Citation: Hongyi LI, Aimin WU, Liuyang ZHAO, Xinpeng LIU, Fengqin CHEN, Aikui LI, Hao HUANG. Effect of Y(PO3)3 double-coating modification on the electrochemical properties of Li[Ni0.8Co0.15Al0.05]O2[J]. Chinese Journal of Inorganic Chemistry, ;2024, 40(7): 1320-1328. doi: 10.11862/CJIC.20230480 shu

Effect of Y(PO3)3 double-coating modification on the electrochemical properties of Li[Ni0.8Co0.15Al0.05]O2

  • 1.

    Key Laboratory of Energy Materials and Device (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian, Liaoning 116024, China

  • 2.

    Shaanxi Coal Chemical Industry Technology Research Institute Co., Ltd., Xi'an 710065, China

  • 3.

    School of Electrical Engineering, Dalian University of Technology, Dalian, Liaoning 116024, China

Figures(7)

  • Aiming at the difficulty that the alkaline substances left on the surface of Li[Ni0.8Co0.15Al0.05]O2 (NCA) precursor preparation and lithium preparation sintering process can seriously affect its cycling stability performance, a proposal was made to employ Y(PO3)3 for surface coating modification. This modification involves utilizing Y(PO3)3 to react with the surface residual LiOH to eliminate surface residual alkali and investigate the impact mechanism of coating modification on the overall performance of NCA. The thickness of the cladding layer was not affected by the residual alkali content on the surface. Test analysis results demonstrate that during low-temperature calcination, a uniform and dense coating layer of Y(PO3)3 and LiPO3 formed on the precursor's surface. LiPO3 exhibited higher ionic conductivity, and the dual coating layer can prevent harmful side reactions between the active material and the electrolyte during the electrochemical cycling process, enhancing the cycling stability of the electrode material. Specifically, for samples with a mass fraction of 1% Y(PO3)3 coating, at 0.1C, the initial Coulombic efficiency increased from 78.65% for unmodified samples to 88.50%. After 150 cycles at 1C, the capacity retention rate increased from 59.38% to 85.33%. Compared to unmodified samples, it showed higher initial Coulombic efficiency and superior cycling performance.
  • 加载中
    1. [1]

      LI X, GE W J, MA X G, PENG G C. Research progress on countermeasures for microcrack-induced capacity degradation of Ni-rich cathode materials[J]. Chem. Ind. Eng. Prog., 2022,41(8):4277-4287.  

    2. [2]

      LUO J, LIU J X, HUANG L, XIAO F M, LI W C, TANG R H, WANG Y. Preparation and performance characterization of LiNi0.88Co0.07 Al0.05O2, a high nickel system cathode material[J]. Chinese J. Inorg. Chem., 2021,37(1):110-120.  

    3. [3]

      Bianchini M, Roca-Ayats M, Hartmann P, Brezesinski T, Janek J. There and back again-the journey of LiNiO2 as a cathode active material[J]. Angew. Chem. Int. Ed., 2019,58(31):10434-10458. doi: 10.1002/anie.201812472

    4. [4]

      Yang J S, Li P, Zhong F P, Feng X M, Chen W H, Ai X P, Yang H X, Xia D G, Cao Y L. Suppressing voltage fading of Li-rich oxide cathode via building a well-protected and partially-protonated surface by polyacrylic acid binder for cycle-stable Li-ion batteries[J]. Adv. Energy Mater., 2020,10(15)1904264. doi: 10.1002/aenm.201904264

    5. [5]

      HUANG L, ZHANG C Z, TAN J. Effect of calcination time on structure and characterization of a full concentration-gradient LiNi0.80Co0.15 Al0.05O2 cathode material[J]. Chinese J. Inorg. Chem., 2023,39(5):979-991.  

    6. [6]

      Natarajan S, Moodakare S B, Haridoss P, Gopalan R. Concentration gradient-driven aluminum diffusion in a single-step coprecipitation of a compositionally graded precursor for LiNi0.8Co0.135Al0.065O2 with mitigated irreversibility of H2 ⇆ H3 phase transition[J]. ACS Appl. Mater. Interfaces, 2020,12(31):34959-34970. doi: 10.1021/acsami.0c08502

    7. [7]

      Kato Y, Nagahara A, Gerile N, Fujinaka S, Hamamoto N, Nishimura H, Nakai H. Investigation of water-washing effect on electrochemical properties of Ni-rich NCA cathode material for lithium-ion batteries[J]. J. Electrochem. Soc., 2022,169(6)60543. doi: 10.1149/1945-7111/ac79d6

    8. [8]

      MAO G H, XIAO F M, TANG R H, HUANG L, LI J, WANG Y. Effect of water washing and re-sintering treatment on microstructure and electrochemical properties of high nickel ternary material LiNi0.88 Co0.07Al0.05O2[J]. Chinese J. Inorg. Chem., 2021,37(9):1649-1658.  

