Citation: FENG Yingjie, WANG Jinping, LIU Lili, WANG Xidong. Self-Conversion from ZnO Nanorod Arrays to Tubular Structures and Their Applications in Nanoencapsulated Phase-Change Materials[J]. Acta Physico-Chimica Sinica, ;2019, 35(6): 644-650. doi: 10.3866/PKU.WHXB201805068 shu

Self-Conversion from ZnO Nanorod Arrays to Tubular Structures and Their Applications in Nanoencapsulated Phase-Change Materials

1.
College of Engineering, Peking University, Beijing 100871, P. R. China
2.
Beijing Research Institute of Chemical Industry, SINOPEC, Beijing 100013, P. R. China

Corresponding author: WANG Xidong, xidong@pku.edu.cn
Received Date: 24 May 2018
Revised Date: 2 July 2018
Accepted Date: 4 July 2018
Available Online: 9 June 2018
Fund Project: The project was supported by the Common Development Fund of Beijing, China and the National Natural Science Foundation of China 北京市公共发展基金及国家自然科学基金The project was supported by the Common Development Fund of Beijing, China and the National Natural Science Foundation of China (51472006)

In the emerging field of nanoscience, tubular structures have been attracting remarkable interest due to their well-defined geometry, high specific area, and exceptional physical and chemical properties. Among them, oriented ZnO tubular arrays are regarded as promising candidates for various applications such as optoelectronics, solar cells, sensors, field emission, piezoelectrics, and catalysis. Although template-directed and selective dissolution synthesizing strategies are commonly used to prepare ZnO nanotubes, repeatability and large scale preparation are still challenging. In this study, ZnO nanotube arrays were controllably prepared by tuning the hydrothermal parameters, without the use of any additives. The mechanism underlying the self-conversion of ZnO nanorods to nanotubes was comprehensively studied based on the surface energy theory. It has been proved that the metastable top surface of the ZnO nanorods dissolves preferentially to reach a stable state during the hydrothermal growth. The specific surface energy of different crystal faces of ZnO nanorods was calculated using molecular dynamics simulation. The top surface of the ZnO nanorod, the Zn-terminated [0001] face, demonstrated much higher surface free energy than did the lateral faces, which indicated that the self-dissolution of top face (002) is energetically favorable. The self-conversion behavior of ZnO nanorod arrays with different diameters was specifically investigated by adjusting the initial precursor concentration, density of the crystal seed layers, and growth time. The dissolution-crystallization equilibrium concentration, determined by crystal surface energy, was found to be a key factor for the formation of the tubular structure. Notably, the critical equilibrium conditions for the self-conversion of ZnO nanorods to nanotubes, including zinc ion concentration and pH, have been identified by studying parameters corresponding to the dissolution-crystallization equilibrium for the metastable top surface of the ZnO nanorods. The preparation of the ZnO nanotube arrays was successfully accelerated and simplified via two-step procedure: (1) preparation of ZnO nanorod arrays and (2) self-conversion of ZnO nanorods to nanotubes. The preparation method based on the self-conversion mechanism from rods to tubes for polar oxides is simpler and more easily controllable as compared to the reported methods involving variety of additives. Because of the advantages of adaptability to a wide range of substrates, excellent conducting properties, and filling ability, the prepared ZnO nanotube array films were used in encapsulating phase-change materials. The encapsulated phase-change material exhibited excellent heat storage/release properties and heat conductivities. This indicates the potential application of precision devices for temperature control.
