Citation: WANG Hao, YANG Xi-Yun, YIN Zhou-Lan, CAO Gai-Fang, XU Hui. Synthesis and Adsorption Properties of ZrO₂-Coated Lithium Ion-Sieve from Salt Lake Brine[J]. Chinese Journal of Inorganic Chemistry, ;2017, 33(10): 1775-1781. doi: 10.11862/CJIC.2017.217 shu

Synthesis and Adsorption Properties of ZrO₂-Coated Lithium Ion-Sieve from Salt Lake Brine

WANG Hao ¹ ,
YANG Xi-Yun ^1,2,, ,
YIN Zhou-Lan ² ,
CAO Gai-Fang ¹ ,
XU Hui ¹

1.
School of Metallurgy and Environment, Central South University, Changsha 410083, China
2.
College of Chemistry and Chemical Engineering, Central South Universiyt, Changsha 410083, China

Corresponding author: YANG Xi-Yun, yxy7412@csu.edu.cn
Received Date: 8 May 2017
Revised Date: 22 August 2017

Figures(9)

ZrO₂-coated H_1.6Mn_1.6O₄ was synthesized from Li_1.6Mn_1.6O₄ precursor prepared by a hydrothermal method. The liquid precipitation process followed by acid washing was utilized to coat ZrO₂ on the precursor. The structure, morphology and composition of the ZrO₂-coated precursor were investigated by SEM, XRD, EDS and HRTEM analysis. The influences of coating content and roasting temperature on Mn dissolution loss ratio and Li adsorption capacity were discussed. The results indicate that a layer of ZrO₂ with 15 nm in thickness is coated on the precursor when ZrO₂ content is 3% and roasting temperature is 450℃. The Mn dissolution loss ratio decreases from 3.14% to 2.65% and Li adsorption capacity of the resulting ion sieve in the salt lake brine maintains 29.4 mg·g^-1. After 10 cycles of adsorption and desorption, the corresponding Mn dissolution loss ratio and Li adsorption capacity is 0.34% and 24.4 mg·g^-1, respectively. The adsorption capacity is higher than the bare lithium ion-sieve (22.9 mg·g^-1). The results suggest that the structure and cycle stability of H_1.6Mn_1.6O₄ are improved by a ZrO₂ coating layer.
- lithium ion-sieve,
- surface coating,
- Mn dissolution loss,
- Li adsorption capacity
1. [1]
  MA Pei-Hua. Adv. Earth Sci., 2000, 14(4):365-375
2. [2]
  Bi Q, Zhang Z, Zhao C, et al. Water Sci. Technol., 2014, 70(10):1690-1694 doi: 10.2166/wst.2014.426
3. [3]
  Xiang W, Liang S, Zhou Z, et al. Hydrometallurgy, 2016, 166:9-15 doi: 10.1016/j.hydromet.2016.08.005
4. [4]
  Zhou Z, Qin W, Liu Y, et al. J. Chem. Eng. Data, 2012, 57(1):82-86 doi: 10.1021/je200803h
5. [5]
  Chitrakar R, Makita Y, Ooi K, et al. Chem. Lett., 2012, 41(12):1647-1649 doi: 10.1246/cl.2012.1647
6. [6]
  Zandevakili S, Ranjbar M, Ehteshamzadeh M. Hydrometallu-rgy, 2014, 149:148-152 doi: 10.1016/j.hydromet.2014.08.004
7. [7]
  Ooi K, Makita Y, Sonoda A, et al. Hydrometallurgy, 2017, 169:31-40 doi: 10.1016/j.hydromet.2016.11.012
8. [8]
  Zhang Q, Li S, Sun S, et al. Chem. Eng. Sci., 2010, 65(1):169-173 doi: 10.1016/j.ces.2009.06.045
9. [9]
  MA Li-Wen, CHEN Bai-Zhen, SHI Xi-Chang, et al. Chinese J. Inorg. Chem., 2011, 27(4):697-703
10. [10]
  Chitrakar R, Makita Y, Ooi K, et al. Bull. Chem. Soc. Jap., 2013, 86(7):850-855 doi: 10.1246/bcsj.20130019
11. [11]
  Chitrakar R, Makita Y, Ooi K, et al. Ind. Eng. Chem. Res., 2014, 53:3682-3688 doi: 10.1021/ie4043642
12. [12]
  Li L, Qu W, Liu F, et al. Appl. Surf. Sci., 2014, 315:59-65 doi: 10.1016/j.apsusc.2014.07.090
13. [13]
  Li C, Zhang H P, Fu L J, et al. Electrochim. Acta, 2006, 51(19):3872-3883 doi: 10.1016/j.electacta.2005.11.015
14. [14]
  Chitrakar R, Kanoh H, Miyai Y, et al. Chem. Mater., 2000, 12(10):3151-3157 doi: 10.1021/cm0000191
15. [15]
