Al₂O₃-Modified Fe₂O₃ Based ld Catalysts with od Thermal Stability

1.
School of Environmental Science and Engineering, Tongji University, Shanghai 200092, P. R. China

Received Date: 18 May 2009
Available Online: 7 September 2009

Al2O3-modified Fe2O3 based ld catalysts with od thermal stability were prepared by co-precipitation and deposition-precipitation method. Characterization techniques, such as transmission electron microscope (TEM), X-ray diffraction (XRD), N2 adsorption-desorption, and thermogravimetry-differential scanning calorimetry (TG-DSC), were used to investigate the structures, and surface morphologies of the catalysts. TEM results showed that after calcination at 500 ℃ the size distribution of the ld particles in the catalyst without Al2O3 doping was wide, the average diameter of the ld particles was about 7.0 nmand the size of the support particles ranged from 50 to 100 nm. However, the size distribution of the ld particles in the Al2O3-doped catalysts was narrow and the average diameter of the ld particles was around 5.0 nm. The Al2O3-doped Fe2O3 based Au particle size remained in a range of 30-50 nm, which is smaller than that of the Fe2O3 grains that were not doped with Al2O3. N2 adsorption-desorption measurements showed that Al2O3 doping resulted in a stable mesoporous structure for the catalysts and remained a higher specific surface area, which promoted the thermal stability of the support. XRD and TG-DSC results indicated that Al2O3 doping retarded the crystallization of the support and consequently inhibited the growth of ld particles during high-temperature calcination. Low temperature CO oxidation was used as a probe reaction to evaluate the catalytic activity. Even when calcined at 500 ℃ for 12 h, the catalyst with Al2O3 doping achieved complete CO conversion at 26.7 ℃ while the lowest temperature of the complete CO conversion (T100) of the catalyst without Al2O3 doping was as high as 61.6 ℃. Apparently, thermal stability is enhanced considerably by Al2O3 doping.
- Nano-structured ld catalyst,
- Ferric oxide support,
- Thermal stability,
- Al2O3,
- CO oxidation at low-temperature
1. [1]
  Jiaxi Xu , Yuan Ma . Influence of Hyperconjugation on the Stability and Stable Conformation of Ethane, Hydrazine, and Hydrogen Peroxide. University Chemistry, 2024, 39(11): 374-377. doi: 10.3866/PKU.DXHX202402049
2. [2]
  Kun WANG , Wenrui LIU , Peng JIANG , Yuhang SONG , Lihua CHEN , Zhao DENG . Hierarchical hollow structured BiOBr-Pt catalysts for photocatalytic CO₂ reduction. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1270-1278. doi: 10.11862/CJIC.20240037
3. [3]
  Xuyang Wang , Jiapei Zhang , Lirui Zhao , Xiaowen Xu , Guizheng Zou , Bin Zhang . Theoretical Study on the Structure and Stability of Copper-Ammonia Coordination Ions. University Chemistry, 2024, 39(3): 384-389. doi: 10.3866/PKU.DXHX202309065
4. [4]
  Wenlong LI , Xinyu JIA , Jie LING , Mengdan MA , Anning ZHOU . Photothermal catalytic CO₂ hydrogenation over a Mg-doped In₂O_3-x catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 919-929. doi: 10.11862/CJIC.20230421
5. [5]
  Zhanggui DUAN , Yi PEI , Shanshan ZHENG , Zhaoyang WANG , Yongguang WANG , Junjie WANG , Yang HU , Chunxin LÜ , Wei ZHONG . Preparation of UiO-66-NH₂ supported copper catalyst and its catalytic activity on alcohol oxidation. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 496-506. doi: 10.11862/CJIC.20230317
6. [6]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
7. [7]
  Siyu HOU , Weiyao LI , Jiadong LIU , Fei WANG , Wensi LIU , Jing YANG , Ying ZHANG . Preparation and catalytic performance of magnetic nano iron oxide by oxidation co-precipitation method. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1577-1582. doi: 10.11862/CJIC.20230469
