Citation: NIU Yi-Fan, YANG Ying, YANG Wen-Tao. Hydrothermal Synthesis and Nanomechanical Performance of One-Dimensional Selenium Nanostructures[J]. Chinese Journal of Inorganic Chemistry, ;2016, 32(12): 2129-2135. doi: 10.11862/CJIC.2016.270 shu

Hydrothermal Synthesis and Nanomechanical Performance of One-Dimensional Selenium Nanostructures

1.
Sino-European Institute of Aviation Engineering, Civil Aviation University of China, Tianjin 300300, China

Corresponding author: NIU Yi-Fan,
Received Date: 25 May 2016
Available Online: 27 September 2016
Fund Project:

One-dimensional trigonal-selenium (t-Se) nanostructures were synthesized using environment-friendly and one-step hydrothermal process, using GeSe₄ glass as raw material in aqueous solution at 80℃. The morphologies and structures of these one-dimensional selenium products were characterized by transmission electron microscope (TEM), Raman spectrometry, scanning electron microscope (SEM) and atomic force microscope (AFM). The experimental results show that the Se nanofibers were grown along[001] direction with a hexagonal cross section. After 144 h of reaction, the length and diameter of Se nanofibers reached millimeter scale and 1~5 μm respectively. AFM based nanoindentation test reported that the hardness and elastic modulus of Se nanofibers were (399.5±20.4) MPa and (1.13±0.05) GPa respectively. The growth speed of Se nanofibers at pH=12.0 (80℃) was faster than that at pH=3.3 and pH=6.3. Se nanofibers were typically 344 μm long and 1.12 μm in diameter after 24 h of reaction in alkaline medium.
- trigonal-selenium;nanofiber;hydrothermal method;nanomechanical properties
1. [1]
  [1] ZHAO Miao(赵渺), YI Shuang-Pin(易双萍), WANG Zhen-Hu(王震虎). J. Funct. Mater. (功能材料), 2011,42(B02):54-57
2. [2]
  [2] GUO Jing(郭静), JIN Jun(靳俊), WEN Zhao-Yin(温兆银), et al. J. Inorg. Mater. (无机材料学报), 2015,30(8):867-871
3. [3]
  [3] Sargent E H. Nat. Photonics., 2012,6(3):133-135
4. [4]
  [4] Kumar S, Scholes G D. Microchim. Acta, 2008,160(3):315-325
5. [5]
  [5] DING Fei(丁菲), YU Jun-Sheng(于俊生). Chinese J. Inorg. Chem. (无机化学学报), 2009,25(4):708-712
6. [6]
  [6] Kundu D, Krumeich F, Nesper R. J. Power Sources, 2013, 15:112-117
7. [7]
  [7] Zhou X M, Gao P, Sun S C, et al. Chem. Mater., 2015,27(19):6730-6736
8. [8]
  [8] Ray C, Dutta S, Sarkar S, et al. RSC Adv., 2013,3(46):24313-24320
9. [9]
  [9] Tian N, Zhou Z Y, Sun S G, et al. Science, 2007,316(5825):732-735
10. [10]
  [10] Pinna N, Garnweitner G, Beato P, et al. Small, 2005,1:112-121
11. [11]
  [11] Chen H, Yoo J B, Liu Y, et al. Electron. Mater. Lett., 2011,7(4):333-336
12. [12]
  [12] LI Zhi-Lin(李志林), HUA Peng-Min(滑鹏敏). Inorg. Chem. Ind. (无机盐工业), 2009,7:32-34
13. [13]
  [13] Liu M H, Chen Y W, Kuo J L, et al. Chem. Commun., 2015, 51(72):13783-13786
14. [14]
  [14] Panahi-Kalamuei M, Panahi-Kalamuei M, Salavati-Niasari M, et al. Ultrason. Sonochem., 2015,23:246-256
15. [15]
  [15] Panahi-Kalamuei M, Salavati-Niasari M, Hosseinpour-Mashkani S M. J. Alloy. Compd., 2014,617:627-632
16. [16]
  [16] Zhu W, Xu H, Wang W, et al. Appl. Phys. A:Mater., 2006, 83(2):281-284
17. [17]
  [17] Oliver W C, Pharr G M. J. Mater. Res., 1992,7(6):1564-1580
18. [18]
  [18] Pokrovski G S, Schott J. Geochim. Cosmochim. Acta, 1998, 62:1631-1642
