XUE Dan, LIU Xiang, LV Wei. Preparation and Properties of Water-soluble Crosslink-graft Starch for Drilling Fluid[J]. Chinese Journal of Applied Chemistry,
;2011, 28(5): 510-515.
doi:
10.3724/SP.J.1095.2011.00383
-
The starch(St) graft sodium acrylate was synthesized by solvent method.It has a high viscosity and a strong shear-resistance.The copolymerization was carried out using N,N'-methylene bisacrylamid as the crosslinker and ammonium persulfate as the initiator.Effects such as the amount of monomer,initiator and crosslinking agent,neutralization degree of the acrylic acid(AA),reaction time and temperature on the apparent viscosity were discussed.Through orthogonal experiment,the optimum graft copolymerization condition was obtained as the follows:the mass ratio of starch to acrylic acid is 1:1.5,the mass fraction of alcohol is 80%,initiator is 1% and crosslinker is 0.6% on the basis of the mass of starch,the reaction time is 2.5 h,the reaction temperature is 55℃,and the neutralization degree of the acrylic acid is 70%.The experiments showed that the graft starch paste has an excellent thixotropy.When 14.0 g/L slurry was dissolved in 4% salt water and base fluid,the apparent viscosity of the slurry was 26 mPa·s and the filtration loss was 7.2 mL.When the dosage of slurry was added up to 23.5 g/L in saturated salt water and base fluid,the apparent viscosity of the slurry was 54.5 mPa·s and the filtration loss was 3.1 mL.Additionally,the apparent viscosity and the filtration loss of the slurry were essentially remained the same after the slurry was treated for 16 h at 80℃.The experimental results show that the graft starch copolymer has good capacities of increasing viscosity and depressing the filtration loss,and it has excellent properties of aging-resistance and salt-resistance.
-
Keywords:
- graft starch,
- apparent viscosity,
- thixotropy,
- drilling fluid
-
-
-
-
[1]
Lin Ding , Jinpeng Zhang , Junfeng Li , Daying Liu . Color Catcher: A Marvelous Encounter of Starch and Iodine. University Chemistry, 2024, 39(6): 334-341. doi: 10.3866/PKU.DXHX202311064
-
[2]
Yutong Dong , Huiling Xu , Yucheng Zhao , Zexin Zhang , Ying Wang . The Hidden World of Surface Tension and Droplets. University Chemistry, 2024, 39(6): 357-365. doi: 10.3866/PKU.DXHX202312022
-
[3]
Yujia Luo , Yunpeng Qi , Huiping Xing , Yuhu Li . The Use of Viscosity Method for Predicting the Life Expectancy of Xuan Paper-based Heritage Objects. University Chemistry, 2024, 39(8): 290-294. doi: 10.3866/PKU.DXHX202401037
-
[4]
Chunai Dai , Yongsheng Han , Luting Yan , Zhen Li , Yingze Cao . Ideological and Political Design of Solid-liquid Contact Angle Measurement Experiment. University Chemistry, 2024, 39(2): 28-33. doi: 10.3866/PKU.DXHX202306065
-
[5]
Feiya Cao , Qixin Wang , Pu Li , Zhirong Xing , Ziyu Song , Heng Zhang , Zhibin Zhou , Wenfang Feng . Magnesium-Ion Conducting Electrolyte Based on Grignard Reaction: Synthesis and Properties. University Chemistry, 2024, 39(3): 359-368. doi: 10.3866/PKU.DXHX202308094
-
[6]
Chongjing Liu , Yujian Xia , Pengjun Zhang , Shiqiang Wei , Dengfeng Cao , Beibei Sheng , Yongheng Chu , Shuangming Chen , Li Song , Xiaosong Liu . Understanding Solid-Gas and Solid-Liquid Interfaces through Near Ambient Pressure X-Ray Photoelectron Spectroscopy. Acta Physico-Chimica Sinica, 2025, 41(2): 100013-. doi: 10.3866/PKU.WHXB202309036
-
[7]
Yanhui Zhong , Ran Wang , Zian Lin . Analysis of Halogenated Quinone Compounds in Environmental Water by Dispersive Solid-Phase Extraction with Liquid Chromatography-Triple Quadrupole Mass Spectrometry. University Chemistry, 2024, 39(11): 296-303. doi: 10.12461/PKU.DXHX202402017
-
[8]
Mingyang Men , Jinghua Wu , Gaozhan Liu , Jing Zhang , Nini Zhang , Xiayin Yao . 液相法制备硫化物固体电解质及其在全固态锂电池中的应用. Acta Physico-Chimica Sinica, 2025, 41(1): 2309019-. doi: 10.3866/PKU.WHXB202309019
-
[9]
Aoyu Huang , Jun Xu , Yu Huang , Gui Chu , Mao Wang , Lili Wang , Yongqi Sun , Zhen Jiang , Xiaobo Zhu . Tailoring Electrode-Electrolyte Interfaces via a Simple Slurry Additive for Stable High-Voltage Lithium-Ion Batteries. Acta Physico-Chimica Sinica, 2025, 41(4): 100037-. doi: 10.3866/PKU.WHXB202408007
-
[1]
Metrics
- PDF Downloads(0)
- Abstract views(216)
- HTML views(9)
DownLoad: