Citation: Tian-Ru HAN, Jing-Jing WU, Zi-Xin QU, Xin TANG. Pyrochlore Structure Y_2-xMg_xRu₂O_7-δ (x=0.05, 0.1, 0.15): Preparation and OER Catalytic Performance[J]. Chinese Journal of Inorganic Chemistry, ;2021, 37(2): 285-294. doi: 10.11862/CJIC.2021.043 shu

Pyrochlore Structure Y_2-xMg_xRu₂O_7-δ (x=0.05, 0.1, 0.15): Preparation and OER Catalytic Performance

Tian-Ru HAN ^{1, 2} ,
Jing-Jing WU ^{1, 2} ,
Zi-Xin QU ^{1, 2} ,
Xin TANG ^{1, 2,,}

1.
Key Lab of New Processing Technology for Nonferrous Metal & Materials, Ministry of Education, Guilin University of Technology, Guilin, Guangxi 541004, China
2.
College of Material Science and Engineering, Guilin University of Technology, Guilin, Guangxi 541004, China

Corresponding author: Xin TANG, xtang@glut.edu.cn
Received Date: 30 August 2020
Revised Date: 9 December 2020

Figures(9)

Herein, pyrochlore structure Y_2-xMg_xRu₂O_7-δ (YMRO-x, x=0.05, 0.1, 0.15) catalysts were prepared by solgel method. The X-ray photoelectron spectroscopy was employed to analyze the surface chemical composition and valence state of as-synthesized YMRO. The results showed that oxygen defects were increased when Mg²⁺ partially substituted Y³⁺ of A site in pyrochlore (A₂B₂O_7-δ). Especially, YMRO-0.1 catalyst possessed the most extraordinary performance in oxygen evolution reaction (OER). Reaching current density of 10 mA·cm^-2 only required 265 mV overpotential, outperformed the RuO₂ (358 mV), Y₂Ru₂O_7-δ (294 mV), YMRO-0.05 (282 mV) and YMRO-0.15 (281 mV). The Tafel slope of YMRO-0.1 was 45 mV·dec^-1, much smaller than that of RuO₂ (88 mV·dec^-1), YRO (64 mV·dec^-1), YMRO-0.05 (51 mV·dec^-1) and YMRO-0.15 (52 mV·dec^-1), having the fastest kinetic process. Turning to stability test of YMRO-0.1, the potential moved little in 12 h, compared with Y₂Ru₂O_7-δ which shifted up 30 mV under acidic environment. Moreover, first principle calculation indicated that the substitution atom Mg_Y formed a complex with oxygen vacancies, favored the formation of oxygen vacancies, narrowed the band gap, and lowered the charge-transfer-energy. In addition, the excellent OER reactivity can be partly attributed to the Ru⁵⁺ ions. Due to the introduction of Mg, the Ru⁴⁺ ions at central active site was oxidized to Ru⁵⁺ ions, donating electron to surface and accelerating the process of oxygen evolution reaction. As a result, the active sites also minimized Gibbs free energy of oxygen radical desorption, which promoted the OER. Based on the results, YMRO should be a promising OER catalytic material which can stably work in acid environment.
- catalysis,
- electrochemistry,
- ab initio calculations,
- sol-gel processes
1. [1]
  Montoya J H, Seitz L C, Chakthranont P, Vojvodic A, Jaramillo T F, Norskov J K. Nat. Mater., 2016, 16:70-81
2. [2]
  Stamenkovic V R, Strmcnik D, Lopes P P, Markovic N M. Nat. Mater., 2016, 16:57-69
3. [3]
  Khajehsaeidi Z, Sangpour P, Ghaffarinejad A. Int. J. Hydrogen Energy, 2019, 44:19816-19826 doi: 10.1016/j.ijhydene.2019.05.161