- ZnO nanotubes,
- Crystal surface energy,
- Dissolution-crystallization equilibrium,
- Self-conversion,
- Encapsulated phase-change materials
1. [1]
  (a) Greyson, E. C.; Babayan, Y.; Odom, T. W. Adv. Mater. 2004, 16, 1348. doi: 10.1002/adma.200400765
  (b) Greene, L. E.; Law, M.; Tan, D. H.; Montano, M.; Goldberger, J.; Somorjai, G.; Yang, P. D. Nano Lett. 2005, 5, 1231. doi: 10.1021/nl050788p
2. [2]
  Sun, Y.; Fuge, G. M.; Fox, N. A.; Riley, D. J.; Ashfold, M. N. R. Adv. Mater. 2005, 17, 2477. doi: 10.1002/adma.200500726 doi: 10.1002/adma.200500726
3. [3]
  s(a) Pan, Z. X.; Dai, Z. R.; Wang, Z. L. Science 2001, 291, 1947. doi: 10.1126/science.1058120
  (b) Wen, X. G.; Fang, Y. P.; Pang, Q.; Yang, C. L.; Wang, J. N.; Ge, W. K.; Wong, K. S.; Yang, S. H. J. Phys. Chem. B 2005, 109, 15303. doi: 10.1021/jp052466f
4. [4]
  (a) Gao, P. X.; Wang, Z. L. J. Am. Chem. Soc. 2003, 125, 11299. doi: 10.1021/ja035569p
  (b) Li, G. R.; Lu, X. H.; Zhao, W. X.; Su, C. Y.; Tong, Y. X. Cryst. Growth Des. 2008, 8, 1276. doi: 10.1021/cg7009995
5. [5]
  (a) Konenkamp, R.; Word, R. C.; Godinez, M. Nano Lett. 2005, 5, 2005. doi: 10.1021/nl051501r
  (b) Flemban, T. H.; Haque, M. A.; Ajia, I.; Alwadai, N.; Mitra, S.; Wu, T.; Roqan, I. S. ACS Appl. Mater. Interfaces 2017, 9, 37120. doi: 10.1021/acsami.7b09645
6. [6]
  (a) Valls, I. G.; Cantu, M. L. Energy Environ. Sci. 2009, 2, 19. doi: 10.1002/adma.200400765
  (b) Martinson, A. B.; Elam, J. W.; Hupp, J. T.; Pelin, M. J. Nano Lett. 2007, 7, 2183. doi: 10.1021/nl070160+
7. [7]
  (a) Yang, K.; She, G. W.; Wang, H.; Ou, X. M.; Zhang, X. H.; Lee, C. S.; Lee, S. T. J. Phys. Chem. C 2009, 113, 20169. doi: 10.1021/jp901894j
  (b) Huang, Y. C.; Chang, S. Y.; Jehng, J. M. J. Phys. Chem. C 2017, 121, 19063. doi: 10.1021/acs.jpcc.7b05806
8. [8]
  (a) Ye, C.; Bando, Y.; Fang, X.; Shen, G.; Goldberg, D. J. Phys. Chem. C 2007, 111, 12673. doi: 10.1021/jp073928n
  (b) Wang, X.; Zhou, J.; Lao, C.; Song, J.; Xu, N.; Wang, Z. L. Adv. Mater. 2007, 19, 1627. doi: 10.1002/adma.200602467
9. [9]
  (a) Wang, X.; Song, J.; Liu, J.; Wang, Z. L. Science 2007, 316, 102. doi: 10.1126/science.1139366
  (b) Lu, M. P.; Song, J. H.; Lu, M. Y.; Chen, M. T.; Gao, Y. F.; Chen, L. J.; Wang, Z. L. Nano Lett. 2009, 9, 1223. doi: 10.1021/nl900115y
10. [10]
  Chouhan, N.; Yeh, C. L.; Hu, S. F.; Liu, R. S.; Chang, W. S.; Chene, K. H. Chem. Comm. 2011, 47, 3493. doi: 10.1039/C0CC05548D doi: 10.1039/C0CC05548D
11. [11]
  Zhao, X. F.; Chen, H.; Wu, H.; Wang, R.; Cui, Y.; Fu, Q.; Yang, F.; Bao, X. H. Acta Phys. -Chim. Sin. 2018, 34, 1373. doi: 10.3866/PKU.WHXB201804131
12. [12]
  Elias, J.; Tena-Zaera, R.; Wang, Y. S.; Lévy-Clément, C. Chem. Mater. 2008, 20, 6633. doi: 10.1021/cm801131t doi: 10.1021/cm801131t
13. [13]
  Xu, L. F.; Liao, Q.; Zhang, J. P.; Ai, X. C.; Xu, D. S. J. Phys. Chem. C 2007, 111, 4549. doi: 10.1021/jp068485m doi: 10.1021/jp068485m
14. [14]
