Citation: Li Zhiwei, Zhong Jialiang, Chen Nannan, Xue Bing, Mi Hongyu. Template-Assisted Preparation and Lithium Storage Performance of Nitrogen Doped Porous Carbon Sheets[J]. Acta Chimica Sinica, ;2018, 76(3): 209-214. doi: 10.6023/A17090425 shu

Template-Assisted Preparation and Lithium Storage Performance of Nitrogen Doped Porous Carbon Sheets

a.
Xinjiang Uygur Autonomous Region Key Laboratory of Clean Coal Conversion and Chemical Process, Xinjiang University, Urumqi 830046
b.
Department of Materials Science and Engineering, Jilin University, Changchun 130025

Corresponding author: Mi Hongyu, mmihongyu@163.com
Received Date: 18 September 2017
Available Online: 22 March 2018
Fund Project: Project supported by the National Natural Science Foundation of China (No. 21563029) and the Natural Science Foundation of Xinjiang Uygur Autonomous Region (No. 2014211A015)the Natural Science Foundation of Xinjiang Uygur Autonomous Region 2014211A015the National Natural Science Foundation of China 21563029

Figures(8)

Nitrogen doped porous carbon sheets (NPCSs) having high lithium storage performance were successfully prepared by a template-assisted approach using magnesium oxide/melamine/polyethylene glycol (MgO/melamine/PEG) as raw materials. In a typical procedure, the precursor, which consisted of MgO, melamine and PEG in a mass ratio of 7:3:10, was carbonized at 700℃ for 3 h in a temperature-programmed tubular furnace under N₂ flow with a heating rate of 5℃·min^-1. The intermediate was immersed into 3 mol·L^-1 HCl solution for several times to remove MgO. Subsequently, the sample was rinsed with water and ethanol until a neutral pH was obtained, and then dried at 80℃ in a vacuum oven. The sample was systematically characterized and analyzed by Fourier transform infrared spectrometer (FTIR), X-ray powder diffractometer (XRD), X-ray photoelectron spectrometer (XPS), scanning electron microscope (SEM), transmission electron microscope (TEM), cyclic voltammetry (CV), galvanostatic charge/discharge (GCD) and electrochemical impedance spectroscopy (EIS). The results indicated that NPCSs showed an interconnected porous carbon sheet networks, showing relatively high specific surface area (370.8 m²·g^-1), hierarchical pore channels, and high nitrogen content (8.5 at%). Such a continuous porous structure could enhance the electron transport on three-dimensional direction, shorten the diffusion distance of lithium ions, enlarge the interface area between lithium ion and electrolyte, and provide the place for the accommodation of lithium ions. Additionally, high N-doping level in NPCSs could provide numerous activated sites for the intercalation and deintercalation of lithium ions, and enhance the electronic conductivity. Based on the unique structure, NPCSs electrode could exhibit high initial reversible specific capacities (after excluding the contribution of acetylene black, 914 mAh·g^-1 at 100 mA·g^-1) and good cycling stability (still remaining a specific capacity of 523 mAh·g^-1 at 1000 mA·g^-1 up to 300 cycles). Moreover, NPCSs displayed high rate capability with a reversible capacity of 355 mAh·g^-1 at a current density of 3000 mA·g^-1. Therefore, the NPCSs obtained are expectable to be widely used as anode material in lithium-ion batteries.
