Citation: Zhou Qinwei, Jiang Anren, Xie Quangen, Peng Ying, Liu Dingjiang, Deng Jingfa*. THE THERMOSTABILITY OF OXYGEN ATOMS AT DIFFERENT SITES IN THE CRYSTAL LATTICE OF HIGH-T_C SUPERCONDUCTOR Ba₂YCu₃O_6.92[J]. Acta Physico-Chimica Sinica, ;1988, 4(03): 229-233. doi: 10.3866/PKU.WHXB19880302 shu

THE THERMOSTABILITY OF OXYGEN ATOMS AT DIFFERENT SITES IN THE CRYSTAL LATTICE OF HIGH-T_C SUPERCONDUCTOR Ba₂YCu₃O_6.92

1.
Department of Chemistry; Fudan University; Shanghai

Received Date: 7 December 1987
Available Online: 15 June 1988

Studies on high-T_c superconductor Ba_2YCu_3O_(6.92) using thermogravimetry, temperature programmed decomposition, oxygen isotopic exchange method are reported. There are six steps in the thermogavimetric graph of Ba_2YCu_3O_(6.92). At the first step, 0.40 oxygen atom per unit cell is released, the amount of which corresponds to that of the oxygen released from the CuO_4 square plane when the oxidation number of copper reduced from +3 to +2. This amount of oxygen plays a key role on the influence on the T_c of superconductor. At the is 0.45, corresponding to the amount of oxygen released from CuO_4 when the oxidation number of copper changed from +2 to +1. The oxygen atom released totally at the last three steps is 1.07 per unit cell, which correspondes to the oxygen released from CuO_5 square pyramid when the oxidation number of copper changed from +2 to +1. The first three steps are almost continuous, so in TPD curve there is only one peak at 514 ℃ with respect to the three steps in TG curve and the decomposition heat of this one is 171±8 kJ mol~(-1). Another peak which is over 900 ℃ on TPD curve is the result of the loss of oxygen from the last three steps in TG curve. The sample released oxygen can recover its supeconductivity after reabsorbing oxygen. Oxygen isotopic exchange method shows that the oxygen atoms of CuO_4 and CuO_5 groups can be interexchanged under certain temperature and indicates that there is some bonding between CuO_4 square plane and CuO_5 square pyramidal groups in the crystal lattice of Ba_2YCu_3O_(6.92).
1. [1]
  Xuewei BA , Cheng CHENG , Huaikang ZHANG , Deqing ZHANG , Shuhua LI . Preparation and luminescent performance of Sr_1-xZrSi₂O₇∶xDy³⁺ phosphor with high thermal stability. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 357-364. doi: 10.11862/CJIC.20240096
2. [2]
  Xuyang Wang , Jiapei Zhang , Lirui Zhao , Xiaowen Xu , Guizheng Zou , Bin Zhang . Theoretical Study on the Structure and Stability of Copper-Ammonia Coordination Ions. University Chemistry, 2024, 39(3): 384-389. doi: 10.3866/PKU.DXHX202309065
3. [3]
  Shitao Fu , Jianming Zhang , Cancan Cao , Zhihui Wang , Chaoran Qin , Jian Zhang , Hui Xiong . Study on the Stability of Purple Cabbage Pigment. University Chemistry, 2024, 39(4): 367-372. doi: 10.3866/PKU.DXHX202401059
4. [4]
  Xiaoning TANG , Junnan LIU , Xingfu YANG , Jie LEI , Qiuyang LUO , Shu XIA , An XUE . Effect of sodium alginate-sodium carboxymethylcellulose gel layer on the stability of Zn anodes. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1452-1460. doi: 10.11862/CJIC.20240191
5. [5]
  Jiaxi Xu , Yuan Ma . Influence of Hyperconjugation on the Stability and Stable Conformation of Ethane, Hydrazine, and Hydrogen Peroxide. University Chemistry, 2024, 39(11): 374-377. doi: 10.3866/PKU.DXHX202402049
6. [6]
  Jing SU , Bingrong LI , Yiyan BAI , Wenjuan JI , Haiying YANG , Zhefeng Fan . Highly sensitive electrochemical dopamine sensor based on a highly stable In-based metal-organic framework with amino-enriched pores. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1337-1346. doi: 10.11862/CJIC.20230414
7. [7]
  Renqing Lü , Shutao Wang , Fang Wang , Guoping Shen . Computational Chemistry Aided Organic Chemistry Teaching: A Case of Comparison of Basicity and Stability of Diazine Isomers. University Chemistry, 2025, 40(3): 76-82. doi: 10.12461/PKU.DXHX202404119
