Citation: TIAN Qi-Feng, ZHANG Yao, TAN Zhi-Cheng, SUN Li-Xian, XU Fen, YUAN Hua-Tang. The Corrosion Behaviors of Mg_0.9－xTi_0.1Pd_xNi(x=0.04～0.1) Hydrogen Storage Alloy Electrodes[J]. Acta Physico-Chimica Sinica, ;2006, 22(03): 301-305. doi: 10.1016/S1872-1508(06)60005-3 shu

The Corrosion Behaviors of Mg_0.9－xTi_0.1Pd_xNi(x=0.04～0.1) Hydrogen Storage Alloy Electrodes

1.
Laboratory of Aerospace Catalysis and New Materials, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, P. R. China; Graduate School of the Chinese Academy of Sciences, Beijing 100049, P. R. China; Institute of New Energy Material Chemistry, Nankai University, Tianjin 300071, P. R. China

Received Date: 23 August 2005
Available Online: 10 March 2006

The effects of partial substitution of Pd for Mg on the corrosion behaviors of Mg0.9－xTi0.1PdxNi(x=0.04～0.1)hydrogen storage alloys were studied in this paper. The alloys were prepared by mechanical alloying. The alloy structures became amorphous after ball milling 120 h, which was confirmed by XRD and TEM analyses. The cyclic charge-discharge tests showed that the Pd addition prolonged the cycle life of the alloys effectively. The corrosion performances of the alloys were investigated by open circuit potential measurements, anodic polarization, electrochemical impedance spectroscopy, and XPS experiments. The increase of Pd content shifted the alloy corrosion potentials towards more positive values. The initial corrosion currents of the alloys and its increment rates along with cycle number decreased with the increase of Pd content in the alloys. The measured electrochemical impedance spectra were fitted well with the proposed equivalent circuit model. The analyses suggested that the thickness and the resistance of passive film on the surface of alloys increased with the increase of Pd content in the alloys. The results of XPS experiments demonstrated that the addition of Pd in the alloys suppressed the oxidation and enhanced the anti-corrosion capabilities of the alloys. When the Pd content reached 0.1, the corrosion resistant performances of Mg0.9－xTi0.1PdxNi(x=0.04～0.1) alloys are the best and the discharge capacity retention rate is the highest.
- Hydrogen storage alloys; Element substitution; Corrosion potential; Corrosion current; Passive film
1. [1]
  Yong Zhou , Jia Guo , Yun Xiong , Luying He , Hui Li . Comprehensive Teaching Experiment on Electrochemical Corrosion in Galvanic Cell for Chemical Safety and Environmental Protection Course. University Chemistry, 2024, 39(7): 330-336. doi: 10.3866/PKU.DXHX202310109
2. [2]
  Shuyong Zhang , Shu'e Song . Ideological and Political Case Design of Experiment of Corrosion and Protection Linking with National Major Projects. University Chemistry, 2024, 39(2): 57-60. doi: 10.3866/PKU.DXHX202304078
3. [3]
  Li Jiang , Changzheng Chen , Yang Su , Hao Song , Yanmao Dong , Yan Yuan , Li Li . Electrochemical Synthesis of Polyaniline and Its Anticorrosive Application: Improvement and Innovative Design of the “Chemical Synthesis of Polyaniline” Experiment. University Chemistry, 2024, 39(3): 336-344. doi: 10.3866/PKU.DXHX202309002
4. [4]
  Wenxiu Yang , Jinfeng Zhang , Quanlong Xu , Yun Yang , Lijie Zhang . Bimetallic AuCu Alloy Decorated Covalent Organic Frameworks for Efficient Photocatalytic Hydrogen Production. Acta Physico-Chimica Sinica, 2024, 40(10): 2312014-. doi: 10.3866/PKU.WHXB202312014
5. [5]
  Yingran Liang , Fei Wang , Jiabao Sun , Hongtao Zheng , Zhenli Zhu . Construction and Application of a New Experimental Device for Determination of Alkaline Metal Elements by Plasma Atomic Emission Spectrometry Based on Solution Cathode Glow Discharge: An Alternative Approach for Fundamental Teaching Experiments in Emission Spectroscopy. University Chemistry, 2024, 39(5): 380-387. doi: 10.3866/PKU.DXHX202312024
6. [6]
  Tong Zhou , Jun Li , Zitian Wen , Yitian Chen , Hailing Li , Zhonghong Gao , Wenyun Wang , Fang Liu , Qing Feng , Zhen Li , Jinyi Yang , Min Liu , Wei Qi . Experiment Improvement of “Redox Reaction and Electrode Potential” Based on the New Medical Concept. University Chemistry, 2024, 39(8): 276-281. doi: 10.3866/PKU.DXHX202401005