- porous carbon sheet,
- carbonization-etching method,
- anode,
- Lithium-ion battery
1. [1]
  Dunn, B.; Kamath, H.; Tarascon, J. M. Science 2011, 334, 928. doi: 10.1126/science.1212741
2. [2]
  Yoshino, A. Angew. Chem. Int. Ed. 2012, 51, 5798. doi: 10.1002/anie.201105006
3. [3]
  Zheng, Z.; Wu, Z. G.; Xiang, W.; Guo, X. D. Acta Chim. Sinica 2017, 75, 501. doi: 10.11862/CJIC.2017.053
4. [4]
  Lv, Z. Y.; Feng, R.; Zhao, J.; Fan, H.; Xu, D.; Wu, Q.; Yang, L. J.; Chen, Q.; Wang, X. Z.; Hu, Z. Acta Chim. Sinica 2015, 73, 1013.
5. [5]
  Palacín, M. R. Chem. Soc. Rev. 2009, 38, 2565. doi: 10.1039/b820555h
6. [6]
  Li, H.; Wang, Z. X.; Chen, L. Q.; Huang, X. J. Adv. Mater. 2009, 21, 4593. doi: 10.1002/adma.v21:45
7. [7]
  Xu, Y. X.; Lin, Z. Y.; Zhong, X.; Papandrea, B.; Huang, Y.; Duan, X. F. Angew. Chem., Int. Ed. 2015, 54, 5345. doi: 10.1002/anie.201500677
8. [8]
  Ou, J. K.; Zhang, Y. Z.; Chen, L.; Zhao, Q.; Meng, Y.; Guo, Y.; Xiao, D. J. Mater. Chem. A 2015, 3, 6534. doi: 10.1039/C4TA06614F
9. [9]
  Du, J.; Lin, N.; Qian, Y. T. Acta Chim. Sinica 2017, 75, 147. doi: 10.3969/j.issn.0253-2409.2017.02.003
10. [10]
  Zhang, N.; Zhao, Q.; Han, X. P.; Yang, J. G.; Chen, J. Nanoscale 2014, 6, 2827. doi: 10.1039/C3NR05523J
11. [11]
  Zhu, X.; Ning, G. Q.; Ma, X. L.; Fan, Z. J.; Xu, C. G.; Gao, J. S.; Xu, C. M.; Wei, F. J. Mater. Chem. A 2013, 1, 14023. doi: 10.1039/c3ta12824e
12. [12]
  Etacheri, V.; Haik, O.; Goffer, Y.; Roberts, G. A.; Stefan, I. C.; Fasching, R.; Aurbach, D. Langmuir 2012, 28, 965. doi: 10.1021/la203712s
13. [13]
  Nan, D.; Huang, Z. Y.; Kang, F. Y.; Shen, W. C. New Carbon Materials 2016, 31, 393.
14. [14]
  Bulusheva, L. G.; Arkhipov, V. E.; Fedorovskaya, E. O.; Zhang, S.; Kurenya, A. G.; Kanygin, M. A.; Asanov, I. P.; Tsygankova, A. R.; Chen, X. H.; Song, H. H.; Okotrub, A. V. J. Power Sources 2016, 311, 42. doi: 10.1016/j.jpowsour.2016.02.036
15. [15]
  Wen, L.; Liu, C. M.; Song, R. S.; Luo, H. Z.; Shi, Y.; Li, F.; Chen, H. M. Acta Chim. Sinica 2014, 72, 333.
16. [16]
  Chen, M.; Yu, C.; Liu, S. H.; Fan, X. M.; Zhao, C. T.; Zhang, X.; Qiu, J. S. Nanoscale 2015, 7, 1791. doi: 10.1039/C4NR05878J
17. [17]
  Zhang, L. J.; Xia, G. L.; Guo, Z. P.; Sun, D. L.; Li, X. G.; Yu, X. B. J. Power Sources 2016, 324, 294. doi: 10.1016/j.jpowsour.2016.05.057
18. [18]
  Li, D. D.; Ding, L. X.; Chen, H. B.; Wang, S. Q.; Li, Z.; Zhu, M.; Wang, H. H. J. Mater. Chem. A 2014, 2, 16617. doi: 10.1039/C4TA03281K
19. [19]
  Roberts, A. D.; Wang, S. X.; Li, X.; Zhang, H. F. J. Mater. Chem. A 2014, 2, 17787.
