Citation: Wang Qian, Wu Kai, Wang Hangchao, Liu Wen, Zhou Henghui. Lithiophilic 3D SnS₂@Carbon Fiber Cloth for Stable Li Metal Anode[J]. Acta Physico-Chimica Sinica, ;2021, 37(1): 200709. doi: 10.3866/PKU.WHXB202007092 shu

Lithiophilic 3D SnS₂@Carbon Fiber Cloth for Stable Li Metal Anode

Wang Qian ^1,† ,
Wu Kai ^1,† ,
Wang Hangchao ^2,† ,
Liu Wen ^2,, ,
Zhou Henghui ^1,3,,

1.
College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, China
2.
College of Science & College of Energy, Beijing University of Chemical Technology, Beijing 100092, China
3.
Beijing Engineering Research Center of Power Lithium-ion Battery, Beijing 102202, China

Corresponding author: Liu Wen, wenliu@mail.buct.edu.cn Zhou Henghui, hhzhou@pku.edu.cn

^†

Received Date: 31 July 2020
Revised Date: 1 September 2020
Accepted Date: 11 September 2020
Available Online: 16 September 2020
Fund Project: The project was supported by the National Natural Science Foundation of China (21771018, 21875004), the National Natural Science Foundation of Beijing (2192018), and the PULEAD Technology Industry Co. Ltdthe National Natural Science Foundation of Beijing 2192018the National Natural Science Foundation of China 21771018the National Natural Science Foundation of China 21875004