  Li, G. R.; Lu, X. H.; Zhao, W. X.; Su, C. Y.; Tong, Y. X. Cryst. Growth Des. 2008, 8, 1276. doi: 10.1021/cg7009995 doi: 10.1021/cg7009995
15. [15]
  Fujimura, N.; Nishihara, T.; Goto, S.; Xu, J. F.; Ito, T. J. Cryst. Growth 1993, 130, 269. doi: 10.1016/0022-0248(93)90861-P doi: 10.1016/0022-0248(93)90861-P
16. [16]
  Wang, Z. L.; Kong, X. Y.; Zuo, J. M. Phys. Rev. Lett. 2003, 91, 185502. doi: 10.1103/PhysRevLett.91.185502 doi: 10.1103/PhysRevLett.91.185502
17. [17]
  Yu, H. D.; Zhang, Z. P.; Han, M. Y.; Hao, X. T.; Zhu, F. R. J. Am. Chem. Soc. 2005, 127, 2378. doi: 10.1021/ja043121y doi: 10.1021/ja043121y
18. [18]
  Zhang, B. P.; Binh, N. T.; Wakatsuki, K.; Segawa, Y.; Yamada, Y.; Usami, N.; Kawasaki, M.; Koinuma, H. J. Phys. Chem. B 2004, 108, 10899. doi: 10.1021/jp048602i doi: 10.1021/jp048602i
19. [19]
  Vayssieres, L.; Keis, K.; Hagfeldt, A.; Lindquist, S. E. Chem. Mater. 2001, 13, 4395. doi: 10.1021/cm011160s doi: 10.1021/cm011160s
20. [20]
  Matijević, E. Langmuir 1994, 10, 8. doi: 10.1021/la00013a003 doi: 10.1021/la00013a003
21. [21]
  Vayssieres, L. Adv. Mater. 2003, 15, 464. doi: 10.1002/adma.200390108 doi: 10.1002/adma.200390108
22. [22]
  Pardeshi, S. K.; Patil, A. B. J. Hazard. Mater. 2009, 163, 403. doi: 10.1016/j.jhazmat.2008.06.111 doi: 10.1016/j.jhazmat.2008.06.111
23. [23]
  Chu, D. W.; Masuda, Y.; Ohji, T.; Kato, K. Langmuir 2010, 26, 2811. doi: 10.1021/la902866a doi: 10.1021/la902866a
24. [24]
  Mondal, S. Appl. Therm. Eng. 2008, 28, 1536. doi: 10.1016/j.applthermaleng.2007.08.009 doi: 10.1016/j.applthermaleng.2007.08.009
25. [25]
  Wu, S. Y.; Zhu, D. S.; Zhang, X. R.; Huang, J. Energy Fuels 2010, 24, 1894. doi: 10.1021/ef9013967 doi: 10.1021/ef9013967
1. [1]
  Ce Liang , Qiuhui Sun , Adel Al-Salihy , Mengxin Chen , Ping Xu . Recent advances in crystal phase induced surface-enhanced Raman scattering. Chinese Chemical Letters, 2024, 35(9): 109306-. doi: 10.1016/j.cclet.2023.109306
2. [2]
  Xinyu Ren , Hong Liu , Jingang Wang , Jiayuan Yu . Electrospinning-derived functional carbon-based materials for energy conversion and storage. Chinese Chemical Letters, 2024, 35(6): 109282-. doi: 10.1016/j.cclet.2023.109282
3. [3]
  Jun Lu , Jinrui Yan , Yaohao Guo , Junjie Qiu , Shuangliang Zhao , Bo Bao . Controlling solid form and crystal habit of triphenylmethanol by antisolvent crystallization in a microfluidic device. Chinese Chemical Letters, 2024, 35(4): 108876-. doi: 10.1016/j.cclet.2023.108876
4. [4]
  Zhao Li , Huimin Yang , Wenjing Cheng , Lin Tian . Recent progress of in situ/operando characterization techniques for electrocatalytic energy conversion reaction. Chinese Chemical Letters, 2024, 35(9): 109237-. doi: 10.1016/j.cclet.2023.109237
5. [5]
  Zhi-Yuan Yue , Hua-Kai Li , Na Wang , Shan-Shan Liu , Le-Ping Miao , Heng-Yun Ye , Chao Shi . Dehydration-triggered structural phase transition-associated ferroelectricity in a hybrid perovskite-type crystal. Chinese Chemical Letters, 2024, 35(10): 109355-. doi: 10.1016/j.cclet.2023.109355
6. [6]
  Xue Xin , Qiming Qu , Islam E. Khalil , Yuting Huang , Mo Wei , Jie Chen , Weina Zhang , Fengwei Huo , Wenjing Liu . Hetero-phase zirconia encapsulated with Au nanoparticles for boosting electrocatalytic nitrogen reduction. Chinese Chemical Letters, 2024, 35(5): 108654-. doi: 10.1016/j.cclet.2023.108654
7. [7]
  Zixuan Zhu , Xianjin Shi , Yongfang Rao , Yu Huang . Recent progress of MgO-based materials in CO₂ adsorption and conversion: Modification methods, reaction condition, and CO₂ hydrogenation. Chinese Chemical Letters, 2024, 35(5): 108954-. doi: 10.1016/j.cclet.2023.108954
