Citation: YUE Ming-Bo, YANG Na, WANG Yi-Meng. Synthesis of Shaped ZSM-5 Zeolites by Dry-Gel Conversion with Seed Gel as Directing Agent[J]. Acta Physico-Chimica Sinica doi: 10.3866/PKU.WHXB201206141 shu

Synthesis of Shaped ZSM-5 Zeolites by Dry-Gel Conversion with Seed Gel as Directing Agent

YUE Ming-Bo ^1,2 ,
YANG Na ² ,
WANG Yi-Meng ^2,

1.
1. Key Laboratory of Life-Organic Analysis of Shandong Province, School of Chemistry and Chemical Engineering, Qufu Normal University, Qufu 273165, Shandong Province, P. R. China;
2. Shanghai Key Laboratory of Green Chemistry and Chemical Processes, Department of Chemistry, East China Normal University, Shanghai 200062, P. R. China

Received Date: 30 March 2012
Available Online: 14 June 2012
Fund Project: 国家自然科学基金(20890124, 21003083) (20890124, 21003083)山东省博士科研奖励基金(BS2009CL031)资助项目 (BS2009CL031)

Shaped binderless ZSM-5 zeolites were prepared via a rapid dry-gel conversion technique from aluminosilicate extrudate. Silica gel and boehmite were well mixed and extruded into cylindrical shaped extrudates with diameter of 2 mm with the aid of silica sol, ZSM-5 zeolite seed gel, and/or tetrapropylammonium hydroxide (TPAOH) solution. The total molar ratio of TPAOH to SiO₂ was fixed at 0.025. With same amounts of structure directing agent (TPAOH), the addition of seed gels accelerated the crystallization of the zeolite. The seed gel directing agent composition was 0.35TPAOH:1SiO₂:20H₂O: 4C₂H₅OH. The seed gel not only provided crystal nuclei for rapid crystallization but also controlled the size of the ZSM-5 crystals. Especially, the morphology of these extrudates was well maintained in the crystallization process. The crystallization processes of zeolite were characterized by X-ray diffraction (XRD), thermogravimetric (TG) analysis, and Fourier transform infrared (FTIR) spectroscopy. The results showed that the growth of the zeolite was accompanied by the occupation of the zeolite channels by TPAOH. When the TPAOH/SiO₂ molar ratio was 0.025, the sample achieved 100% relative crystallinity after 3 h crystallization. The morphology and textural properties were characterized by scanning electron microscopy (SEM) and nitrogen sorption isotherms. The obtained shaped zeolites comprised nanosized crystals (200 nm) and exhibited a hierarchical structure with high mesopore volume (0.28 cm³·g^-1). The temperature- programmed desorption of ammonia (NH₃-TPD) was used to assess the acidity of these shaped zeolites. The results showed that this shaped zeolite possessed an acidity similar to that of a commercial H-ZSM-5 catalyst.
- Shaped ZSM-5 zeolite,
- Dry-gel conversion,
- Hierarchical structure,
- Seed structure directing gel,
- Nanoscale zeolite
1. [1]
  
