Influence of Reductive Treatment on the Performance of CeO₂-ZrO₂-Al₂O₃ Composite Oxide

1.
National Engineering Research Center of Chemical Fertilizer Catalyst, Fuzhou University, Fuzhou 350002, P. R. China

Received Date: 2 September 2011
Available Online: 7 November 2011
Fund Project: 福建省工业科技重大项目(2010H6014)资助 (2010H6014)

A CeO₂-ZrO₂-Al₂O₃ composite oxide (CZA) and a CeO₂-ZrO₂ composite oxide (CZ) were prepared by the co-precipitation method. The samples were thermally aged in a flowing air atmosphere and in 10% H₂/Ar flow. The structure and performance of the composite oxides were studied by X-ray diffraction (XRD), oxygen storage capacity (OSC) measurements, and H₂ temperature-programmed reduction (H₂- TPR). The results show that a CeAlO₃ phase was formed after CZA was reductively aged at 950 °C and an increase in temperature benefited the formation of CeAlO₃. The OSC of CZA increased with an increase in the reductive treatment temperature and it was 1270.3 μmol·g^-1 when the temperature reached 900 °C. However, the OSC decreased with an increase in the temperature. After CZA was reduced at 1100 °C the OSC was only 23.2 μmol·g^-1. We found that the OSC and the reducibility of the material were remarkably influenced by the formation of a CeAlO₃ phase after CZA was reductively aged.
- CeO₂-ZrO₂-Al₂O₃ composite oxide,
- Reductive treatment,
- CeAlO₃,
- Oxygen storage capacity,
- Reducibility
1. [1]
  (1) Heck, R. M.; Farrauto, R. J. Appl. Catal. A 2001, 221, 443.
2. [2]
  (2) Di Monte, R.; Fornasiero, P.; Desinan, S.; Kaspar, J. Chem. Mater. 2004, 16, 4273.
3. [3]
  (3) Chuang, C. C.; Hsiang, H. I.; Hwang, J. S.;Wang, T. S. J. Alloy. Compd. 2009, 470, 387.
4. [4]
  (4) Kaspar, J.; Fornasiero, P.; Hickey, N. Catal. Today 2003, 77, 419.
5. [5]
  (5) Guo, J. X.; Yuan, S. H.; ng, M. C.; Zhang, L.;Wu, D. D.; Zhao, M.; Chen, Y. Q. Acta Phys. -Chim. Sin. 2007, 23 (1), 73. [郭家秀, 袁书华, 龚茂初, 张磊, 吴冬冬, 赵明, 陈耀强. 物理化学学报, 2007, 23 (1), 73.]
6. [6]
  (6) Wei, Z. L.; Li, H. M.; Zhang, X. Y.; Yan, S. H.; Lv, Z.; Chen, Y. Q.; ng, M. C. J. Alloy. Compd. 2008, 455, 322.
7. [7]
  (7) Zhang, X. Y.; Long, E.Y.; Li, Y. L.; Guo, J. X.; Zhang, L. J.; ng, M. C.;Wang, M. H.; Chen, Y. Q. J. Nat. Gas Chem. 2009, 18, 139.
8. [8]
  (8) Cai, L.; Zhao, M.; Pi, Z.; ng, M. C.; Chen, Y. Q. Chin. J. Catal. 2008, 29, 108. [蔡黎, 赵明,皮展, 龚茂初, 陈耀强. 催化学报, 2008, 29, 108.]
9. [9]
  (9) Cai, L.;Wang, K. C.; Zhao, M.; ng, M. C.; Chen, Y. Q. Acta Phys. -Chim. Sin. 2009, 25 (5), 859. [蔡黎, 王康才, 赵明, 龚茂初, 陈耀强. 物理化学学报, 2009, 25 (5), 859.]
10. [10]
  (10) Morikawa, A.; Suzuki, T.; Kanazawa, T.; Kikuta, K.; Suda, A.; Shinjo, H. Appl. Catal. B 2008, 78, 210.
11. [11]
  (11) Shyu, J. Z.;Weber,W. H.; Gandhi, H. S. J. Phys. Chem. 1988, 92 (17), 4964.
12. [12]
  (12) Miki, T.; Ogawa, T.; Ueno, A.; Matsuura, S.; Sato, M. Chem. Lett. 1988, 565.
13. [13]
  (13) Morikawa, A.; Kikuta, K.; Suda, A.; Shinjo, H. Appl. Catal. B 2009, 88, 542.
14. [14]
  (14) Vidal, H.; Bernal, S., Ka?par, J. Catal. Today 1999, 54, 93.
15. [15]
  (15) Hietikko, M.; Lassi, U.; Kallinen, K.; Savim?ki, A.; H?rk?nen, M.; Pursiainen, J.; Laitinen, R. S.; Keiski, R. L. Appl. Cata. A 2004, 277, 107.
16. [16]
  (16) Lassi, U.; Polvinen, R.; Suhonen, S.; Kallinen, K.; Savim?ki, A.; H?rk?nen, M.; Valden, M.; Keiski, R. L. Appl. Catal. A 2004, 263, 241.
17. [17]
  (17) Wang, J.;Wen, J.; Shen, M. Q. J. Phys. Chem. C 2008, 112, 5113.
18. [18]