8. [8]
  Xiuzheng Deng , Changhai Liu , Xiaotong Yan , Jingshan Fan , Qian Liang , Zhongyu Li . Carbon dots anchored NiAl-LDH@In₂O₃ hierarchical nanotubes for promoting selective CO₂ photoreduction into CH₄. Chinese Chemical Letters, 2024, 35(6): 108942-. doi: 10.1016/j.cclet.2023.108942
9. [9]
  Kezhen Qi , Shu-yuan Liu , Ruchun Li . Selective dissolution for stabilizing solid electrolyte interphase. Chinese Chemical Letters, 2024, 35(5): 109460-. doi: 10.1016/j.cclet.2023.109460
10. [10]
  Jie Ren , Hao Zong , Yaqun Han , Tianyi Liu , Shufen Zhang , Qiang Xu , Suli Wu . Visual identification of silver ornament by the structural color based on Mie scattering of ZnO spheres. Chinese Chemical Letters, 2024, 35(9): 109350-. doi: 10.1016/j.cclet.2023.109350
11. [11]
  Asif Hassan Raza , Shumail Farhan , Zhixian Yu , Yan Wu . 用于高效制氢的双S型ZnS/ZnO/CdS异质结构光催化剂. Acta Physico-Chimica Sinica, 2024, 40(11): 2406020-. doi: 10.3866/PKU.WHXB202406020
12. [12]
  Xiuzheng Deng , Yi Ke , Jiawen Ding , Yingtang Zhou , Hui Huang , Qian Liang , Zhenhui Kang . Construction of ZnO@CDs@Co₃O₄ sandwich heterostructure with multi-interfacial electron-transfer toward enhanced photocatalytic CO₂ reduction. Chinese Chemical Letters, 2024, 35(4): 109064-. doi: 10.1016/j.cclet.2023.109064
13. [13]
  Jiakun Bai , Junhui Jia , Aisen Li . An elastic organic crystal with piezochromic luminescent behavior. Chinese Journal of Structural Chemistry, 2024, 43(6): 100323-100323. doi: 10.1016/j.cjsc.2024.100323
14. [14]
  Zhiwei Zhong , Yanbin Huang , Wantai Yang . A simple photochemical method for surface fluorination using perfluoroketones. Chinese Chemical Letters, 2024, 35(5): 109339-. doi: 10.1016/j.cclet.2023.109339
15. [15]
  Yukai Tong , Zhijun Wu , Bo Zhou , Min Hu , Anpei Ye . Surface tension of single suspended aerosol microdroplets. Chinese Chemical Letters, 2024, 35(4): 109062-. doi: 10.1016/j.cclet.2023.109062
16. [16]
  Yu He , Hao Jiang , Shaoxuan Yuan , Jiayi Lu , Qiang Sun . On-surface photo-induced dechlorination. Chinese Chemical Letters, 2024, 35(9): 109807-. doi: 10.1016/j.cclet.2024.109807
17. [17]
  You Wu , Chang Cheng , Kezhen Qi , Bei Cheng , Jianjun Zhang , Jiaguo Yu , Liuyang Zhang . ZnO/D-A共轭聚合物S型异质结高效光催化产H₂O₂及其电荷转移动力学研究. Acta Physico-Chimica Sinica, 2024, 40(11): 2406027-. doi: 10.3866/PKU.WHXB202406027
18. [18]
  Peng Meng , Qian-Cheng Luo , Aidan Brock , Xiaodong Wang , Mahboobeh Shahbazi , Aaron Micallef , John McMurtrie , Dongchen Qi , Yan-Zhen Zheng , Jingsan Xu . Molar ratio induced crystal transformation from coordination complex to coordination polymers. Chinese Chemical Letters, 2024, 35(4): 108542-. doi: 10.1016/j.cclet.2023.108542
19. [19]
  Xiumei LI , Yanju HUANG , Bo LIU , Yaru PAN . Syntheses, crystal structures, and quantum chemistry calculation of two Ni(Ⅱ) coordination polymers. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 2031-2039. doi: 10.11862/CJIC.20240109
20. [20]
  Changzhu Huang , Wei Dai , Shimao Deng , Yixin Tian , Xiaolin Liu , Jia Lin , Hong Chen . A self-cleaning window for high-efficiency photodegradation of indoor formaldehyde. Chinese Chemical Letters, 2024, 35(9): 109429-. doi: 10.1016/j.cclet.2023.109429

Get Citation

PDF

XML

Metrics

PDF Downloads(16)
Abstract views(374)
HTML views(41)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142