Citation: Deng Zong-Wu, Guo Wei-Min, Liu Huan-Ming, Cao Li-Li. Band Bending of Cleaved GaAs(100) Surface[J]. Acta Physico-Chimica Sinica, 1999, 15(06): 528-532. doi: 10.3866/PKU.WHXB19990609
GaAs(100)解理面的能带弯曲
English
Band Bending of Cleaved GaAs(100) Surface
After cleaved in UHV, the dynamic band bending of GaAs(110) surface was investigated using in situ XPS measurement. It was found that the Fermi level of heavy doped n-GaAs and p-GaAs shifted to the midgap 0. 4 eV and 0. 3 eV, respectively. Fermi level difference of 1. 3eV between heavy doped n-GaAs and p-GaAs was revealed. In fact, the theoretical band gap of GaAs is 1. 42 eV, which suggests that our experimental results should be believable. Based on the experimental results, it was concluded that the surface band bending was caused neither by intrinsic surface states in GaAs, the residual gas in UHV, nor the X-ray radiation. The band bending should be caused mainly by the surface defects induced during the cleavage and more probably during lattice relaxation.
-
Key words:
-
GaAs
- / Bnd bending
- / Dynamic process
- / XPS
扫一扫看文章
计量
- PDF下载量: 2790
- 文章访问数: 3469
- HTML全文浏览量: 114
下载: