Citation: LIU Chun-ling, WEN Yue-hua, CHENG Jie, GUO Quan-gui, CAO Gao-ping, LIU Lang, YANG Yu-sheng. Influence of Pore Structure of Phenolic Resin Based Activated Carbon Fibers on the Electrochemical Performance of Electrical Double-layer Capacitors[J]. Acta Physico-Chimica Sinica, ;2005, 21(07): 786-791. doi: 10.3866/PKU.WHXB20050717 shu

Influence of Pore Structure of Phenolic Resin Based Activated Carbon Fibers on the Electrochemical Performance of Electrical Double-layer Capacitors

1.
Key laboratory of carbon Materials, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001；Research Institute of Chemical Defense, Beijing 100083

Received Date: 14 December 2004
Available Online: 15 July 2005

Phenolic resin based activated carbon fibers (ACF-H2O) prepared using steam activation at 800 ℃ were investigated by means of N2 adsorption, AC impedance and constant current discharge techniques. The relationship between the specific surface area and pore size distribution of ACF-H2O with their electrochemical performance as electrodes of electric double layer capacitors (EDLC) in 1 mol•L-1 LiClO4/PC was discussed in detail. It is found that the ultramicropores(d ＜ 0.7 nm＝ cannot be accessed by electrolyte solution. With increasing steam activation time, the specific surface area and pore volume increase gradually, whereas the micropore (2.0 nm＞ d ＞ 0.7 nm ) and meso-pore ratios change little due to the deepening and broadening of the micropore formed during carbonization. However, excessive activation destroyed the pore structure, causing a sharp decrease of both specific surface area and pore volume. For those samples with well-developed pore structure, there is a linear relationship between capacitance and specific surface area (C－S), and a maximum specific capacitance of 109.6 F•g-1 was achieved. The double layer capacitance per unit surface area is not the same for all porous surface, and the capacitances of 8.44 μF•cm-2 and 4.29 μF•cm-2 are obtained, for the micropore and mesopore surfaces respectively. The double layer capacitance and AC impedance data strongly depend on the porous structure, the bigger the pore, the easier and faster being accessed electrochemically, the less the time constant and resistance should be, and it can be discharged/charged at higher current density. ACF with larger pore surface and less ultramicropore is desirable for those applications either as energy devices or as power storage devices. Steam activation can only obtain carbon materials with small mesopore, thus the higher electrochemical behavior attainable in EDLC using non-aqueous electrolyte is restricted.
- Phenolic resin based activated carbon fiber;Pore structure; Electrochemical performance
1. [1]
  Kun Xu , Xinxin Song , Zhilei Yin , Jian Yang , Qisheng Song . Comprehensive Experimental Design of Preferential Orientation of Zinc Metal by Heat Treatment for Enhanced Electrochemical Performance. University Chemistry, 2024, 39(4): 192-197. doi: 10.3866/PKU.DXHX202309050
2. [2]
  Xinpeng LIU , Liuyang ZHAO , Hongyi LI , Yatu CHEN , Aimin WU , Aikui LI , Hao HUANG . Ga₂O₃ coated modification and electrochemical performance of Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ cathode material. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1105-1113. doi: 10.11862/CJIC.20230488
3. [3]
  Jiahong ZHENG , Jiajun SHEN , Xin BAI . Preparation and electrochemical properties of nickel foam loaded NiMoO₄/NiMoS₄ composites. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 581-590. doi: 10.11862/CJIC.20230253
4. [4]
  Qi Li , Pingan Li , Zetong Liu , Jiahui Zhang , Hao Zhang , Weilai Yu , Xianluo Hu . Fabricating Micro/Nanostructured Separators and Electrode Materials by Coaxial Electrospinning for Lithium-Ion Batteries: From Fundamentals to Applications. Acta Physico-Chimica Sinica, 2024, 40(10): 2311030-. doi: 10.3866/PKU.WHXB202311030
5. [5]
  Zhihuan XU , Qing KANG , Yuzhen LONG , Qian YUAN , Cidong LIU , Xin LI , Genghuai TANG , Yuqing LIAO . Effect of graphene oxide concentration on the electrochemical properties of reduced graphene oxide/ZnS. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1329-1336. doi: 10.11862/CJIC.20230447
6. [6]
