Citation: ZHOU Jin, LI Wen, XING Wei, ZHUO Shu-Ping. Capacitive Performance of Tunable Ordered Mesoporous Carbons in Organic and H₂SO₄ Electrolytes[J]. Acta Physico-Chimica Sinica, ;2011, 27(06): 1431-1438. doi: 10.3866/PKU.WHXB20110634 shu

Capacitive Performance of Tunable Ordered Mesoporous Carbons in Organic and H₂SO₄ Electrolytes

1.
School of Chemical Engineering, Shandong University of Technology, Zibo 255049, Shandong Province, P. R. China

Received Date: 28 March 2011
Available Online: 10 May 2011
Fund Project: 山东省优秀中青年科学家科研奖励基金(BS2009NJ014, 2008BS09007)资助项目 (BS2009NJ014, 2008BS09007)

Ordered mesoporous carbon materials were prepared by doping boric acid using a hard- templating method. The capacitive performance of these carbons was investigated in organic and H₂SO₄ electrolytes. As demonstrated by structure analysis the prepared carbons possessed parallel mesoporous channels. The pore size increased from 3.3 to 5.7 nm and the molar fraction of oxygenated groups on the carbon surface increased from 2.0% to 5.2% with an increase in the amount of boric acid doping from 0 to 50% (molar fraction). In the organic electrolyte, the carbons mainly showed typical electric double layer capacitive performance and no visible pseudo-capacitance was induced. In H₂SO₄ electrolytes, BOMC-5 showed the highest specific mass capacitance of 140.9 F·g^-1 and the specific surface capacitance of the prepared carbons increased with an increase in the oxygenated groups and this carbon showed visible pseudo-capacitance because of the rapid redox reactions of the oxygenated groups. The capacitance retention ratio depends on the surface chemical properties, which determines the wettability of the carbon surface and the electrolytes.
- Ordered mesoporous carbon,
- Organic electrolyte,
- H₂SO₄ electrolyte,
- Supercapacitor,
- Surface chemical property
1. [1]
  