19. [19]
  [19] Pokrovski G S, Schott J. Geochim. Cosmochim. Acta, 1998, 62:3413-3428
20. [20]
  [20] ZHANG Xu(张旭), XIE Yi(谢毅), XU Fen(徐芬), et al. Chinese J. Inorg. Chem.(无机化学学报), 2003,19(1):77-80
21. [21]
  [21] Mooradian A, Wright G B. The Physics of Selenium & Tellurium, New York:Pergamon, 1967.
22. [22]
  [22] GAO Xue-Yu(高雪玉), YANG Qing-Sheng(杨庆生), LIU Zhi-Yuan(刘志远), et al. Acta Mater. Compos. Sin. (复合材料学报), 2012,29(5):209-214
23. [23]
  [23] Perera G, Doremus R H, Lanford W. J. Am. Ceram. Soc., 1991,74(7):1554-1558
24. [24]
  [24] Bureau B, Troles J, Le Floch M, et al. J. Non-Cryst. Solids, 2003,319(1):145-153
25. [25]
  [25] Boolchand P, Feng X, Bresser W J. J. Non-Cryst. Solids, 2001,293:348-356
26. [26]
  [26] Lucovsky G, Galeener F L, Keezer R C, et al. Phys. Rev. B, 1974,10(12):5134
27. [27]
  [27] Zhu W, Xu H, Wang W, et al. Appl. Phys. A:Mater., 2006, 83:281-284
28. [28]
  [28] Studart A R, Amstad E, Gauckler L J. Langmuir, 2007,23(3):1081-1090
29. [29]
  [29] Song J M, Zhu J H, Yu S H. J. Phys. Chem. B, 2006,110:23790-23795
30. [30]
  [30] Ogorelec Z, Tonejc A. Mater. Lett., 2000,42:81-85
1. [1]
  Juan WANG , Zhongqiu WANG , Qin SHANG , Guohong WANG , Jinmao LI . NiS and Pt as dual co-catalysts for the enhanced photocatalytic H₂ production activity of BaTiO₃ nanofibers. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1719-1730. doi: 10.11862/CJIC.20240102
2. [2]
  Zhiwen HU , Weixia DONG , Qifu BAO , Ping LI . Low-temperature synthesis of tetragonal BaTiO₃ for piezocatalysis. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 857-866. doi: 10.11862/CJIC.20230462
3. [3]
  Yufang GAO , Nan HOU , Yaning LIANG , Ning LI , Yanting ZHANG , Zelong LI , Xiaofeng LI . Nano-thin layer MCM-22 zeolite: Synthesis and catalytic properties of trimethylbenzene isomerization reaction. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1079-1087. doi: 10.11862/CJIC.20240036
4. [4]
  Jiao CHEN , Yi LI , Yi XIE , Dandan DIAO , Qiang XIAO . Vapor-phase transport of MFI nanosheets for the fabrication of ultrathin b-axis oriented zeolite membranes. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 507-514. doi: 10.11862/CJIC.20230403
5. [5]
  Guimin ZHANG , Wenjuan MA , Wenqiang DING , Zhengyi FU . Synthesis and catalytic properties of hollow AgPd bimetallic nanospheres. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 963-971. doi: 10.11862/CJIC.20230293
6. [6]
  Yuhao SUN , Qingzhe DONG , Lei ZHAO , Xiaodan JIANG , Hailing GUO , Xianglong MENG , Yongmei GUO . Synthesis and antibacterial properties of silver-loaded sod-based zeolite. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 761-770. doi: 10.11862/CJIC.20230169
7. [7]
  Jingke LIU , Jia CHEN , Yingchao HAN . Nano hydroxyapatite stable suspension system: Preparation and cobalt adsorption performance. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1763-1774. doi: 10.11862/CJIC.20240060
8. [8]
  Weihan Zhang , Menglu Wang , Ankang Jia , Wei Deng , Shuxing Bai . 表面硫物种对钯-硫纳米片加氢性能的影响. Acta Physico-Chimica Sinica, 2024, 40(11): 2309043-. doi: 10.3866/PKU.WHXB202309043
9. [9]
