Citation: GUO Ning-Ning, WANG Yu, WANG Run-Wei, ZHANG Zong-Tao, QIU Shi-Lun. Synthesis of Sulfur Doped Porous Carbon at Room Temperature for CO₂ Adsorption[J]. Chinese Journal of Inorganic Chemistry, ;2017, 33(11): 2147-2152. doi: 10.11862/CJIC.2017.272 shu

Synthesis of Sulfur Doped Porous Carbon at Room Temperature for CO₂ Adsorption

State Key Laboratory of Inorganic Synthesis and Preparative Chemistry, College of Chemistry, Jilin University, Changchun 130012, China

Corresponding author: WANG Run-Wei, rwwang@jlu.edu.cn
Received Date: 24 October 2017
Revised Date: 27 October 2017

Figures(5)

Sulfur doped porous carbon (S-PC) were obtained by direct carbonization of sulfur containing phenolic resins, which were synthesized through one step reaction between phloroglucinol and benzo[b]thiophenc-3-carboxaldehyde under room temperature. The material was characterized by scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and N₂ sorption-desorption experiments. The obtained porous carbons possess high surface area with abundant of micropores. What's more, ultra-high surface area of 997 m²·g^-1 along with ultra-large micropore volume of 0.44 cm³·g^-1 could be obtained after carefully regulation the concentration of reactants. Owing to these fascinating characters like high surface area and rich of micropores, both high CO₂ uptake capacity (5.13 and 3.22 mmol·g^-1 for 273 and 298 K respectively) and high selectivity was obtained, which indicating it's promising sorbents for CO₂.
- sulfur doped porous carbon,
- phenolic resin,
- CO₂ sorption
1. [1]
  Pham T D, Hudson M R, Brown C M, et al. ChemSusChem, 2017, 10(5):946-957 doi: 10.1002/cssc.v10.5
2. [2]
  Pan Y, Zhao Y X, Mu S J, et al. J. Mater. Chem. A, 2017, 5: 9544-9552 doi: 10.1039/C7TA00162B
3. [3]
  Li X N, Bai S Y, Zhu Z J, et al. Langmuir, 2017, 33(5):1248-1255 doi: 10.1021/acs.langmuir.6b04131
4. [4]
  Kiciński W, Szala M, Bystrzejewski M. Carbon, 2014, 68:1-32 doi: 10.1016/j.carbon.2013.11.004
5. [5]
  Pei Z, Li H, Huang Y, et al. Energy Environ. Sci., 2017, 10 (3):742-749 doi: 10.1039/C6EE03265F
6. [6]
  XU Feng-Qin, HU Xiao-Fei, CHENG Fang-Yi, et al. Chinese J. Inorg. Chem., 2015, 31(1):103-108
7. [7]
  Li Y J, Wang G L, Wei T, et al. Nano Energy, 2016, 19:165-175 doi: 10.1016/j.nanoen.2015.10.038
8. [8]
  Xu D, Zhang D L, Zou H B, et al. Chem. Commun., 2016, 52 (69):10513-10516 doi: 10.1039/C6CC05366A
9. [9]
  PAN Xu-Chen, TANG Jing, XUE-Hai-Rong, et al. Chinese J. Inorg. Chem., 2015, 31(2):282-290
10. [10]
  Wang Y, Zou H B, Zeng S J, et al. Chem. Commun., 2015, 51(62):12423-12426 doi: 10.1039/C5CC03945B
11. [11]
  Bandosz T J, Seredych M, Rodríguez-Castellón E, et al. Carbon, 2016, 96:856-863 doi: 10.1016/j.carbon.2015.10.007
12. [12]
  Yu J, Guo M Y, Muhammad F, et al. Carbon, 2014, 69:502-514 doi: 10.1016/j.carbon.2013.12.058
13. [13]
  Sun Y H, Zhao J H, Wang J L, et al. J. Phys. Chem. C, 2017, 121(18):10000-10009 doi: 10.1021/acs.jpcc.7b02195
14. [14]
  de Yuso A M, De Fina M, Nita C, et al. Microporous Mesoporous Mater., 2017, 243:135-146 doi: 10.1016/j.micromeso.2016.12.001
15. [15]
  Kwiatkowski M, Policicchio A, Seredych M, et al. Carbon, 2016, 98:250-258 doi: 10.1016/j.carbon.2015.11.019
16. [16]
  Xia Y D, Zhu Y Q, Tang Y. Carbon, 2012, 50(15):5543-5553 doi: 10.1016/j.carbon.2012.07.044
17. [17]
  Saha D, Orkoulas G, Chen J H, et al. Microporous Mesoporous Mater., 2017, 241:226-237 doi: 10.1016/j.micromeso.2016.12.015