4. [4]
  Zhao Z J, Zhao J, Wang H B, Li X L, Yang L Q, Zhao Z W, Liu X Y, Liu Y Z, Liu P, Cai Z Y. Int. J. Hydrogen Energy, 2020, 45:14199-14207 doi: 10.1016/j.ijhydene.2019.11.007
5. [5]
  Kim J S, Kim B, Kim H, Kang K. Adv. Energy Mater., 2018, 8:1702774 doi: 10.1002/aenm.201702774
6. [6]
  Xu H M, Ci S Q, Ding Y C, Wang G X, Wen Z H. J. Mater. Chem. A, 2019, 7:8006-8029 doi: 10.1039/C9TA00833K
7. [7]
  Roy C, Rao R R, Stoerzinger K A, Hwang J, Rossmeisl J, Chorkendorff I, Shao-Horn Y, Stephens I E L. ACS. Energy Lett., 2018, 3:2045-2051 doi: 10.1021/acsenergylett.8b01178
8. [8]
  Cherevko S, Zeradjanin A R, Topalov A A, Kulyk N, Katsounaros I, Mayrhofer K J J. ChemCatChem, 2014, 6:2219-2223 doi: 10.1002/cctc.201402194
9. [9]
  Zhu Y L, Zhou W, Yu J, Chen Y B, Liu M L, Shao Z. Chem. Mater., 2016, 28:1691-1697 doi: 10.1021/acs.chemmater.5b04457
10. [10]
  Suntivich J, May K J, Gasteiger H A, Goodenough J B, Shao-Horn Y. Science, 2011, 334:1383-1385 doi: 10.1126/science.1212858
11. [11]
  Zhu J K, Gao Q M. Microporous Mesoporous Mater., 2009, 124:144-152 doi: 10.1016/j.micromeso.2009.05.003
12. [12]
  Dresp S, Thanh T N, Klingenhof M, Brückner S, Hauke P, Strasser P. Energy Environ. Sci., 2020, 13:1725-1729 doi: 10.1039/D0EE01125H
13. [13]
  Zhong H H, Liu T Y, Zhang S W, Li D Q, Tang P G, Alonso-Vante N, Feng Y J. J. Energy Chem., 2019, 33:130-137 doi: 10.1016/j.jechem.2018.09.005
14. [14]
  Sardar K, Petrucco E, Hiley C I, Sharman J D, Wells P P, Russell A E, Kashtiban R J, Sloan J, Walton R I. Angew. Chem. Int. Ed., 2014, 53:10960-10964 doi: 10.1002/anie.201406668
15. [15]
  Kötz R, Stucki S. Electrochim. Acta, 1986, 31:1311-1316 doi: 10.1016/0013-4686(86)80153-0
16. [16]
  Hodnik N, Jovanovič P, Pavlišič A, Jozinović B, Zorko M, Bele M, Šelih V S, Šala M, Hočevar S, Gaberšček M. J. Phys. Chem. C, 2015, 119:10140-10147 doi: 10.1021/acs.jpcc.5b01832
17. [17]
  Audichon T, Napporn T W, Canaff C, Morais C, Comminges C, Kokoh K B. J. Phys. Chem. C, 2016, 120:2562-2573 doi: 10.1021/acs.jpcc.5b11868
18. [18]
  Talanov M V, Talanov V M. CrystEngComm, 2020, 22:1176-1187 doi: 10.1039/C9CE01635J
19. [19]
  Fukina D G, Suleimanov E V, Fukin G K, Boryakov A V, Zubkov S Y, Istomin L A. J. Solid State Chem., 2020, 286:121267 doi: 10.1016/j.jssc.2020.121267
20. [20]
  Kim J, Shih P C, Tsao K C, Pan Y T, Yin X, Sun C J, Yang H. J. Am. Chem. Soc., 2017, 139:12076-12083 doi: 10.1021/jacs.7b06808
21. [21]
  Park J, Park M, Nam G, Kim M G, Cho J. Nano Lett., 2017, 17:3974-3981 doi: 10.1021/acs.nanolett.7b01812
22. [22]
  Kuznetsov D A, Naeem M A, Kumar P V, Abdala P M, Fedorov A, Muller C R. J. Am. Chem. Soc., 2020, 142:7883-7888 doi: 10.1021/jacs.0c01135
23. [23]
  Cheng F Y, Shen J, Peng B, Pan Y D, Tao Z L, Chen J. Nat. Chem., 2011, 3:79-84 doi: 10.1038/nchem.931
24. [24]
  Li H, Shang J, Zhu H J, Yang Z P, Ai Z H, Zhang L Z. ACS Catal., 2016, 6:8276-8285 doi: 10.1021/acscatal.6b02613
25. [25]