Li metal batteries (LMBs) have attracted worldwide attention in recent years with a focus on the extremely high theoretical energy density of 3580 Wh·kg^-1 (Li-O₂) and 2600 Wh·kg^-1 (Li-S), which benefit from the highest specific capacity (3860 mAh·g^-1) and the lowest negative potential (-3.04 V) of Li metal anodes. However, further development and practical applications are hindered by the formation of Li dendrites and a large volume expansion, which not only lowers the coulombic efficiency but also leads to many security risks, such as internal short circuits, fires, and even explosions. In this study, we selected a low-cost and commercial carbon fiber cloth (CC) as a 3D framework for accommodating Li metal and relieving the volume expansion during the Li plating/stripping process. In addition, lithiophilic SnS₂ nano-sheet arrays were grown on the surface of carbon fiber cloth via a one-step method. The SnS₂ arrays can be partially converted to Li-Sn alloy and Li₂S components during the Li plating process. The as-formed Li-Sn alloy can provide reversible sites for further Li deposition and improve the electrochemical kinetics process. As a typical component of the solid electrolyte interface (SEI), Li₂S can promote Li⁺ migration at SEI and ensure a homogeneous distribution of Li⁺-flux near the electrode surface, thereby reducing the overpotential of Li deposition and suppressing the formation and growth of Li dendrites. Meanwhile, the 3D carbon skeleton can also reduce the local current density of the electrode because of its high specific surface area to ensure uniform Li deposition. Benefiting from the design of the combination bulk and the surface, the composite SnS₂@carbon fiber cloth (SnS₂@CC) demonstrated excellent prospects for practical applications. Upon pairing with Li foils, the SnS₂@CC electrode displayed stable cycling performance with improved coulombic efficiency (> 98%) over 100 cycles at 1.0 mA·cm^-2/5.0 mAh·cm^-2. After loading 10 mAh·cm^-2 Li metal, the composite Li metal anode could run over 400 h with a low overpotential of 60 mV at a current density of 1.0 mA·cm^-2, even when the current density was increased to 2.0 mA·cm^-2; additionally, a low overpotential of 85 mV could also be maintained over 350 h, manifesting one of the most stable composite Li metal anodes to date. Moreover, when the composite Li metal anode was assembled with a LiFePO₄ cathode, the full cells exhibited a high initial specific discharge capacity of 160.6 mAh·g^-1 and high cycling stability. At a rate of 2.0C, the cell showed a high capacity retention of 80.6% after 500 cycles.We believe that the lithiophilic SnS₂@CC composite electrode offers a simple and effective strategy to suppress dendritic Li growth and relieve the volume change during the charging/discharging process.
- Composite Li anode,
- Current collector,
- Lithium dendrite,
- Carbon fiber cloth,
- Li alloy
1. [1]
  Larcher, D.; Tarascon, J. M. Nat. Chem. 2015, 7, 19. doi: 10.1038/nchem.2085 doi: 10.1038/nchem.2085
2. [2]
  Udaeta, M. E. M.; Galvao, L. C. R.; Rigolin, P. H. D.; Bernal, J. L. D. Renew. Sust. Energy Rev. 2016, 66, 190. doi: 10.1016/j.rser.2016.07.008 doi: 10.1016/j.rser.2016.07.008
3. [3]