  Zandevakili S, Ranjbar M, Ehteshamzadeh M. Hydrometallu-rgy, 2014, 149:148-152 doi: 10.1016/j.hydromet.2014.08.004
16. [16]
  Hu S K, Cheng G H, Cheng M Y, et al. J. Power Sources, 2009, 188(2):564-569 doi: 10.1016/j.jpowsour.2008.11.113
17. [17]
  CHEN Yong-Xi, ZHOU Li-Juan, GUO Li-Ping, et al. J. Wuhan Univ. Technol., 2001, 23(10):1-3 doi: 10.3321/j.issn:1671-4431.2001.10.001
18. [18]
  MA Li-Wen, CHEN Bai-Zhen, SHI Xi-Chang, et al. Chinese J. Inorg. Chem., 2010, 26(3):413-418
19. [19]
  Shi X C, Zhou D F, Zhang Z B, et al. Hydrometallurgy, 2011, 110(1):99-106
20. [20]
  Eichler A. Phys. Rev. B, 2001, 64(17):607-611
21. [21]
  Sun S Y, Xiao J L, Wang J, et al. Ind. Eng. Chem. Res., 2014, 53(40):15517-15521 doi: 10.1021/ie5004625
22. [22]
  Wang D, Li X H, Wang Z X, et al. Electrochim. Acta, 2016, 196:101-109 doi: 10.1016/j.electacta.2016.02.156
1. [1]
  Xinlong WANG , Zhenguo CHENG , Guo WANG , Xiaokuen ZHANG , Yong XIANG , Xinquan WANG . Enhancement of the fragile interface of high voltage LiCoO₂ by surface gradient permeation of trace amounts of Mg/F. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 571-580. doi: 10.11862/CJIC.20230259
2. [2]
  Junke LIU , Kungui ZHENG , Wenjing SUN , Gaoyang BAI , Guodong BAI , Zuwei YIN , Yao ZHOU , Juntao LI . Preparation of modified high-nickel layered cathode with LiAlO₂/cyclopolyacrylonitrile dual-functional coating. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1461-1473. doi: 10.11862/CJIC.20240189
3. [3]
  Siyu Zhang , Kunhong Gu , Bing'an Lu , Junwei Han , Jiang Zhou . Hydrometallurgical Processes on Recycling of Spent Lithium-lon Battery Cathode: Advances and Applications in Sustainable Technologies. Acta Physico-Chimica Sinica, 2024, 40(10): 2309028-. doi: 10.3866/PKU.WHXB202309028
4. [4]
  Qi Li , Pingan Li , Zetong Liu , Jiahui Zhang , Hao Zhang , Weilai Yu , Xianluo Hu . Fabricating Micro/Nanostructured Separators and Electrode Materials by Coaxial Electrospinning for Lithium-Ion Batteries: From Fundamentals to Applications. Acta Physico-Chimica Sinica, 2024, 40(10): 2311030-. doi: 10.3866/PKU.WHXB202311030
5. [5]
  Doudou Qin , Junyang Ding , Chu Liang , Qian Liu , Ligang Feng , Yang Luo , Guangzhi Hu , Jun Luo , Xijun Liu . Addressing Challenges and Enhancing Performance of Manganese-based Cathode Materials in Aqueous Zinc-Ion Batteries. Acta Physico-Chimica Sinica, 2024, 40(10): 2310034-. doi: 10.3866/PKU.WHXB202310034
6. [6]
  Yuhao SUN , Qingzhe DONG , Lei ZHAO , Xiaodan JIANG , Hailing GUO , Xianglong MENG , Yongmei GUO . Synthesis and antibacterial properties of silver-loaded sod-based zeolite. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 761-770. doi: 10.11862/CJIC.20230169
7. [7]
  Xiaosong PU , Hangkai WU , Taohong LI , Huijuan LI , Shouqing LIU , Yuanbo HUANG , Xuemei LI . Adsorption performance and removal mechanism of Cd(Ⅱ) in water by magnesium modified carbon foam. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1537-1548. doi: 10.11862/CJIC.20240030
8. [8]
  Jingke LIU , Jia CHEN , Yingchao HAN . Nano hydroxyapatite stable suspension system: Preparation and cobalt adsorption performance. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1763-1774. doi: 10.11862/CJIC.20240060
9. [9]
  Yufang GAO , Nan HOU , Yaning LIANG , Ning LI , Yanting ZHANG , Zelong LI , Xiaofeng LI . Nano-thin layer MCM-22 zeolite: Synthesis and catalytic properties of trimethylbenzene isomerization reaction. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1079-1087. doi: 10.11862/CJIC.20240036
