Supported Catalyst LaCoO₃/γ-Al₂O₃ Prepared by Impregnating under Ultrasound

1.
School of Engineering of Tianjin University of Commerce, Tianjin　300400; 1Chemical Engineering College of Tianjin University, Tianjin　300072

Received Date: 10 December 2002
Available Online: 15 July 2003

The supported catalyst LaCoO3/γ-Al2O3 was prepared by ultrasound during the impregnating preparation steps and the effects of ultrasound with various frequencies on the properties of catalyst were investigated in this paper. 　　For the preparation of LaCoO3/γ-Al2O3, 5 g ofγ-Al2O3 ( 20 mesh) was added to 20 mL of molar ratio 1:1 mixture of aqueous solution of La(NO3)3 and Co(NO3)2. Ultrasonic irradiation was performed with direct immersion horn (with various frequencies i.e. 33, 40, 50 and 70 kHz) at 20 ℃. The precursors were filtered off, washed with water, dried for 2 h at 120 ℃ and were calcined for 5 h at 850 ℃. The formation of LaCoO3 was determined by XRD. Another sample (O＃ sample) for comparision LaCoO3/γ-Al2O3 was prepared under the same experimental conditions and steps except ultrasonic irradiation was replaced by mechanical stirring for 2 h in impregnating step. 　　The effects of ultrasonic irradiation frequencies and irradiation time in impregnating step on loading of LaCoO3 were studied. The results showed that ultrasonic irradiation could decrease impregnating time and increase loading of LaCoO3. And ultrasonic irradiation with 50 kHz frequencies showed the best experimental result. The loading of LaCoO3 of LaCoO3/γ-Al2O3 ( 1＃ sample ), prepared by ultrasonic irradiation ( with 50 kHz for 5 min), was 25％ more than that of 0＃ sample. Transmission electron micrograph showed that on the support surface of 1＃ sample, the average particle size of LaCoO3 was 8 nm. The scanning electron micrographs and electron microprobe analyzer scans showed that on the support surface of 1＃ sample, distribution of LaCoO3 particles was better compared with that on the support surface of 0＃ sample. Using the BET method, surface area and pore distribution were determined. They were 133.17 m2•g－1(1＃ sample) and 114.71 m2•g－1 (0＃ sample )respectirely. 1＃ sample have more micropores than 0＃ sample. According to the results of activities evaluation of decomposition of NO, the catalytic activity of 1＃ sample was higher than that of 0＃ sample. Therefore, using ultrasonic irradiation in the impregnating step of catalyst preparation is an effective method for enhancing catalytic activity of the catalyst.
- Ultrasound;Provskitetype oxide;Supported catalyst;Preparation
1. [1]
  Qiuping Liu , Yongxian Fan , Wenxian Chen , Mengdi Wang , Mei Mei , Genrong Qiang . Design of Ideological and Political Education for the Preparation Experiment of Ferrous Sulfate. University Chemistry, 2024, 39(2): 116-120. doi: 10.3866/PKU.DXHX202309083
2. [2]
  Yongming Guo , Jie Li , Chaoyong Liu . Green Improvement and Educational Design in the Synthesis and Characterization of Silver Nanoparticles. University Chemistry, 2024, 39(3): 258-265. doi: 10.3866/PKU.DXHX202309057
3. [3]
  Zhanggui DUAN , Yi PEI , Shanshan ZHENG , Zhaoyang WANG , Yongguang WANG , Junjie WANG , Yang HU , Chunxin LÜ , Wei ZHONG . Preparation of UiO-66-NH₂ supported copper catalyst and its catalytic activity on alcohol oxidation. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 496-506. doi: 10.11862/CJIC.20230317
4. [4]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
5. [5]
  Yanan Liu , Yufei He , Dianqing Li . Preparation of Highly Dispersed LDHs-based Catalysts and Testing of Nitro Compound Reduction Performance: A Comprehensive Chemical Experiment for Research Transformation. University Chemistry, 2024, 39(8): 306-313. doi: 10.3866/PKU.DXHX202401081
6. [6]
  Ping ZHANG , Chenchen ZHAO , Xiaoyun CUI , Bing XIE , Yihan LIU , Haiyu LIN , Jiale ZHANG , Yu'nan CHEN . Preparation and adsorption-photocatalytic performance of ZnAl@layered double oxides. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1965-1974. doi: 10.11862/CJIC.20240014
7. [7]
  Dan Li , Hui Xin , Xiaofeng Yi . Comprehensive Experimental Design on Ni-based Catalyst for Biofuel Production. University Chemistry, 2024, 39(8): 204-211. doi: 10.3866/PKU.DXHX202312046
8. [8]
  Xinyuan Shi , Chenyangjiang , Changyu Zhai , Xuemei Lu , Jia Li , Zhu Mao . Preparation and Photoelectric Performance Characterization of Perovskite CsPbBr₃ Thin Films. University Chemistry, 2024, 39(6): 383-389. doi: 10.3866/PKU.DXHX202312019
9. [9]
  Wen YANG , Didi WANG , Ziyi HUANG , Yaping ZHOU , Yanyan FENG . La promoted hydrotalcite derived Ni-based catalysts: In situ preparation and CO₂ methanation performance. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 561-570. doi: 10.11862/CJIC.20230276
10. [10]
  Qingqing SHEN , Xiangbowen DU , Kaicheng QIAN , Zhikang JIN , Zheng FANG , Tong WEI , Renhong LI . Self-supporting Cu/α-FeOOH/foam nickel composite catalyst for efficient hydrogen production by coupling methanol oxidation and water electrolysis. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1953-1964. doi: 10.11862/CJIC.20240028
11. [11]
  Juntao Yan , Liang Wei . 2D S-Scheme Heterojunction Photocatalyst. Acta Physico-Chimica Sinica, 2024, 40(10): 2312024-. doi: 10.3866/PKU.WHXB202312024
12. [12]
  Jiapei Zou , Junyang Zhang , Xuming Wu , Cong Wei , Simin Fang , Yuxi Wang . A Comprehensive Experiment Based on Electrocatalytic Nitrate Reduction into Ammonia: Synthesis, Characterization, Performance Exploration, and Applicable Design of Copper-based Catalysts. University Chemistry, 2024, 39(6): 373-382. doi: 10.3866/PKU.DXHX202312081
13. [13]
  Yixuan Gao , Lingxing Zan , Wenlin Zhang , Qingbo Wei . Comprehensive Innovation Experiment: Preparation and Characterization of Carbon-based Perovskite Solar Cells. University Chemistry, 2024, 39(4): 178-183. doi: 10.3866/PKU.DXHX202311091
14. [14]
  Asif Hassan Raza , Shumail Farhan , Zhixian Yu , Yan Wu . 用于高效制氢的双S型ZnS/ZnO/CdS异质结构光催化剂. Acta Physico-Chimica Sinica, 2024, 40(11): 2406020-. doi: 10.3866/PKU.WHXB202406020
15. [15]
  Zhiquan Zhang , Baker Rhimi , Zheyang Liu , Min Zhou , Guowei Deng , Wei Wei , Liang Mao , Huaming Li , Zhifeng Jiang . Insights into the Development of Copper-based Photocatalysts for CO₂ Conversion. Acta Physico-Chimica Sinica, 2024, 40(12): 2406029-. doi: 10.3866/PKU.WHXB202406029
16. [16]
  Ke Li , Chuang Liu , Jingping Li , Guohong Wang , Kai Wang . 钛酸铋/氮化碳无机有机复合S型异质结纯水光催化产过氧化氢. Acta Physico-Chimica Sinica, 2024, 40(11): 2403009-. doi: 10.3866/PKU.WHXB202403009
17. [17]
  Ruolin CHENG , Haoran WANG , Jing REN , Yingying MA , Huagen LIANG . Efficient photocatalytic CO₂ cycloaddition over W₁₈O₄₉/NH₂-UiO-66 composite catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 523-532. doi: 10.11862/CJIC.20230349
18. [18]
  Fan JIA , Wenbao XU , Fangbin LIU , Haihua ZHANG , Hongbing FU . Synthesis and electroluminescence properties of Mn²⁺ doped quasi-two-dimensional perovskites (PEA)₂Pb_yMn_1-yBr₄. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1114-1122. doi: 10.11862/CJIC.20230473
19. [19]
  Yi YANG , Shuang WANG , Wendan WANG , Limiao CHEN . Photocatalytic CO₂ reduction performance of Z-scheme Ag-Cu₂O/BiVO₄ photocatalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 895-906. doi: 10.11862/CJIC.20230434
20. [20]
  Jiahong ZHENG , Jiajun SHEN , Xin BAI . Preparation and electrochemical properties of nickel foam loaded NiMoO₄/NiMoS₄ composites. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 581-590. doi: 10.11862/CJIC.20230253

Get Citation

PDF

XML

Metrics

PDF Downloads(2510)
Abstract views(3670)
HTML views(71)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

Supported Catalyst LaCoO3/γ-Al2O3 Prepared by Impregnating under Ultrasound

Metrics

通讯作者: 陈斌, bchen63@163.com

Supported Catalyst LaCoO₃/γ-Al₂O₃ Prepared by Impregnating under Ultrasound