Citation: WEN Xiao-Ling, OUYANG Jian-Ming. Adsorption Properties of Bovine Serum Albumin on Micron/Nano Calcium Oxalate Monohydrate and Dihydrate Crystals[J]. Chinese Journal of Inorganic Chemistry, ;2016, 32(1): 103-110. doi: 10.11862/CJIC.2016.011 shu

Adsorption Properties of Bovine Serum Albumin on Micron/Nano Calcium Oxalate Monohydrate and Dihydrate Crystals

WEN Xiao-Ling ,
OUYANG Jian-Ming ^*,,

Institute of Biomineralization and Lithiasis Research, Jinan University, Guangzhou 510632, China

Corresponding author: OUYANG Jian-Ming, toyjm@jnu.edu.cn
Received Date: 10 August 2015
Revised Date: 27 September 2015

Figures(5)

The adsorption isotherms of bovine serum albumin (BSA) on calcium oxalate monohydrate (COM) and calcium oxalate dehydrate (COD) crystals with a size of 100 nm and 3 μm were detected, and Zeta potential of the crystals after adsorption of various concentration of BSA was measured. Adsorption quality change of BSA at different pH value were also measured. Results showed that the adsorption quality of BSA were positively related to the specific surface area of crystals, that was, following the order: COD-100nm > COM-100 nm≥COD-3 μm > COM-3 μm. However, after surface area normalization, the adsorption order was COD-3 μm > COM-3 μm > COM-100 nm > COD-100 nm. It indicated that the crystal water and charge density on crystal surface of COM and COD also affected BSA adsorption. These adsorption isotherms were fitted better with Langmuir model, indicating a monolayer adsorption of BSA on micron/nano COD and COM surface. The isoelectric point of the four crystals followed an order: COM-100 nm (7.2) > COD-100 nm (6.7)≥COM-3 μm (4.7) > COD-3 μm (4.3), which indicated more serious aggregation of nanocrystals under pathophysiological conditions (pH≈6.3). The maximum BSA adsorption occurred at around isoelectric point of BSA (pH=4.8). The adsorption of BSA on micron/nano COM is related to the specific surface area of crystals, its surface charge, crystal aggregation, crystal water number, and the pH value of system. These results can help to clarify the effect of various urine microcrystalline and urine proteins on the formation of CaO_x stones.
- nano,
- micron,
- calcium oxalate,
- bovine serum albumin,
- adsorption isotherms,
- isoelectric point,
- pH value
1. [1]
  Cerini C, Geider S, Dussol B, et al. Kidney Int., 1999, 55(5): 1776-1786 doi: 10.1046/j.1523-1755.1999.00426.x
2. [2]
  Liu J F, Jiang H D, Liu X Y. J. Phys. Chem. B, 2006, 110: 9085-9089 doi: 10.1021/jp057403b
3. [3]
  Farmanesh S, Ramamoorthy S, Chung J, et al. J. Am. Chem. Soc., 2013, 136(1):367-376
4. [4]
  Grohe B, Taller A, Vincent P L, et al. Langmuir, 2009, 25 (19):11635-11646 doi: 10.1021/la901145d
5. [5]
  Grohe B, O′Young J, Ionescu D A, et al. J. Am. Chem. Soc., 2007, 129:14946-14951 doi: 10.1021/ja0745613
6. [6]
  Taller A, Grohe B, Rogers K A, et al. Biophys. J., 2007, 93 (5):1768-1777 doi: 10.1529/biophysj.106.101881
7. [7]
  LIU Yi-Ming, XIA Zhi-Yue, OUYANG Jing-Ming, et al. Chinese J. Inorg. Chem., 2013, 29(5):903-909
8. [8]
  Ouyang J M, Xia Z Y, Zhang G N, et al. Rev. Inorg. Chem., 2012, 32(2/3/4):101-110
9. [9]
  He J Y, Deng S P, Ouyang J M. IEEE Trans. Nanobiosci., 2010, 9(2):156-163 doi: 10.1109/TNB.2010.2045510
10. [10]
  Sun X Y, Ouyang J M, Liu A J, et al. Mater. Sci. Eng. C, 2015, 57:147-156 doi: 10.1016/j.msec.2015.07.032
11. [11]
  Oliva F Y, Avalle L B, Cámara O R, et al. J. Colloid Interface Sci., 2003, 261(2):299-311 doi: 10.1016/S0021-9797(03)00029-8
