Citation: XU Jiang, ZHUO Cheng-Zhi, JIANG Shu-Yun. Effect of Nanoparticles on the Erosion-Corrosion Resistance Property of a Ni-Based Alloying Layer[J]. Acta Physico-Chimica Sinica, ;2009, 25(10): 1958-1966. doi: 10.3866/PKU.WHXB20090921 shu

Effect of Nanoparticles on the Erosion-Corrosion Resistance Property of a Ni-Based Alloying Layer

1.
College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, P. R. China

Received Date: 6 March 2009
Available Online: 31 July 2009

A nanoparticle reinforced Ni-based alloying layer was prepared by a duplex surface treatment on the surface of AISI 316L stainless steel. This steel contained Ni/nano-SiO2 or Ni/nano-SiC layer which was predeposited by brush plating and subsequent surface alloying with Ni-Cr-Mo-Cu by a double glow process. The microstructures of the two kinds of nanoparticles that reinforced the Ni-based alloying layers were investigated by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The corrosion behaviors of the composite layers under hydrodynamic conditions and at different rotational speeds were characterized by current responses at a potential of +0.2 V, a potentiodynamic polarization curve and electrochemical impedance spectroscopy (EIS) under a static state (3.5%(w, mass fraction) NaCl solution) and under slurry flow conditions (3.5%(w) NaCl solution+10%(w) sand particles). To assess possible erosion-corrosion mechanisms, the worn sample surfaces were observed by SEM. Electrochemical tests showed that the corrosion resistance of the composite layer with the brush plated Ni/nano-SiO2 particle interlayer was slightly lower than that of the single Ni-based alloying layer produced under static state conditions. However, under hydrodynamic conditions, the corrosion resistance of the composite layer with the brush plated Ni/nano-SiO2 particle interlayer was obviously superior to that of the single Ni-based alloying layer. The corrosion resistance of the composite layer produced with the brush plated Ni/nano-SiC particle interlayer was lower than that of the single Ni-morphologies we found that highly dispersive nano-SiO2 particles were helpful in improving the erosion-corrosion resistance of the Ni-based alloying layer whereas the carbides and silicide phases were deleterious to the Ni-based alloying layer.
- Nanoparticle,
- Duplex surface treatment,
- Polarization curve,
- Erosion-corrosion,
- Eelectrochemical impedance spectroscopy
1. [1]
  Yongjie ZHANG , Bintong HUANG , Yueming ZHAI . Research progress of formation mechanism and characterization techniques of protein corona on the surface of nanoparticles. Chinese Journal of Inorganic Chemistry, 2024, 40(12): 2318-2334. doi: 10.11862/CJIC.20240247
2. [2]
  Zhuoya WANG , Le HE , Zhiquan LIN , Yingxi WANG , Ling LI . Multifunctional nanozyme Prussian blue modified copper peroxide: Synthesis and photothermal enhanced catalytic therapy of self-provided hydrogen peroxide. Chinese Journal of Inorganic Chemistry, 2024, 40(12): 2445-2454. doi: 10.11862/CJIC.20240194
3. [3]
  Zhuo WANG , Xiaotong LI , Zhipeng HU , Junqiao PAN . Three-dimensional porous carbon decorated with nano bismuth particles: Preparation and sodium storage properties. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 267-274. doi: 10.11862/CJIC.20240223
4. [4]
  Ziliang KANG , Jiamin ZHANG , Hong AN , Xiaohua LIU , Yang CHEN , Jinping LI , Libo LI . Preparation and water adsorption properties of CaCl₂@MOF-808 in-situ composite moulded particles. Chinese Journal of Inorganic Chemistry, 2024, 40(11): 2133-2140. doi: 10.11862/CJIC.20240282
5. [5]
  Chenye An , Abiduweili Sikandaier , Xue Guo , Yukun Zhu , Hua Tang , Dongjiang Yang . 红磷纳米颗粒嵌入花状CeO₂分级S型异质结高效光催化产氢. Acta Physico-Chimica Sinica, 2024, 40(11): 2405019-. doi: 10.3866/PKU.WHXB202405019
6. [6]