  Kim J, Yin X, Tsao K C, Fang S H, Yang H. J. Am. Chem. Soc., 2014, 136:14646-14649 doi: 10.1021/ja506254g
26. [26]
  Sheetz R M, Ponomareva I, Richter E, Andriotis A N, Menon M. Phys. Rev. B, 2009, 80:195314 doi: 10.1103/PhysRevB.80.195314
27. [27]
  Zhang S T, Li C M, Yan H, Wei M, Evans D G, Duan X. J. Phys. Chem. C, 2014, 118:3514-3522
28. [28]
  Lan G Q, Song J, Yang Z. J. Alloys Compd., 2018, 749:909-925 doi: 10.1016/j.jallcom.2018.03.336
29. [29]
  Banger K K, Yamashita Y, Mori K, Peterson R L, Leedham T, Rickard J, Sirringhaus H. Nat. Mater., 2011, 10:45-50 doi: 10.1038/nmat2914
30. [30]
  Fan J C C, Goodenough B J. J. Appl. Phys., 1977, 48:3524-3531 doi: 10.1063/1.324149
31. [31]
  Lu X F, Wu D J, Li R Z, Li Q, Ye S H, Tong Y X, Li G R. J. Mater. Chem. A, 2014, 2:4706-4713 doi: 10.1039/C3TA14930G
32. [32]
  Chen S, Huang H, Jiang P, Yang K, Diao J F, Gong S P, Liu S, Huang M X, Wang H, Chen Q W. ACS Catal., 2019, 10:1152-1160
33. [33]
  Patra A S, Gogoi G, Sahu R K, Qureshi M. Phys. Chem. Chem. Phys., 2017, 19:12167-12174 doi: 10.1039/C7CP01444A
34. [34]
  Berti G, Sanna S, Castellano C, DuiJn J V, Ruiz-Bustos R, Bordonali L, Bussetti G, Calloni A, Demartin F, Duò L, Brambilla A. J. Phys. Chem. C, 2016, 120:11763-11768 doi: 10.1021/acs.jpcc.5b12411
35. [35]
  Feng Q, Zhao Z L, Yuan X Z, Li H, Wang H J. Appl. Catal. B, 2020, 260:118176 doi: 10.1016/j.apcatb.2019.118176
36. [36]
  Kim M, Ju H, Kim J. Chem. Eng. J., 2019, 358:11-19 doi: 10.1016/j.cej.2018.09.204
37. [37]
  Huang Y, Li K, Li S, Lin Y, Liu H, Tong Y. ChemistrySelect, 2018, 3:7423-7428 doi: 10.1002/slct.201800908
38. [38]
  Park J, Risch M, Nam G, Park M, Shin T J, Park S, Kim M G, Shao-Horn Y, Cho J. Energy Environ. Sci., 2017, 10:129-136 doi: 10.1039/C6EE03046G
39. [39]
  Kim M, Ju H, Kim J. J. Mater. Chem. A, 2018, 6:8523-8530 doi: 10.1039/C8TA01374H
40. [40]
  Kim M, Ju H, Kim J. Dalton Trans., 2018, 47:15217-15225 doi: 10.1039/C8DT03217C
41. [41]
  Yuan X, Wang H, Colinsun J, Zhang J. Int. J. Hydrogen Energy, 2007, 32:4365-4380 doi: 10.1016/j.ijhydene.2007.05.036
42. [42]
  Ehora G, Daviero-Minaud S, Steil M C, Gengembre L, Mentré O. Chem. Mater., 2008, 20:7425-7433 doi: 10.1021/cm801942c
43. [43]
  Li X N, Zhang J, Feng Q, Pu C Y, Zhang L Z, Hu M M, Zhou X Y, Zhong X W, Yi W D, Tang J, Li Z W, Zhao X Z, Li H, Xu B M. J. Mater. Chem. A, 2018, 6:17288-17296 doi: 10.1039/C8TA05599H
44. [44]
  Palma-Goyes R E, Vazquez-Arenas J, Romero-Ibarra I C, Ostos C. ChemistrySelect, 2018, 3:12937-12945 doi: 10.1002/slct.201802695
45. [45]
  Subramanian M A, Aravamudan G, Rao G V S. Prog. Solid state. Chem., 1983, 15:55-143 doi: 10.1016/0079-6786(83)90001-8
46. [46]
  Hong W T, Stoerzinger K A, Lee Y L, Giordano L, Grimaud A, Johnson A M, Hwang J, Crumlin E J, Yang W L, Shao-Horn Y. Energy Environ. Sci., 2017, 10:2190-2200 doi: 10.1039/C7EE02052J
1. [1]