12. [12]
  Song L, Yang K, Jiang W, et al. Colloids Surf. B, 2012, 94: 341-346 doi: 10.1016/j.colsurfb.2012.02.011
13. [13]
  Tunik L, Fueredi-Milhofer H, Garti N. Langmuir, 1998, 14 (12):3351-3355 doi: 10.1021/la9708041
14. [14]
  Walton R C, Kavanagh J P, Heywood B R, et al. BBA-Gen. Subjects, 2005, 1723(1/2/3):175-183
15. [15]
  Rezwan K, Meier L P, Rezwan M, et al. Langmuir, 2004, 20 (23):10055-10061 doi: 10.1021/la048459k
16. [16]
  Sikiri M D, Füredi-Milhofer H. Adv. Colloid Interface Sci., 2006, 128:135-158
17. [17]
  Mohsen-Nia M, Bidgoli M M, Behrashi M, et al. Protein J., 2012, 31(2):150-157 doi: 10.1007/s10930-011-9384-3
18. [18]
  Puskas J E, Dahman Y, Margaritis A. Biomacromolecules, 2004, 5(4):1412-1421 doi: 10.1021/bm034497r
19. [19]
  Kandori K, Oda S, Tsuyama S. J. Phys. Chem. B, 2008, 112 (8):2542-2547 doi: 10.1021/jp076421l
20. [20]
  Thielbeer F, Donaldson K, Bradley M. Bioconjugate Chem., 2011, 22(2):144-150 doi: 10.1021/bc1005015
21. [21]
  Srinivasan S, Kalaiselvi P, Sakthivel R, et al. Clin. Chim. Acta, 2005, 353(1):45-51
22. [22]
  Gao J, Xue J F, Xu M, et al. Int. J. Nanomed., 2014, 9: 4399
23. [23]
  Finlayson B, Reid S. Invest. Urol., 1978, 15:442-448
24. [24]
  Kok D J, Khan S R. Kidney Int., 1994, 46:847 doi: 10.1038/ki.1994.341
25. [25]
  Shemetov A A, Nabiev I, Sukhanova A. ACS Nano, 2012, 6 (6):4585-4602 doi: 10.1021/nn300415x
26. [26]
  Zhang X, Bai R, Tong Y W. Sep. Purif. Technol., 2006, 52 (1):161-169 doi: 10.1016/j.seppur.2006.04.001
27. [27]
  Alkan M, Demirba Doan M, et al. Microporous Mesoporous Mater., 2006, 96(1):331-340
1. [1]
  Xinyu ZENG , Guhua TANG , Jianming OUYANG . Inhibitory effect of Desmodium styracifolium polysaccharides with different content of carboxyl groups on the growth, aggregation and cell adhesion of calcium oxalate crystals. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1563-1576. doi: 10.11862/CJIC.20230374
2. [2]
  Di WU , Ruimeng SHI , Zhaoyang WANG , Yuehua SHI , Fan YANG , Leyong ZENG . Construction of pH/photothermal dual-responsive delivery nanosystem for combination therapy of drug-resistant bladder cancer cell. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1679-1688. doi: 10.11862/CJIC.20240135
3. [3]
  Jingke LIU , Jia CHEN , Yingchao HAN . Nano hydroxyapatite stable suspension system: Preparation and cobalt adsorption performance. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1763-1774. doi: 10.11862/CJIC.20240060
4. [4]
  Liangyu Gong , Jie Wang , Fengyu Du , Lubin Xu , Chuanli Ma , Shihai Yan , Zhuwei Song , Fuheng Liu , Xiuzhong Wang . Construction and Practice of “One-Point, Two-Lines and Three-Sides” Innovative Experimental Platform. University Chemistry, 2024, 39(4): 26-32. doi: 10.3866/PKU.DXHX202308023
5. [5]
  Zeyu XU , Anlei DANG , Bihua DENG , Xiaoxin ZUO , Yu LU , Ping YANG , Wenzhu YIN . Evaluation of the efficacy of graphene oxide quantum dots as an ovalbumin delivery platform and adjuvant for immune enhancement. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1065-1078. doi: 10.11862/CJIC.20240099
6. [6]
  Gaofeng Zeng , Shuyu Liu , Manle Jiang , Yu Wang , Ping Xu , Lei Wang . Micro/Nanorobots for Pollution Detection and Toxic Removal. University Chemistry, 2024, 39(9): 229-234. doi: 10.12461/PKU.DXHX202311055
7. [7]
  Jianye Kang , Xinyu Yang , Xuhao Yang , Jiahui Sun , Yuhang Liu , Shutao Wang , Wenlong Song . Carbon dots-enhanced pH-responsive lubricating hydrogel based on reversible dynamic covalent bondings. Chinese Chemical Letters, 2024, 35(5): 109297-. doi: 10.1016/j.cclet.2023.109297
