Citation: WU Tao, TAO Jie, DENG Jie, TANG Yu-Xin, ZHU Hong, GAO Peng. Preparation and Characterization of One-Dimensional TiO₂ Nanowire Films on a Flexible Stainless Steel Substrate[J]. Acta Physico-Chimica Sinica, ;2010, 26(11): 3087-3094. doi: 10.3866/PKU.WHXB20101103 shu

Preparation and Characterization of One-Dimensional TiO₂ Nanowire Films on a Flexible Stainless Steel Substrate

1.
College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, P. R. China

Received Date: 15 April 2010
Available Online: 8 September 2010
Fund Project: 江苏省自然科学基金(BK2004129) (BK2004129)航空基金(04H5209) (04H5209)南京航空航天大学基本科研业务费专项科研项目助(NS2010153)资助 (NS2010153)

We synthesized a one dimensional (1D) TiO₂ nanowire with a large aspect ratio on non-Ti substrate in NaOH aqueous solution by the hydrothermal treatment of pure titanium films deposited by direct current magnetron sputtering on a flexible stainless steel substrate (50 μm). The samples were characterized by field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), transmission electron microscopy (TEM), and photoelectro- chemical methods. Results show that the density and crystallinity of the titanium film as well as the binding strength between the Ti film and the stainless steel substrate increased with an increase in substrate temperature. The optimum hydrothermal temperature for the formation of the 1D TiO₂ nanowire was 130-150 ℃when the concentration of NaOH was kept at 10 mol·L^-1. TiO₂ nanowires with diameters of 10-30 nm and lengths of up to several microns grow in a crosswise manner and form a 3D network structure. Moreover, linear sweep voltammetry and transient photocurrent response curves indicated that the 1D TiO₂ nanowire film electrode had better photoelectrochemical performance than the TiO₂ nanoparticle electrode. This technique provides a new method for the fabrication of 1D TiO₂ nanowire films on different non-Ti heterogeneous substrates.
- Direct currentmagnetron sputtering,
- Titaniumthin film,
- TiO₂,
- Nanowire,
- Hydrothermalmethod
1. [1]
  
  1. Fujishima, A.; Honda, K. Nature, 1972, 238: 37
2. [2]
  2. Chen, X. Q.; Liu, H. B.; Gu, G. B. Materials Chemistry and Physics, 2005, 91: 317
3. [3]
  3. Ao, Y. H.; Xu, J. J.; Fu, D. G.; Yuan, C. W. Applied Surface Science, 2008, 255: 3137
4. [4]
  4. Mor, G. K.; Carvalho, M. A.; Varghese, O. K.; Pishko, M. V.; Grimes, C. A. J. Mater. Res., 2004, 19(2): 628
5. [5]
  5. Kang, M. G.; Park, N. G.; Ryu, K. S.; Chang, S. H.; Kim, K. J. Sol. Energy Mater. Sol. Cells, 2006, 90: 574
6. [6]
  6. O'Regan, B.; Grätzel, M. Nature, 1991, 353: 737
7. [7]
  7. Kasuga, T.; Hiramatsu, M.; Hoson, A.; Sekino, T.; Niihara, K. Adv. Mater., 1999, 15(11): 1307
8. [8]
  8. Zhao, Y.; Lee, U.; Suh, M.; Kwon, Y. Bull. Korean Chem. Soc., 2004, 25: 1341
9. [9]
  9. Wang, Y. F.; Wu, M. Y.; Zhang, W. F. Electrochimica Acta, 2008, 53: 7863
10. [10]
  10. Seo, H. K.; Kim, G. S.; Ansari, S. G.; Kim, Y. S.; Shin, H. S.; Shim, K. H.; Suh, E. K. Sol. Energy Mater. Sol. Cells, 2008, 92: 1533
11. [11]
  11. Costa, L. L.; Prado, A. G. S. Journal of Photochemistry and Photobiology A-Chemistry, 2009, 201: 45
12. [12]
  12. Tian, Z. R.; James, A. V.; Liu, J.; Bonnie, M.; Xu, H. F. J. Am. Chem. Soc., 2003, 125(41): 12384
13. [13]
  13. Peng, X. S.; Chen, A. C. Adv. Funct. Mater., 2006, 16: 1355
14. [14]
  14. Bo, C.; Erick, S. V.; Tetsuro, J. J. Nanosci. Nanotechnol., 2007, 7: 668
15. [15]
  15. Guo, Y. P.; Lee, N. H.; Oh, H. J.; Yoon, C. R.; Park, K. S.; Lee, H. G.; Lee, K. S.; Kim, S. J. Nanotechnology, 2007, 18: 295608
16. [16]
  16. Guo, Y. P.; Lee, N. H.; Oh, H. J.; Yoon, C. R.; Park, K. S.; Lee, W. H.; Li, Y. Z.; Lee, H. G.; Lee, K. S.; Kim, S. J. Thin Solid Films, 2008, 516: 8363
17. [17]
  17. Guo, Y. P.; Lee, N. H.; Oh, H. J.; Park, K. S.; Jung, S. C.; Kim, S. J. J. Nanosci. Nanotechnol., 2008, 8: 5316
18. [18]
  18. Guo, Y. P.; Lee, N. H.; Oh, H. J.; Yoon, C. R.; Park, K. S.; Jung, S. C.; Kim, S. J. Surface&Coatings Technology, 2008, 202: 5431
19. [19]
  19. Mor, G. K.; Varghese, O. K.; Paulose, M.; Grimes, C. A. Adv. Funct. Mater., 2005, 15: 1291
20. [20]
  20. Tang, Y. X.; Tao, J.; Tao, H. J.; Zhang, Y. Y.; Li, Z. L.; Tian, X. L. Rare Metal Materials and Engineering, 2008, 37(12): 2186 [汤育欣,陶杰,陶海军, 张焱焱,李转利,田西林. 稀有金属材料与工程, 2008, 37(12): 2186]
21. [21]
  21. Tang, Y. X.; Tao, J.; Zhang, Y. Y.;Wu, T.; Tao, H. J.; Bao, Z. G. Acta Phys. -Chim. Sin., 2008, 24(12): 2191 [汤育欣, 陶杰, 张焱焱, 吴涛,陶海军,包祖国.物理化学学报, 2008, 24(12): 2191]
22. [22]
  22. Cullity, B. D. Elements of X-ray diffraction. Massachussets: Addison-Wesley Publishing Company Press, 1978: 447
23. [23]
  23. Dong, X.; Tao, J.; Li, Y. Y.; Wang, T.; Zhu, H. Acta Phys. -Chim. Sin., 2009, 25(9): 1874 [董祥,陶杰,李莹滢,汪涛,朱宏. 物理化学学报, 2009, 25(9): 1874]
1. [1]
  Shengjuan Huo , Xiaoyan Zhang , Xiangheng Li , Xiangning Li , Tianfang Chen , Yuting Shen . Unveiling the Marvels of Titanium: Popularizing Multifunctional Colored Titanium Product Films. University Chemistry, 2024, 39(5): 184-192. doi: 10.3866/PKU.DXHX202310127
2. [2]
  Ruiqing LIU , Wenxiu LIU , Kun XIE , Yiran LIU , Hui CHENG , Xiaoyu WANG , Chenxu TIAN , Xiujing LIN , Xiaomiao FENG . Three-dimensional porous titanium nitride as a highly efficient sulfur host. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 867-876. doi: 10.11862/CJIC.20230441
3. [3]
  Bing LIU , Huang ZHANG , Hongliang HAN , Changwen HU , Yinglei ZHANG . Visible light degradation of methylene blue from water by triangle Au@TiO₂ mesoporous catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 941-952. doi: 10.11862/CJIC.20230398
4. [4]
  Xinyuan Shi , Chenyangjiang , Changyu Zhai , Xuemei Lu , Jia Li , Zhu Mao . Preparation and Photoelectric Performance Characterization of Perovskite CsPbBr₃ Thin Films. University Chemistry, 2024, 39(6): 383-389. doi: 10.3866/PKU.DXHX202312019
5. [5]
  Jiaxin Su , Jiaqi Zhang , Shuming Chai , Yankun Wang , Sibo Wang , Yuanxing Fang . Optimizing Poly(heptazine imide) Photoanodes Using Binary Molten Salt Synthesis for Water Oxidation Reaction. Acta Physico-Chimica Sinica, 2024, 40(12): 2408012-. doi: 10.3866/PKU.WHXB202408012
6. [6]