    9. [9]

      Zou L F, Zhao W G, Jia H P, Zheng J M, Li L Z, Abraham D P, Chen G Y, Croy J R, Zhang J G, Wang C M. The role of secondary particle structures in surface phase transitions of Ni-rich cathodes[J]. Chem. Mat., 2020,32(7):2884-2892. doi: 10.1021/acs.chemmater.9b04938

    10. [10]

      Cheng W D, Hao S, Ji Y Y, Li L, Liu L, Xiao Y, Wu Y X, Huo J S, Tang F, Liu X Q. Optimizing surface residual alkali and enhancing electrochemical performance of LiNi0.8Co0.15Al0.05O2 cathode by LiH2PO4[J]. Nanotechnology, 2021,33(4)045404.

    11. [11]

      Tang Z F, Wu R, Huang P F, Wang Q S, Chen C H. Improving the electrochemical performance of Ni-rich cathode material LiNi0.815 Co0.15Al0.035O2 by removing the lithium residues and forming Li3PO4 coating layer[J]. J. Alloy. Compd., 2017,693:1157-1163. doi: 10.1016/j.jallcom.2016.10.099

    12. [12]

      HUANG L, WANG Y, TANG R H, XIAO F M, LI W C. Effect of surfactant on structure and properties of LiNi0.80Co0.15Al0.05O2[J]. Chinese J. Inorg. Chem., 2020,36(8):1465-1474.  

    13. [13]

      Ha T H, Park J S, Cho G B, Ahn H J, Kim K W, Ahn J H, Cho K K. The Effect of Si doping or/and Ti coating on the electrochemical properties of Ni-rich NCA (LiNi0.8Co0.15Al0.05O2) cathode material for lithium-ion batteries[J]. Sci. Adv. Mater., 2020,12(10):1581-1585. doi: 10.1166/sam.2020.3797

    14. [14]

      Zhang X W, Liu G B, Li S M, Dong H, Liu H, Mei J. Preparation of a homogeneous Li3PO4 coating and its effect on the electrochemical properties of LiNi0.8Co0.15Al0.05O2[J]. J. Electron. Mater., 2019,48(7):4443-4451. doi: 10.1007/s11664-019-07223-5

    15. [15]

      Feng Z, Rajagopalan R, Sun D, Tang Y G, Wang H Y. In-situ formation of hybrid Li3PO4-AlPO4-Al(PO3)3 coating layer on LiNi0.8Co0.1 Mn0.1O2 cathode with enhanced electrochemical properties for lithium-ion battery[J]. Chem. Eng. J., 2020,382122959. doi: 10.1016/j.cej.2019.122959

    16. [16]

      Zhang M L, Zhao H Y, Tan M, Liu J T, Hu Y Z, Liu S S, Shu X H, Li H, Ran Q W, Cai J J, Liu X Q. Yttrium modified Ni-rich LiNi0.8Co0.1 Mn0.1O2 with enhanced electrochemical performance as high energy density cathode material at 4.5 V high voltage[J]. J. Alloy. Compd., 2019,774:82-92. doi: 10.1016/j.jallcom.2018.09.281

    17. [17]

      Xia S B, Huang W J, Shen X, Liu J M, Cheng F X, Liu J J, Yang X F, Guo H. Rearrangement on surface structures by boride to enhanced cycle stability for LiNi0.80Co0.15Al0.05O2 cathode in lithium ion batteries[J]. J. Energy Chem., 2020,45:110-118. doi: 10.1016/j.jechem.2019.09.023

    18. [18]

      Money B K, Hariharan K. Phase dependent heterogeneous dynamics of Li+ ion in LiPO3 based systems[J]. Integr. Ferroelectr., 2010,120(1):75-89. doi: 10.1080/10584587.2010.491729

    19. [19]

      Tang Z F, Bao J J, Du Q X, Shao Y, Gao M H, Zou B K, Chen C H. Surface surgery of the nickel-rich cathode material LiNi0.815Co0.15 Al0.035O2: Toward a complete and ordered surface layered structure and better electrochemical properties[J]. ACS Appl. Mater. Interfaces, 2016,8(50):34879-34887. doi: 10.1021/acsami.6b11431

