Citation: Li Tiantian, Zhao Jikuan, Li Yao, Quan Zhenlan, Xu Jie. Synthesis and Electrochemical Properties of Nitrogen-Doped Partially Graphitized Carbon/Cobalt Iron Oxides Composite[J]. Acta Chimica Sinica, ;2017, 75(5): 485-493. doi: 10.6023/A17010012 shu

Synthesis and Electrochemical Properties of Nitrogen-Doped Partially Graphitized Carbon/Cobalt Iron Oxides Composite

State Key Laboratory Base of Eco-Chemical Engineering (Qingdao University of Science and Technology), College of Chemistry and Molecular Engineering, Qingdao 266042

Corresponding author: Zhao Jikuan, forestzhao@163.com
Received Date: 10 January 2017

Fund Project: the Natural Science Foundation of Shandong Province of China ZR2013BQ013the National Natural Science Foundation of China 21403121the Project of Shandong Province Higher Educational Science and Technology J14LC13

Figures(10)

With the renewable biopolymer chitosan (CTS) as a structure directing agent and organic precursor, facile coprecipitation method was applied for the cobalt and iron nitrates in solution to prepare CTS/cobalt iron layered double hydroxides composite. The LDHs sample was calcinated in a tubular furnace under Ar atmosphere via heating ramps of 5 ℃· min^-1 from room temperature to 200 ℃ and kept for 1 h, then heated to 600 ℃ and remained for 2 h. After the sample was cooled naturally to room temperature, it was heated again to 250 ℃ under air atmosphere and kept for 12 h to oxidize the transition metal elements. As a result, nitrogen-doped partially graphitized carbon/cobalt iron transition metal oxides nanocomposite (N-PGC/CoFe-TMOs) was obtained. X-ray diffraction, Raman spectroscopy, N₂ adsorption-desorption analysis, scanning electron microscopy, high resolution transmission electron microscopy, energy-dispersive X-ray spectroscopy were carried out to characterize the structure, morphology and elemental composition of the product. Cyclic voltammetry and galvanostatic charge-discharge measurements were conducted to evaluate the electrochemical properties of N-PGC/CoFe-TMOs. Experimental results showed that the CTS precursor was converted into partially graphitized carbon by pyrolysis with the help of catalysis graphitization action of transition metal elements. At the same time, the derived carbon material was successfully doped with nitrogen in situ and the N/C atomic ratio was about 1/18. N-PGC/CoFe-TMOs possessed bimodal porous texture including macropores and mesopores, exhibited combined characters of electrical double-layer supercapacitor and pseudocapacitor when used as supercapacitor electrode material. At the current density of 2 A·g^-1, N-PGC/CoFe-TMOs composite delivered a large discharge capacity of 671.1 F·g^-1, far higher than 283.3 F·g^-1 of pure cobalt iron oxides, indicating the typical synergistic effect between nitrogen-doped partially graphitized carbon and transition metal oxides. Even at the high current density of 10 A·g^-1, N-PGC/CoFe-TMOs composite still remained a specific capacity of 573.3 F·g^-1. After 5000 charge-discharge cycles at 10 A·g^-1, the capacitance retention was 66.4%. The reported synthesis method in this work is simple and universal, and calcination process combines the nitrogen-doping, partially graphitized carbon formation with redox-active transition metal oxides synthesis in one step, endowing the product with excellent electrochemical properties.
- chitosan,
- nitrogen doping,
- partially graphitized carbon,