  Yang, Z. G.; Zhang, J. L.; M. Kintner-Meyer, C. W.; Lu, X. C.; Choi, D. W.; Lemmon, J. P.; Liu, B. J. Chem. Rev. 2011, 111, 3577. doi: 10.1021/cr100290v doi: 10.1021/cr100290v
4. [4]
  Dunn, B.; Kamath, H.; Tarascon, J. M. Science 2011, 334, 928. doi: 10.1126/science.1212741 doi: 10.1126/science.1212741
5. [5]
  Chu, S.; Majumdar, A. Nature 2012, 488, 294. doi: 10.1038/nature11475 doi: 10.1038/nature11475
6. [6]
  Armand, M.; Tarascon, J. M. Nature 2008, 451, 652. doi: 10.1038/451652a doi: 10.1038/451652a
7. [7]
  Thackeray, M. M.; Wolverton, C.; Isaacs, E. D. Energy Environ. Sci 2012, 5, 7854. doi: 10.1039/c2ee21892e doi: 10.1039/c2ee21892e
8. [8]
  Chu, S.; Cui, Y.; Liu, N. Nat. Mater. 2017, 16, 16. doi: 10.1038/nmat4834 doi: 10.1038/nmat4834
9. [9]
  Janek, J.; Zeier, W. G. Nat. Energy 2016, 1, 16141. doi: 10.1038/nenergy.2016.141 doi: 10.1038/nenergy.2016.141
10. [10]
  Choi, N. S.; Chen, Z. H.; Freunberger, S. A.; Ji, X. L.; Sun, Y. K.; Amine, K.; Yushin, G.; Nazar, L. F.; Cho, J.; Bruce, P. G. Angew. Chem. Int. Ed. 2012, 51, 9994. doi: /10.1002/anie.201201429 doi: 10.1002/anie.201201429
11. [11]
  Li, S.; Jiang, M. W.; Xie, Y.; Xu, H.; Jia, J. Y.; Li, J. Adv. Mater. 2018, 30, 1706375. doi: 10.1002/adma.201706375 doi: 10.1002/adma.201706375
12. [12]
  Liu, B.; Zhang, J. G.; Xu, W. Joule 2018, 2, 833. doi: 10.1016/j.joule.2018.03.008 doi: 10.1016/j.joule.2018.03.008
13. [13]
  Liu, S.; Yao, L.; Zhang, Q.; Li, L. L.; Hu, N. T.; Wei, L. M.; Wei, H. Acta Phys. -Chim. Sin.2017, 33, 2339. doi: 10.3866/PKU.WHXB201706021
14. [14]
  Lin, D. C.; Liu, Y. Y.; Cui, Y. Nat. Nanotech.2017, 12, 194. doi: 10.1038/nnano.2017.16 doi: 10.1038/nnano.2017.16
15. [15]
  Bruce, P. G.; Freunberger, S. A.; Hardwick, L. J.; Tarascon, J. M. Nat. Mater.2012, 11, 19. doi: 10.1038/nmat3191 doi: 10.1038/nmat3191
16. [16]
  Mizuno, F.; Arthur, T. S.; Takechi, K. ACS Energy Lett. 2016, 1, 542. doi: 10.1021/acsenergylett.6b00200 doi: 10.1021/acsenergylett.6b00200
17. [17]
  Tikekar, M. D.; Choudhury, S.; Tu, Z. Y.; Archer, L. A. Nat. Energy 2016, 1, 1. doi: 10.1038/nenergy.2016.114 doi: 10.1038/nenergy.2016.114
18. [18]
  Li, P. R.; Xu, T. H.; Ding, P.; Deng, J.; Zha, C. Y.; Wu, Y. L.; Wang, Y. Y.; Li, Y. G. Energy Storage Mater. 2018, 15, 8. doi: 10.1016/j.ensm.2018.03.008 doi: 10.1016/j.ensm.2018.03.008
19. [19]
  Zhang, X. Q.; Chen, X.; Cheng, X. B.; Li, B. Q.; Shen, X.; Yan, C.; Huang, J. Q.; Zhang, Q. Angew. Chem. Int. Ed. 2018, 57, 5301. doi: 10.1002/anie.201801513 doi: 10.1002/anie.201801513
20. [20]
  Wang, Q.; Yang, C. K.; Yang, J. J.; Wu, K.; Hu, C. J.; Lu, J.; Liu, W.; Sun, X. M.; Qiu, J. Y.; Zhou, H. H. Adv. Mater. 2019, 31, 1903248. doi: 10.1002/adma.201903248 doi: 10.1002/adma.201903248
21. [21]
  Wang, Q.; Yang, C. K.; Zhang, Y. F.; Yang, J. J.; Wu, K.; Hu, C. J.; Lu, J.; Liu, W.; Zhou, H. H. ACS Appl. Energy Mater. 2019, 2, 4602. doi: 10.1021/acsaem.9b00929 doi: 10.1021/acsaem.9b00929
22. [22]
  Zheng, G. Y.; Lee, S. W.; Liang, Z.; Lee, H. W.; Yan, K.; Yao, H. B.; Wang, H. T.; Li, W. Y.; Chu, S.; Cui, Y. Nat. Nanotechnol. 2014, 9, 618. doi: 10.1038/nnano.2014.152 doi: 10.1038/nnano.2014.152
23. [23]
  Zhu, B.; Jin, Y.; Hu, X. Z.; Zheng, Q. H.; Zhang, S.; Wang, Q. J.; Zhu, J. Adv. Mater. 2017, 29, 1603755. doi: 10.1002/adma.201603755 doi: 10.1002/adma.201603755
24. [24]
  Lu, L. L.; Ge, J.; Yang, J. N.; Chen, S. M.; Yao, H. B.; Zhou, F.; Yu, S. H. Nano Lett. 2016, 16, 4431. doi: 10.1021/acs.nanolett.6b01581 doi: 10.1021/acs.nanolett.6b01581
25. [25]
  Wang, Q.; Yang, C. K.; Yang, J. J.; Wu, K.; Qi, L. Y.; Tang, H.; Zhang, Z. Y.; Liu, W.; Zhou, H. H. Energy Storage Mater. 2018, 15, 249. doi: 10.1016/j.ensm.2018.04.030 doi: 10.1016/j.ensm.2018.04.030
26. [26]
  Yang, C. P.; Yin, Y. X.; Zhang, S. F.; Li, N. W.; Guo, Y. G. Nat. Commun.2015, 6, 8058. doi: 10.1038/ncomms9058 doi: 10.1038/ncomms9058
27. [27]
  Chao, J. F.; Zhang, X. T.; Xing, S. M.; Fan, Q. F.; Yang, J. P.; Zhao, L. H.; Li, X. Mater. Sci. Eng. B-Solid State Mater. Adv. 2016, 210, 24. doi: 10.1016/j.mseb.2016.03.007 doi: 10.1016/j.mseb.2016.03.007
28. [28]
  Cheng, X. B.; Yan, C.; Peng, H. J.; Huang, J. Q.; Yang, S. T.; Zhang, Q. Energy Storage Mater. 2018, 10, 199. doi: 10.1016/j.ensm.2017.03.008 doi: 10.1016/j.ensm.2017.03.008
29. [29]
  Wan, G. J.; Guo, F. H.; Li, H.; Cao, Y. L.; Ai, X. P.; Qian, J. F.; Li, Y. X.; Yang, H. X. ACS Appl. Mater. Interfaces 2018, 10, 593. doi: 10.1021/acsami.7b14662 doi: 10.1021/acsami.7b14662
1. [1]
  Zhiyuan TONG , Ziyuan LI , Ke ZHANG . Three-dimensional porous collector based on Cu-Li_6.4La₃Zr_1.4Ta_0.6O₁₂ composite layer for the construction of stable lithium metal anode. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 499-508. doi: 10.11862/CJIC.20240238
2. [2]
  Yifeng Xu , Jiquan Liu , Bin Cui , Yan Li , Gang Xie , Ying Yang . “Xiao Li’s School Adventures: The Working Principles and Safety Risks of Lithium-ion Batteries”. University Chemistry, 2024, 39(9): 259-265. doi: 10.12461/PKU.DXHX202404009
3. [3]
  .
  南开大学师唯/华北电力大学（保定）刘景维：二维配位聚合物中有序的亲锂冠醚位点用于无枝晶锂沉积
  . CCS Chemistry, 2025, 7(0): -.
4. [4]
  Xueyu Lin , Ruiqi Wang , Wujie Dong , Fuqiang Huang . 高性能双金属氧化物负极的理性设计及储锂特性. Acta Physico-Chimica Sinica, 2025, 41(3): 2311005-. doi: 10.3866/PKU.WHXB202311005
5. [5]
  Bowen Yang , Rui Wang , Benjian Xin , Lili Liu , Zhiqiang Niu . C-SnO₂/MWCNTs Composite with Stable Conductive Network for Lithium-based Semi-Solid Flow Batteries. Acta Physico-Chimica Sinica, 2025, 41(2): 100015-. doi: 10.3866/PKU.WHXB202310024
6. [6]
  Junke LIU , Kungui ZHENG , Wenjing SUN , Gaoyang BAI , Guodong BAI , Zuwei YIN , Yao ZHOU , Juntao LI . Preparation of modified high-nickel layered cathode with LiAlO₂/cyclopolyacrylonitrile dual-functional coating. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1461-1473. doi: 10.11862/CJIC.20240189
7. [7]
  Xiaoning TANG , Junnan LIU , Xingfu YANG , Jie LEI , Qiuyang LUO , Shu XIA , An XUE . Effect of sodium alginate-sodium carboxymethylcellulose gel layer on the stability of Zn anodes. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1452-1460. doi: 10.11862/CJIC.20240191
8. [8]
  Wenxiu Yang , Jinfeng Zhang , Quanlong Xu , Yun Yang , Lijie Zhang . Bimetallic AuCu Alloy Decorated Covalent Organic Frameworks for Efficient Photocatalytic Hydrogen Production. Acta Physico-Chimica Sinica, 2024, 40(10): 2312014-. doi: 10.3866/PKU.WHXB202312014
9. [9]
  Xi Xu , Chaokai Zhu , Leiqing Cao , Zhuozhao Wu , Cao Guan . Experiential Education and 3D-Printed Alloys: Innovative Exploration and Student Development. University Chemistry, 2024, 39(2): 347-357. doi: 10.3866/PKU.DXHX202308039
10. [10]
