Citation: TANG Yu-Xin, TAO Jie, ZHANG Yan-Yan, WU Tao, TAO Hai-Jun, BAO Zu-Guo. Preparation and Characterization of TiO₂ Nanotube Arrays via Anodization of Titanium Films Deposited on FTO Conducting Glass at Room Temperature[J]. Acta Physico-Chimica Sinica, ;2008, 24(12): 2191-2197. doi: 10.1016/S1872-1508(08)60082-0 shu

Preparation and Characterization of TiO₂ Nanotube Arrays via Anodization of Titanium Films Deposited on FTO Conducting Glass at Room Temperature

1.
College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, P. R. China

Received Date: 14 July 2008
Available Online: 19 October 2008

Self-organized TiO2 nanotube arrays with micro-scale length were prepared on fluorine-doped tin oxide (FTO) conducting glass in NH4F/glycerol electrolyte by electrochemical anodization of pure titanium films deposited by radio frequency magnetron sputtering (RFMS) at roomtemperature. The samples were characterized by means of field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), and photoelectrochemistry methods. The results showed that Ti films prepared at the condition of Ar pressure 0.5 Pa, power 150 W, and 0.5 h at room temperature possessed the zone T model structure with od homogeneity and high denseness. When the anodization time was prolonged from 1 to 3 h at the voltage of 30 V, the pore diameter of TiO2 nanotubes increased from 50 to 75 nm, and the length increased from750 to 1100 nmand then gradually decreased to 800 nm, while their wall morphology changed from smooth to rough. Also with increasing the anodization voltage, the pore diameter became larger, and the remaining oxide layer reduced, which could be easily removed by ultrasonic-chemical cleaning in 0.05% (w, mass fraction) diluted HF solution. Moreover, the photocurrent response curves and electrochemical impedance spectroscopy (EIS) results indicated that UV-illumination clearly enhanced the effective separation of the electron-hole pairs and the crystallized electrodes from the annealing treatment of as-anodized electrodes at 450 ℃ exhibited a better photoelectrochemical performance.
- Radio frequency magnetron sputtering,
- Roomtemperature,
- FTO conducting glass,
- TiO2 nanotube arrays,
- NH4F/glycerol
1. [1]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
2. [2]
  Xiufang Wang , Donglin Zhao , Kehua Zhang , Xiaojie Song . “Preparation of Carbon Nanotube/SnS₂ Photoanode Materials”: A Comprehensive University Chemistry Experiment. University Chemistry, 2024, 39(4): 157-162. doi: 10.3866/PKU.DXHX202308025
3. [3]
  Maosen Xu , Pengfei Zhu , Qinghong Cai , Meichun Bu , Chenghua Zhang , Hong Wu , Youzhou He , Min Fu , Siqi Li , Xingyan Liu . In-situ fabrication of TiO₂/NH₂−MIL-125(Ti) via MOF-driven strategy to promote efficient interfacial effects for enhancing photocatalytic NO removal activity. Chinese Chemical Letters, 2024, 35(10): 109524-. doi: 10.1016/j.cclet.2024.109524
4. [4]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369
5. [5]
  Shuangxi Li , Huijun Yu , Tianwei Lan , Liyi Shi , Danhong Cheng , Lupeng Han , Dengsong Zhang . NO_x reduction against alkali poisoning over Ce(SO₄)₂-V₂O₅/TiO₂ catalysts by constructing the Ce⁴⁺–SO₄²⁻ pair sites. Chinese Chemical Letters, 2024, 35(5): 108240-. doi: 10.1016/j.cclet.2023.108240
6. [6]
  Fanxin Kong , Hongzhi Wang , Huimei Duan . Inhibition effect of sulfation on Pt/TiO2 catalysts in methane combustion. Chinese Journal of Structural Chemistry, 2024, 43(5): 100287-100287. doi: 10.1016/j.cjsc.2024.100287
7. [7]
  Lihua HUANG , Jian HUA . Denitration performance of HoCeMn/TiO₂ catalysts prepared by co-precipitation and impregnation methods. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 629-645. doi: 10.11862/CJIC.20230315
8. [8]