8. [8]
  Shitao Fu , Jianming Zhang , Cancan Cao , Zhihui Wang , Chaoran Qin , Jian Zhang , Hui Xiong . Study on the Stability of Purple Cabbage Pigment. University Chemistry, 2024, 39(4): 367-372. doi: 10.3866/PKU.DXHX202401059
9. [9]
  Ruolin CHENG , Haoran WANG , Jing REN , Yingying MA , Huagen LIANG . Efficient photocatalytic CO₂ cycloaddition over W₁₈O₄₉/NH₂-UiO-66 composite catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 523-532. doi: 10.11862/CJIC.20230349
10. [10]
  Yi YANG , Shuang WANG , Wendan WANG , Limiao CHEN . Photocatalytic CO₂ reduction performance of Z-scheme Ag-Cu₂O/BiVO₄ photocatalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 895-906. doi: 10.11862/CJIC.20230434
11. [11]
  Qingqing SHEN , Xiangbowen DU , Kaicheng QIAN , Zhikang JIN , Zheng FANG , Tong WEI , Renhong LI . Self-supporting Cu/α-FeOOH/foam nickel composite catalyst for efficient hydrogen production by coupling methanol oxidation and water electrolysis. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1953-1964. doi: 10.11862/CJIC.20240028
12. [12]
  Zhiquan Zhang , Baker Rhimi , Zheyang Liu , Min Zhou , Guowei Deng , Wei Wei , Liang Mao , Huaming Li , Zhifeng Jiang . Insights into the Development of Copper-based Photocatalysts for CO₂ Conversion. Acta Physico-Chimica Sinica, 2024, 40(12): 2406029-. doi: 10.3866/PKU.WHXB202406029
13. [13]
  Juan WANG , Zhongqiu WANG , Qin SHANG , Guohong WANG , Jinmao LI . NiS and Pt as dual co-catalysts for the enhanced photocatalytic H₂ production activity of BaTiO₃ nanofibers. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1719-1730. doi: 10.11862/CJIC.20240102
14. [14]
  Wen YANG , Didi WANG , Ziyi HUANG , Yaping ZHOU , Yanyan FENG . La promoted hydrotalcite derived Ni-based catalysts: In situ preparation and CO₂ methanation performance. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 561-570. doi: 10.11862/CJIC.20230276
15. [15]
  Hongyi LI , Aimin WU , Liuyang ZHAO , Xinpeng LIU , Fengqin CHEN , Aikui LI , Hao HUANG . Effect of Y(PO₃)₃ double-coating modification on the electrochemical properties of Li[Ni_0.8Co_0.15Al_0.05]O₂. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1320-1328. doi: 10.11862/CJIC.20230480
16. [16]
  Wei Zhong , Dan Zheng , Yuanxin Ou , Aiyun Meng , Yaorong Su . K原子掺杂高度面间结晶的g-C₃N₄光催化剂及其高效H₂O₂光合成. Acta Physico-Chimica Sinica, 2024, 40(11): 2406005-. doi: 10.3866/PKU.WHXB202406005
17. [17]
  Xiaoning TANG , Junnan LIU , Xingfu YANG , Jie LEI , Qiuyang LUO , Shu XIA , An XUE . Effect of sodium alginate-sodium carboxymethylcellulose gel layer on the stability of Zn anodes. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1452-1460. doi: 10.11862/CJIC.20240191
18. [18]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369
19. [19]
  Jing SU , Bingrong LI , Yiyan BAI , Wenjuan JI , Haiying YANG , Zhefeng Fan . Highly sensitive electrochemical dopamine sensor based on a highly stable In-based metal-organic framework with amino-enriched pores. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1337-1346. doi: 10.11862/CJIC.20230414
20. [20]
  Zijian Jiang , Yuang Liu , Yijian Zong , Yong Fan , Wanchun Zhu , Yupeng Guo . Preparation of Nano Zinc Oxide by Microemulsion Method and Study on Its Photocatalytic Activity. University Chemistry, 2024, 39(5): 266-273. doi: 10.3866/PKU.DXHX202311101

Get Citation

PDF

XML

Metrics

PDF Downloads(1369)
Abstract views(2624)
HTML views(10)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

Al2O3-Modified Fe2O3 Based ld Catalysts with od Thermal Stability

Metrics

通讯作者: 陈斌, bchen63@163.com

Al₂O₃-Modified Fe₂O₃ Based ld Catalysts with od Thermal Stability