10. [10]
  Zizheng LU , Wanyi SU , Qin SHI , Honghui PAN , Chuanqi ZHAO , Chengfeng HUANG , Jinguo PENG . Surface state behavior of W doped BiVO₄ photoanode for ciprofloxacin degradation. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 591-600. doi: 10.11862/CJIC.20230225
11. [11]
  Hong LI , Xiaoying DING , Cihang LIU , Jinghan ZHANG , Yanying RAO . Detection of iron and copper ions based on gold nanorod etching colorimetry. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 953-962. doi: 10.11862/CJIC.20230370
12. [12]
  Xinpeng LIU , Liuyang ZHAO , Hongyi LI , Yatu CHEN , Aimin WU , Aikui LI , Hao HUANG . Ga₂O₃ coated modification and electrochemical performance of Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ cathode material. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1105-1113. doi: 10.11862/CJIC.20230488
13. [13]
  Zhaomei LIU , Wenshi ZHONG , Jiaxin LI , Gengshen HU . Preparation of nitrogen-doped porous carbons with ultra-high surface areas for high-performance supercapacitors. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 677-685. doi: 10.11862/CJIC.20230404
14. [14]
  Jie ZHAO , Sen LIU , Qikang YIN , Xiaoqing LU , Zhaojie WANG . Theoretical calculation of selective adsorption and separation of CO₂ by alkali metal modified naphthalene/naphthalenediyne. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 515-522. doi: 10.11862/CJIC.20230385
15. [15]
  Youlin SI , Shuquan SUN , Junsong YANG , Zijun BIE , Yan CHEN , Li LUO . Synthesis and adsorption properties of Zn(Ⅱ) metal-organic framework based on 3, 3', 5, 5'-tetraimidazolyl biphenyl ligands. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1755-1762. doi: 10.11862/CJIC.20240061
16. [16]
  Peiran ZHAO , Yuqian LIU , Cheng HE , Chunying DUAN . A functionalized Eu³⁺ metal-organic framework for selective fluorescent detection of pyrene. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 713-724. doi: 10.11862/CJIC.20230355
17. [17]
  Wendian XIE , Yuehua LONG , Jianyang XIE , Liqun XING , Shixiong SHE , Yan YANG , Zhihao HUANG . Preparation and ion separation performance of oligoether chains enriched covalent organic framework membrane. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1528-1536. doi: 10.11862/CJIC.20240050
18. [18]
  Qingtang ZHANG , Xiaoyu WU , Zheng WANG , Xiaomei WANG . Performance of nano Li₂FeSiO₄/C cathode material co-doped by potassium and chlorine ions. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1689-1696. doi: 10.11862/CJIC.20240115
19. [19]
  Xiaoning TANG , Shu XIA , Jie LEI , Xingfu YANG , Qiuyang LUO , Junnan LIU , An XUE . Fluorine-doped MnO₂ with oxygen vacancy for stabilizing Zn-ion batteries. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1671-1678. doi: 10.11862/CJIC.20240149
20. [20]
  Yingchun ZHANG , Yiwei SHI , Ruijie YANG , Xin WANG , Zhiguo SONG , Min WANG . Dual ligands manganese complexes based on benzene sulfonic acid and 2, 2′-bipyridine: Structure and catalytic properties and mechanism in Mannich reaction. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1501-1510. doi: 10.11862/CJIC.20240078

Get Citation

PDF

XML

Metrics

PDF Downloads(3)
Abstract views(1910)
HTML views(154)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Synthesis and Adsorption Properties of ZrO2-Coated Lithium Ion-Sieve from Salt Lake Brine

Metrics

通讯作者: 陈斌, bchen63@163.com

Synthesis and Adsorption Properties of ZrO₂-Coated Lithium Ion-Sieve from Salt Lake Brine