Citation: TANG Yu-Xin, TAO Jie, TAO Hai-Jun, WU Tao, WANG Ling, ZHANG Yan-Yan, LI Zhuan-Li, TIAN Xi-Lin. Fabrication and Characterization for Transparent Electrodes of TiO₂ Nanotube Arrays on Fluorine-Doped Tin Oxide-Coated Glass[J]. Acta Physico-Chimica Sinica, ;2008, 24(06): 1120-1126. doi: 10.3866/PKU.WHXB20080637 shu

Fabrication and Characterization for Transparent Electrodes of TiO₂ Nanotube Arrays on Fluorine-Doped Tin Oxide-Coated Glass

1.
College of Material Science and Technology, Nangjing University of Aeronautics and Astronautics, Nangjing 210016, P. R. China

Received Date: 29 January 2008
Available Online: 9 April 2008

A highly ordered TiO2 nanotube layer was fabricated on fluorine-doped tin oxide-coated glass substrate (FTO) by potentiostatic anodization of pure titanium film at room temperature, which was deposited by radio frequency (RF) magnetron sputtering. The structure and the composition of the as prepared TiO2 nanotubes were characterized by field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), UV-Vis transmission spectra, and photoelectrochemistry methods. The results showed that the Ti films converted to TiO2 nanotubes of 380 nm length, 90 nm pore diameter, and 15 nm wall thickness at the voltage of 20 V for 50 min. After annealing at 500 ℃ for 6 h in air, the anatase phase of TiO2 nanotube/FTO transparent electrodes were obtained, which had an average transmittance of 80% in visible wavelength range. The bandgap of TiO2 was determined as 3.28 eV, with a bandgap tail extending to 2.6 eV. Moreover, the photoelectrochemistry measurements indicated that the crystallized electrode exhibited a significant improvement of photoelectrochemical current response in comparison with the as-anodized electrode, and both the electrode potential and UV-illumination surely enhanced the effective separation of the electron-hole pairs, leading to the fact that the photo-induced electrons transferred quickly to the conducting glass via external circuit and formed photocurrent.
- RF magnetron sputtering; Ti thin films; Anodic oxidation; TiO2 nanotube arrays; Transparent electrode
1. [1]
  Xiufang Wang , Donglin Zhao , Kehua Zhang , Xiaojie Song . “Preparation of Carbon Nanotube/SnS₂ Photoanode Materials”: A Comprehensive University Chemistry Experiment. University Chemistry, 2024, 39(4): 157-162. doi: 10.3866/PKU.DXHX202308025
2. [2]
  Jiaxin Su , Jiaqi Zhang , Shuming Chai , Yankun Wang , Sibo Wang , Yuanxing Fang . Optimizing Poly(heptazine imide) Photoanodes Using Binary Molten Salt Synthesis for Water Oxidation Reaction. Acta Physico-Chimica Sinica, 2024, 40(12): 2408012-. doi: 10.3866/PKU.WHXB202408012
3. [3]
  Xinyuan Shi , Chenyangjiang , Changyu Zhai , Xuemei Lu , Jia Li , Zhu Mao . Preparation and Photoelectric Performance Characterization of Perovskite CsPbBr₃ Thin Films. University Chemistry, 2024, 39(6): 383-389. doi: 10.3866/PKU.DXHX202312019
4. [4]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369
5. [5]
  Hongyun Liu , Jiarun Li , Xinyi Li , Zhe Liu , Jiaxuan Li , Cong Xiao . Course Ideological and Political Design of a Comprehensive Chemistry Experiment: Constructing a Visual Molecular Logic System Based on Intelligent Hydrogel Film Electrodes. University Chemistry, 2024, 39(2): 227-233. doi: 10.3866/PKU.DXHX202309070
6. [6]
  Tong Zhou , Jun Li , Zitian Wen , Yitian Chen , Hailing Li , Zhonghong Gao , Wenyun Wang , Fang Liu , Qing Feng , Zhen Li , Jinyi Yang , Min Liu , Wei Qi . Experiment Improvement of “Redox Reaction and Electrode Potential” Based on the New Medical Concept. University Chemistry, 2024, 39(8): 276-281. doi: 10.3866/PKU.DXHX202401005
7. [7]
  Ji-Quan Liu , Huilin Guo , Ying Yang , Xiaohui Guo . Calculation and Discussion of Electrode Potentials in Redox Reactions of Water. University Chemistry, 2024, 39(8): 351-358. doi: 10.3866/PKU.DXHX202401031
