppuluri, S., Morrison, F.A. and Dvornic, P.R., Macromolecules, 2000, 33: 2551
24. [24]
  Vukovi?, J., Jovanovi?, S., Lechner, M.D. and Vodnik, V., J. Appl. Polym. Sci., 2009, 112: 2925
25. [25]
  Lyulin, A.V., Adolf, D.B. and Davies, G.R., Macromolecules, 2001, 34: 3783
26. [26]
  Tu Cam Le. Computer simulation of hyperbranched polymer melts under shear, Doctoral thesis, Swinburne University of Technology (Australia), 2010
27. [27]
  Ahn, D.U. and Kwak, S.Y., Macromol. Mater. Eng., 2001, 286: 17
28. [28]
  Han, C.D. and Kim, J.K., Macromolecules, 1989, 22: 4292
29. [29]
  Han, C.D. and Jhon, M.S., J. Appl. Polym. Sci., 1986, 32: 3809
30. [30]
  Van Gurp, M. and Palmen, J., Rheol. Bull., 1998, 67: 5
31. [31]
  Carella, J.M., Gotro, J.T. and Graessley, W.W., Macromolecules, 1986, 19: 659
32. [32]
  Graessley, W.W., Macromolecules, 1982, 15: 1164
33. [33]
  Ferry, J. D., Viscoelastic properties of polymers, 3rd ed, Wiley-Interscience, New York, 1980
34. [34]
  Scherrenberg, R., Coussens, B., van Vliet, P., Edouard, G., Brackman, J., de Brabander, E. and Mortensen, K., Macromolecules, 1998, 31: 456
35. [35]
  Lescanec, R.L. and Muthukumar, M., Macromolecules, 1990, 23: 2280
36. [36]
  Ye, Z., AlObaidi, F. and Zhu, S., Macromol. Chem. Phys., 2004, 205: 897
37. [37]
  Jackson, J.K. and Winter, H.H., Rheol. Acta, 1996, 35: 645
38. [38]
  Jackson, J.K. and Winter, H.H., Macromolecules, 1995, 28: 3146
39. [39]
  Struglinski, M.J., Doctoral Thesis, Northwestern University 1984, as cited in Graessley WW, Chap. 10 of Polymer liquids and networks dynamics and rheology, Garland Science, London, 2008
40. [40]
  Rattamaprom, C. and Larso, R.G., Rheol. Acta, 2001, 40: 516
41. [41]
  Riemann, R.E., Cantow, H.J. and Friedrich, C., Polym. Bull., 1996, 36: 637
42. [42]
  Riemann, R.E., Cantow, H.J. and Friedrich, C., Macromolecules, 1997, 30: 5476
43. [43]
  Clarke, N., Luca, E.D., Dodds, J.M., Kimani, S.M. and Hutchings, L.R., Eur. Polym. J., 2008, 44: 665
44. [44]
  Jahromi, S., Palmen, J.H.M. and Steeman, P.A.M., Macromolecules, 2000, 33: 577
45. [45]
  Bird, R.B., Curtiss, C.F., Armstrong, R.C. and Hassager, O., Dynamics of polymeric liquids, 2nd ed., John Wiley Sons, New York, 1987
46. [46]
  Tande, B.M., Wagner, N.J. and Kim, Y.H., Macromolecules, 2003, 36: 4619
47. [47]
  Li, Y., Hu, M. and McKenna, G.B., J. Rheol., 2013, 57: 1411
48. [48]
  Sui, C. and McKenna, G.B., Rheol. Acta, 2007, 46: 877
49. [49]
  Sui, C. and McKenna, G.B., J. Rheol., 2007, 51: 341
50. [50]
  Marrucci, G.J., J. Non-Newtonian. Fluid. Mech., 1996, 62: 279
51. [51]
  Mhetar, V. and Archer, L.A., J. Non-Newtonian. Fluid. Mech., 1999, 81: 71
52. [52]
  Adams, N. and Lodge, A.S., Phil. Trans. R. Soc. Lond. A, 1964, 256: 149
53. [53]
  Alcoutlabi, M., Baek, S.G., Magda, J.J., Shi, X., Hutcheson, S.A. and Mckenna, G.B., Rheol. Acta, 2009, 48: 191

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 1344
HTML全文浏览量: 20

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Rheological Behaviors of a Series of Hyperbranched Polyethers

English

Rheological Behaviors of a Series of Hyperbranched Polyethers

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

Rheological Behaviors of a Series of Hyperbranched Polyethers

English

Rheological Behaviors of a Series of Hyperbranched Polyethers

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南： 你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

文章相关

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs