Citation: WANG Jie, XU You-Long, SUN Xiao-Fei, XIAO Fang, MAO Sheng-Chun. Capacitance Properties of Porous Polypyrrole Thick Films Prepared Electrochemically by Multi-step Polymerization[J]. Acta Physico-Chimica Sinica, ;2007, 23(06): 877-882. doi: 10.3866/PKU.WHXB20070616 shu

Capacitance Properties of Porous Polypyrrole Thick Films Prepared Electrochemically by Multi-step Polymerization

1.

School of Electronic and Information Engineering, Xi’an Jiaotong University, Xi’an 710049, P. R. China

Received Date: 29 December 2006
Available Online: 28 April 2007

To obtain polypyrrole (PPy) films with high area specific capacitance as electrode material for supercapacitors, the multi-step polymerization method was proposed for preparing PPy thick films with polymerization charge of 8, 10, and 12 mAh·cm-2, doped with Cl- and p-toluenesulfonate (TOS-), respectively. The capacitance properties of the PPy films were investigated by galvanostatic charge/discharge, cyclic voltammetry (CV), and electrochemical impedance spectrum (EIS) technologies. The section morphology of the PPy films was observed by using field emission electron scanning microscope (SEM). The results showed that two kinds of even porous PPy films with area specific capacitance up to 5 F·cm-2 could be obtained by multi-step method. Moreover, the mass specific capacitance (referring to the masses of polymer and doping ions) of PPy-Cl could reach 330 F·g-1, and the value of PPy-TOS could reach 191 F·g-1, which were similar with that of PPy thin films. However, the discharge rate of the PPy-TOS film was more rapid than that of the PPy-Cl film. In addition, the growth processes of PPy films from one-step
polymerization method and multi-step polymerization method were discussed.
- Polypyrrole; Supercapacitors; Capacitance; Morphology; Porous
1. [1]
  Jin CHANG . Supercapacitor performance and first-principles calculation study of Co-doping Ni(OH)₂. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1697-1707. doi: 10.11862/CJIC.20240108
2. [2]
  Yanhui XUE , Shaofei CHAO , Man XU , Qiong WU , Fufa WU , Sufyan Javed Muhammad . Construction of high energy density hexagonal hole MXene aqueous supercapacitor by vacancy defect control strategy. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1640-1652. doi: 10.11862/CJIC.20240183
3. [3]
  Zhaomei LIU , Wenshi ZHONG , Jiaxin LI , Gengshen HU . Preparation of nitrogen-doped porous carbons with ultra-high surface areas for high-performance supercapacitors. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 677-685. doi: 10.11862/CJIC.20230404
4. [4]
  Hongyi Zhang , Zhihong Shi , Zhijun Zhang . A New Strategy for “De-formulized” Calculation of Dynamic Buffer Capacity in Analytical Chemistry Education. University Chemistry, 2024, 39(3): 390-394. doi: 10.3866/PKU.DXHX202309030
5. [5]
  Ruiqing LIU , Wenxiu LIU , Kun XIE , Yiran LIU , Hui CHENG , Xiaoyu WANG , Chenxu TIAN , Xiujing LIN , Xiaomiao FENG . Three-dimensional porous titanium nitride as a highly efficient sulfur host. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 867-876. doi: 10.11862/CJIC.20230441
6. [6]
  Qin ZHU , Jiao MA , Zhihui QIAN , Yuxu LUO , Yujiao GUO , Mingwu XIANG , Xiaofang LIU , Ping NING , Junming GUO . Morphological evolution and electrochemical properties of cathode material LiAl_0.08Mn_1.92O₄ single crystal particles. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1549-1562. doi: 10.11862/CJIC.20240022
7. [7]
  Juan Yuan , Bin Zhang , Jinping Wu , Mengfan Wang . Design of a Comprehensive Experiment on Preparation and Characterization of Cu₂(Salen)₂ Nanomaterials with Two Distinct Morphologies. University Chemistry, 2024, 39(10): 420-425. doi: 10.3866/PKU.DXHX202402014
8. [8]
  Yangrui Xu , Yewei Ren , Xinlin Liu , Hongping Li , Ziyang Lu . 具有高传质和亲和表面的NH₂-UIO-66基疏水多孔液体用于增强CO₂光还原. Acta Physico-Chimica Sinica, 2024, 40(11): 2403032-. doi: 10.3866/PKU.WHXB202403032
9. [9]
  Zongfei YANG , Xiaosen ZHAO , Jing LI , Wenchang ZHUANG . Research advances in heteropolyoxoniobates. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 465-480. doi: 10.11862/CJIC.20230306
10. [10]
  Ziheng Zhuang , Xiao Xu , Kin Shing Chan . Superdrugs for Superbugs. University Chemistry, 2024, 39(9): 128-133. doi: 10.3866/PKU.DXHX202309040
11. [11]
  Tingting Yu , Si Chen , Lianglong Sun , Tongtong Shi , Kai Sun , Xin Wang . Comprehensive Experimental Design for the Photochemical Synthesis, Analysis, and Characterization of Difluoropyrroles. University Chemistry, 2024, 39(11): 196-203. doi: 10.3866/PKU.DXHX202401022
12. [12]
  Hong Zheng , Xin Peng , Chunwang Yi . The Tale of Caprolactam Cyclic Oligomers: The Ever-changing Life of “Princess Cyclo”. University Chemistry, 2024, 39(9): 40-47. doi: 10.12461/PKU.DXHX202403058
13. [13]
  Chengqian Mao , Yanghan Chen , Haotong Bai , Junru Huang , Junpeng Zhuang . Photodimerization of Styrylpyridinium Salt and Its Application in Silk Screen Printing. University Chemistry, 2024, 39(5): 354-362. doi: 10.3866/PKU.DXHX202312014
14. [14]
  Jiaxin Su , Jiaqi Zhang , Shuming Chai , Yankun Wang , Sibo Wang , Yuanxing Fang . Optimizing Poly(heptazine imide) Photoanodes Using Binary Molten Salt Synthesis for Water Oxidation Reaction. Acta Physico-Chimica Sinica, 2024, 40(12): 2408012-. doi: 10.3866/PKU.WHXB202408012
15. [15]
  Xiaochen Zhang , Fei Yu , Jie Ma . 多角度数理模拟在电容去离子中的前沿应用. Acta Physico-Chimica Sinica, 2024, 40(11): 2311026-. doi: 10.3866/PKU.WHXB202311026

Get Citation

PDF

XML

Metrics

PDF Downloads(2879)
Abstract views(4676)
HTML views(88)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return