Citation: WANG Hui-Gang, ZHANG Qi, ZHANG Ji-Long, YU Feng, LI Rui-Feng. Nano Sulfated Zirconia Synthesis and Its Catalytic Properties in the Transesterification[J]. Chinese Journal of Inorganic Chemistry, ;2016, 32(11): 1959-1964. doi: 10.11862/CJIC.2016.264 shu

Nano Sulfated Zirconia Synthesis and Its Catalytic Properties in the Transesterification

1.
College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024, China

Corresponding author: YU Feng,
Received Date: 8 April 2016
Available Online: 29 September 2016
Fund Project:

Nano SO₄^2-/ZrO₂ solid acid catalysts were prepared by two-step crystallization-post impregnation method and their catalytic performance in the transesterification of vegetable oil with methanol was investigated. The results of XRD, N₂ adsorption-desorption and TEM showed that the single tetragonal phase catalyst calcined at 600℃ was composed of nano crystals about 5~10 nm and had the specific surface area of 137 m²·g^-1 and the pore size of 3.7 nm. NH₃-TPD data indicated that the calcination temperature could improve the content and intensity of the surface acid, and that more superacid content was favorable to effect the efficient conversion under general conditions. In the transesterification reaction, under the operating conditions of 5%(w/w) of catalyst calcined at 600℃, the molar ratio of methanol to oil 20:1, at 135℃ and for 6 h, vegetable oil could be completely converted to fatty acid methyl esters. Compared with the traditional SO₄^2-/ZrO₂ catalyst, the nano SO₄^2-/ZrO₂ catalyst had a higher catalytic performance and good reuse at low reaction temperature.
- biodiesel;nano material;SO₄^2-/ZrO₂;solid acid catalyst;transesterification
1. [1]
  [1] Talebian-Kiakalaieh A, Amin N A S, Mazaheri H. Appl. Energy, 2013,104(2):683-710
2. [2]
  [2] Helwani Z, Othman M R, Aziz N, et al. Appl. Catal. A:Gen., 2009,363(1):1-10
3. [3]
  [3] Lam M K, Lee K T, Mohamed A R. Biotechnol. Adv., 2010, 28(4):500-518
4. [4]
  [4] YU Hui(于荟), ZHU Yin-hua(朱银华), LIU Chang(刘畅), et al. Chin. J. Catal.(催化学报), 2009,30(3):265-271
5. [5]
  [5] Reddy B M, Patil M K. Chem. Rev., 2009,109(6):2185-2208
6. [6]
  [6] Saravanan K, Tyagi B, Shukla R S, et al. Appl. Catal. B: Environ., 2015,172-173:108-115
7. [7]
  [7] Sharma Y C, Singh B, Korstad J. Biofuel Bioprod. Biorefin., 2011,5(1):69-92
8. [8]
  [8] Deshmane V G, Adewuyi Y G. Appl. Catal. A:Gen., 2013, 462:196-206
9. [9]
  [9] Chen H, Wang J F. Chin. J. Process Eng., 2006,6(4):571-575
10. [10]
  [10] Jitputti J, Kitiyanan B, Rangsunvigit P, et al. Chem. Eng. J., 2006,116(1):61-66
11. [11]
  [11] Rattanaphra D, Harvey A. Top Catal., 2010,53(11/12):773-782
12. [12]
  [12] Garcia C M, Teixeira S, Marciniuk L L, et al. Bioresour. Technol., 2008,99(14):6608-6613
13. [13]
  [13] ZHANG Qi(张琪), ZHANG Ji-Long(张继龙), WANG Hui-Gang(王会刚), et al. Mod. Chem. Ind.(现代化工), 2013,33(8):134-138
14. [14]
  [14] Zhang Q Q, Ming W X, Ma J H, et al. J. Mater. Chem. A, 2014,2(23):8712-8718
15. [15]
  [15] Cristian D M M, Alfonso E R S, et al. J. Mol. Catal. A:Chem., 2015,398:325-335
16. [16]
  [16] Boskovic G C, Zarubica A R, et al. J. Therm. Anal. Calorim., 2008,91:849-854