8. [8]
  Shuang Li , Jiayu Sun , Guocheng Liu , Shuo Zhang , Zhong Zhang , Xiuli Wang . A new Keggin-type polyoxometallate-based bifunctional catalyst for trace detection and pH-universal photodegradation of phenol. Chinese Chemical Letters, 2024, 35(8): 109148-. doi: 10.1016/j.cclet.2023.109148
9. [9]
  Rui Wang , He Qi , Haijiao Zheng , Qiong Jia . Light/pH dual-responsive magnetic metal-organic frameworks composites for phosphorylated peptide enrichment. Chinese Chemical Letters, 2024, 35(7): 109215-. doi: 10.1016/j.cclet.2023.109215
10. [10]
  Yan Liu , Yang Wang , Jiayi Zhu , Xuxian Su , Xudong Lin , Liang Xu , Xiwen Xing . Employing pH-responsive RNA triplex to control CRISPR/Cas9-mediated gene manipulation in mammalian cells. Chinese Chemical Letters, 2024, 35(9): 109427-. doi: 10.1016/j.cclet.2023.109427
11. [11]
  Tongyu Zheng , Teng Li , Xiaoyu Han , Yupei Chai , Kexin Zhao , Quan Liu , Xiaohui Ji . A DIY pH Detection Agent Using Persimmon Extract for Acid-Base Discoloration Popularization Experiment. University Chemistry, 2024, 39(5): 27-36. doi: 10.3866/PKU.DXHX202309107
12. [12]
  Jiao CHEN , Yi LI , Yi XIE , Dandan DIAO , Qiang XIAO . Vapor-phase transport of MFI nanosheets for the fabrication of ultrathin b-axis oriented zeolite membranes. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 507-514. doi: 10.11862/CJIC.20230403
13. [13]
  Hong LI , Xiaoying DING , Cihang LIU , Jinghan ZHANG , Yanying RAO . Detection of iron and copper ions based on gold nanorod etching colorimetry. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 953-962. doi: 10.11862/CJIC.20230370
14. [14]
  Guimin ZHANG , Wenjuan MA , Wenqiang DING , Zhengyi FU . Synthesis and catalytic properties of hollow AgPd bimetallic nanospheres. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 963-971. doi: 10.11862/CJIC.20230293
15. [15]
  Yuhao SUN , Qingzhe DONG , Lei ZHAO , Xiaodan JIANG , Hailing GUO , Xianglong MENG , Yongmei GUO . Synthesis and antibacterial properties of silver-loaded sod-based zeolite. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 761-770. doi: 10.11862/CJIC.20230169
16. [16]
  Weihan Zhang , Menglu Wang , Ankang Jia , Wei Deng , Shuxing Bai . 表面硫物种对钯-硫纳米片加氢性能的影响. Acta Physico-Chimica Sinica, 2024, 40(11): 2309043-. doi: 10.3866/PKU.WHXB202309043
17. [17]
  Haiyu Nie , Chenhui Zhang , Fengpei Du . Ideological and Political Design for the Preparation, Characterization and Particle Size Control Experiment of Nanoemulsion. University Chemistry, 2024, 39(2): 41-46. doi: 10.3866/PKU.DXHX202306055
18. [18]
  Yongming Guo , Jie Li , Chaoyong Liu . Green Improvement and Educational Design in the Synthesis and Characterization of Silver Nanoparticles. University Chemistry, 2024, 39(3): 258-265. doi: 10.3866/PKU.DXHX202309057
19. [19]
  Zijian Jiang , Yuang Liu , Yijian Zong , Yong Fan , Wanchun Zhu , Yupeng Guo . Preparation of Nano Zinc Oxide by Microemulsion Method and Study on Its Photocatalytic Activity. University Chemistry, 2024, 39(5): 266-273. doi: 10.3866/PKU.DXHX202311101
20. [20]
  Zhengli Hu , Jia Wang , Yi-Lun Ying , Shaochuang Liu , Hui Ma , Wenwei Zhang , Jianrong Zhang , Yi-Tao Long . Exploration of Ideological and Political Elements in the Development History of Nanopore Electrochemistry. University Chemistry, 2024, 39(8): 344-350. doi: 10.3866/PKU.DXHX202401072

Get Citation

PDF

XML

Metrics

PDF Downloads(0)
Abstract views(438)
HTML views(95)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142