  (1) Conway, B. E. Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications; Chemical Industry Press: Beijing, 2005; translated by Chen, A.,Wu, M. Q., Zhang, X. L., Gao, N.W.
2. [2]
  [Conway, B. E. 电化学超级电容器——科学原理及技术应用. 陈艾, 吴孟强, 张绪礼, 高能武, 译. 北京: 化学工业出版社, 2005.]
3. [3]
  (2) Aricò, A. S.; Bruce, P.; Scrosati, B.; Tarascon, J. M.; Van Schalkwijk,W. Nat. Mater. 2005, 4, 366.
4. [4]
  (3) Li, L. M.; Liu, E. H.; Li, J.; Yang, Y. J.; Shen, H. J.; Huang, Z. Z.; Xiang, X. X. Acta Phys. -Chim. Sin. 2010, 26, 1521.
5. [5]
  [李利民, 刘恩辉, 李剑, 杨艳静, 沈海杰, 黄铮铮, 向晓霞. 物理化学学报, 2010, 26, 1521.]
6. [6]
  (4) Ji, Q. Q.; Guo, P. Z.; Zhao. X. S. Acta Phys. -Chim. Sin. 2010, 26, 1254.
7. [7]
  [季倩倩, 郭培志, 赵修松. 物理化学学报, 2010, 26, 1254.]
8. [8]
  (5) Pandolfo, A. G.; Hollenkamp, A. F. J. Power Sources 2006, 157, 11.
9. [9]
  (6) Liu, Y. X.; Li, L. X.; Chen, X. H.; Song, H. H. Acta Phys. -Chim. Sin. 2007, 23, 1399.
10. [10]
  [刘宇林, 李丽霞, 陈晓红, 宋怀河. 物理化学学报, 2007, 23, 1399.]
11. [11]
  (7) Zhou, J.; Yuan, X.; Xing,W.; Si,W.; Zhuo, S. Carbon 2010, 48, 2765.
12. [12]
  (8) Li,W.; Zhou, J.; Xing,W.; Zhuo, S. Lü, Y. Acta Phys. -Chim. Sin. 2011, 27, 620.
13. [13]
  [李文, 周晋, 邢伟, 禚淑萍, 吕忆民. 物理化学学报, 2011, 27, 620.]
14. [14]
  (9) Itoi, H.; Nishihara, H.; Kogure, T.; Kyotani, T. J. Am. Chem. Soc. 2011, 133, 1165.
15. [15]
  (10) Kajdos, A.; Kvit, A.; Jones, F.; Jagiello, J. Yushin, G. J. Am. Chem. Soc. 2010, 132, 3252.
16. [16]
  (11) Daffos, B.; Taberna, P. L.; sti, Y.; Simon, P. Fuel Cell 2010, 10, 819.
17. [17]
  (12) Jin, J.; Tanaka, S.; Egashira, Y.; Nishiyama, N. Carbon 2010, 45, 1985.
18. [18]
  (13) Xing,W.; Huang, C. C.; Zhuo, S. P.; Yuan, X.;Wang, G. Q.; Hulicova-Jurcakova, D.; Yan, Z. F.; Lu, G. Q. Carbon 2009, 47, 1715.
19. [19]
  (14) Kim,W.; Joo, J. B.; Kim, N.; Oh, S.; Kim, P.; Yi, J. Carbon 2009, 47, 1407.
20. [20]
  (15) Fuertes, A. B.; Lota, G.; Centeno, T. A.; Frackowiak, E. Electrochimica Acta 2005, 50, 2799.
21. [21]
  (16) Banham, D.; Feng, F.; Burt, J.; Alsrayheen, E.; Birss, V. Carbon 2010, 48, 1056.
22. [22]
  (17) Jiang, J.; Gao, Q.; Xia, K.; Hu, J. Microporous Mesoporous Mat. 2009, 118, 28.
23. [23]
  (18) Li, L.; Song, H.; Chen, X. Electrochimica Acta 2006, 51, 5715.
24. [24]
  (19) Xing,W.; Qiao, S. Z.; Ding, R. G.; Li, F.; Lu, G. Q.; Yan, Z. F.; Cheng, H. M. Carbon 2006, 44, 216.
25. [25]
  (20) Wang, D.; Li, F; Fang, H. T.; Liu. M.; Lu, G.; Cheng, H. J. Phys. Chem. B 2006, 110, 8570.
26. [26]
  (21) Li, H. Q.; Luo, J.; Zhou, X. F.; Yu, C. Z.; Xia, Y. J. Electrochem. Soc. 2007, 154, A731.
27. [27]
  (22) Wang, D.W.; Li, F.; Liu, M.; Lu, G. Q.; Cheng, H. J. Phys. Chem. C 2008, 112, 9950.
28. [28]
  (23) Jang, I. Y.; Muramatsu, H.; Park, K. C.; Kim, Y. J.; Endo, M. Electrochem. Commun. 2009, 11, 719.
29. [29]
  (24) Zhao, D.; Feng, J.; Huo, Q.; Melosh, N.; Fredrickson, G. H.; Chmelka, B. F.; Stucky, G. D. Science 1998, 279, 548.
30. [30]
  (25) Jun, S.; Joo, S. H.; Ryoo, R.; Kruk, M.; Jaroniec, M.; Liu, Z.; Ohsuna, T.; Terasaki, O. J. Am. Chem. Soc. 2000, 122, 10712.
31. [31]
  (26) Wang, D.; Li, F.; Liu, M.; Cheng, H. M. New Carbon Materials 2007, 22, 307.
1. [1]
  Zhaomei LIU , Wenshi ZHONG , Jiaxin LI , Gengshen HU . Preparation of nitrogen-doped porous carbons with ultra-high surface areas for high-performance supercapacitors. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 677-685. doi: 10.11862/CJIC.20230404
2. [2]
  Yanhui XUE , Shaofei CHAO , Man XU , Qiong WU , Fufa WU , Sufyan Javed Muhammad . Construction of high energy density hexagonal hole MXene aqueous supercapacitor by vacancy defect control strategy. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1640-1652. doi: 10.11862/CJIC.20240183
3. [3]
  Jin CHANG . Supercapacitor performance and first-principles calculation study of Co-doping Ni(OH)₂. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1697-1707. doi: 10.11862/CJIC.20240108
4. [4]
  Jiahong ZHENG , Jingyun YANG . Preparation and electrochemical properties of hollow dodecahedral CoNi₂S₄ supported by MnO₂ nanowires. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1881-1891. doi: 10.11862/CJIC.20240170
5. [5]
  Jiahong ZHENG , Jiajun SHEN , Xin BAI . Preparation and electrochemical properties of nickel foam loaded NiMoO₄/NiMoS₄ composites. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 581-590. doi: 10.11862/CJIC.20230253
6. [6]