18. [18]
  Wu M, Dou Z Y, Chang J J, et al. RSC Adv., 2016, 6(27): 22781-22790 doi: 10.1039/C5RA22136F
19. [19]
  Kiciński W, Dziura A. Carbon, 2014, 75:56-67 doi: 10.1016/j.carbon.2014.02.085
20. [20]
  Nelson K M, Mahurin S M, Mayes R T, et al. Microporous Mesoporous Mater., 2016, 222:94-103 doi: 10.1016/j.micromeso.2015.09.050
21. [21]
  Xu Y J, Wu S P, Ren S J, et al. RSC Adv., 2017, 7(52): 32496-32501 doi: 10.1039/C7RA05551J
22. [22]
  Liu F Q, Wang L L, Li G H, et al. ACS Appl. Mater. Interfaces, 2017, 9(39):33997-34004 doi: 10.1021/acsami.7b11492
23. [23]
  Wang J, Senkovska I, Oschatz M, et al. J. Mater. Chem. A, 2013, 1(36):10951-10961 doi: 10.1039/c3ta11995e
24. [24]
  Luo H, Zhu C C, Tan Z C, et al. RSC Adv., 2016, 6(45): 38724-38730 doi: 10.1039/C6RA04106J
1. [1]
  Xianghai Song , Xiaoying Liu , Zhixiang Ren , Xiang Liu , Mei Wang , Yuanfeng Wu , Weiqiang Zhou , Zhi Zhu , Pengwei Huo . Insights into the greatly improved catalytic performance of N-doped BiOBr for CO₂ photoreduction. Acta Physico-Chimica Sinica, 2025, 41(6): 100055-0. doi: 10.1016/j.actphy.2025.100055
2. [2]
  Xueqi Yang , Juntao Zhao , Jiawei Ye , Desen Zhou , Tingmin Di , Jun Zhang . 调节NNU-55(Fe)的d带中心以增强CO₂吸附和光催化活性. Acta Physico-Chimica Sinica, 2025, 41(7): 100074-0. doi: 10.1016/j.actphy.2025.100074
3. [3]
  Feifan Zhao , Feiyan Xu , Jiaguo Yu . Interfacial stabilization of alkali metal oxides on carbon spheres for high-performance CO₂ chemisorption. Acta Physico-Chimica Sinica, 2026, 42(5): 100234-0. doi: 10.1016/j.actphy.2025.100234
4. [4]
  Wenlong Wang , Wentao Hao , Lang He , Jia Qiao , Ning Li , Chaoqiu Chen , Yong Qin . Bandgap and adsorption engineering of carbon dots/TiO₂ S-scheme heterojunctions for enhanced photocatalytic CO₂ methanation. Acta Physico-Chimica Sinica, 2025, 41(9): 100116-0. doi: 10.1016/j.actphy.2025.100116
5. [5]
  Xiangyu CAO , Jiaying ZHANG , Yun FENG , Linkun SHEN , Xiuling ZHANG , Juanzhi YAN . Synthesis and electrochemical properties of bimetallic-doped porous carbon cathode material. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 509-520. doi: 10.11862/CJIC.20240270
6. [6]
  Yongwei ZHANG , Chuang ZHU , Wenbin WU , Yongyong MA , Heng YANG . Efficient hydrogen evolution reaction activity induced by ZnSe@nitrogen doped porous carbon heterojunction. Chinese Journal of Inorganic Chemistry, 2025, 41(4): 650-660. doi: 10.11862/CJIC.20240386
7. [7]
  Zhaomei LIU , Wenshi ZHONG , Jiaxin LI , Gengshen HU . Preparation of nitrogen-doped porous carbons with ultra-high surface areas for high-performance supercapacitors. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 677-685. doi: 10.11862/CJIC.20230404
8. [8]
  Jun Huang , Pengfei Nie , Yongchao Lu , Jiayang Li , Yiwen Wang , Jianyun Liu . 丝光沸石负载自支撑氮掺杂多孔碳纳米纤维电容器及高效选择性去除硬度离子. Acta Physico-Chimica Sinica, 2025, 41(7): 100066-0. doi: 10.1016/j.actphy.2025.100066
9. [9]
  Wenlong LI , Xinyu JIA , Jie LING , Mengdan MA , Anning ZHOU . Photothermal catalytic CO₂ hydrogenation over a Mg-doped In₂O_3-x catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 919-929. doi: 10.11862/CJIC.20230421
10. [10]
  Haotong Ma , Mingyu Heng , Yang Xu , Wei Bi , Yingchun Miao , Shuning Xiao . Synergistic carbon doping and Cu loading on boron nitride via microwave synthesis for enhanced atmospheric CO₂ photoreduction. Acta Physico-Chimica Sinica, 2025, 41(11): 100132-0. doi: 10.1016/j.actphy.2025.100132
