The Influence of Rare Earth Ions on the Rheological Behavior of Polyamide

Citation: Xin-xin Sang, Jing-nan Zhang, Yu-cai Ke, Xin-yu Cao, Yong-mei Ma, Fosong Wang. The Influence of Rare Earth Ions on the Rheological Behavior of Polyamide[J]. Chinese Journal of Polymer Science, 2015, 33(10): 1453-1461. doi: 10.1007/s10118-015-1699-7 shu

The Influence of Rare Earth Ions on the Rheological Behavior of Polyamide

1.
1. Key Laboratory of Green Printing, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100190, China
2.
2. University of Chinese Academy of Sciences, Beijing 100049, China
3.
4.
Key Laboratory of Green Printing, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100190, China

通讯作者: Yong-mei Ma,

基金项目:
This work was financially supported by the National Science-Technology Support Plan Projects (No. 2014BAC03B05), the National Natural Science Foundation of China (No. 51373184) and MoST973 Research Program (Nos. 2012CB933801 and 2014CB931803).

摘要: The polyamide 66 (PA66)/lanthanum acetate blends with small amounts of salt loadings ( 1 wt% of PA) have been prepared in a twin-screw extruder. The rheology of PA66 and its blends has been investigated by a rotational rheometer. The results suggested that with the salt loading in excess of 0.2 wt% the typical Newtonian viscosity plateau disappeared and both the low-frequency complex viscosities * and storage modulus G' of blends were much higher than those of neat PA66, the storage modulus was higher than the loss modulus at low frequencies (tan 1), i.e., the melt changed from a viscoelastic liquid for unfilled polymer to a viscoelastic solid (G' G''). While the viscosity followed a strong shear thinning with increasing frequency, the * and G' decreased significantly even lower than those of neat PA66 at high frequencies. The combination of dynamic mechanical analysis (DMA) and X-ray photoelectron spectroscopy (XPS) analysis has revealed that coordination effect occurred between lanthanum and carbonyl oxygen atoms in amide groups of the polymer to form pseudocrosslinked network structure, which makes the glass transition temperatures (Tg) and storage modulus (E') of blends enhanced. The network structure formation-destruction and chains entanglement-disentanglement processes at different frequencies are responsible for the above rheological behaviors of blends.

关键词:

English

The Influence of Rare Earth Ions on the Rheological Behavior of Polyamide

1.
1. Key Laboratory of Green Printing, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100190, China
2.
2. University of Chinese Academy of Sciences, Beijing 100049, China
3.
4.
Key Laboratory of Green Printing, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100190, China

Corresponding author: Yong-mei Ma,

Received Date: 23 March 2015
Revised Date: 02 June 2015
Available Online: 05 October 2015
Fund Project:
This work was financially supported by the National Science-Technology Support Plan Projects (No. 2014BAC03B05), the National Natural Science Foundation of China (No. 51373184) and MoST973 Research Program (Nos. 2012CB933801 and 2014CB931803).

Abstract: The polyamide 66 (PA66)/lanthanum acetate blends with small amounts of salt loadings ( 1 wt% of PA) have been prepared in a twin-screw extruder. The rheology of PA66 and its blends has been investigated by a rotational rheometer. The results suggested that with the salt loading in excess of 0.2 wt% the typical Newtonian viscosity plateau disappeared and both the low-frequency complex viscosities * and storage modulus G' of blends were much higher than those of neat PA66, the storage modulus was higher than the loss modulus at low frequencies (tan 1), i.e., the melt changed from a viscoelastic liquid for unfilled polymer to a viscoelastic solid (G' G''). While the viscosity followed a strong shear thinning with increasing frequency, the * and G' decreased significantly even lower than those of neat PA66 at high frequencies. The combination of dynamic mechanical analysis (DMA) and X-ray photoelectron spectroscopy (XPS) analysis has revealed that coordination effect occurred between lanthanum and carbonyl oxygen atoms in amide groups of the polymer to form pseudocrosslinked network structure, which makes the glass transition temperatures (Tg) and storage modulus (E') of blends enhanced. The network structure formation-destruction and chains entanglement-disentanglement processes at different frequencies are responsible for the above rheological behaviors of blends.

Key words:

1. [1]
  Clement, O., Rapko, B.M. and Hay, B.P., Coord. Chem. Rev., 1998, 170(1): 203
2. [2]
  Ciferri, A., Bianchi, E., Marchese, F. and Tealdi, A., Makromol. Chem., 1971, 150(1): 265
3. [3]
  Valenti, B., Bianchi, E., Greppi, G., Tealdi, A. and Ciferri, A., J. Phys. Chem., 1973, 77(3): 389
4. [4]
  Wu, Y., Xu, Y., Wang, D., Zhao, Y., Weng, S., Xu, D. and Wu, J., J. Appl. Polym. Sci., 2004, 91(5): 2869
5. [5]
  Siegmann, A. and Baraam, Z., Int. J. Polym. Mater., 1980, 8(4): 243
6. [6]
  Valenti, B., Bianchi, E., Tealdi, A., Russo, S. and Ciferri, A., Macromolecules, 1976, 9(1): 117
7. [7]
  Siegmann, A. and Baraam, Z., J. Appl. Polym. Sci., 1980, 25(6): 1137
8. [8]
  Kim, H.G. and Harget, P.J., J. Appl. Phys., 1979, 50(10): 6072
9. [9]
  Mehta, M.J. and Andrews, R.D., Polym. Prep., 1973, 14: 1260
10. [10]
  La Mantia, F.P. and Acierno, D., Colloid Polym. Sci., 1981, 259(7): 693
11. [11]
  Acierno, D., Bianchi, E., Ciferri, A., Decindio, B., Migliaresi, C. and Nicolais L., J. Polym. Sci., Part C: Polym. Symp.,1976, 54: 259
12. [12]
  Acierno, D., La Mantia, F.P., Polizzotti, G., Russo, S. and Titomanlio, G., J. Appl. Polym. Sci., 1980, 25(9): 2001
13. [13]
  Afshari, M., Gupta, A., Jung, D., Kotek, R., Tonelli, A.E. and Vasanthan, N., Polymer, 2008, 49(5): 1297
14. [14]
  Siegmann, A. and Baraam, Z., Macromol. Rapid Commun., 1980, 1(2): 113
15. [15]
  Hansen, J.E., 1971, U.S. Pat., 3,591,565
16. [16]
  Mckelvey, J.M., Polymer processing, John Wiley and Sons, New York, 1962
17. [17]
  Xie, A., Zhang, Z., Gu, B., Yang, G., Tao, D., Weng, S., Wu, J., Xu, G., Hu, X., Liu, X., Zhao, Y., Xu, Y. and Xu, D., J. Mater. Sci. Lett., 2002, 21(4): 345
18. [18]
  Acierno, D., D'Amico, R., La Mantia, F.P. and Russo, S., Polym. Eng. Sci., 1980, 20(12): 783
19. [19]
  Shenoy, A.V., Saini, D.R. and Nadkarni, V.M., J. