Citation: WANG Ting, JIANG Xin, LI Xi. Preparation of TiO₂ Nanoparticles on Surface of Different Supports by Adsorption Phase Reaction Technique[J]. Acta Physico-Chimica Sinica, ;2007, 23(09): 1375-1380. doi: 10.3866/PKU.WHXB20070913 shu

Preparation of TiO₂ Nanoparticles on Surface of Different Supports by Adsorption Phase Reaction Technique

1.
College of Material and Chemical Engineering, Zhejiang University, Hangzhou 310027, P. R. China

Received Date: 18 April 2007
Available Online: 28 June 2007

The influence of supports on the preparation of TiO2 nanoparticles in adsorption phase nanoreactor formed by the adsorption layer on silica surface was studied. Series temperature experiments of two types of supports (support A: size 20 nm, specific surface area 640 m2·g-1; support SiO2 B: size 12 nm, surface area 200 m2·g-1) were designed. Electronic energy spectrum indicated that the concentration of TiO2 on the two supports both decreased with temperature increasing. TiO2 quantity on support A decreased sharply between 40-60 ℃, whereas the coresponding temperature range for support B was between 30-50 ℃. TiO2 particles on support B were more uniform than those on support A in TEM. The grain size curve by XRD suggested that size of TiO2 particles on support A reduced with temperature rising and there was also a sharp decrease as in quantity curve of TiO2, but TiO2 particles on support B had a substantially constant size. Based on the characteristics of adsorption on silica surface, the generality of adsorption on SiO2 was proposed to explain the same changes in Ti concentration on different supports. The different characteristics of internal/external surface induced variant temperature-sensitivities and characteristics of adsorption on support surface. Moreover these different adsorptions led variance of content and grain size, as well as characteristics of TiO2 on the two types of supports.
- Adsorption phase reaction technique; TiO2 nanoparticles; Characteristics of support; Internal/external surface
1. [1]
  Zhuoyan Lv , Yangming Ding , Leilei Kang , Lin Li , Xiao Yan Liu , Aiqin Wang , Tao Zhang . Light-Enhanced Direct Epoxidation of Propylene by Molecular Oxygen over CuO_x/TiO₂ Catalyst. Acta Physico-Chimica Sinica, 2025, 41(4): 100038-. doi: 10.3866/PKU.WHXB202408015
2. [2]
  Yongjie ZHANG , Bintong HUANG , Yueming ZHAI . Research progress of formation mechanism and characterization techniques of protein corona on the surface of nanoparticles. Chinese Journal of Inorganic Chemistry, 2024, 40(12): 2318-2334. doi: 10.11862/CJIC.20240247
3. [3]
  Fanxin Kong , Hongzhi Wang , Huimei Duan . Inhibition effect of sulfation on Pt/TiO2 catalysts in methane combustion. Chinese Journal of Structural Chemistry, 2024, 43(5): 100287-100287. doi: 10.1016/j.cjsc.2024.100287
4. [4]
  Zhiqiang Wang , Yajie Gao , Tianjun Wang , Wei Chen , Zefeng Ren , Xueming Yang , Chuanyao Zhou . Photocatalyzed oxidation of water on oxygen pretreated rutile TiO₂(110). Chinese Chemical Letters, 2025, 36(4): 110602-. doi: 10.1016/j.cclet.2024.110602
5. [5]
  Juan Yuan , Bin Zhang , Jinping Wu , Mengfan Wang . Design of a Comprehensive Experiment on Preparation and Characterization of Cu₂(Salen)₂ Nanomaterials with Two Distinct Morphologies. University Chemistry, 2024, 39(10): 420-425. doi: 10.3866/PKU.DXHX202402014
6. [6]
  Linlu Bai , Wensen Li , Xiaoyu Chu , Haochun Yin , Yang Qu , Ekaterina Kozlova , Zhao-Di Yang , Liqiang Jing . Effects of nanosized Au on the interface of zinc phthalocyanine/TiO₂ for CO₂ photoreduction. Chinese Chemical Letters, 2025, 36(2): 109931-. doi: 10.1016/j.cclet.2024.109931
7. [7]
  Lihua HUANG , Jian HUA . Denitration performance of HoCeMn/TiO₂ catalysts prepared by co-precipitation and impregnation methods. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 629-645. doi: 10.11862/CJIC.20230315
8. [8]
  Hongye Bai , Lihao Yu , Jinfu Xu , Xuliang Pang , Yajie Bai , Jianguo Cui , Weiqiang Fan . Controllable Decoration of Ni-MOF on TiO2: Understanding the Role of Coordination State on Photoelectrochemical Performance. Chinese Journal of Structural Chemistry, 2023, 42(10): 100096-100096. doi: 10.1016/j.cjsc.2023.100096