  Feiya Cao , Qixin Wang , Pu Li , Zhirong Xing , Ziyu Song , Heng Zhang , Zhibin Zhou , Wenfang Feng . Magnesium-Ion Conducting Electrolyte Based on Grignard Reaction: Synthesis and Properties. University Chemistry, 2024, 39(3): 359-368. doi: 10.3866/PKU.DXHX202308094
7. [7]
  Kuaibing Wang , Honglin Zhang , Wenjie Lu , Weihua Zhang . Experimental Design and Practice for Recycling and Nickel Content Detection from Waste Nickel-Metal Hydride Batteries. University Chemistry, 2024, 39(11): 335-341. doi: 10.12461/PKU.DXHX202403084
8. [8]
  Liang MA , Honghua ZHANG , Weilu ZHENG , Aoqi YOU , Zhiyong OUYANG , Junjiang CAO . Construction of highly ordered ZIF-8/Au nanocomposite structure arrays and application of surface-enhanced Raman spectroscopy. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1743-1754. doi: 10.11862/CJIC.20240075
9. [9]
  Yuanpei ZHANG , Jiahong WANG , Jinming HUANG , Zhi HU . Preparation of magnetic mesoporous carbon loaded nano zero-valent iron for removal of Cr(Ⅲ) organic complexes from high-salt wastewater. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1731-1742. doi: 10.11862/CJIC.20240077
10. [10]
  Lu XU , Chengyu ZHANG , Wenjuan JI , Haiying YANG , Yunlong FU . Zinc metal-organic framework with high-density free carboxyl oxygen functionalized pore walls for targeted electrochemical sensing of paracetamol. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 907-918. doi: 10.11862/CJIC.20230431
11. [11]
  Jing SU , Bingrong LI , Yiyan BAI , Wenjuan JI , Haiying YANG , Zhefeng Fan . Highly sensitive electrochemical dopamine sensor based on a highly stable In-based metal-organic framework with amino-enriched pores. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1337-1346. doi: 10.11862/CJIC.20230414
12. [12]
  Wen LUO , Lin JIN , Palanisamy Kannan , Jinle HOU , Peng HUO , Jinzhong YAO , Peng WANG . Preparation of high-performance supercapacitor based on bimetallic high nuclearity titanium-oxo-cluster based electrodes. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 782-790. doi: 10.11862/CJIC.20230418
13. [13]
  Tianyun Chen , Ruilin Xiao , Xinsheng Gu , Yunyi Shao , Qiujun Lu . Synthesis, Crystal Structure, and Mechanoluminescence Properties of Lanthanide-Based Organometallic Complexes. University Chemistry, 2024, 39(5): 363-370. doi: 10.3866/PKU.DXHX202312017
14. [14]
  Yutong Dong , Huiling Xu , Yucheng Zhao , Zexin Zhang , Ying Wang . The Hidden World of Surface Tension and Droplets. University Chemistry, 2024, 39(6): 357-365. doi: 10.3866/PKU.DXHX202312022
15. [15]
  Yihao Zhao , Jitian Rao , Jie Han . Synthesis and Photochromic Properties of 3,3-Diphenyl-3H-Naphthopyran: Design and Teaching Practice of a Comprehensive Organic Experiment. University Chemistry, 2024, 39(10): 149-155. doi: 10.3866/PKU.DXHX202402050
16. [16]
  Fuxian Wan , Ying Li , Yuanhong Zhang , Shuhua Zhu , Jing Xu , Yanfang Wang , Lili Zhang . Exploration and Practice of Teaching in Agricultural Characteristic Organic Chemistry Course. University Chemistry, 2024, 39(2): 298-306. doi: 10.3866/PKU.DXHX202308041
17. [17]
  Zhichang Xiao , Xiaohui Li , Ling Zhang , Huimin Liu . Exploration of Ideological and Political Construction in University Foundation Course of Organic Chemistry. University Chemistry, 2024, 39(2): 314-320. doi: 10.3866/PKU.DXHX202308058
18. [18]
  Gang Liu , Heng Zhang , Ying Ma , Shiling Yuan , Qisheng Song , Zhenghu Xu , Jichao Sun . Exploration and Practice on Improving the Teaching Quality of Organic Chemistry Laboratory Course. University Chemistry, 2024, 39(4): 70-74. doi: 10.3866/PKU.DXHX202309079
19. [19]
  Houjin Li , Wenjian Lan . Name Reactions in University Organic Chemistry Laboratory. University Chemistry, 2024, 39(4): 268-279. doi: 10.3866/PKU.DXHX202310016
20. [20]
  Yong Wang , Yingying Zhao , Boshun Wan . Analysis of Organic Questions in the 37th Chinese Chemistry Olympiad (Preliminary). University Chemistry, 2024, 39(11): 406-416. doi: 10.12461/PKU.DXHX202403009

Get Citation

PDF

XML

Metrics

PDF Downloads(984)
Abstract views(2434)
HTML views(4)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Capacitive Performance of Tunable Ordered Mesoporous Carbons in Organic and H2SO4 Electrolytes

Metrics

通讯作者: 陈斌, bchen63@163.com

Capacitive Performance of Tunable Ordered Mesoporous Carbons in Organic and H₂SO₄ Electrolytes