8. [8]
  Baitong Wei , Jinxin Guo , Xigong Liu , Rongxiu Zhu , Lei Liu . Theoretical Study on the Structure, Stability of Hydrocarbon Free Radicals and Selectivity of Alkane Chlorination Reaction. University Chemistry, 2025, 40(3): 402-407. doi: 10.12461/PKU.DXHX202406003
9. [9]
  Ming ZHENG , Yixiao ZHANG , Jian YANG , Pengfei GUAN , Xiudong LI . Energy storage and photoluminescence properties of Sm³⁺-doped Ba_0.85Ca_0.15Ti_0.90Zr_0.10O₃ lead-free multifunctional ferroelectric ceramics. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 686-692. doi: 10.11862/CJIC.20230388
10. [10]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
11. [11]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369
12. [12]
  Zhiyuan TONG , Ziyuan LI , Ke ZHANG . Three-dimensional porous collector based on Cu-Li_6.4La₃Zr_1.4Ta_0.6O₁₂ composite layer for the construction of stable lithium metal anode. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 499-508. doi: 10.11862/CJIC.20240238
13. [13]
  Yuan GAO , Yiming LIU , Chunhui WANG , Zhe HAN , Chaoyue FAN , Jie QIU . A hexanuclear cerium oxo cluster stabilized by furoate: Synthesis, structure, and remarkable ability to scavenge hydroxyl radicals. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 491-498. doi: 10.11862/CJIC.20240271
14. [14]
  Juan Yuan , Bin Zhang , Jinping Wu , Mengfan Wang . Design of a Comprehensive Experiment on Preparation and Characterization of Cu₂(Salen)₂ Nanomaterials with Two Distinct Morphologies. University Chemistry, 2024, 39(10): 420-425. doi: 10.3866/PKU.DXHX202402014
15. [15]
  Yang Xia , Kangyan Zhang , Heng Yang , Lijuan Shi , Qun Yi . 构建双通道路径增强iCOF/Bi₂O₃ S型异质结在纯水体系中光催化合成H₂O₂性能. Acta Physico-Chimica Sinica, 2024, 40(11): 2407012-. doi: 10.3866/PKU.WHXB202407012
16. [16]
  Xinpeng LIU , Liuyang ZHAO , Hongyi LI , Yatu CHEN , Aimin WU , Aikui LI , Hao HUANG . Ga₂O₃ coated modification and electrochemical performance of Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ cathode material. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1105-1113. doi: 10.11862/CJIC.20230488
17. [17]
  Xuanzhu Huo , Yixi Liu , Qiyu Wu , Zhiqiang Dong , Chanzi Ruan , Yanping Ren . Integrated Experiment of “Electrolytic Preparation of Cu₂O and Gasometric Determination of Avogadro’s Constant: Implementation, Results, and Discussion: A Micro-Experiment Recommended for Freshmen in Higher Education at Various Levels Across the Nation. University Chemistry, 2024, 39(3): 302-307. doi: 10.3866/PKU.DXHX202308095
18. [18]
  Yan ZHAO , Jiaxu WANG , Zhonghu LI , Changli LIU , Xingsheng ZHAO , Hengwei ZHOU , Xiaokang JIANG . Gd³⁺-doped Sc₂W3O₁₂: Eu³⁺ red phosphor: Preparation and luminescence performance. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 461-468. doi: 10.11862/CJIC.20240316
19. [19]
  Wei HE , Jing XI , Tianpei HE , Na CHEN , Quan YUAN . Application of solar-driven inorganic semiconductor-microbe hybrids in carbon dioxide fixation and biomanufacturing. Chinese Journal of Inorganic Chemistry, 2025, 41(1): 35-44. doi: 10.11862/CJIC.20240364
20. [20]
  Juan Guo , Mingyuan Fang , Qingsong Liu , Xiao Ren , Yongqiang Qiao , Mingju Chao , Erjun Liang , Qilong Gao . Zero thermal expansion in Cs₂W₃O₁₀. Chinese Chemical Letters, 2024, 35(7): 108957-. doi: 10.1016/j.cclet.2023.108957

Get Citation

PDF

XML

Metrics

PDF Downloads(1795)
Abstract views(1964)
HTML views(14)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

THE THERMOSTABILITY OF OXYGEN ATOMS AT DIFFERENT SITES IN THE CRYSTAL LATTICE OF HIGH-TC SUPERCONDUCTOR Ba2YCu3O6.92

Metrics

通讯作者: 陈斌, bchen63@163.com

THE THERMOSTABILITY OF OXYGEN ATOMS AT DIFFERENT SITES IN THE CRYSTAL LATTICE OF HIGH-T_C SUPERCONDUCTOR Ba₂YCu₃O_6.92