7. [7]
  Siyao Zhan , Yajiao Wang , Zhihuan Cai , Ayizhada Maimaitiyumier , Tilan Duan , Xiangfeng Wei , Qi Wang , Jiehua Liu , Xianghua Kong . Exploration of the Chemical Elements across Time and Space. University Chemistry, 2024, 39(9): 5-10. doi: 10.12461/PKU.DXHX202403071
8. [8]
  Xiao Liu , Guangzhong Cao , Mingli Gao , Hong Wu , Hongyan Feng , Chenxiao Jiang , Tongwen Xu . Seawater Salinity Gradient Energy’s Job Application in the Field of Membranes. University Chemistry, 2024, 39(9): 279-282. doi: 10.3866/PKU.DXHX202306043
9. [9]
  Shuyu Liu , Xiaomin Sun , Bohan Song , Gaofeng Zeng , Bingbing Du , Chongshen Guo , Cong Wang , Lei Wang . Design and Fabrication of Phospholipid-Vesicle-based Artificial Cells towards Biomedical Applications. University Chemistry, 2024, 39(11): 182-188. doi: 10.12461/PKU.DXHX202404113
10. [10]
  Xiangli Wang , Yuanfu Deng . Teaching Design of Elemental Chemistry from the Perspective of “Curriculum Ideology and Politics”: Taking Arsenic as an Example. University Chemistry, 2024, 39(2): 270-279. doi: 10.3866/PKU.DXHX202308092
11. [11]
  Jiao CHEN , Yi LI , Yi XIE , Dandan DIAO , Qiang XIAO . Vapor-phase transport of MFI nanosheets for the fabrication of ultrathin b-axis oriented zeolite membranes. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 507-514. doi: 10.11862/CJIC.20230403
12. [12]
  Shengjuan Huo , Xiaoyan Zhang , Xiangheng Li , Xiangning Li , Tianfang Chen , Yuting Shen . Unveiling the Marvels of Titanium: Popularizing Multifunctional Colored Titanium Product Films. University Chemistry, 2024, 39(5): 184-192. doi: 10.3866/PKU.DXHX202310127
13. [13]
  Lan Ma , Cailu He , Ziqi Liu , Yaohan Yang , Qingxia Ming , Xue Luo , Tianfeng He , Liyun Zhang . Magical Surface Chemistry: Fabrication and Application of Oil-Water Separation Membranes. University Chemistry, 2024, 39(5): 218-227. doi: 10.3866/PKU.DXHX202311046
14. [14]
  Yonghui Wang , Weilin Chen , Yangguang Li . Knowledge Construction of “Solubility of Inorganic Substances” in Elemental Chemistry Teaching. University Chemistry, 2024, 39(4): 261-267. doi: 10.3866/PKU.DXHX202312102
15. [15]
  Huan Zhang , Linyu Pu , Wei Wang , Yatang Dai , Xu Huang . Curriculum Development and Blended Teaching Practice in the Graduate Course on Elemental Inorganic Chemistry. University Chemistry, 2024, 39(6): 166-173. doi: 10.3866/PKU.DXHX202402010
16. [16]
  Zhengli Hu , Jia Wang , Yi-Lun Ying , Shaochuang Liu , Hui Ma , Wenwei Zhang , Jianrong Zhang , Yi-Tao Long . Exploration of Ideological and Political Elements in the Development History of Nanopore Electrochemistry. University Chemistry, 2024, 39(8): 344-350. doi: 10.3866/PKU.DXHX202401072
17. [17]
  Linhan Tian , Changsheng Lu . Discussion on Sextuple Bonding in Diatomic Motifs of Chromium Family Elements. University Chemistry, 2024, 39(8): 395-402. doi: 10.3866/PKU.DXHX202401056
18. [18]
  Yang Lv , Yingping Jia , Yanhua Li , Hexiang Zhong , Xinping Wang . Integrating the Ideological Elements with the “Chemical Reaction Heat” Teaching. University Chemistry, 2024, 39(11): 44-51. doi: 10.12461/PKU.DXHX202402059
19. [19]
  Xi Xu , Chaokai Zhu , Leiqing Cao , Zhuozhao Wu , Cao Guan . Experiential Education and 3D-Printed Alloys: Innovative Exploration and Student Development. University Chemistry, 2024, 39(2): 347-357. doi: 10.3866/PKU.DXHX202308039
20. [20]
  Yan LIU , Jiaxin GUO , Song YANG , Shixian XU , Yanyan YANG , Zhongliang YU , Xiaogang HAO . Exclusionary recovery of phosphate anions with low concentration from wastewater using a CoNi-layered double hydroxide/graphene electronically controlled separation film. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1775-1783. doi: 10.11862/CJIC.20240043

Get Citation

PDF

XML

Metrics

PDF Downloads(3049)
Abstract views(3628)
HTML views(11)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

The Corrosion Behaviors of Mg0.9－xTi0.1PdxNi(x=0.04～0.1) Hydrogen Storage Alloy Electrodes

Metrics

通讯作者: 陈斌, bchen63@163.com

The Corrosion Behaviors of Mg_0.9－xTi_0.1Pd_xNi(x=0.04～0.1) Hydrogen Storage Alloy Electrodes