  Zijian Jiang , Yuang Liu , Yijian Zong , Yong Fan , Wanchun Zhu , Yupeng Guo . Preparation of Nano Zinc Oxide by Microemulsion Method and Study on Its Photocatalytic Activity. University Chemistry, 2024, 39(5): 266-273. doi: 10.3866/PKU.DXHX202311101
10. [10]
  Wenjiang LI , Pingli GUAN , Rui YU , Yuansheng CHENG , Xianwen WEI . C₆₀-MoP-C nanoflowers van der Waals heterojunctions and its electrocatalytic hydrogen evolution performance. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 771-781. doi: 10.11862/CJIC.20230289
11. [11]
  Siyu HOU , Weiyao LI , Jiadong LIU , Fei WANG , Wensi LIU , Jing YANG , Ying ZHANG . Preparation and catalytic performance of magnetic nano iron oxide by oxidation co-precipitation method. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1577-1582. doi: 10.11862/CJIC.20230469
12. [12]
  Guangming YIN , Huaiyao WANG , Jianhua ZHENG , Xinyue DONG , Jian LI , Yi'nan SUN , Yiming GAO , Bingbing WANG . Preparation and photocatalytic degradation performance of Ag/protonated g-C₃N₄ nanorod materials. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1491-1500. doi: 10.11862/CJIC.20240086
13. [13]
  Qingtang ZHANG , Xiaoyu WU , Zheng WANG , Xiaomei WANG . Performance of nano Li₂FeSiO₄/C cathode material co-doped by potassium and chlorine ions. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1689-1696. doi: 10.11862/CJIC.20240115
14. [14]
  Haiyuan Wang , Yiming Tang , Haoran Guo , Guohui Chen , Yajing Sun , Chao Zhao , Zhen Zhang . Comprehensive Chemistry Experimental Teaching Design Based on the Integration of Science and Education: Preparation and Catalytic Properties of Silver Nanomaterials. University Chemistry, 2024, 39(10): 219-228. doi: 10.12461/PKU.DXHX202404067
15. [15]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
16. [16]
  Jiahong ZHENG , Jingyun YANG . Preparation and electrochemical properties of hollow dodecahedral CoNi₂S₄ supported by MnO₂ nanowires. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1881-1891. doi: 10.11862/CJIC.20240170
17. [17]
  Min LI , Xianfeng MENG . Preparation and microwave absorption properties of ZIF-67 derived Co@C/MoS₂ nanocomposites. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1932-1942. doi: 10.11862/CJIC.20240065
18. [18]
  Jinyi Sun , Lin Ma , Yanjie Xi , Jing Wang . Preparation and Electrocatalytic Nitrogen Reduction Performance Study of Vanadium Nitride@Nitrogen-Doped Carbon Composite Nanomaterials: A Recommended Comprehensive Chemistry Experiment. University Chemistry, 2024, 39(4): 184-191. doi: 10.3866/PKU.DXHX202310094
19. [19]
  Haihua Yang , Minjie Zhou , Binhong He , Wenyuan Xu , Bing Chen , Enxiang Liang . Synthesis and Electrocatalytic Performance of Iron Phosphide@Carbon Nanotubes as Cathode Material for Zinc-Air Battery: a Comprehensive Undergraduate Chemical Experiment. University Chemistry, 2024, 39(10): 426-432. doi: 10.12461/PKU.DXHX202405100
20. [20]
  Zhuo WANG , Junshan ZHANG , Shaoyan YANG , Lingyan ZHOU , Yedi LI , Yuanpei LAN . Preparation and photocatalytic performance of CeO₂-reduced graphene oxide by thermal decomposition. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1708-1718. doi: 10.11862/CJIC.20240067

Get Citation

PDF

XML

Metrics

PDF Downloads(0)
Abstract views(282)
HTML views(35)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142