  (1) Holma, M. S.; Taarninga, E.; Egeblada, K.; Christensen, C. H.Catal. Today 2011, 168, 3. doi: 10.1016/j.cattod.2011.01.007
2. [2]
  (2) Jones, C.W.; Tsuji, K.; Davis, M. E. Nature 1998, 393, 52. doi: 10.1038/29959
3. [3]
  (3) Zhai, S. R.;Wei, L.; Yang, D. J.;Wu, D.; Sun, Y. H. Prog. Chem.2006, 18, 1330. [翟尚儒, 魏莉, 杨东江, 吴东, 孙予罕.化学进展, 2006, 18, 1330.]
4. [4]
  (4) Tao, Y.; Kanoh, H.; Abrams, L.; Kaneko, K. Chem. Rev. 2006,106, 896. doi: 10.1021/cr040204o
5. [5]
  (5) Perez-Ramirez, J.; Christensen, C. H.; Egeblad, K.; Groen, J. C.Chem. Soc. Rev. 2008, 37, 2530. doi: 10.1039/b809030k
6. [6]
  (6) Egeblad, K.; Christensen, C. H.; Kustova, M. Chem. Mater.2008, 20, 946. doi: 10.1021/cm702224p
7. [7]
  (7) Ma, Y. H.; Zhao, H. L.; Tang, S. J.; Hu, J.; Liu, H. L. Acta Phys. -Chim. Sin. 2011, 27, 689. [马燕辉, 赵会玲, 唐圣杰,胡军, 刘洪来. 物理化学学报, 2011, 27, 689.] doi: 10.3866/PKU.WHXB20110335
8. [8]
  (8) Choi, M.; Cho, H. S.; Srivastava, R.; Venkatesan, C.; Choi, D.H.; Ryoo, R. Nat. Mater. 2006, 5, 718. doi: 10.1038/nmat1705
9. [9]
  (9) Zhang, Z. T.; Han, Y.; Zhu, L.;Wang, R.W.; Yu, Y.; Qiu, S. L.;Zhao, D. Y.; Xiao, F. S. Angew. Chem. Int. Edit. 2001, 40, 1258.doi: 10.1002/1521-3773(20010401)40:7<1258::AIDANIE1258>3.0.CO;2-C
10. [10]
  (10) Hu, G.; Ma, D.; Liu, L.; Cheng, M. J.; Bao, X. H. Angew. Chem. Int. Edit. 2004, 43, 3452. doi: 10.1002/anie.200453777
11. [11]
  (11) Li,W. C.; Lu, A. H.; Palkovits, R.; Schmidt,W.; Spliethoff, B.;Schuth, F. J. Am. Chem. Soc. 2005, 127, 12595. doi: 10.1021/ja052693v
12. [12]
  (12) Yoo,W. C.; Kumar, S.; Penn, R. L.; Tsapatsis, M.; Stein, A.J. Am. Chem. Soc. 2009, 131, 12377. doi: 10.1021/ja904466v
13. [13]
  (13) Tong, Y.; Zhao, T.; Li, F.;Wang, Y. Chem. Mater. 2006, 18,4218. doi: 10.1021/cm060035j
14. [14]
  (14) Zhao, T.; Xu, X.; Tong, Y.; Lei, Q.; Li, F.; Zhang, L. Catal. Lett.2010, 136, 266. doi: 10.1007/s10562-009-0131-8
15. [15]
  (15) Dong, A. G.;Wang, Y. J.; Tang, Y.; Zhang, Y. H.; Ren, N.; Gao,Z. Adv. Mater. 2002, 14, 1506. doi: 10.1002/1521-4095(20021016)14:20<1506::AID-ADMA1506>3.0.CO;2-Z
16. [16]
  (16) Lee, Y. J.; Kim, Y.W.; Jun, K.W.; Viswanadham, N.; Bae, J.W.;Park, H. S. Catal. Lett. 2009, 129, 408. doi: 10.1007/s10562-008-9811-z
17. [17]
  (17) Saini, V. K.; Pinto, M. L.; Pires, J. Colloids Surf. A 2011, 373,158. doi: 10.1016/j.colsurfa.2010.10.047
18. [18]
  (18) Huang, Y.; Dong, D.; Yao, J.; He, L.; Ho, J.; Kong, C.; Hill, A.J.;Wang, H. Chem. Mater. 2010, 22, 5271. doi: 10.1021/cm101408n
19. [19]
  (19) Wang, D. J.; Liu, Z. N.; Xie, Z. K. J. Inorg. Mater. 2008, 23 (3),592. [王德举, 刘仲能, 谢在库. 无机材料学报, 2008, 23 (3),592.] doi: 10.3724/SP.J.1077.2008.00592
20. [20]
  (20) Tokudome, Y.; Nakanishi, K.; Kosaka, S.; Kariya, A.; Kaji, H.;Hanada, T. Microporous Mesoporous Mat. 2010, 132, 538. doi: 10.1016/j.micromeso.2010.04.005
21. [21]
  (21) Möller, K.; Yilmaz, B.; Jacubinas, R. M.; Müller, U.; Bein, T.J. Am. Chem. Soc. 2011, 133, 5284. doi: 10.1021/ja108698s
22. [22]
  (22) Shi, J.; Ren, N.; Zhang, Y. H.; Tang, Y. Microporous Mesoporous Mat. 2010, 132, 181. doi: 10.1016/j.micromeso.2010.02.018
23. [23]