  (18) Kishimoto, H.; Omata, T.; Otsuka-Yao-Matsuo,S.; Ueda, K.; Hosono, H.; Kawazoe, H. J. Alloy. Compd. 2000, 312, 94.
19. [19]
  (19) Yamamoto, T.; Suzuki, A.; Nagai, Y.; Tanabe, T.; Dong, F.; Inada, Y.; Nomura, M.; Tada, M.; Iwasawa, Y. Angew. Chem. Int. Edit. 2007, 46, 9253.
20. [20]
  (20) Liotta, L. F.; Lon , A.; Pantaleo, G.; Di Carlo, G.; Martorana, A.; Cimino, S.; Russo, G.; Degandllo, G. Appl. Catal. B 2009, 90, 470.
21. [21]
  (21) Zhu, Q. C.; Li, X. M.; Li, H. M.; Zheng, L. M.; Chen, Y. Q.; ng, M. C. J. Inorg. Mater. 2010, 25 (1), 13. [祝清超, 黎秀敏, 李红梅, 郑灵敏, 陈耀强, 龚茂初. 无机材料学报, 2010, 25 (1), 13.]
22. [22]
  (22) Nagai, Y.; Yamamoto, T.; Tanaka, T.; Yoshida, S.; Nonaka, T.; Okamoto, T.; Suda, A.; Sugiura, M. Catal. Today 2002, 74, 225.
23. [23]
  (23) Wang, H. F.; Guo, Y. L.; Lu, G. Z.; Hu, P. Angew. Chem. Int. Edit. 2009, 48, 8289.
24. [24]
  (24) Prakash, A. S.; Shivakumara, C.; Hegde, M. S. Mater. Sci. Engin. B 2007, 139, 55.
25. [25]
  (25) Kakuta, N.; Ikawa, S.; Eguchi, T.; Murakami, K.; Ohkita, H.; Mizushima, T. J. Alloy. Compd. 2006, 408-412, 1078.
26. [26]
  (26) Damyanova, S.; Pawelec, B.; Arishtirova, K. Appl. Catal. A 2008, 337, 86.
27. [27]
  (27) Fornasiero, P.; DiMonte, R.; Rao, G. R.; Kašpar, J.; Meriani, S.; Trovarelli, A.; Grazinai, M. J. Catal. 1995, 151 (1), 168.
28. [28]
  (28) Yao, M. H.; Baird, R. J.; Kunz, F.W.; Hoost, T. E. J. Catal. 1997, 166 (1), 67.
1. [1]
  Jianyu Qin , Yuejiao An , Yanfeng Zhang . In Situ Assembled ZnWO₄/g-C₃N₄ S-Scheme Heterojunction with Nitrogen Defect for CO₂ Photoreduction. Acta Physico-Chimica Sinica, 2024, 40(12): 2408002-. doi: 10.3866/PKU.WHXB202408002
2. [2]
  Jinyi Sun , Lin Ma , Yanjie Xi , Jing Wang . Preparation and Electrocatalytic Nitrogen Reduction Performance Study of Vanadium Nitride@Nitrogen-Doped Carbon Composite Nanomaterials: A Recommended Comprehensive Chemistry Experiment. University Chemistry, 2024, 39(4): 184-191. doi: 10.3866/PKU.DXHX202310094
3. [3]
  Yanan Liu , Yufei He , Dianqing Li . Preparation of Highly Dispersed LDHs-based Catalysts and Testing of Nitro Compound Reduction Performance: A Comprehensive Chemical Experiment for Research Transformation. University Chemistry, 2024, 39(8): 306-313. doi: 10.3866/PKU.DXHX202401081
4. [4]
  Ping ZHANG , Chenchen ZHAO , Xiaoyun CUI , Bing XIE , Yihan LIU , Haiyu LIN , Jiale ZHANG , Yu'nan CHEN . Preparation and adsorption-photocatalytic performance of ZnAl@layered double oxides. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1965-1974. doi: 10.11862/CJIC.20240014
5. [5]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
6. [6]
  Xiaofeng Zhu , Bingbing Xiao , Jiaxin Su , Shuai Wang , Qingran Zhang , Jun Wang . Transition Metal Oxides/Chalcogenides for Electrochemical Oxygen Reduction into Hydrogen Peroxides. Acta Physico-Chimica Sinica, 2024, 40(12): 2407005-. doi: 10.3866/PKU.WHXB202407005
7. [7]
  Chuanming GUO , Kaiyang ZHANG , Yun WU , Rui YAO , Qiang ZHAO , Jinping LI , Guang LIU . Performance of MnO₂-0.39IrO_x composite oxides for water oxidation reaction in acidic media. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1135-1142. doi: 10.11862/CJIC.20230459
8. [8]
  Kun Xu , Xinxin Song , Zhilei Yin , Jian Yang , Qisheng Song . Comprehensive Experimental Design of Preferential Orientation of Zinc Metal by Heat Treatment for Enhanced Electrochemical Performance. University Chemistry, 2024, 39(4): 192-197. doi: 10.3866/PKU.DXHX202309050
