Citation: Cun-wei Zhang, Rong-jie Yang, Xiang-mei Li, De-qi Yi. Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study[J]. Chinese Journal of Polymer Science, ;2016, 34(6): 688-696. doi: 10.1007/s10118-016-1791-7 shu

Preparation of Polystyrene/Triphenyl Phosphate Composites by Suspension Polymerization and Melt Extrusion Method——A Comparative Study

a.
National Engineering Research Center of Flame Retardant Materials, School of Materials, Beijing Institute of Technology, Beijing 100081, China
b.
Fire Command Department, Chinese People's Armed Police Forces Academy, Langfang 065000, China

Corresponding author: Xiang-mei Li, bjlglxm@bit.edu.cn
Received Date: 26 November 2015
Revised Date: 28 January 2016
Accepted Date: 18 February 2016

Polystyrene (PS)/triphenyl phosphate (TPP) composites were prepared by both suspension polymerization and melt extrusion, and a comparative study of the flame retardance and mechanical properties was carried out. The results showed that suspension polymerization was a better technique than melt extrusion for obtaining good dispersity of the PS/TPP composite. The TPP nanoparticles, which were approximately 50 nm in size, were homogenously and uniformly dispersed in the PS matrix by suspension polymerization in one-step. However, the PS/TPP composite was partially agglomerated, exhibiting irregularly shaped micron-scale particles as a result of melt extrusion. In contrast to the melt extrusion, the limited oxygen index (LOI) of the PS/TPP nanocomposite by suspension polymerization increased to 22.6% from 21.8%, and time to ignition (TTI) increased by 12.3%, the peak heat release rate (PHRR) decreased by 8.5%, and the total heat release (THR) decreased by 11.0%. The mechanical properties of the PS/TPP nanocomposite by suspension polymerization also increased. The tensile strength, elongation at break, and flexural strength increased by 36.4%, 8.5%, and 108%, respectively.
- Polystyrene,
- Triphenyl phosphate,
- Flame retardance,
- Suspension polymerization,
- Melt extrusion
1. [1]
  Levchik, S.V. and Weil, E.D., Polym. Int., 2008, 57: 431
2. [2]
  Tai, Q.L., Chen, L.J., Song, L., Nie, S.B., Hu, Y. and Yuen, R.K.K., Polym. Degrad. Stab., 2010, 95: 830
3. [3]
  Utevski, L., Scheinker, M., Georlette, P. and Lach, S., J. Fire Sci., 1997, 15: 375
4. [4]
  Chen, L. and Wang, Y.Z., Polym. Adv. Technol., 2010, 21: 1
5. [5]
  Liu, Y.Y., Wang, S.J., Xiao, M. and Meng. Y.Z., Res J Chem Environ, 2007, 11: 84
6. [6]
  Bourbigot, S. and Duquesne, S., J. Mater. Chem., 2007, 17: 2283
7. [7]
  Zhou, K.Q., Zhang, Q.J., Liu, J.J., Wang, B., Jiang, S.H., Shi, Y.Q., Hu, Y. and Gui, Z., RSC Adv., 2014, 4: 13205
8. [8]
  Liu, J.C., Yu, Z.L., Chang, H.B., Zhang, Y.B., Shi, Y.Z., Luo, J., Pan, B.L. and Lu, C., Polym. Degrad. Stab., 2014, 103: 83
9. [9]
  Yan, Y.W., Chen, L., Jian, R.K., Kong, S. and Wang, Y.Z., Polym. Degrad. Stab., 2012, 97: 1423
10. [10]
  Braun, U. and Schartel, B., Macromol. Chem. Phys., 2004, 205: 2185
11. [11]
  Czégény, Z. and Blazso, M., J. Anal. Appl. Pyrolysis, 2008, 81: 218
12. [12]
  Cui, W.G., Guo, F. and Chen, J.F., Fire Safety J., 2007, 42: 232
13. [13]
  Yan, Y.W., Huang, J.Q, Guan, Y.H., Shang, K., Jian, R.K. and Wang, Y.Z., Polym. Degrad. Stab., 2014, 99: 35
14. [14]
  Li, B.Y., Wang, Y.P., Niu, X.B. and Liu, Z.M., Chinese J. Polym. Sci., 2014, 32(2): 123
15. [15]
  Brooks, B. W., Chem. Eng. Technol., 2010, 33: 1737
16. [16]
  Zhou, K.Q., Liu, J.J., Shi, Y.Q., Jiang, S.H., Wang, D., Hu, Y. and Gui, Z., ACS Appl. Mater. Inter., 2015, 7: 6070
17. [17]
  Raheel, M., Yao, K., Gong, J., Chen, X.C., Liu, D.T., Lin, Y.C., Cui, D.M., Siddiq, M. and Tang, T., Chinese J. Polym. Sci., 2015, 33(2): 329
18. [18]
  Alansi, A.M., Alkayali, W.Z., Al-qunaibit, M.H., Qahtan, T.F. and Saleh, T.A., RSC Adv., 2015, 5: 71441
19. [19]
  Xie, X.L., Liu, Q.X., Li, R.K.Y., Zhou, X.P., Zhang, Q.X., Yu, Z.Z. and Mai, Y.W., Polymer, 2004, 45: 6665