  (23) Wang, D. J.; Liu, Z. N.;Wang, H.; Xie, Z. K.; Tang, Y.Microporous Mesoporous Mat. 2010, 132, 428. doi: 10.1016/j.micromeso.2010.03.023
24. [24]
  (24) Lei, Q.; Zhao, T.; Li, F.;Wang, Y. F.; Hou, L. J. Porous Mater.2008, 15, 643. doi: 10.1007/s10934-007-9144-0
25. [25]
  (25) Xu, X.; Zhao, T.; Qi, J.; Guo, Y.; Miao, C.; Li, F.; Liang, M.Mater. Lett. 2010, 64, 1660. doi: 10.1016/j.matlet.2010.04.057
26. [26]
  (26) Schmidt, I.; Madsen, C.; Jacobsen, C. J. H. Inorg. Chem. 2000,39, 2279. doi: 10.1021/ic991280q
27. [27]
  (27) Ren, N.; Yang, Z. J.; Liu, X. C.; Shi, J.; Zhang, Y. H.; Tang, Y.Microporous Mesoporous Mat. 2010, 131, 103. doi: 10.1016/j.micromeso.2009.12.009
28. [28]
  (28) Jacobs, P. A.; Beyer, H. K.; Valyon, J. Zeolites 1981, 1, 161. doi: 10.1016/S0144-2449(81)80006-1
29. [29]
  (29) Jansen, J. C.; Vander-Gaag, F. J.; Van-Bekkum, H. Zeolites1984, 4, 369. doi: 10.1016/0144-2449(84)90013-7
30. [30]
  (30) Kruk, M.; Jaroniec, M. Chem. Mater. 2001, 13, 3169. doi: 10.1021/cm0101069
1. [1]
  Yuhao SUN , Qingzhe DONG , Lei ZHAO , Xiaodan JIANG , Hailing GUO , Xianglong MENG , Yongmei GUO . Synthesis and antibacterial properties of silver-loaded sod-based zeolite. Chinese Journal of Inorganic Chemistry, doi: 10.11862/CJIC.20230169
2. [2]
  Yufang GAO , Nan HOU , Yaning LIANG , Ning LI , Yanting ZHANG , Zelong LI , Xiaofeng LI . Nano-thin layer MCM-22 zeolite: Synthesis and catalytic properties of trimethylbenzene isomerization reaction. Chinese Journal of Inorganic Chemistry, doi: 10.11862/CJIC.20240036
3. [3]
  Yong Shu , Xing Chen , Sai Duan , Rongzhen Liao . How to Determine the Equilibrium Bond Distance of Homonuclear Diatomic Molecules: A Case Study of H₂. University Chemistry, doi: 10.3866/PKU.DXHX202310102
4. [4]
  Feng Zheng , Ruxun Yuan , Xiaogang Wang . “Research-Oriented” Comprehensive Experimental Design in Polymer Chemistry: the Case of Polyimide Aerogels. University Chemistry, doi: 10.12461/PKU.DXHX202404027
5. [5]
  Qiangqiang SUN , Pengcheng ZHAO , Ruoyu WU , Baoyue CAO . Multistage microporous bifunctional catalyst constructed by P-doped nickel-based sulfide ultra-thin nanosheets for energy-efficient hydrogen production from water electrolysis. Chinese Journal of Inorganic Chemistry, doi: 10.11862/CJIC.20230454
6. [6]
  Yinyin Qian , Rui Xu . Utilizing VESTA Software in the Context of Material Chemistry: Analyzing Twin Crystal Nanostructures in Indium Antimonide. University Chemistry, doi: 10.3866/PKU.DXHX202307051
7. [7]
  Wenyan Dan , Weijie Li , Xiaogang Wang . The Technical Analysis of Visual Software ShelXle for Refinement of Small Molecular Crystal Structure. University Chemistry, doi: 10.3866/PKU.DXHX202302060
8. [8]
  Hongyun Liu , Jiarun Li , Xinyi Li , Zhe Liu , Jiaxuan Li , Cong Xiao . Course Ideological and Political Design of a Comprehensive Chemistry Experiment: Constructing a Visual Molecular Logic System Based on Intelligent Hydrogel Film Electrodes. University Chemistry, doi: 10.3866/PKU.DXHX202309070
9. [9]