17. [17]
  [17] Patel A, Brahmkhatri V, Singh N. Renewable Energ., 2013, 51:227-233
18. [18]
  [18] Liao Y, Huang X, Liao X P, et al. J. Mol. Catal. A:Chem., 2011,347(1):46-51
19. [19]
  [19] Yuan Q, Li L L, Lu S L, et al. J. Phys. Chem. C, 2009,113(10):4117-4124
20. [20]
  [20] Yue Z, Wong W T, Yung K F. Appl. Energy, 2014,116(3): 191-198
21. [21]
  [21] Ivanov V K, Baranchikov A Y, et al. J. Solid State Chem., 2013,198(2):496-505
22. [22]
  [22] Velasquez-Orta S B, Lee J G M, Harvey A P. Biochem. Eng. J., 2013,76:83-89
23. [23]
  [23] Fu B, Gao L, Lei N, et al. Energy Fuels, 2009,23(1):569-572
24. [24]
  [24] Furuta S, Matsuhashi H, Arata K. Catal. Commun., 2004,5(12):721-723
25. [25]
  [25] Shu Q, Song Q, Yang B, et al. Catal. Commun., 2007,8(12): 2159-2165
26. [26]
  [26] Suwannakarn K, Lotero E, Goodwin J G, et al. J. Catal., 2008,255(2):279-286
1. [1]
  Juan Yuan , Bin Zhang , Jinping Wu , Mengfan Wang . Design of a Comprehensive Experiment on Preparation and Characterization of Cu₂(Salen)₂ Nanomaterials with Two Distinct Morphologies. University Chemistry, 2024, 39(10): 420-425. doi: 10.3866/PKU.DXHX202402014
2. [2]
  Zunyuan Xie , Lijin Yang , Zixiao Wan , Xiaoyu Liu , Yushan He . Exploration of the Preparation and Characterization of Nano Barium Titanate and Its Application in Inorganic Chemistry Laboratory Teaching. University Chemistry, 2024, 39(4): 62-69. doi: 10.3866/PKU.DXHX202310137
3. [3]
  Simin Fang , Wei Huang , Guanghua Yu , Cong Wei , Mingli Gao , Guangshui Li , Hongjun Tian , Wan Li . Integrating Science and Education in a Comprehensive Chemistry Design Experiment: The Preparation of Copper(I) Oxide Nanoparticles and Its Application in Dye Water Remediation. University Chemistry, 2024, 39(8): 282-289. doi: 10.3866/PKU.DXHX202401023
4. [4]
  Wenjun Zheng . Application in Inorganic Synthesis of Ionic Liquids. University Chemistry, 2024, 39(8): 163-168. doi: 10.3866/PKU.DXHX202401020
5. [5]
  Dan Li , Hui Xin , Xiaofeng Yi . Comprehensive Experimental Design on Ni-based Catalyst for Biofuel Production. University Chemistry, 2024, 39(8): 204-211. doi: 10.3866/PKU.DXHX202312046
6. [6]
  Juan WANG , Zhongqiu WANG , Qin SHANG , Guohong WANG , Jinmao LI . NiS and Pt as dual co-catalysts for the enhanced photocatalytic H₂ production activity of BaTiO₃ nanofibers. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1719-1730. doi: 10.11862/CJIC.20240102
7. [7]
  Wenlong LI , Xinyu JIA , Jie LING , Mengdan MA , Anning ZHOU . Photothermal catalytic CO₂ hydrogenation over a Mg-doped In₂O_3-x catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 919-929. doi: 10.11862/CJIC.20230421
8. [8]
  Kun WANG , Wenrui LIU , Peng JIANG , Yuhang SONG , Lihua CHEN , Zhao DENG . Hierarchical hollow structured BiOBr-Pt catalysts for photocatalytic CO₂ reduction. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1270-1278. doi: 10.11862/CJIC.20240037
9. [9]
  Zhanggui DUAN , Yi PEI , Shanshan ZHENG , Zhaoyang WANG , Yongguang WANG , Junjie WANG , Yang HU , Chunxin LÜ , Wei ZHONG . Preparation of UiO-66-NH₂ supported copper catalyst and its catalytic activity on alcohol oxidation. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 496-506. doi: 10.11862/CJIC.20230317