- transition metal oxides,
- supercapacitor
1. [1]
  Miller, J. R.; Simon, P. Science 2008, 321, 651. doi: 10.1126/science.1158736
2. [2]
  Simon, P.; Gogotsi, Y. Nature Mater. 2008, 7, 845. doi: 10.1038/nmat2297
3. [3]
  Wang, G.; Zhang, L.; Zhang, J. Chem. Soc. Rev. 2012, 41, 797. doi: 10.1039/C1CS15060J
4. [4]
  Zhang, Y.; Feng, H.; Wu, X.; Wang, L.; Zhang, A.; Xia, T.; Dong, H.; Li, X.; Zhang, L. Int. J. Hydrogen Energy 2009, 34, 4889. doi: 10.1016/j.ijhydene.2009.04.005
5. [5]
  Li, X.-Q.; Chang, L.; Zhao, S.-L.; Hao, C.-L.; Lu, C.-G.; Zhu, Y.-H.; Tang, Z.-Y. Acta Phys.-Chim. Sinica 2017, 33, 130.
6. [6]
  Liu, Z.; Chen, W.; Fan, X.; Yu, J.; Zhao, Y. Chin. J. Chem. 2016, 34, 839. doi: 10.1002/cjoc.v34.8
7. [7]
  Wu, J.; Zhou, A.; Huang, Z.; Li, L.; Bai, H. Chin. J. Chem. 2016, 34, 67. doi: 10.1002/cjoc.v34.1
8. [8]
  Yang, J.; Yu, C.; Fan, X.; Liang, S.; Li, S.; Huang, H.; Ling, Z.; Hao, C.; Qiu, J. Energy Environ. Sci. 2016, 9, 1299. doi: 10.1039/C5EE03633J
9. [9]
  Staaf, L. G. H.; Lundgren, P.; Enoksson, P. Nano Energy 2014, 9, 128. doi: 10.1016/j.nanoen.2014.06.028
10. [10]
  Mun, Y.; Jo, C.; Hyeon, T.; Lee, J.; Ha, K.-S.; Jun, K.-W.; Lee, S.-H.; Hong, S.-W.; Lee, H. I.; Yoon, S.; Lee, J. Carbon 2013, 64, 391. doi: 10.1016/j.carbon.2013.07.092
11. [11]
  Gao, W.; Wan, Y.; Dou, Y.; Zhao, D. Adv. Energy Mater. 2011, 1, 115. doi: 10.1002/aenm.201000009
12. [12]
  Wang, D.-W.; Li, F.; Liu, M.; Lu, G. Q.; Cheng, H.-M. Angew. Chem. Int. Ed. 2008, 47, 373. doi: 10.1002/(ISSN)1521-3773
13. [13]
  Lin, T.; Chen, I.-W.; Liu, F.; Yang, C.; Bi, H.; Xu, F.; Huang, F. Science 2015, 350, 1508. doi: 10.1126/science.aab3798
14. [14]
  Yang, M.; Zhong, Y.; Bao, J.; Zhou, X.; Wei, J.; Zhou, Z. J. Mater. Chem. A 2015, 3, 11387. doi: 10.1039/C5TA02584B
15. [15]
  Su, S.; Lai, Q.; Liang, Y. Acta Chim. Sinica 2015, 73, 735. doi: 10.3969/j.issn.0253-2409.2015.06.014
16. [16]
  Li, Z.-H.; Li, S.-J.; Zhou, J.; Zhu, T.-T.; Shen, H.-L.; Zhuo, S.-P. Acta Phys.-Chim. Sinica 2015, 31, 676. doi: 10.3866/PKU.WHXB201501281
17. [17]
  Titirici, M.-M.; White, R. J.; Brun, N.; Budarin, V. L.; Su, D. S.; Monte, F. D.; Clark, J. H.; MacLachlan, M. J. Chem. Soc. Rev. 2015, 44, 250. doi: 10.1039/C4CS00232F
18. [18]
  Primo, A.; Atienzar, P.; Sanchez, E.; Delgado, J. M.; García, H. Chem. Commun. 2012, 48, 9254. doi: 10.1039/c2cc34978g
19. [19]
  Hao, P.; Zhao, Z.; Leng, Y.; Tian, J.; Sang, Y.; Boughton, R. I.; Wong, C. P.; Liu, H.; Yang, B. Nano Energy 2015, 15, 9. doi: 10.1016/j.nanoen.2015.02.035
20. [20]
  Tong, X.; Zhuo, H.; Wang, S.; Zhong, L.; Hu, Y.; Peng, X.; Zhou, W.; Sun, R. RSC Adv. 2016, 6, 34261. doi: 10.1039/C6RA01565D
21. [21]
  Rybarczyk, M. K.; Lieder, M.; Jablonska, M. RSC Adv. 2015, 5, 44969. doi: 10.1039/C5RA05725F
22. [22]
  Shao, M.; Zhang, R.; Li, Z.; Wei, M.; Evans, D. G.; Duan, X. Chem. Commun. 2015, 51, 15880. doi: 10.1039/C5CC07296D
23. [23]
  Yang, Q.; Lu, Z.; Liu, J.; Lei, X.; Chang, Z.; Luo, L.; Sun, X. Prog. Nat. Sci.: Mater. Int. 2013, 23, 351. doi: 10.1016/j.pnsc.2013.06.015
24. [24]
  Zhao, M.-Q.; Zhang, Q.; Huang, J.-Q.; Wei, F. Adv. Funct. Mater. 2012, 22, 20.
25. [25]
  Yan, L.; Kong, H.; Li, Z. Acta Chim. Sinica 2013, 71, 822.
26. [26]
  Jeong, G. H.; Baek, S.; Lee, S.; Kim, S.-W. Chem. Asian J. 2016, 11, 949. doi: 10.1002/asia.v11.7
27. [27]
  Jia, W.; Xu, M.; Lei, C.; Bao, S.; Jia, D. Acta Chim. Sinica 2011, 69, 1773.
28. [28]
  Chen, Y.; Zhang, Z.-L.; Sui, Z.-J.; Liu, Z.-T.; Zhou, J.-H.; Zhou, X.-G. Acta Phys.-Chim. Sinica 2015, 31, 1105. doi: 10.3866/PKU.WHXB201504081