  Xinyu You , Xin Zhang , Shican Jiang , Yiru Ye , Lin Gu , Hexun Zhou , Pandong Ma , Jamal Ftouni , Abhishek Dutta Chowdhury . Efficacy of Ca/ZSM-5 zeolites derived from precipitated calcium carbonate in the methanol-to-olefin process. Chinese Journal of Structural Chemistry, doi: 10.1016/j.cjsc.2024.100265
10. [10]
  Bingliang Li , Yuying Han , Dianyang Li , Dandan Liu , Wenbin Shang . One-Step Synthesis of Benorilate Guided by Green Chemistry Principles and in vivo Dynamic Evaluation. University Chemistry, doi: 10.3866/PKU.DXHX202311070
11. [11]
  Xingyang LI , Tianju LIU , Yang GAO , Dandan ZHANG , Yong ZHOU , Meng PAN . A superior methanol-to-propylene catalyst: Construction via synergistic regulation of pore structure and acidic property of high-silica ZSM-5 zeolite. Chinese Journal of Inorganic Chemistry, doi: 10.11862/CJIC.20240026
12. [12]
  Wenliang Wang , Weina Wang , Sufan Wang , Tian Sheng , Tao Zhou , Nan Wei . “Schrödinger Equation – Approximate Models – Core Concepts – Simple Applications”: Constructing a Logical Framework and Knowledge Graph of Atom and Molecule Structures. University Chemistry, doi: 10.3866/PKU.DXHX202312084
13. [13]
  Hongwei Ma , Hui Li . Three Methods for Structure Determination from Powder Diffraction Data. University Chemistry, doi: 10.3866/PKU.DXHX202310035
14. [14]
  Bing LIU , Huang ZHANG , Hongliang HAN , Changwen HU , Yinglei ZHANG . Visible light degradation of methylene blue from water by triangle Au@TiO₂ mesoporous catalyst. Chinese Journal of Inorganic Chemistry, doi: 10.11862/CJIC.20230398
15. [15]
  Yuanpei ZHANG , Jiahong WANG , Jinming HUANG , Zhi HU . Preparation of magnetic mesoporous carbon loaded nano zero-valent iron for removal of Cr(Ⅲ) organic complexes from high-salt wastewater. Chinese Journal of Inorganic Chemistry, doi: 10.11862/CJIC.20240077
16. [16]
  Yuqiao Zhou , Weidi Cao , Shunxi Dong , Lili Lin , Xiaohua Liu . Study on the Teaching Reformation of Practical X-ray Crystallography. University Chemistry, doi: 10.3866/PKU.DXHX202303003
17. [17]
  Haiping Wang . A Streamlined Method for Drawing Lewis Structures Using the Valence State of Outer Atoms. University Chemistry, doi: 10.12461/PKU.DXHX202401073
18. [18]
  Kun WANG , Wenrui LIU , Peng JIANG , Yuhang SONG , Lihua CHEN , Zhao DENG . Hierarchical hollow structured BiOBr-Pt catalysts for photocatalytic CO₂ reduction. Chinese Journal of Inorganic Chemistry, doi: 10.11862/CJIC.20240037
19. [19]
  Qiying Xia , Guokui Liu , Yunzhi Li , Yaoyao Wei , Xia Leng , Guangli Zhou , Aixiang Wang , Congcong Mi , Dengxue Ma . Construction and Practice of “Teaching-Learning-Assessment Integration” Model Based on Outcome Orientation: Taking “Structural Chemistry” as an Example. University Chemistry, doi: 10.3866/PKU.DXHX202311007
20. [20]
  Juan Yuan , Bin Zhang , Jinping Wu , Mengfan Wang . Design of a Comprehensive Experiment on Preparation and Characterization of Cu₂(Salen)₂ Nanomaterials with Two Distinct Morphologies. University Chemistry, doi: 10.3866/PKU.DXHX202402014

Get Citation

PDF

XML

Metrics

PDF Downloads(1120)
Abstract views(2600)
HTML views(70)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142