20. [20]
  Yang, D.Y., Liu, Q.X., Xie, X.L. and Zeng, F.D., J. Therm. Anal. Calorim., 2006, 84: 355
21. [21]
  Liu, C., Luo, Y.F., Jia, Z.X., Li, S.Q., Huang, D. and Jia, D.M., Polym. Compos., 2014, 35: 856
22. [22]
  Bao, Y.Z., Huang, Z.M. and Weng, Z.X., J. Appl. Polym. Sci., 2006, 102: 1471
23. [23]
  Zheng, Z.H., Li, W.J., Sun, H.M., Cheng, A.Q., Yan, J.T., Wang, H.W. and Cui, X.J., Polym. Compos., 2013, 34: 1110
24. [24]
  Yan, J.T., Miao, X.J., Zhang, Q.Y., Cui, X.J., Li, J.F. and Wang, H.Y., Polym. Eng. Sci., 2011, 51: 294
25. [25]
  Hwu, J.M., Ko, T.H., Yang, W.T., Lin, J.C., Jiang, G.J., Xie, W. and Pan, W.P., J. Appl. Polym. Sci., 2004, 91: 101
26. [26]
  Xie, W., Hwu, J.M., Jiang, G.J., Buthelezi, T.M. and Pan, W.P., Polym. Eng. Sci., 2003, 43: 214
27. [27]
  Wang, W.P. and Pan, C.Y., Polymer, 2004, 45: 3987
28. [28]
  Lee, K., Yoon, K., Kima, J., Bae, J., Yang, J. and Hong, S., Polym. Degrad. Stab., 2003, 81: 173
29. [29]
  Wang, Q.F. and Shi, W.F., Polym. Degrad. Stab., 2006, 91: 1289
30. [30]
  Huang, Z.G. and Shi, W.F., Eur. Polym. J., 2006, 42: 1506
31. [31]
  Muller, N., Lauterbur, P.C. and Goldenson, J., J. Am. Chem. Soc., 1956, 78: 3557
32. [32]
  Armstrong, K.M. and Kilian, P., Eur. J. Inorg. Chem., 2011, 13: 2138
33. [33]
  Chimanowsky, Jr. J.P., Neto, R.P.C. and Tavares, M.I.B., Polym. Degrad. Stab., 2015, 118: 178
34. [34]
  Sanchez-Olivares, G., Sanchez-Solis1, A., Camino, G. and Manero, O., Express Polym. Lett., 2008, 2: 569
35. [35]
  Wang, Y., Jow J., Su, K. and Zhang, J., J. Fire Sci., 2012, 30: 477
36. [36]
  Babrauskas, V. and Peacock, R.D., Fire Safety J., 1992, 18: 255
37. [37]
  Zhou, K.Q., Jiang, S.H., Shi, Y.Q., Liu, J.J., Wang, B., Hu, Y. and Gui, Z., RSC Adv., 2014, 4: 40170
38. [38]
  Ishida, H. and Allen, D.J., Polymer, 1996, 37: 4487
39. [39]
  Rimdusit, S., Thamprasom, N., Suppakarn, N., Jubsilp, C., Takeichi, T. and Tiptipakorn, S., J. Appl. Polym. Sci., 2013, 130: 1074
40. [40]
  Herrera, N., Mathew, A.P. and Oksman, K., Compos. Sci. Technol., 2015, 106: 149
41. [41]
  Zou, H., Sun, J., Gu, X.Y., Jiang, P., Liu, X.S. and Zhang, S., Chinese J. Polym. Sci., 2015, 33(4): 554
42. [42]
  Russo, P., Acierno, D., Rosa, R., Leonelli, C., Corradi, A. and Rizzuti, A., Surf. Coat. Tech., 2014, 243: 65
1. [1]
  Hailong He , Wenbing Wang , Wenmin Pang , Chen Zou , Dan Peng . Double stimulus-responsive palladium catalysts for ethylene polymerization and copolymerization. Chinese Chemical Letters, 2024, 35(7): 109534-. doi: 10.1016/j.cclet.2024.109534
2. [2]
  Lingna Wang , Chenxin Tian , Ruobin Dai , Zhiwei Wang . Eco-friendly regeneration of end-of-life PVDF membrane with triethyl phosphate: Efficiency and mechanism. Chinese Chemical Letters, 2024, 35(9): 109356-. doi: 10.1016/j.cclet.2023.109356
3. [3]
  Xinxiu Yan , Xizhe Huang , Yangyang Liu , Weishang Jia , Hualin Chen , Qi Yao , Tao Chen . Hyperbranched polyamidoamine protective layer with phosphate and carboxyl groups for dendrite-free Zn metal anodes. Chinese Chemical Letters, 2024, 35(10): 109426-. doi: 10.1016/j.cclet.2023.109426
4. [4]
  Xue Zhao , Mengshan Chen , Dan Wang , Haoran Zhang , Guangzhi Hu , Yingtang Zhou . Ultrafine nano-copper derived from dopamine polymerization & synchronous adsorption achieve electrochemical purification of nitrate to ammonia in complex water environments. Chinese Chemical Letters, 2024, 35(8): 109327-. doi: 10.1016/j.cclet.2023.109327
5. [5]
  Fei Yin , Erli Yang , Xue Ge , Qian Sun , Fan Mo , Guoqiu Wu , Yanfei Shen . Coupling WO₃₋_x dots-encapsulated metal-organic frameworks and template-free branched polymerization for dual signal-amplified electrochemiluminescence biosensing. Chinese Chemical Letters, 2024, 35(4): 108753-. doi: 10.1016/j.cclet.2023.108753

Get Citation

PDF

XML

Metrics

PDF Downloads(0)
Abstract views(575)
HTML views(0)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return