9. [9]
  Wenhao Wang , Guangpu Zhang , Qiufeng Wang , Fancang Meng , Hongbin Jia , Wei Jiang , Qingmin Ji . Hybrid nanoarchitectonics of TiO₂/aramid nanofiber membranes with softness and durability for photocatalytic dye degradation. Chinese Chemical Letters, 2024, 35(7): 109193-. doi: 10.1016/j.cclet.2023.109193
10. [10]
  Mengli Xu , Zhenmin Xu , Zhenfeng Bian . Achieving Ullmann coupling reaction via photothermal synergy with ultrafine Pd nanoclusters supported on mesoporous TiO2. Chinese Journal of Structural Chemistry, 2024, 43(7): 100305-100305. doi: 10.1016/j.cjsc.2024.100305
11. [11]
  Fei ZHOU , Xiaolin JIA . Co₃O₄/TiO₂ composite photocatalyst: Preparation and synergistic degradation performance of toluene. Chinese Journal of Inorganic Chemistry, 2024, 40(11): 2232-2240. doi: 10.11862/CJIC.20240236
12. [12]
  Jiatong Li , Linlin Zhang , Peng Huang , Chengjun Ge . Carbon bridge effects regulate TiO₂–acrylate fluoroboron coatings for efficient marine antifouling. Chinese Chemical Letters, 2025, 36(2): 109970-. doi: 10.1016/j.cclet.2024.109970
13. [13]
  Bo YANG , Gongxuan LÜ , Jiantai MA . Corrosion inhibition of nickel-cobalt-phosphide in water by coating TiO₂ layer. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 365-384. doi: 10.11862/CJIC.20240063
14. [14]
  Xingang Kong , Yabei Su , Cuijuan Xing , Weijie Cheng , Jianfeng Huang , Lifeng Zhang , Haibo Ouyang , Qi Feng . Facile synthesis of porous TiO₂/SnO₂ nanocomposite as lithium ion battery anode with enhanced cycling stability via nanoconfinement effect. Chinese Chemical Letters, 2024, 35(11): 109428-. doi: 10.1016/j.cclet.2023.109428
15. [15]
  Cailiang Yue , Nan Sun , Yixing Qiu , Linlin Zhu , Zhiling Du , Fuqiang Liu . A direct Z-scheme 0D α-Fe₂O₃/TiO₂ heterojunction for enhanced photo-Fenton activity with low H₂O₂ consumption. Chinese Chemical Letters, 2024, 35(12): 109698-. doi: 10.1016/j.cclet.2024.109698
16. [16]
  Yifen He , Chao Qu , Na Ren , Dawei Liang . Enhanced degradation of refractory organics in ORR-EO system with a blue TiO₂ nanotube array modified Ti-based Ni-Sb co-doped SnO₂ anode. Chinese Chemical Letters, 2024, 35(8): 109262-. doi: 10.1016/j.cclet.2023.109262
17. [17]
  Maosen Xu , Pengfei Zhu , Qinghong Cai , Meichun Bu , Chenghua Zhang , Hong Wu , Youzhou He , Min Fu , Siqi Li , Xingyan Liu . In-situ fabrication of TiO₂/NH₂−MIL-125(Ti) via MOF-driven strategy to promote efficient interfacial effects for enhancing photocatalytic NO removal activity. Chinese Chemical Letters, 2024, 35(10): 109524-. doi: 10.1016/j.cclet.2024.109524
18. [18]
  Peng YUE , Liyao SHI , Jinglei CUI , Huirong ZHANG , Yanxia GUO . Effects of Ce and Mn promoters on the selective oxidation of ammonia over V₂O₅/TiO₂ catalyst. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 293-307. doi: 10.11862/CJIC.20240210
19. [19]
  Xing Xiao , Yunling Jia , Wanyu Hong , Yuqing He , Yanjun Wang , Lizhi Zhao , Huiqin An , Zhen Yin . Sulfur-defective ZnIn2S4 nanosheets decorated by TiO2 nanosheets with exposed {001} facets to accelerate charge transfer for efficient photocatalytic hydrogen evolution. Chinese Journal of Structural Chemistry, 2024, 43(12): 100474-100474. doi: 10.1016/j.cjsc.2024.100474
20. [20]
  Shuangxi Li , Huijun Yu , Tianwei Lan , Liyi Shi , Danhong Cheng , Lupeng Han , Dengsong Zhang . NO_x reduction against alkali poisoning over Ce(SO₄)₂-V₂O₅/TiO₂ catalysts by constructing the Ce⁴⁺–SO₄²⁻ pair sites. Chinese Chemical Letters, 2024, 35(5): 108240-. doi: 10.1016/j.cclet.2023.108240

Get Citation

PDF

XML

Metrics

PDF Downloads(2809)
Abstract views(3623)
HTML views(3)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

Preparation of TiO2 Nanoparticles on Surface of Different Supports by Adsorption Phase Reaction Technique

Metrics

通讯作者: 陈斌, bchen63@163.com

Preparation of TiO₂ Nanoparticles on Surface of Different Supports by Adsorption Phase Reaction Technique