Citation: Liang Jian, Huang Hui-Zhong, Xie You-Chang. The Phases of ZrO₂-Al₂O₃ Composites with High Specific Surface Prepared by Co-precipitation[J]. Acta Physico-Chimica Sinica, ;2003, 19(01): 30-34. doi: 10.3866/PKU.WHXB20030108 shu

The Phases of ZrO₂-Al₂O₃ Composites with High Specific Surface Prepared by Co-precipitation

1.
Institute of Physical Chemistry, State Key Laboratory for Structural Chemistry of Unstable ＆ Stable Species, College of Chemistry and Molecular Engineering, Peking University, Beijing　100871

Received Date: 26 April 2002
Available Online: 15 January 2003

A series of ZrO2-Al2O3 composites with various compositions were synthesized through heat decomposition of metal hydroxides, which were prepared by co-precipitation with NH4OH from aqueous solution of nitrates. The samples were characterized by XRD, XPS and BET measurements. It was found that with content increasing, one component tended to dissolve into the bulk phase of the other to form solid solution first. After the dissolution reached saturation, a component started to disperse onto the surface of the crystallite of the solid solution of the other component. The formation of the separate crystalline phase of one component was observed only when its content was higher than a certain percentage. The XRD peaks of the composites were significantly broadened, and the BET specific surface areas of the composites were larger than those of the pure oxides, which suggested that the crystallites became smaller. The experimental results showed the existence of mutual dispersion of both components in this system. It means that in a certain content range, the crystallite of the solid solution of each component can accept the dispersion of the other component. The phenomenon of mutual dispersion and formation of solid solution would make the crystallites smaller, and lead to higher surface area, since the process could hinder the interface diffusion and crystallite sintering.
- ZrO₂;Al₂O₃;Nanocomposite oxide;　Mutual monolayer dispersion
1. [1]
  Liuyun Chen , Wenju Wang , Tairong Lu , Xuan Luo , Xinling Xie , Kelin Huang , Shanli Qin , Tongming Su , Zuzeng Qin , Hongbing Ji . Soft template-induced deep pore structure of Cu/Al₂O₃ for promoting plasma-catalyzed CO₂ hydrogenation to DME. Acta Physico-Chimica Sinica, 2025, 41(6): 100054-0. doi: 10.1016/j.actphy.2025.100054
2. [2]
  Shiqi Peng , Yongfang Rao , Tan Li , Yufei Zhang , Jun-ji Cao , Shuncheng Lee , Yu Huang . Regulating the electronic structure of Ir single atoms by ZrO₂ nanoparticles for enhanced catalytic oxidation of formaldehyde at room temperature. Chinese Chemical Letters, 2024, 35(7): 109219-. doi: 10.1016/j.cclet.2023.109219
3. [3]
  Chuanming GUO , Kaiyang ZHANG , Yun WU , Rui YAO , Qiang ZHAO , Jinping LI , Guang LIU . Performance of MnO₂-0.39IrO_x composite oxides for water oxidation reaction in acidic media. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1135-1142. doi: 10.11862/CJIC.20230459
4. [4]
  Xiaorui Chen , Xuan Luo , Tongming Su , Xinling Xie , Liuyun Chen , Yuejing Bin , Zuzeng Qin , Hongbing Ji . Ga-doped Cu/γ-Al₂O₃ bifunctional interface sites promote the direct hydrogenation of CO₂ to DME. Acta Physico-Chimica Sinica, 2025, 41(10): 100126-0. doi: 10.1016/j.actphy.2025.100126
5. [5]
  Haotian Zhang , Shengfa Feng , Mufan Cao , Xiong Xiong Liu , Pengcheng Yuan , Yaping Wang , Min Gao , Long Pan , Zhengming Sun . Al₂O₃ coated polyimide porous films enable thin yet strong polymer-in-salt solid-state electrolytes for dendrite-free lithium metal batteries. Chinese Chemical Letters, 2025, 36(8): 111096-. doi: 10.1016/j.cclet.2025.111096
6. [6]
  Lina Guo , Ruizhe Li , Chuang Sun , Xiaoli Luo , Yiqiu Shi , Hong Yuan , Shuxin Ouyang , Tierui Zhang . Effect of Interlayer Anions in Layered Double Hydroxides on the Photothermocatalytic CO₂ Methanation of Derived Ni-Al₂O₃ Catalysts. Acta Physico-Chimica Sinica, 2025, 41(1): 100002-0. doi: 10.3866/PKU.WHXB202309002
7. [7]
  Yaping ZHANG , Tongchen WU , Yun ZHENG , Bizhou LIN . Z-scheme heterojunction β-Bi₂O₃ pillared CoAl layered double hydroxide nanohybrid: Fabrication and photocatalytic degradation property. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 531-539. doi: 10.11862/CJIC.20240256
8. [8]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369
9. [9]
  Feifan Zhao , Feiyan Xu , Jiaguo Yu . Interfacial stabilization of alkali metal oxides on carbon spheres for high-performance CO₂ chemisorption. Acta Physico-Chimica Sinica, 2026, 42(5): 100234-0. doi: 10.1016/j.actphy.2025.100234
10. [10]
  Doudou Liu , Weiwei Guo , Guoliang Mei , Youpeng Dan , Rong Yang , Chao Huang , Yanling Zhai , Xiaoquan Lu . Application of catalyst Cu-t-ZrO₂ based on the electronic metal-support interaction in electrocatalytic nitrate reduction. Chinese Chemical Letters, 2025, 36(8): 110578-. doi: 10.1016/j.cclet.2024.110578
11. [11]
  Shuhao FENG , Feibing XIONG , Yaqing LIN , Han SU , Xu HAN . Preparation and luminescent properties of alkaline metal doped Cd₃Al₂Ge₃O₁₂: Pr³⁺ orange phosphors. Chinese Journal of Inorganic Chemistry, 2026, 42(2): 284-296. doi: 10.11862/CJIC.20250171
12. [12]
  Ruixin XU , Hongtuo LI , Chen SHI , Yanhong YAN . Factors influencing the spectral properties of composite luminescent materials SrTiO₃: Eu³⁺/SrAl₂O₄: Eu²⁺, Dy³⁺. Chinese Journal of Inorganic Chemistry, 2025, 41(11): 2307-2316. doi: 10.11862/CJIC.20250055
13. [13]
  Ruolin CHENG , Yue WANG , Xiyao NIU , Huagen LIANG , Ling LIU , Shijian LU . Efficient photothermal catalytic CO₂ cycloaddition over W₁₈O₄₉/rGO composites. Chinese Journal of Inorganic Chemistry, 2025, 41(7): 1276-1284. doi: 10.11862/CJIC.20240424
14. [14]
  Hongyi LI , Aimin WU , Liuyang ZHAO , Xinpeng LIU , Fengqin CHEN , Aikui LI , Hao HUANG . Effect of Y(PO₃)₃ double-coating modification on the electrochemical properties of Li[Ni_0.8Co_0.15Al_0.05]O₂. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1320-1328. doi: 10.11862/CJIC.20230480
15. [15]
  Zehao Zhang , Zheng Wang , Haibo Li . Preparation of 2D V₂O₃@Pourous Carbon Nanosheets Derived from V₂CF_x MXene for Capacitive Desalination. Acta Physico-Chimica Sinica, 2024, 40(8): 2308020-0. doi: 10.3866/PKU.WHXB202308020
16. [16]
  Shiyi WANG , Chaolong CHEN , Xiangjian KONG , Lansun ZHENG , Lasheng LONG . Polynuclear lanthanide compound [Ce₄^ⅢCe₆^Ⅳ(μ₃-O)₄(μ₄-O)₄(acac)₁₄(CH₃O)₆]·2CH₃OH for the hydroboration of amides to amine. Chinese Journal of Inorganic Chemistry, 2025, 41(1): 88-96. doi: 10.11862/CJIC.20240342
17. [17]
  Guoqiang Chen , Zixuan Zheng , Wei Zhong , Guohong Wang , Xinhe Wu . Molten Intermediate Transportation-Oriented Synthesis of Amino-Rich g-C₃N₄ Nanosheets for Efficient Photocatalytic H₂O₂ Production. Acta Physico-Chimica Sinica, 2024, 40(11): 2406021-0. doi: 10.3866/PKU.WHXB202406021
18. [18]
  Wei Sun , Yongjing Wang , Kun Xiang , Saishuai Bai , Haitao Wang , Jing Zou , Arramel , Jizhou Jiang . CoP Decorated on Ti₃C₂T_x MXene Nanocomposites as Robust Electrocatalyst for Hydrogen Evolution Reaction. Acta Physico-Chimica Sinica, 2024, 40(8): 2308015-0. doi: 10.3866/PKU.WHXB202308015
19. [19]
  Ze Luo , Yukun Zhu , Yadan Luo , Guangmin Ren , Yonghong Wang , Hua Tang . Photocatalytic selective oxidation of 5-hydroxymethylfurfural coupled with H₂ evolution over In₂O₃/ZnIn₂S₄ S-scheme heterojunction. Acta Physico-Chimica Sinica, 2026, 42(3): 100166-0. doi: 10.1016/j.actphy.2025.100166
20. [20]
  Dan LUO , Xingcheng LIU , Dong LI , Tong CHANG . Metal-support interaction effects on CO activation over Co_n/SiO₂ catalysts. Chinese Journal of Inorganic Chemistry, 2025, 41(11): 2337-2344. doi: 10.11862/CJIC.20250003

Get Citation

PDF

XML

Metrics

PDF Downloads(2596)
Abstract views(3757)
HTML views(29)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

The Phases of ZrO2-Al2O3 Composites with High Specific Surface Prepared by Co-precipitation

Metrics

通讯作者: 陈斌, bchen63@163.com

The Phases of ZrO₂-Al₂O₃ Composites with High Specific Surface Prepared by Co-precipitation