29. [29]
  Yang, J.; Yu, C.; Fan, X.; Zhao, C.; Qiu, J. Adv. Funct. Mater. 2015, 25, 2109. doi: 10.1002/adfm.v25.14
30. [30]
  Yang, J.; Yu, C.; Fan, X.; Qiu, J. Adv. Energy Mater. 2014, 1400761.
31. [31]
  Yu, C.; Yang, J.; Zhao, C.; Fan, X.; Wang, G.; Qiu, J. Nanoscale 2014, 6, 3097. doi: 10.1039/C3NR05477B
32. [32]
  Yang, J.; Yu, C.; Fan, X.; Ling, Z.; Qiu, J.; Gogotsi, Y. J. Mater. Chem. A 2013, 1, 1963. doi: 10.1039/C2TA00832G
33. [33]
  Xu, J.; He, F.; Gai, S.; Zhang, S.; Li, L.; Yang, P. Nanoscale 2014, 6, 10887. doi: 10.1039/C4NR02756F
34. [34]
  Hao, P.; Zhao, Z.; Li, L.; Tuan, C.-C.; Li, H.; Sang, Y.; Jiang, H.; Wong, C. P.; Liu, H. Nanoscale 2015, 7, 14401. doi: 10.1039/C5NR04421A
35. [35]
  Zhang, H.-J.; Zhang, X.-G.; Yuan, C.-Z.; Gao, B.; Sun, K.; Fu, Q.-B.; Lu, X.-J.; Jiang, J.-C. Acta Phys.-Chim. Sinica 2011, 27, 455. doi: 10.3866/PKU.WHXB20110228
36. [36]
  Ren, L.; Hui, K. N.; Hui, K. S.; Liu, Y.; Qi, X.; Zhong, J.; Du, Y.; Yang, J. Sci. Rep. 2015, 5, 14229. doi: 10.1038/srep14229
37. [37]
  Baird, T.; Campbell, K. C.; Holliman, P. J.; Hoyle, R.; Noble, G.; Stirling, D.; Williams, B. P. J. Mater. Chem. 2003, 13, 2341. doi: 10.1039/B303449F
38. [38]
  Wu, J.; Xu, H.; Zhang, J. Acta Chim. Sinica 2014, 72, 301.
39. [39]
  Depan, D.; Singh, R. P. J. Appl. Polym. Sci. 2010, 115, 3636. doi: 10.1002/app.v115:6
40. [40]
  Xu, Z. P.; Braterman, P. S. J. Mater. Chem. 2003, 13, 268. doi: 10.1039/b207540g
41. [41]
  Pardieu, E.; Pronkin, S.; Dolci, M.; Dintzer, T.; Pichon, B. P.; Begin, D.; Pham-Huu, C.; Schaaf, P.; Begin-Colin, S.; Boulmedais, F. J. Mater. Chem. A 2015, 3, 22877. doi: 10.1039/C5TA05132K
1. [1]
  Zhaomei LIU , Wenshi ZHONG , Jiaxin LI , Gengshen HU . Preparation of nitrogen-doped porous carbons with ultra-high surface areas for high-performance supercapacitors. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 677-685. doi: 10.11862/CJIC.20230404
2. [2]
  Jin CHANG . Supercapacitor performance and first-principles calculation study of Co-doping Ni(OH)₂. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1697-1707. doi: 10.11862/CJIC.20240108
3. [3]
  Yanhui XUE , Shaofei CHAO , Man XU , Qiong WU , Fufa WU , Sufyan Javed Muhammad . Construction of high energy density hexagonal hole MXene aqueous supercapacitor by vacancy defect control strategy. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1640-1652. doi: 10.11862/CJIC.20240183
4. [4]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369
5. [5]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
6. [6]
  Jiahong ZHENG , Jingyun YANG . Preparation and electrochemical properties of hollow dodecahedral CoNi₂S₄ supported by MnO₂ nanowires. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1881-1891. doi: 10.11862/CJIC.20240170
7. [7]
  Kuaibing Wang , Honglin Zhang , Wenjie Lu , Weihua Zhang . Experimental Design and Practice for Recycling and Nickel Content Detection from Waste Nickel-Metal Hydride Batteries. University Chemistry, 2024, 39(11): 335-341. doi: 10.12461/PKU.DXHX202403084
8. [8]
  Jiahong ZHENG , Jiajun SHEN , Xin BAI . Preparation and electrochemical properties of nickel foam loaded NiMoO₄/NiMoS₄ composites. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 581-590. doi: 10.11862/CJIC.20230253
9. [9]