  Qin ZHU , Jiao MA , Zhihui QIAN , Yuxu LUO , Yujiao GUO , Mingwu XIANG , Xiaofang LIU , Ping NING , Junming GUO . Morphological evolution and electrochemical properties of cathode material LiAl_0.08Mn_1.92O₄ single crystal particles. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1549-1562. doi: 10.11862/CJIC.20240022
7. [7]
  Qingtang ZHANG , Xiaoyu WU , Zheng WANG , Xiaomei WANG . Performance of nano Li₂FeSiO₄/C cathode material co-doped by potassium and chlorine ions. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1689-1696. doi: 10.11862/CJIC.20240115
8. [8]
  Lu XU , Chengyu ZHANG , Wenjuan JI , Haiying YANG , Yunlong FU . Zinc metal-organic framework with high-density free carboxyl oxygen functionalized pore walls for targeted electrochemical sensing of paracetamol. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 907-918. doi: 10.11862/CJIC.20230431
9. [9]
  Jing SU , Bingrong LI , Yiyan BAI , Wenjuan JI , Haiying YANG , Zhefeng Fan . Highly sensitive electrochemical dopamine sensor based on a highly stable In-based metal-organic framework with amino-enriched pores. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1337-1346. doi: 10.11862/CJIC.20230414
10. [10]
  Yuanchao LI , Weifeng HUANG , Pengchao LIANG , Zifang ZHAO , Baoyan XING , Dongliang YAN , Li YANG , Songlin WANG . Effect of heterogeneous dual carbon sources on electrochemical properties of LiMn_0.8Fe_0.2PO₄/C composites. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 751-760. doi: 10.11862/CJIC.20230252
11. [11]
  Jiahong ZHENG , Jingyun YANG . Preparation and electrochemical properties of hollow dodecahedral CoNi₂S₄ supported by MnO₂ nanowires. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1881-1891. doi: 10.11862/CJIC.20240170
12. [12]
  Jinyao Du , Xingchao Zang , Ningning Xu , Yongjun Liu , Weisi Guo . Electrochemical Thiocyanation of 4-Bromoethylbenzene. University Chemistry, 2024, 39(6): 312-317. doi: 10.3866/PKU.DXHX202310039
13. [13]
  Hongyi LI , Aimin WU , Liuyang ZHAO , Xinpeng LIU , Fengqin CHEN , Aikui LI , Hao HUANG . Effect of Y(PO₃)₃ double-coating modification on the electrochemical properties of Li[Ni_0.8Co_0.15Al_0.05]O₂. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1320-1328. doi: 10.11862/CJIC.20230480
14. [14]
  Linbao Zhang , Weisi Guo , Shuwen Wang , Ran Song , Ming Li . Electrochemical Oxidation of Sulfides to Sulfoxides. University Chemistry, 2024, 39(11): 204-209. doi: 10.3866/PKU.DXHX202401009
15. [15]
  Yongming Zhu , Huili Hu , Yuanchun Yu , Xudong Li , Peng Gao . Construction and Practice on New Form Stereoscopic Textbook of Electrochemistry for Energy Storage Science and Engineering: Taking Basic Course of Electrochemistry as an Example. University Chemistry, 2024, 39(8): 44-47. doi: 10.3866/PKU.DXHX202312086
16. [16]
  Liangzhen Hu , Li Ni , Ziyi Liu , Xiaohui Zhang , Bo Qin , Yan Xiong . A Green Chemistry Experiment on Electrochemical Synthesis of Benzophenone. University Chemistry, 2024, 39(6): 350-356. doi: 10.3866/PKU.DXHX202312001
17. [17]
  Yong Zhou , Jia Guo , Yun Xiong , Luying He , Hui Li . Comprehensive Teaching Experiment on Electrochemical Corrosion in Galvanic Cell for Chemical Safety and Environmental Protection Course. University Chemistry, 2024, 39(7): 330-336. doi: 10.3866/PKU.DXHX202310109
18. [18]
  Zhengli Hu , Jia Wang , Yi-Lun Ying , Shaochuang Liu , Hui Ma , Wenwei Zhang , Jianrong Zhang , Yi-Tao Long . Exploration of Ideological and Political Elements in the Development History of Nanopore Electrochemistry. University Chemistry, 2024, 39(8): 344-350. doi: 10.3866/PKU.DXHX202401072
19. [19]
  Yan Liu , Yuexiang Zhu , Luhua Lai . Introduction to Blended and Small-Class Teaching in Structural Chemistry: Exploring the Structure and Properties of Crystals. University Chemistry, 2024, 39(3): 1-4. doi: 10.3866/PKU.DXHX202306084
20. [20]
  Haitang WANG , Yanni LING , Xiaqing MA , Yuxin CHEN , Rui ZHANG , Keyi WANG , Ying ZHANG , Wenmin WANG . Construction, crystal structures, and biological activities of two Ln^Ⅲ₃ complexes. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1474-1482. doi: 10.11862/CJIC.20240188

Get Citation

PDF

XML

Metrics

PDF Downloads(2849)
Abstract views(3804)
HTML views(14)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return