Hong Mei YANG, Qiang ZHENG. The Dynamic Viscoelasticity of Polyethylene Based Montmorillonite Intercalated Nanocomposites[J]. Chinese Chemical Letters,
2004, 15(1): 74-76.
Citation: Hong Mei YANG, Qiang ZHENG. The Dynamic Viscoelasticity of Polyethylene Based Montmorillonite Intercalated Nanocomposites[J]. Chinese Chemical Letters, 2004, 15(1): 74-76.
Citation: Hong Mei YANG, Qiang ZHENG. The Dynamic Viscoelasticity of Polyethylene Based Montmorillonite Intercalated Nanocomposites[J]. Chinese Chemical Letters, 2004, 15(1): 74-76.
The Dynamic Viscoelasticity of Polyethylene Based Montmorillonite Intercalated Nanocomposites
摘要:
The viscoelastic behavior of melts for two systems composed of intercalated nanocomposites based on low density polyethylene and 3 wt% loading of cetyltrimethyl-ammonium bromide modified montmorillonite was studied. The results obtained through examining the dynamic storage module G'and dynamic loss module G" values of the composite revealed that the dynamic viscoelastic properties of composite strongly depended on intercalation of polymer, and exhibited dramatically change with altering intercalation conditions. Only when modified montmorillonite content was about 3 wt%, the composite showed a trend of pseudo-solidlike at lower frequencies.
-
关键词:
- Viscoelasticity
- / polyethylene
- / montmorillonite
- / nanocomposites
English
The Dynamic Viscoelasticity of Polyethylene Based Montmorillonite Intercalated Nanocomposites
Abstract:
The viscoelastic behavior of melts for two systems composed of intercalated nanocomposites based on low density polyethylene and 3 wt% loading of cetyltrimethyl-ammonium bromide modified montmorillonite was studied. The results obtained through examining the dynamic storage module G'and dynamic loss module G" values of the composite revealed that the dynamic viscoelastic properties of composite strongly depended on intercalation of polymer, and exhibited dramatically change with altering intercalation conditions. Only when modified montmorillonite content was about 3 wt%, the composite showed a trend of pseudo-solidlike at lower frequencies.
-