  Hongyi LI , Aimin WU , Liuyang ZHAO , Xinpeng LIU , Fengqin CHEN , Aikui LI , Hao HUANG . Effect of Y(PO₃)₃ double-coating modification on the electrochemical properties of Li[Ni_0.8Co_0.15Al_0.05]O₂. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1320-1328. doi: 10.11862/CJIC.20230480
2. [2]
  Jin CHANG . Supercapacitor performance and first-principles calculation study of Co-doping Ni(OH)₂. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1697-1707. doi: 10.11862/CJIC.20240108
3. [3]
  Xin XIONG , Qian CHEN , Quan XIE . First principles study of the photoelectric properties and magnetism of La and Yb doped AlN. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1519-1527. doi: 10.11862/CJIC.20240064
4. [4]
  Cuiwu MO , Gangmin ZHANG , Chao WU , Zhipeng HUANG , Chi ZHANG . A(NH₂SO₃) (A=Li, Na): Two ultraviolet transparent sulfamates exhibiting second harmonic generation response. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1387-1396. doi: 10.11862/CJIC.20240045
5. [5]
  Cheng PENG , Jianwei WEI , Yating CHEN , Nan HU , Hui ZENG . First principles investigation about interference effects of electronic and optical properties of inorganic and lead-free perovskite Cs₃Bi₂X₉ (X=Cl, Br, I). Chinese Journal of Inorganic Chemistry, 2024, 40(3): 555-560. doi: 10.11862/CJIC.20230282
6. [6]
  Jiahong ZHENG , Jiajun SHEN , Xin BAI . Preparation and electrochemical properties of nickel foam loaded NiMoO₄/NiMoS₄ composites. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 581-590. doi: 10.11862/CJIC.20230253
7. [7]
  Tiantian MA , Sumei LI , Chengyu ZHANG , Lu XU , Yiyan BAI , Yunlong FU , Wenjuan JI , Haiying YANG . Methyl-functionalized Cd-based metal-organic framework for highly sensitive electrochemical sensing of dopamine. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 725-735. doi: 10.11862/CJIC.20230351
8. [8]
  Zhihuan XU , Qing KANG , Yuzhen LONG , Qian YUAN , Cidong LIU , Xin LI , Genghuai TANG , Yuqing LIAO . Effect of graphene oxide concentration on the electrochemical properties of reduced graphene oxide/ZnS. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1329-1336. doi: 10.11862/CJIC.20230447
9. [9]
  Qin ZHU , Jiao MA , Zhihui QIAN , Yuxu LUO , Yujiao GUO , Mingwu XIANG , Xiaofang LIU , Ping NING , Junming GUO . Morphological evolution and electrochemical properties of cathode material LiAl_0.08Mn_1.92O₄ single crystal particles. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1549-1562. doi: 10.11862/CJIC.20240022
10. [10]
  Qingtang ZHANG , Xiaoyu WU , Zheng WANG , Xiaomei WANG . Performance of nano Li₂FeSiO₄/C cathode material co-doped by potassium and chlorine ions. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1689-1696. doi: 10.11862/CJIC.20240115
11. [11]
  Lu XU , Chengyu ZHANG , Wenjuan JI , Haiying YANG , Yunlong FU . Zinc metal-organic framework with high-density free carboxyl oxygen functionalized pore walls for targeted electrochemical sensing of paracetamol. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 907-918. doi: 10.11862/CJIC.20230431
12. [12]
  Yuanchao LI , Weifeng HUANG , Pengchao LIANG , Zifang ZHAO , Baoyan XING , Dongliang YAN , Li YANG , Songlin WANG . Effect of heterogeneous dual carbon sources on electrochemical properties of LiMn_0.8Fe_0.2PO₄/C composites. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 751-760. doi: 10.11862/CJIC.20230252
13. [13]
  Xinpeng LIU , Liuyang ZHAO , Hongyi LI , Yatu CHEN , Aimin WU , Aikui LI , Hao HUANG . Ga₂O₃ coated modification and electrochemical performance of Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ cathode material. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1105-1113. doi: 10.11862/CJIC.20230488
14. [14]
  Jing SU , Bingrong LI , Yiyan BAI , Wenjuan JI , Haiying YANG , Zhefeng Fan . Highly sensitive electrochemical dopamine sensor based on a highly stable In-based metal-organic framework with amino-enriched pores. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1337-1346. doi: 10.11862/CJIC.20230414
15. [15]
  Kexin Dong , Chuqi Shen , Ruyu Yan , Yanping Liu , Chunqiang Zhuang , Shijie Li . Integration of Plasmonic Effect and S-Scheme Heterojunction into Ag/Ag₃PO₄/C₃N₅ Photocatalyst for Boosted Photocatalytic Levofloxacin Degradation. Acta Physico-Chimica Sinica, 2024, 40(10): 2310013-. doi: 10.3866/PKU.WHXB202310013
16. [16]
  Wenlong LI , Xinyu JIA , Jie LING , Mengdan MA , Anning ZHOU . Photothermal catalytic CO₂ hydrogenation over a Mg-doped In₂O_3-x catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 919-929. doi: 10.11862/CJIC.20230421
17. [17]
  Kun WANG , Wenrui LIU , Peng JIANG , Yuhang SONG , Lihua CHEN , Zhao DENG . Hierarchical hollow structured BiOBr-Pt catalysts for photocatalytic CO₂ reduction. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1270-1278. doi: 10.11862/CJIC.20240037
18. [18]
  Zhanggui DUAN , Yi PEI , Shanshan ZHENG , Zhaoyang WANG , Yongguang WANG , Junjie WANG , Yang HU , Chunxin LÜ , Wei ZHONG . Preparation of UiO-66-NH₂ supported copper catalyst and its catalytic activity on alcohol oxidation. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 496-506. doi: 10.11862/CJIC.20230317
19. [19]
  Juan WANG , Zhongqiu WANG , Qin SHANG , Guohong WANG , Jinmao LI . NiS and Pt as dual co-catalysts for the enhanced photocatalytic H₂ production activity of BaTiO₃ nanofibers. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1719-1730. doi: 10.11862/CJIC.20240102
20. [20]
  Ruolin CHENG , Haoran WANG , Jing REN , Yingying MA , Huagen LIANG . Efficient photocatalytic CO₂ cycloaddition over W₁₈O₄₉/NH₂-UiO-66 composite catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 523-532. doi: 10.11862/CJIC.20230349

Get Citation

PDF

XML

Metrics

PDF Downloads(23)
Abstract views(1537)
HTML views(322)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Pyrochlore Structure Y2-xMgxRu2O7-δ (x=0.05, 0.1, 0.15): Preparation and OER Catalytic Performance

Metrics

通讯作者: 陈斌, bchen63@163.com

Pyrochlore Structure Y_2-xMg_xRu₂O_7-δ (x=0.05, 0.1, 0.15): Preparation and OER Catalytic Performance