9. [9]
  Zhuo WANG , Junshan ZHANG , Shaoyan YANG , Lingyan ZHOU , Yedi LI , Yuanpei LAN . Preparation and photocatalytic performance of CeO₂-reduced graphene oxide by thermal decomposition. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1708-1718. doi: 10.11862/CJIC.20240067
10. [10]
  Zhihuan XU , Qing KANG , Yuzhen LONG , Qian YUAN , Cidong LIU , Xin LI , Genghuai TANG , Yuqing LIAO . Effect of graphene oxide concentration on the electrochemical properties of reduced graphene oxide/ZnS. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1329-1336. doi: 10.11862/CJIC.20230447
11. [11]
  Limei CHEN , Mengfei ZHAO , Lin CHEN , Ding LI , Wei LI , Weiye HAN , Hongbin WANG . Preparation and performance of paraffin/alkali modified diatomite/expanded graphite composite phase change thermal storage material. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 533-543. doi: 10.11862/CJIC.20230312
12. [12]
  Ming ZHENG , Yixiao ZHANG , Jian YANG , Pengfei GUAN , Xiudong LI . Energy storage and photoluminescence properties of Sm³⁺-doped Ba_0.85Ca_0.15Ti_0.90Zr_0.10O₃ lead-free multifunctional ferroelectric ceramics. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 686-692. doi: 10.11862/CJIC.20230388
13. [13]
  Yi YANG , Shuang WANG , Wendan WANG , Limiao CHEN . Photocatalytic CO₂ reduction performance of Z-scheme Ag-Cu₂O/BiVO₄ photocatalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 895-906. doi: 10.11862/CJIC.20230434
14. [14]
  Jiapei Zou , Junyang Zhang , Xuming Wu , Cong Wei , Simin Fang , Yuxi Wang . A Comprehensive Experiment Based on Electrocatalytic Nitrate Reduction into Ammonia: Synthesis, Characterization, Performance Exploration, and Applicable Design of Copper-based Catalysts. University Chemistry, 2024, 39(6): 373-382. doi: 10.3866/PKU.DXHX202312081
15. [15]
  Yunting Shang , Yue Dai , Jianxin Zhang , Nan Zhu , Yan Su . Something about RGO (Reduced Graphene Oxide). University Chemistry, 2024, 39(9): 273-278. doi: 10.3866/PKU.DXHX202306050
16. [16]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369
17. [17]
  Xuejiao Wang , Suiying Dong , Kezhen Qi , Vadim Popkov , Xianglin Xiang . Photocatalytic CO₂ Reduction by Modified g-C₃N₄. Acta Physico-Chimica Sinica, 2024, 40(12): 2408005-. doi: 10.3866/PKU.WHXB202408005
18. [18]
  Hui Shi , Shuangyan Huan , Yuzhi Wang . Ideological and Political Design of Potassium Permanganate Oxidation-Reduction Titration Experiment. University Chemistry, 2024, 39(2): 175-180. doi: 10.3866/PKU.DXHX202308042
19. [19]
  Tong Zhou , Jun Li , Zitian Wen , Yitian Chen , Hailing Li , Zhonghong Gao , Wenyun Wang , Fang Liu , Qing Feng , Zhen Li , Jinyi Yang , Min Liu , Wei Qi . Experiment Improvement of “Redox Reaction and Electrode Potential” Based on the New Medical Concept. University Chemistry, 2024, 39(8): 276-281. doi: 10.3866/PKU.DXHX202401005
20. [20]
  Ji-Quan Liu , Huilin Guo , Ying Yang , Xiaohui Guo . Calculation and Discussion of Electrode Potentials in Redox Reactions of Water. University Chemistry, 2024, 39(8): 351-358. doi: 10.3866/PKU.DXHX202401031

Get Citation

PDF

XML

Metrics

PDF Downloads(839)
Abstract views(2347)
HTML views(4)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Influence of Reductive Treatment on the Performance of CeO2-ZrO2-Al2O3 Composite Oxide

Metrics

通讯作者: 陈斌, bchen63@163.com

Influence of Reductive Treatment on the Performance of CeO₂-ZrO₂-Al₂O₃ Composite Oxide