8. [8]
  Xiaomei Ning , Liang Zhan , Xiaosong Zhou , Jin Luo , Xunfu Zhou , Cuifen Luo . Preparation and Electro-Oxidation Performance of PtBi Supported on Carbon Cloth: A Recommended Comprehensive Chemical Experiment. University Chemistry, 2024, 39(11): 217-224. doi: 10.3866/PKU.DXHX202401085
9. [9]
  Fanxin Kong , Hongzhi Wang , Huimei Duan . Inhibition effect of sulfation on Pt/TiO2 catalysts in methane combustion. Chinese Journal of Structural Chemistry, 2024, 43(5): 100287-100287. doi: 10.1016/j.cjsc.2024.100287
10. [10]
  Ke Li , Chuang Liu , Jingping Li , Guohong Wang , Kai Wang . 钛酸铋/氮化碳无机有机复合S型异质结纯水光催化产过氧化氢. Acta Physico-Chimica Sinica, 2024, 40(11): 2403009-. doi: 10.3866/PKU.WHXB202403009
11. [11]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
12. [12]
  Qi Li , Pingan Li , Zetong Liu , Jiahui Zhang , Hao Zhang , Weilai Yu , Xianluo Hu . Fabricating Micro/Nanostructured Separators and Electrode Materials by Coaxial Electrospinning for Lithium-Ion Batteries: From Fundamentals to Applications. Acta Physico-Chimica Sinica, 2024, 40(10): 2311030-. doi: 10.3866/PKU.WHXB202311030
13. [13]
  Lihua HUANG , Jian HUA . Denitration performance of HoCeMn/TiO₂ catalysts prepared by co-precipitation and impregnation methods. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 629-645. doi: 10.11862/CJIC.20230315
14. [14]
  Hongye Bai , Lihao Yu , Jinfu Xu , Xuliang Pang , Yajie Bai , Jianguo Cui , Weiqiang Fan . Controllable Decoration of Ni-MOF on TiO2: Understanding the Role of Coordination State on Photoelectrochemical Performance. Chinese Journal of Structural Chemistry, 2023, 42(10): 100096-100096. doi: 10.1016/j.cjsc.2023.100096
15. [15]
  Wenhao Wang , Guangpu Zhang , Qiufeng Wang , Fancang Meng , Hongbin Jia , Wei Jiang , Qingmin Ji . Hybrid nanoarchitectonics of TiO₂/aramid nanofiber membranes with softness and durability for photocatalytic dye degradation. Chinese Chemical Letters, 2024, 35(7): 109193-. doi: 10.1016/j.cclet.2023.109193
16. [16]
  Mengli Xu , Zhenmin Xu , Zhenfeng Bian . Achieving Ullmann coupling reaction via photothermal synergy with ultrafine Pd nanoclusters supported on mesoporous TiO2. Chinese Journal of Structural Chemistry, 2024, 43(7): 100305-100305. doi: 10.1016/j.cjsc.2024.100305
17. [17]
  Hao BAI , Weizhi JI , Jinyan CHEN , Hongji LI , Mingji LI . Preparation of Cu₂O/Cu-vertical graphene microelectrode and detection of uric acid/electroencephalogram. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1309-1319. doi: 10.11862/CJIC.20240001
18. [18]
  Chuanming GUO , Kaiyang ZHANG , Yun WU , Rui YAO , Qiang ZHAO , Jinping LI , Guang LIU . Performance of MnO₂-0.39IrO_x composite oxides for water oxidation reaction in acidic media. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1135-1142. doi: 10.11862/CJIC.20230459
19. [19]
  Xin Zhou , Zhi Zhang , Yun Yang , Shuijin Yang . A Study on the Enhancement of Photocatalytic Performance in C/Bi/Bi₂MoO₆ Composites by Ferroelectric Polarization: A Recommended Comprehensive Chemical Experiment. University Chemistry, 2024, 39(4): 296-304. doi: 10.3866/PKU.DXHX202310008
20. [20]
  Fan JIA , Wenbao XU , Fangbin LIU , Haihua ZHANG , Hongbing FU . Synthesis and electroluminescence properties of Mn²⁺ doped quasi-two-dimensional perovskites (PEA)₂Pb_yMn_1-yBr₄. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1114-1122. doi: 10.11862/CJIC.20230473

Get Citation

PDF

XML

Metrics

PDF Downloads(3201)
Abstract views(4282)
HTML views(128)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

Fabrication and Characterization for Transparent Electrodes of TiO2 Nanotube Arrays on Fluorine-Doped Tin Oxide-Coated Glass

Metrics

通讯作者: 陈斌, bchen63@163.com

Fabrication and Characterization for Transparent Electrodes of TiO₂ Nanotube Arrays on Fluorine-Doped Tin Oxide-Coated Glass