    20. [20]

      Che W, Wan X W, Zhang D Y, Chang C K. Stabilized performance of LiNi0.90Co0.07Al0.03O2 cathodes via Zr4+ doping upon 4.5 V application due to the suppression of H2-H3 phase transitions[J]. ACS Sustain. Chem. Eng., 2021,9(16):5536-5545. doi: 10.1021/acssuschemeng.0c08736

    21. [21]

      Huang B, Li X H, Wang Z X, Guo H J, Xiong X H. Synthesis of Mg-doped LiNi0.8Co0.15Al0.05O2 oxide and its electrochemical behavior in high-voltage lithium-ion batteries[J]. Ceram. Int., 2014,40(8):13223-13230. doi: 10.1016/j.ceramint.2014.05.029

    22. [22]

      Noh H J, Youn S, Yoon C S, Sun Y K. Comparison of the structural and electrochemical properties of layered Li[NixCoyMnz]O2 (x=1/3, 0.5, 0.6, 0.7, 0.8 and 0.85) cathode material for lithium-ion batteries[J]. J. Power Sources, 2013,233:121-130. doi: 10.1016/j.jpowsour.2013.01.063

  • 加载中
    1. [1]

      Yongming Zhu ,  Huili Hu ,  Yuanchun Yu ,  Xudong Li ,  Peng Gao . Construction and Practice on New Form Stereoscopic Textbook of Electrochemistry for Energy Storage Science and Engineering: Taking Basic Course of Electrochemistry as an Example. University Chemistry, 2024, 39(8): 44-47. doi: 10.3866/PKU.DXHX202312086

    2. [2]

      Kuaibing Wang ,  Honglin Zhang ,  Wenjie Lu ,  Weihua Zhang . Experimental Design and Practice for Recycling and Nickel Content Detection from Waste Nickel-Metal Hydride Batteries. University Chemistry, 2024, 39(11): 335-341. doi: 10.12461/PKU.DXHX202403084

    3. [3]

      Linbao Zhang ,  Weisi Guo ,  Shuwen Wang ,  Ran Song ,  Ming Li . Electrochemical Oxidation of Sulfides to Sulfoxides. University Chemistry, 2024, 39(11): 204-209. doi: 10.3866/PKU.DXHX202401009

    4. [4]

      Jianfeng Yan ,  Yating Xiao ,  Xin Zuo ,  Caixia Lin ,  Yaofeng Yuan . Comprehensive Chemistry Experimental Design of Ferrocenylphenyl Derivatives. University Chemistry, 2024, 39(4): 329-337. doi: 10.3866/PKU.DXHX202310005

    5. [5]

      Yifei Cheng ,  Jiahui Yang ,  Wei Shao ,  Wanqun Zhang ,  Wanqun Hu ,  Weiwei Li ,  Kaiping Yang . Learning Goes Beyond the Written Word: Practical Insights from the “Leaf Electroplating” Popular Science Experiment. University Chemistry, 2024, 39(9): 319-327. doi: 10.3866/PKU.DXHX202310033

    6. [6]

      Yan LIU , Jiaxin GUO , Song YANG , Shixian XU , Yanyan YANG , Zhongliang YU , Xiaogang HAO . Exclusionary recovery of phosphate anions with low concentration from wastewater using a CoNi-layered double hydroxide/graphene electronically controlled separation film. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1775-1783. doi: 10.11862/CJIC.20240043

    7. [7]

      Jing SU , Bingrong LI , Yiyan BAI , Wenjuan JI , Haiying YANG , Zhefeng Fan . Highly sensitive electrochemical dopamine sensor based on a highly stable In-based metal-organic framework with amino-enriched pores. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1337-1346. doi: 10.11862/CJIC.20230414

    8. [8]

      Jiahong ZHENG , Jiajun SHEN , Xin BAI . Preparation and electrochemical properties of nickel foam loaded NiMoO4/NiMoS4 composites. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 581-590. doi: 10.11862/CJIC.20230253

    9. [9]

      Qin ZHU , Jiao MA , Zhihui QIAN , Yuxu LUO , Yujiao GUO , Mingwu XIANG , Xiaofang LIU , Ping NING , Junming GUO . Morphological evolution and electrochemical properties of cathode material LiAl0.08Mn1.92O4 single crystal particles. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1549-1562. doi: 10.11862/CJIC.20240022