  Hongye Bai , Lihao Yu , Jinfu Xu , Xuliang Pang , Yajie Bai , Jianguo Cui , Weiqiang Fan . Controllable Decoration of Ni-MOF on TiO2: Understanding the Role of Coordination State on Photoelectrochemical Performance. Chinese Journal of Structural Chemistry, 2023, 42(10): 100096-100096. doi: 10.1016/j.cjsc.2023.100096
9. [9]
  Wenhao Wang , Guangpu Zhang , Qiufeng Wang , Fancang Meng , Hongbin Jia , Wei Jiang , Qingmin Ji . Hybrid nanoarchitectonics of TiO₂/aramid nanofiber membranes with softness and durability for photocatalytic dye degradation. Chinese Chemical Letters, 2024, 35(7): 109193-. doi: 10.1016/j.cclet.2023.109193
10. [10]
  Mengli Xu , Zhenmin Xu , Zhenfeng Bian . Achieving Ullmann coupling reaction via photothermal synergy with ultrafine Pd nanoclusters supported on mesoporous TiO2. Chinese Journal of Structural Chemistry, 2024, 43(7): 100305-100305. doi: 10.1016/j.cjsc.2024.100305
11. [11]
  Yifen He , Chao Qu , Na Ren , Dawei Liang . Enhanced degradation of refractory organics in ORR-EO system with a blue TiO₂ nanotube array modified Ti-based Ni-Sb co-doped SnO₂ anode. Chinese Chemical Letters, 2024, 35(8): 109262-. doi: 10.1016/j.cclet.2023.109262
12. [12]
  Xin Jiang , Han Jiang , Yimin Tang , Huizhu Zhang , Libin Yang , Xiuwen Wang , Bing Zhao . g-C₃N₄/TiO_2-X heterojunction with high-efficiency carrier separation and multiple charge transfer paths for ultrasensitive SERS sensing. Chinese Chemical Letters, 2024, 35(10): 109415-. doi: 10.1016/j.cclet.2023.109415
13. [13]
  Peng ZHOU , Xiao CAI , Qingxiang MA , Xu LIU . Effects of Cu doping on the structure and optical properties of Au₁₁(dppf)₄Cl₂ nanocluster. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1254-1260. doi: 10.11862/CJIC.20240047
14. [14]
  Qingtang ZHANG , Xiaoyu WU , Zheng WANG , Xiaomei WANG . Performance of nano Li₂FeSiO₄/C cathode material co-doped by potassium and chlorine ions. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1689-1696. doi: 10.11862/CJIC.20240115
15. [15]
  Guoqiang Chen , Zixuan Zheng , Wei Zhong , Guohong Wang , Xinhe Wu . 熔融中间体运输导向合成富氨基g-C₃N₄纳米片用于高效光催化产H₂O₂. Acta Physico-Chimica Sinica, 2024, 40(11): 2406021-. doi: 10.3866/PKU.WHXB202406021
16. [16]
  Jiahong ZHENG , Jingyun YANG . Preparation and electrochemical properties of hollow dodecahedral CoNi₂S₄ supported by MnO₂ nanowires. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1881-1891. doi: 10.11862/CJIC.20240170
17. [17]
  Zhao Lu , Hu Lv , Qinzhuang Liu , Zhongliao Wang . Modulating NH₂ Lewis Basicity in CTF-NH₂ through Donor-Acceptor Groups for Optimizing Photocatalytic Water Splitting. Acta Physico-Chimica Sinica, 2024, 40(12): 2405005-. doi: 10.3866/PKU.WHXB202405005
18. [18]
  Tengjiao Wang , Tian Cheng , Rongjun Liu , Zeyi Wang , Yuxuan Qiao , An Wang , Peng Li . Conductive Hydrogel-based Flexible Electronic System: Innovative Experimental Design in Flexible Electronics. University Chemistry, 2024, 39(4): 286-295. doi: 10.3866/PKU.DXHX202309094
19. [19]
  Cuiwu MO , Gangmin ZHANG , Chao WU , Zhipeng HUANG , Chi ZHANG . A(NH₂SO₃) (A=Li, Na): Two ultraviolet transparent sulfamates exhibiting second harmonic generation response. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1387-1396. doi: 10.11862/CJIC.20240045
20. [20]
  Xinlong WANG , Zhenguo CHENG , Guo WANG , Xiaokuen ZHANG , Yong XIANG , Xinquan WANG . Enhancement of the fragile interface of high voltage LiCoO₂ by surface gradient permeation of trace amounts of Mg/F. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 571-580. doi: 10.11862/CJIC.20230259

Get Citation

PDF

XML

Metrics

PDF Downloads(2222)
Abstract views(3949)
HTML views(145)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

Preparation and Characterization of TiO2 Nanotube Arrays via Anodization of Titanium Films Deposited on FTO Conducting Glass at Room Temperature

Metrics

通讯作者: 陈斌, bchen63@163.com

Preparation and Characterization of TiO₂ Nanotube Arrays via Anodization of Titanium Films Deposited on FTO Conducting Glass at Room Temperature