  Xin Zhou , Zhi Zhang , Yun Yang , Shuijin Yang . A Study on the Enhancement of Photocatalytic Performance in C/Bi/Bi₂MoO₆ Composites by Ferroelectric Polarization: A Recommended Comprehensive Chemical Experiment. University Chemistry, 2024, 39(4): 296-304. doi: 10.3866/PKU.DXHX202310008
7. [7]
  Liang MA , Honghua ZHANG , Weilu ZHENG , Aoqi YOU , Zhiyong OUYANG , Junjiang CAO . Construction of highly ordered ZIF-8/Au nanocomposite structure arrays and application of surface-enhanced Raman spectroscopy. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1743-1754. doi: 10.11862/CJIC.20240075
8. [8]
  Min LI , Xianfeng MENG . Preparation and microwave absorption properties of ZIF-67 derived Co@C/MoS₂ nanocomposites. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1932-1942. doi: 10.11862/CJIC.20240065
9. [9]
  Jinyi Sun , Lin Ma , Yanjie Xi , Jing Wang . Preparation and Electrocatalytic Nitrogen Reduction Performance Study of Vanadium Nitride@Nitrogen-Doped Carbon Composite Nanomaterials: A Recommended Comprehensive Chemistry Experiment. University Chemistry, 2024, 39(4): 184-191. doi: 10.3866/PKU.DXHX202310094
10. [10]
  Na Li , Limin Shao . Deduction of the General Formula of the Inverse Function of the Titration Curve. University Chemistry, 2025, 40(3): 390-401. doi: 10.12461/PKU.DXHX202409134
11. [11]
  Hao Wu , Zhen Liu , Dachang Bai . ¹H NMR Spectrum of Amide Compounds. University Chemistry, 2024, 39(3): 231-238. doi: 10.3866/PKU.DXHX202309020
12. [12]
  Qin ZHU , Jiao MA , Zhihui QIAN , Yuxu LUO , Yujiao GUO , Mingwu XIANG , Xiaofang LIU , Ping NING , Junming GUO . Morphological evolution and electrochemical properties of cathode material LiAl_0.08Mn_1.92O₄ single crystal particles. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1549-1562. doi: 10.11862/CJIC.20240022
13. [13]
  Ruilin Han , Xiaoqi Yan . Comparison of Multiple Function Methods for Fitting Surface Tension and Concentration Curves. University Chemistry, 2024, 39(7): 381-385. doi: 10.3866/PKU.DXHX202311023
14. [14]
  Zelong LIANG , Shijia QIN , Pengfei GUO , Hang XU , Bin ZHAO . Synthesis and electrocatalytic CO₂ reduction performance of metal-organic framework catalysts loaded with silver particles. Chinese Journal of Inorganic Chemistry, 2025, 41(1): 165-173. doi: 10.11862/CJIC.20240409
15. [15]
  Wenjun Yang , Qiaoling Tan , Wenjiao Xie , Xiaoyu Pan , Youyong Yuan . Construction and Characterization of Calcium Alginate Microparticle Drug Delivery System: A Novel Design and Teaching Practice in Polymer Experiments. University Chemistry, 2025, 40(3): 371-380. doi: 10.12461/PKU.DXHX202405150
16. [16]
  Chongjing Liu , Yujian Xia , Pengjun Zhang , Shiqiang Wei , Dengfeng Cao , Beibei Sheng , Yongheng Chu , Shuangming Chen , Li Song , Xiaosong Liu . Understanding Solid-Gas and Solid-Liquid Interfaces through Near Ambient Pressure X-Ray Photoelectron Spectroscopy. Acta Physico-Chimica Sinica, 2025, 41(2): 100013-. doi: 10.3866/PKU.WHXB202309036
17. [17]
  Gaofeng Zeng , Shuyu Liu , Manle Jiang , Yu Wang , Ping Xu , Lei Wang . Micro/Nanorobots for Pollution Detection and Toxic Removal. University Chemistry, 2024, 39(9): 229-234. doi: 10.12461/PKU.DXHX202311055
18. [18]
  Limin Shao , Na Li . A Unified Equation Derived from the Charge Balance Equation for Constructing Acid-Base Titration Curve and Calculating Endpoint Error. University Chemistry, 2024, 39(11): 365-373. doi: 10.3866/PKU.DXHX202401086
19. [19]
  Zhuoming Liang , Ming Chen , Zhiwen Zheng , Kai Chen . Multidimensional Studies on Ketone-Enol Tautomerism of 1,3-Diketones By ¹H NMR. University Chemistry, 2024, 39(7): 361-367. doi: 10.3866/PKU.DXHX202311029
20. [20]
  Jiao CHEN , Yi LI , Yi XIE , Dandan DIAO , Qiang XIAO . Vapor-phase transport of MFI nanosheets for the fabrication of ultrathin b-axis oriented zeolite membranes. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 507-514. doi: 10.11862/CJIC.20230403

Get Citation

PDF

XML

Metrics

PDF Downloads(1361)
Abstract views(2745)
HTML views(52)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return