    10. [10]

      Qingtang ZHANG , Xiaoyu WU , Zheng WANG , Xiaomei WANG . Performance of nano Li2FeSiO4/C cathode material co-doped by potassium and chlorine ions. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1689-1696. doi: 10.11862/CJIC.20240115

    11. [11]

      Xinpeng LIU , Liuyang ZHAO , Hongyi LI , Yatu CHEN , Aimin WU , Aikui LI , Hao HUANG . Ga2O3 coated modification and electrochemical performance of Li1.2Mn0.54Ni0.13Co0.13O2 cathode material. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1105-1113. doi: 10.11862/CJIC.20230488

    12. [12]

      Yuanchao LI , Weifeng HUANG , Pengchao LIANG , Zifang ZHAO , Baoyan XING , Dongliang YAN , Li YANG , Songlin WANG . Effect of heterogeneous dual carbon sources on electrochemical properties of LiMn0.8Fe0.2PO4/C composites. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 751-760. doi: 10.11862/CJIC.20230252

    13. [13]

      Junke LIU , Kungui ZHENG , Wenjing SUN , Gaoyang BAI , Guodong BAI , Zuwei YIN , Yao ZHOU , Juntao LI . Preparation of modified high-nickel layered cathode with LiAlO2/cyclopolyacrylonitrile dual-functional coating. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1461-1473. doi: 10.11862/CJIC.20240189

    14. [14]

      Xiaoning TANG , Junnan LIU , Xingfu YANG , Jie LEI , Qiuyang LUO , Shu XIA , An XUE . Effect of sodium alginate-sodium carboxymethylcellulose gel layer on the stability of Zn anodes. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1452-1460. doi: 10.11862/CJIC.20240191

    15. [15]

      Shengbiao Zheng ,  Liang Li ,  Nini Zhang ,  Ruimin Bao ,  Ruizhang Hu ,  Jing Tang . Metal-Organic Framework-Derived Materials Modified Electrode for Electrochemical Sensing of Tert-Butylhydroquinone: A Recommended Comprehensive Chemistry Experiment for Translating Research Results. University Chemistry, 2024, 39(7): 345-353. doi: 10.3866/PKU.DXHX202310096

    16. [16]

      Guang Huang ,  Lei Li ,  Dingyi Zhang ,  Xingze Wang ,  Yugai Huang ,  Wenhui Liang ,  Zhifen Guo ,  Wenmei Jiao . Cobalt’s Valor, Nickel’s Foe: A Comprehensive Chemical Experiment Utilizing a Cobalt-based Imidazolate Framework for Nickel Ion Removal. University Chemistry, 2024, 39(8): 174-183. doi: 10.3866/PKU.DXHX202311051

    17. [17]

      Liangzhen Hu ,  Li Ni ,  Ziyi Liu ,  Xiaohui Zhang ,  Bo Qin ,  Yan Xiong . A Green Chemistry Experiment on Electrochemical Synthesis of Benzophenone. University Chemistry, 2024, 39(6): 350-356. doi: 10.3866/PKU.DXHX202312001

    18. [18]

      Jinyao Du ,  Xingchao Zang ,  Ningning Xu ,  Yongjun Liu ,  Weisi Guo . Electrochemical Thiocyanation of 4-Bromoethylbenzene. University Chemistry, 2024, 39(6): 312-317. doi: 10.3866/PKU.DXHX202310039

    19. [19]

      Yong Zhou ,  Jia Guo ,  Yun Xiong ,  Luying He ,  Hui Li . Comprehensive Teaching Experiment on Electrochemical Corrosion in Galvanic Cell for Chemical Safety and Environmental Protection Course. University Chemistry, 2024, 39(7): 330-336. doi: 10.3866/PKU.DXHX202310109

    20. [20]

      Zhengli Hu ,  Jia Wang ,  Yi-Lun Ying ,  Shaochuang Liu ,  Hui Ma ,  Wenwei Zhang ,  Jianrong Zhang ,  Yi-Tao Long . Exploration of Ideological and Political Elements in the Development History of Nanopore Electrochemistry. University Chemistry, 2024, 39(8): 344-350. doi: 10.3866/PKU.DXHX202401072

Get Citation
PDF
XML
Metrics
  • PDF Downloads(0)
  • Abstract views(365)
  • HTML views(23)

通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索
Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888
Powered By info@rhhz.net

/

DownLoad:  Full-Size Img  PowerPoint
Return