20. [20]
  Akiyama, T.; Zhu, C. Y. Green Chem. 2016, 18, 2106. doi: 10.1039/C5GC02397A
21. [21]
  Wang, C. Y.; Feng, L. L.; Li, W.; Zheng, J.; Tian, W. H.; Li, X. G. Solar Energy Mater. Solar Cells 2012, 105, 21. doi: 10.1016/j.solmat.2012.05.031
22. [22]
  Zhong, J. L.; Guo, F. J.; Mi, H. Y. Chinese J. Inorg. Chem. 2015, 31, 2128.
23. [23]
  Zhang, X. J.; Zhu, G.; Wang, M.; Li, J. B.; Lu, T.; Pan, L. K. Carbon 2017, 116, 686. doi: 10.1016/j.carbon.2017.02.057
24. [24]
  Guo, N. N.; Li, M.; Wang, H.; Sun, X. K.; Wang, F.; Yang, R. RSC Adv. 2016, 6, 101372. doi: 10.1039/C6RA22426A
25. [25]
  Pumera, M. Energy Environ. Sci. 2011, 4, 668. doi: 10.1039/C0EE00295J
26. [26]
  You, L. J.; Zhang, Y. T.; Xu, S.; Guo, J.; Wang, C. C. ACS Appl. Mater. Interfaces 2014, 6, 15179. doi: 10.1021/am503421z
27. [27]
  Huang, C. W.; Wu, Y. T.; Hu, C. C.; Li, Y. Y. J. Power Sources 2007, 172, 460. doi: 10.1016/j.jpowsour.2007.07.009
28. [28]
  Wang, S. X.; Chen, S. L.; Wei, Q. L.; Zhang, X. K.; Wong, S. Y.; Sun, S. H.; Li, X. Chem. Mater. 2015, 27, 336. doi: 10.1021/cm504042s
29. [29]
  Jeong, H. M.; Lee, J. W.; Shin, W. H.; Choi, Y. J.; Shin, H. J.; Kang, J. K.; Choi, J. W. Nano Lett. 2011, 11, 2472. doi: 10.1021/nl2009058
30. [30]
  Li, Z.; Xu, Z. W.; Tan, X. H.; Wang, H. L.; Holt, C. M. B.; Stephenson, T.; Olsen, B. C.; Mitlin, D. Energy Environ. Sci. 2013, 6, 871. doi: 10.1039/c2ee23599d
31. [31]
  Wang, H. G.; Wang, Y. H.; Li, Y. H.; Wan, Y. C.; Duan, Q. Carbon 2015, 82, 116. doi: 10.1016/j.carbon.2014.10.041
32. [32]
  Sui, Z. Y.; Wang, C. Y.; Yang, Q. S.; Shu, K. W.; Liu, Y. W.; Han, B. H.; Wallace, G. G. J. Mater. Chem. A 2015, 3, 18229. doi: 10.1039/C5TA05759K
33. [33]
  Chang, K.; Chen, W. X. ACS Nano 2011, 5, 4720. doi: 10.1021/nn200659w
34. [34]
  Etacheri, V.; Hong, C. N.; Pol, V. G. Environ. Sci. Technol. 2015, 49, 11191. doi: 10.1021/acs.est.5b01896
35. [35]
  Zhu, C. Y.; Akiyama, T. Green Chem. 2015, 18, 2106.
36. [36]
  Song, R.; Song, H. H.; Zhou, J. S.; Chen, X. T.; Wu, B.; Yang, H. Y. J. Mater. Chem. 2012, 22, 12369. doi: 10.1039/c2jm31910a
37. [37]
  Ou, J. K.; Yang, L.; Zhang, Y. Z.; Chen, L.; Guo, Y.; Xiao, D. Chinese J. Chem. 2015, 33, 1293. doi: 10.1002/cjoc.v33.11
38. [38]
  Qie, L.; Chen, W. M.; Wang, Z. H.; Shao, Q. G.; Li, X.; Yuan, L. X.; Hu, X. L.; Zhang, W. X.; Huang, Y. H. Adv. Mater. 2012, 24, 2047. doi: 10.1002/adma.201104634
39. [39]
  He, B.; Li, W. C.; Lu, A. H. J. Mater. Chem. A 2015, 3, 579. doi: 10.1039/C4TA05056H
40. [40]
  Zhang, W. L.; Yin, J.; Lin, Z. Q.; Lin, H. B.; Lu, H. Y.; Wang, Y.; Huang, W. M. Electrochim. Acta 2015, 176, 1136. doi: 10.1016/j.electacta.2015.08.001
1. [1]
  Qi Li , Pingan Li , Zetong Liu , Jiahui Zhang , Hao Zhang , Weilai Yu , Xianluo Hu . Fabricating Micro/Nanostructured Separators and Electrode Materials by Coaxial Electrospinning for Lithium-Ion Batteries: From Fundamentals to Applications. Acta Physico-Chimica Sinica, 2024, 40(10): 2311030-. doi: 10.3866/PKU.WHXB202311030