  Yan LIU , Jiaxin GUO , Song YANG , Shixian XU , Yanyan YANG , Zhongliang YU , Xiaogang HAO . Exclusionary recovery of phosphate anions with low concentration from wastewater using a CoNi-layered double hydroxide/graphene electronically controlled separation film. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1775-1783. doi: 10.11862/CJIC.20240043
10. [10]
  Kai CHEN , Fengshun WU , Shun XIAO , Jinbao ZHANG , Lihua ZHU . PtRu/nitrogen-doped carbon for electrocatalytic methanol oxidation and hydrogen evolution by water electrolysis. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1357-1367. doi: 10.11862/CJIC.20230350
11. [11]
  Xiaofeng Zhu , Bingbing Xiao , Jiaxin Su , Shuai Wang , Qingran Zhang , Jun Wang . Transition Metal Oxides/Chalcogenides for Electrochemical Oxygen Reduction into Hydrogen Peroxides. Acta Physico-Chimica Sinica, 2024, 40(12): 2407005-. doi: 10.3866/PKU.WHXB202407005
12. [12]
  Kaihui Huang , Dejun Chen , Xin Zhang , Rongchen Shen , Peng Zhang , Difa Xu , Xin Li . Constructing Covalent Triazine Frameworks/N-Doped Carbon-Coated Cu₂O S-Scheme Heterojunctions for Boosting Photocatalytic Hydrogen Production. Acta Physico-Chimica Sinica, 2024, 40(12): 2407020-. doi: 10.3866/PKU.WHXB202407020
13. [13]
  Ping ZHANG , Chenchen ZHAO , Xiaoyun CUI , Bing XIE , Yihan LIU , Haiyu LIN , Jiale ZHANG , Yu'nan CHEN . Preparation and adsorption-photocatalytic performance of ZnAl@layered double oxides. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1965-1974. doi: 10.11862/CJIC.20240014
14. [14]
  Wen LUO , Lin JIN , Palanisamy Kannan , Jinle HOU , Peng HUO , Jinzhong YAO , Peng WANG . Preparation of high-performance supercapacitor based on bimetallic high nuclearity titanium-oxo-cluster based electrodes. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 782-790. doi: 10.11862/CJIC.20230418
15. [15]
  Yongpo Zhang , Xinfeng Li , Yafei Song , Mengyao Sun , Congcong Yin , Chunyan Gao , Jinzhong Zhao . Synthesis of Chlorine-Bridged Binuclear Cu(I) Complexes Based on Conjugation-Driven Cu(II) Oxidized Secondary Amines. University Chemistry, 2024, 39(5): 44-51. doi: 10.3866/PKU.DXHX202309092
16. [16]
  Junli Liu . Practice and Exploration of Research-Oriented Classroom Teaching in the Integration of Science and Education: a Case Study on the Synthesis of Sub-Nanometer Metal Oxide Materials and Their Application in Battery Energy Storage. University Chemistry, 2024, 39(10): 249-254. doi: 10.12461/PKU.DXHX202404023
17. [17]
  Geyang Song , Dong Xue , Gang Li . Recent Advances in Transition Metal-Catalyzed Synthesis of Anilines from Aryl Halides. University Chemistry, 2024, 39(2): 321-329. doi: 10.3866/PKU.DXHX202308030
18. [18]
  Chuanming GUO , Kaiyang ZHANG , Yun WU , Rui YAO , Qiang ZHAO , Jinping LI , Guang LIU . Performance of MnO₂-0.39IrO_x composite oxides for water oxidation reaction in acidic media. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1135-1142. doi: 10.11862/CJIC.20230459
19. [19]
  Jinyi Sun , Lin Ma , Yanjie Xi , Jing Wang . Preparation and Electrocatalytic Nitrogen Reduction Performance Study of Vanadium Nitride@Nitrogen-Doped Carbon Composite Nanomaterials: A Recommended Comprehensive Chemistry Experiment. University Chemistry, 2024, 39(4): 184-191. doi: 10.3866/PKU.DXHX202310094
20. [20]
  Yunting Shang , Yue Dai , Jianxin Zhang , Nan Zhu , Yan Su . Something about RGO (Reduced Graphene Oxide). University Chemistry, 2024, 39(9): 273-278. doi: 10.3866/PKU.DXHX202306050

Get Citation

PDF

XML

Metrics

PDF Downloads(6)
Abstract views(1296)
HTML views(252)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142