10. [10]
  Guangming YIN , Huaiyao WANG , Jianhua ZHENG , Xinyue DONG , Jian LI , Yi'nan SUN , Yiming GAO , Bingbing WANG . Preparation and photocatalytic degradation performance of Ag/protonated g-C₃N₄ nanorod materials. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1491-1500. doi: 10.11862/CJIC.20240086
11. [11]
  Haiyuan Wang , Yiming Tang , Haoran Guo , Guohui Chen , Yajing Sun , Chao Zhao , Zhen Zhang . Comprehensive Chemistry Experimental Teaching Design Based on the Integration of Science and Education: Preparation and Catalytic Properties of Silver Nanomaterials. University Chemistry, 2024, 39(10): 219-228. doi: 10.12461/PKU.DXHX202404067
12. [12]
  Hong Lu , Yidie Zhai , Xingxing Cheng , Yujia Gao , Qing Wei , Hao Wei . Advancements and Expansions in the Proline-Catalyzed Asymmetric Aldol Reaction. University Chemistry, 2024, 39(5): 154-162. doi: 10.3866/PKU.DXHX202310074
13. [13]
  Qingtang ZHANG , Xiaoyu WU , Zheng WANG , Xiaomei WANG . Performance of nano Li₂FeSiO₄/C cathode material co-doped by potassium and chlorine ions. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1689-1696. doi: 10.11862/CJIC.20240115
14. [14]
  Xiufang Wang , Donglin Zhao , Kehua Zhang , Xiaojie Song . “Preparation of Carbon Nanotube/SnS₂ Photoanode Materials”: A Comprehensive University Chemistry Experiment. University Chemistry, 2024, 39(4): 157-162. doi: 10.3866/PKU.DXHX202308025
15. [15]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
16. [16]
  Qiangqiang SUN , Pengcheng ZHAO , Ruoyu WU , Baoyue CAO . Multistage microporous bifunctional catalyst constructed by P-doped nickel-based sulfide ultra-thin nanosheets for energy-efficient hydrogen production from water electrolysis. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1151-1161. doi: 10.11862/CJIC.20230454
17. [17]
  Wen YANG , Didi WANG , Ziyi HUANG , Yaping ZHOU , Yanyan FENG . La promoted hydrotalcite derived Ni-based catalysts: In situ preparation and CO₂ methanation performance. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 561-570. doi: 10.11862/CJIC.20230276
18. [18]
  Ruolin CHENG , Haoran WANG , Jing REN , Yingying MA , Huagen LIANG . Efficient photocatalytic CO₂ cycloaddition over W₁₈O₄₉/NH₂-UiO-66 composite catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 523-532. doi: 10.11862/CJIC.20230349
19. [19]
  Yi YANG , Shuang WANG , Wendan WANG , Limiao CHEN . Photocatalytic CO₂ reduction performance of Z-scheme Ag-Cu₂O/BiVO₄ photocatalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 895-906. doi: 10.11862/CJIC.20230434
20. [20]
  Jinyi Sun , Lin Ma , Yanjie Xi , Jing Wang . Preparation and Electrocatalytic Nitrogen Reduction Performance Study of Vanadium Nitride@Nitrogen-Doped Carbon Composite Nanomaterials: A Recommended Comprehensive Chemistry Experiment. University Chemistry, 2024, 39(4): 184-191. doi: 10.3866/PKU.DXHX202310094

Get Citation

PDF

XML

Metrics

PDF Downloads(9)
Abstract views(367)
HTML views(20)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142