2. [2]
  Qingtang ZHANG , Xiaoyu WU , Zheng WANG , Xiaomei WANG . Performance of nano Li₂FeSiO₄/C cathode material co-doped by potassium and chlorine ions. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1689-1696. doi: 10.11862/CJIC.20240115
3. [3]
  Yifeng Xu , Jiquan Liu , Bin Cui , Yan Li , Gang Xie , Ying Yang . “Xiao Li’s School Adventures: The Working Principles and Safety Risks of Lithium-ion Batteries”. University Chemistry, 2024, 39(9): 259-265. doi: 10.12461/PKU.DXHX202404009
4. [4]
  Siyu Zhang , Kunhong Gu , Bing'an Lu , Junwei Han , Jiang Zhou . Hydrometallurgical Processes on Recycling of Spent Lithium-lon Battery Cathode: Advances and Applications in Sustainable Technologies. Acta Physico-Chimica Sinica, 2024, 40(10): 2309028-. doi: 10.3866/PKU.WHXB202309028
5. [5]
  Yuanchao LI , Weifeng HUANG , Pengchao LIANG , Zifang ZHAO , Baoyan XING , Dongliang YAN , Li YANG , Songlin WANG . Effect of heterogeneous dual carbon sources on electrochemical properties of LiMn_0.8Fe_0.2PO₄/C composites. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 751-760. doi: 10.11862/CJIC.20230252
6. [6]
  Xinpeng LIU , Liuyang ZHAO , Hongyi LI , Yatu CHEN , Aimin WU , Aikui LI , Hao HUANG . Ga₂O₃ coated modification and electrochemical performance of Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ cathode material. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1105-1113. doi: 10.11862/CJIC.20230488
7. [7]
  Junke LIU , Kungui ZHENG , Wenjing SUN , Gaoyang BAI , Guodong BAI , Zuwei YIN , Yao ZHOU , Juntao LI . Preparation of modified high-nickel layered cathode with LiAlO₂/cyclopolyacrylonitrile dual-functional coating. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1461-1473. doi: 10.11862/CJIC.20240189
8. [8]
  Zhihuan XU , Qing KANG , Yuzhen LONG , Qian YUAN , Cidong LIU , Xin LI , Genghuai TANG , Yuqing LIAO . Effect of graphene oxide concentration on the electrochemical properties of reduced graphene oxide/ZnS. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1329-1336. doi: 10.11862/CJIC.20230447
9. [9]
  Zhenming Xu , Mingbo Zheng , Zhenhui Liu , Duo Chen , Qingsheng Liu . Experimental Design of Project-Driven Teaching in Computational Materials Science: First-Principles Calculations of the LiFePO₄ Cathode Material for Lithium-Ion Batteries. University Chemistry, 2024, 39(4): 140-148. doi: 10.3866/PKU.DXHX202307022
10. [10]
  Doudou Qin , Junyang Ding , Chu Liang , Qian Liu , Ligang Feng , Yang Luo , Guangzhi Hu , Jun Luo , Xijun Liu . Addressing Challenges and Enhancing Performance of Manganese-based Cathode Materials in Aqueous Zinc-Ion Batteries. Acta Physico-Chimica Sinica, 2024, 40(10): 2310034-. doi: 10.3866/PKU.WHXB202310034
11. [11]