11. [11]
  Haoyu Sun , Dun Li , Yuanyuan Min , Yingying Wang , Yanyun Ma , Yiqun Zheng , Hongwen Huang . Hierarchical Palladium-Copper-Silver Porous Nanoflowers as Efficient Electrocatalysts for CO₂ Reduction to C₂₊ Products. Acta Physico-Chimica Sinica, 2024, 40(6): 2307007-0. doi: 10.3866/PKU.WHXB202307007
12. [12]
  Yangrui Xu , Yewei Ren , Xinlin Liu , Hongping Li , Ziyang Lu . NH₂-UIO-66 Based Hydrophobic Porous Liquid with High Mass Transfer and Affinity Surface for Enhancing CO₂ Photoreduction. Acta Physico-Chimica Sinica, 2024, 40(11): 2403032-0. doi: 10.3866/PKU.WHXB202403032
13. [13]
  Jie ZHAO , Sen LIU , Qikang YIN , Xiaoqing LU , Zhaojie WANG . Theoretical calculation of selective adsorption and separation of CO₂ by alkali metal modified naphthalene/naphthalenediyne. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 515-522. doi: 10.11862/CJIC.20230385
14. [14]
  Wenjuan SHI , Yuke LU , Xiuyuan LI , Lei HOU , Yaoyu WANG . Mg(Ⅱ) metal-organic frameworks based on biphenyltetracarboxylic acid: Synthesis and CO₂ adsorption and catalytic conversion performance. Chinese Journal of Inorganic Chemistry, 2025, 41(12): 2455-2463. doi: 10.11862/CJIC.20250220
15. [15]
  Xiaorui Chen , Xuan Luo , Tongming Su , Xinling Xie , Liuyun Chen , Yuejing Bin , Zuzeng Qin , Hongbing Ji . Ga-doped Cu/γ-Al₂O₃ bifunctional interface sites promote the direct hydrogenation of CO₂ to DME. Acta Physico-Chimica Sinica, 2025, 41(10): 100126-0. doi: 10.1016/j.actphy.2025.100126
16. [16]
  Xue Dong , Xiaofu Sun , Shuaiqiang Jia , Shitao Han , Dawei Zhou , Ting Yao , Min Wang , Minghui Fang , Haihong Wu , Buxing Han . Electrochemical CO₂ Reduction to C₂₊ Products with Ampere-Level Current on Carbon-Modified Copper Catalysts. Acta Physico-Chimica Sinica, 2025, 41(3): 100024-0. doi: 10.3866/PKU.WHXB202404012
17. [17]
  Xiting Zhou , Zhipeng Han , Xinlei Zhang , Shixuan Zhu , Cheng Che , Liang Xu , Zhenyu Sun , Leiduan Hao , Zhiyu Yang . Dual Modulation via Ag-Doped CuO Catalyst and Iodide-Containing Electrolyte for Enhanced Electrocatalytic CO₂ Reduction to Multi-Carbon Products: A Comprehensive Chemistry Experiment. University Chemistry, 2025, 40(7): 336-344. doi: 10.12461/PKU.DXHX202412070
18. [18]
  Zhipeng Bao , Yilin Wang , Yu Chen , Beirui Jia , Congcong Wang , Zean Xie , Xuehua Yu , Zhen Zhao . Digital and Intelligent Integration under the “Dual Carbon” Strategy: Plasma Reaction-Separation Coupling for CO₂ Hydrogenation to Methanol. University Chemistry, 2026, 41(1): 29-40. doi: 10.12461/PKU.DXHX202506009
19. [19]
  Xiaomin Kang , Chuanbao Jiao . Application of Metal-Organic Frameworks in CO₂ Catalytic Conversion: Promoting “Double Carbon” Actions for a Beautiful China. University Chemistry, 2026, 41(2): 208-217. doi: 10.12461/PKU.DXHX202503011
20. [20]
  Xue Xiao , Jiachun Li , Xiangtong Meng , Jieshan Qiu . Sulfur-Doped Carbon-Coated Fe_0.95S_1.05 Nanospheres as Anodes for High-Performance Sodium Storage. Acta Physico-Chimica Sinica, 2024, 40(6): 2307006-0. doi: 10.3866/PKU.WHXB202307006

Get Citation

PDF

XML

Metrics

PDF Downloads(9)
Abstract views(2509)
HTML views(541)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Synthesis of Sulfur Doped Porous Carbon at Room Temperature for CO2 Adsorption

Metrics

通讯作者: 陈斌, bchen63@163.com

Synthesis of Sulfur Doped Porous Carbon at Room Temperature for CO₂ Adsorption