  Yiping HUANG , Liqin TANG , Yufan JI , Cheng CHEN , Shuangtao LI , Jingjing HUANG , Xuechao GAO , Xuehong GU . Hollow fiber NaA zeolite membrane for deep dehydration of ethanol solvent by vapor permeation. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 225-234. doi: 10.11862/CJIC.20240224
11. [11]
  Xiaomei Ning , Liang Zhan , Xiaosong Zhou , Jin Luo , Xunfu Zhou , Cuifen Luo . Preparation and Electro-Oxidation Performance of PtBi Supported on Carbon Cloth: A Recommended Comprehensive Chemical Experiment. University Chemistry, 2024, 39(11): 217-224. doi: 10.3866/PKU.DXHX202401085
12. [12]
  Xin Han , Zhihao Cheng , Jinfeng Zhang , Jie Liu , Cheng Zhong , Wenbin Hu . Design of Amorphous High-Entropy FeCoCrMnBS (Oxy) Hydroxides for Boosting Oxygen Evolution Reaction. Acta Physico-Chimica Sinica, 2025, 41(4): 100033-. doi: 10.3866/PKU.WHXB202404023
13. [13]
  Juan WANG , Zhongqiu WANG , Qin SHANG , Guohong WANG , Jinmao LI . NiS and Pt as dual co-catalysts for the enhanced photocatalytic H₂ production activity of BaTiO₃ nanofibers. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1719-1730. doi: 10.11862/CJIC.20240102
14. [14]
  Yu Guo , Zhiwei Huang , Yuqing Hu , Junzhe Li , Jie Xu . 钠离子电池中铁基异质结构负极材料的最新研究进展. Acta Physico-Chimica Sinica, 2025, 41(3): 2311015-. doi: 10.3866/PKU.WHXB202311015
15. [15]
  Yinyin Qian , Rui Xu . Utilizing VESTA Software in the Context of Material Chemistry: Analyzing Twin Crystal Nanostructures in Indium Antimonide. University Chemistry, 2024, 39(3): 103-107. doi: 10.3866/PKU.DXHX202307051
16. [16]
  Shijie Li , Ke Rong , Xiaoqin Wang , Chuqi Shen , Fang Yang , Qinghong Zhang . Design of Carbon Quantum Dots/CdS/Ta₃N₅ S-Scheme Heterojunction Nanofibers for Efficient Photocatalytic Antibiotic Removal. Acta Physico-Chimica Sinica, 2024, 40(12): 2403005-. doi: 10.3866/PKU.WHXB202403005
17. [17]
  Qiuyang LUO , Xiaoning TANG , Shu XIA , Junnan LIU , Xingfu YANG , Jie LEI . Application of a densely hydrophobic copper metal layer in-situ prepared with organic solvents for protecting zinc anodes. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1243-1253. doi: 10.11862/CJIC.20240110
18. [18]
  Yuting ZHANG , Zunyi LIU , Ning LI , Dongqiang ZHANG , Shiling ZHAO , Yu ZHAO . Nickel vanadate anode material with high specific surface area through improved co-precipitation method: Preparation and electrochemical properties. Chinese Journal of Inorganic Chemistry, 2024, 40(11): 2163-2174. doi: 10.11862/CJIC.20240204
19. [19]
  Shanghua Li , Malin Li , Xiwen Chi , Xin Yin , Zhaodi Luo , Jihong Yu . 基于高离子迁移动力学的取向ZnQ分子筛保护层实现高稳定水系锌金属负极的构筑. Acta Physico-Chimica Sinica, 2025, 41(1): 2309003-. doi: 10.3866/PKU.WHXB202309003
20. [20]
  Ziliang KANG , Jiamin ZHANG , Hong AN , Xiaohua LIU , Yang CHEN , Jinping LI , Libo LI . Preparation and water adsorption properties of CaCl₂@MOF-808 in-situ composite moulded particles. Chinese Journal of Inorganic Chemistry, 2024, 40(11): 2133-2140. doi: 10.11862/CJIC.20240282

Get Citation

PDF

XML

Metrics

PDF Downloads(26)
Abstract views(1572)
HTML views(309)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Lithiophilic 3D SnS2@Carbon Fiber Cloth for Stable Li Metal Anode

南开大学师唯/华北电力大学（保定）刘景维：二维配位聚合物中有序的亲锂冠醚位点用于无枝晶锂沉积

Metrics

通讯作者: 陈斌, bchen63@163.com

Lithiophilic 3D SnS₂@Carbon Fiber Cloth for Stable Li Metal Anode