  Zhihong LUO , Yan SHI , Jinyu AN , Deyi ZHENG , Long LI , Quansheng OUYANG , Bin SHI , Jiaojing SHAO . Two-dimensional silica-modified polyethylene oxide solid polymer electrolyte to enhance the performance of lithium-ion batteries. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 1005-1014. doi: 10.11862/CJIC.20230444
12. [12]
  Qingyan JIANG , Yanyong SHA , Chen CHEN , Xiaojuan CHEN , Wenlong LIU , Hao HUANG , Hongjiang LIU , Qi LIU . Constructing a one-dimensional Cu-coordination polymer-based cathode material for Li-ion batteries. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 657-668. doi: 10.11862/CJIC.20240004
13. [13]
  Jie XIE , Hongnan XU , Jianfeng LIAO , Ruoyu CHEN , Lin SUN , Zhong JIN . Nitrogen-doped 3D graphene-carbon nanotube network for efficient lithium storage. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1840-1849. doi: 10.11862/CJIC.20240216
14. [14]
  Jianbao Mei , Bei Li , Shu Zhang , Dongdong Xiao , Pu Hu , Geng Zhang . Enhanced Performance of Ternary NASICON-Type Na_3.5-xMn_0.5V_1.5-xZr_x(PO₄)₃/C Cathodes for Sodium-Ion Batteries. Acta Physico-Chimica Sinica, 2024, 40(12): 2407023-. doi: 10.3866/PKU.WHXB202407023
15. [15]
  Hong LI , Xiaoying DING , Cihang LIU , Jinghan ZHANG , Yanying RAO . Detection of iron and copper ions based on gold nanorod etching colorimetry. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 953-962. doi: 10.11862/CJIC.20230370
16. [16]
  Zhaomei LIU , Wenshi ZHONG , Jiaxin LI , Gengshen HU . Preparation of nitrogen-doped porous carbons with ultra-high surface areas for high-performance supercapacitors. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 677-685. doi: 10.11862/CJIC.20230404
17. [17]
  Wendian XIE , Yuehua LONG , Jianyang XIE , Liqun XING , Shixiong SHE , Yan YANG , Zhihao HUANG . Preparation and ion separation performance of oligoether chains enriched covalent organic framework membrane. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1528-1536. doi: 10.11862/CJIC.20240050
18. [18]
  Guang Huang , Lei Li , Dingyi Zhang , Xingze Wang , Yugai Huang , Wenhui Liang , Zhifen Guo , Wenmei Jiao . Cobalt’s Valor, Nickel’s Foe: A Comprehensive Chemical Experiment Utilizing a Cobalt-based Imidazolate Framework for Nickel Ion Removal. University Chemistry, 2024, 39(8): 174-183. doi: 10.3866/PKU.DXHX202311051
19. [19]
  Xiaoning TANG , Shu XIA , Jie LEI , Xingfu YANG , Qiuyang LUO , Junnan LIU , An XUE . Fluorine-doped MnO₂ with oxygen vacancy for stabilizing Zn-ion batteries. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1671-1678. doi: 10.11862/CJIC.20240149
20. [20]
  Xiaoning TANG , Junnan LIU , Xingfu YANG , Jie LEI , Qiuyang LUO , Shu XIA , An XUE . Effect of sodium alginate-sodium carboxymethylcellulose gel layer on the stability of Zn anodes. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1452-1460. doi: 10.11862/CJIC.20240191

Get Citation

PDF

XML

Metrics

PDF Downloads(4)
Abstract views(1058)
HTML views(226)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142