  Xiaoning TANG , Shu XIA , Jie LEI , Xingfu YANG , Qiuyang LUO , Junnan LIU , An XUE . Fluorine-doped MnO₂ with oxygen vacancy for stabilizing Zn-ion batteries. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1671-1678. doi: 10.11862/CJIC.20240149
7. [7]
  Zhiquan Zhang , Baker Rhimi , Zheyang Liu , Min Zhou , Guowei Deng , Wei Wei , Liang Mao , Huaming Li , Zhifeng Jiang . Insights into the Development of Copper-based Photocatalysts for CO₂ Conversion. Acta Physico-Chimica Sinica, 2024, 40(12): 2406029-. doi: 10.3866/PKU.WHXB202406029
8. [8]
  Caixia Lin , Zhaojiang Shi , Yi Yu , Jianfeng Yan , Keyin Ye , Yaofeng Yuan . Ideological and Political Design for the Electrochemical Synthesis of Benzoxathiazine Dioxide Experiment. University Chemistry, 2024, 39(2): 61-66. doi: 10.3866/PKU.DXHX202309005
9. [9]
  Jiahong ZHENG , Jingyun YANG . Preparation and electrochemical properties of hollow dodecahedral CoNi₂S₄ supported by MnO₂ nanowires. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1881-1891. doi: 10.11862/CJIC.20240170
10. [10]
  Fan JIA , Wenbao XU , Fangbin LIU , Haihua ZHANG , Hongbing FU . Synthesis and electroluminescence properties of Mn²⁺ doped quasi-two-dimensional perovskites (PEA)₂Pb_yMn_1-yBr₄. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1114-1122. doi: 10.11862/CJIC.20230473
11. [11]
  Ke Li , Chuang Liu , Jingping Li , Guohong Wang , Kai Wang . 钛酸铋/氮化碳无机有机复合S型异质结纯水光催化产过氧化氢. Acta Physico-Chimica Sinica, 2024, 40(11): 2403009-. doi: 10.3866/PKU.WHXB202403009
12. [12]
  Hongyun Liu , Jiarun Li , Xinyi Li , Zhe Liu , Jiaxuan Li , Cong Xiao . Course Ideological and Political Design of a Comprehensive Chemistry Experiment: Constructing a Visual Molecular Logic System Based on Intelligent Hydrogel Film Electrodes. University Chemistry, 2024, 39(2): 227-233. doi: 10.3866/PKU.DXHX202309070
13. [13]
  Rui Li , Huan Liu , Yinan Jiao , Shengjian Qin , Jie Meng , Jiayu Song , Rongrong Yan , Hang Su , Hengbin Chen , Zixuan Shang , Jinjin Zhao . 卤化物钙钛矿的单双向离子迁移. Acta Physico-Chimica Sinica, 2024, 40(11): 2311011-. doi: 10.3866/PKU.WHXB202311011
14. [14]
  Yixuan Gao , Lingxing Zan , Wenlin Zhang , Qingbo Wei . Comprehensive Innovation Experiment: Preparation and Characterization of Carbon-based Perovskite Solar Cells. University Chemistry, 2024, 39(4): 178-183. doi: 10.3866/PKU.DXHX202311091
15. [15]
  Lin Song , Dourong Wang , Biao Zhang . Innovative Experimental Design and Research on Preparing Flexible Perovskite Fluorescent Gels Using 3D Printing. University Chemistry, 2024, 39(7): 337-344. doi: 10.3866/PKU.DXHX202310107
16. [16]
  Zhuo WANG , Junshan ZHANG , Shaoyan YANG , Lingyan ZHOU , Yedi LI , Yuanpei LAN . Preparation and photocatalytic performance of CeO₂-reduced graphene oxide by thermal decomposition. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1708-1718. doi: 10.11862/CJIC.20240067
17. [17]
  Zeyuan WANG , Songzhi ZHENG , Hao LI , Jingbo WENG , Wei WANG , Yang WANG , Weihai SUN . Effect of I₂ interface modification engineering on the performance of all-inorganic CsPbBr₃ perovskite solar cells. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1290-1300. doi: 10.11862/CJIC.20240021
18. [18]
  Jizhou Liu , Chenbin Ai , Chenrui Hu , Bei Cheng , Jianjun Zhang . 六氯锡酸铵促进钙钛矿太阳能电池界面电子转移及其飞秒瞬态吸收光谱研究. Acta Physico-Chimica Sinica, 2024, 40(11): 2402006-. doi: 10.3866/PKU.WHXB202402006
19. [19]
  Hui Shi , Shuangyan Huan , Yuzhi Wang . Ideological and Political Design of Potassium Permanganate Oxidation-Reduction Titration Experiment. University Chemistry, 2024, 39(2): 175-180. doi: 10.3866/PKU.DXHX202308042
20. [20]
  Kai CHEN , Fengshun WU , Shun XIAO , Jinbao ZHANG , Lihua ZHU . PtRu/nitrogen-doped carbon for electrocatalytic methanol oxidation and hydrogen evolution by water electrolysis. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1357-1367. doi: 10.11862/CJIC.20230350

Get Citation

PDF

XML

Metrics

PDF Downloads(1979)
Abstract views(3341)
HTML views(85)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Preparation and Characterization of One-Dimensional TiO2 Nanowire Films on a Flexible Stainless Steel Substrate

Metrics

通讯作者: 陈斌, bchen63@163.com

Preparation and Characterization of One-Dimensional TiO₂ Nanowire Films on a Flexible Stainless Steel Substrate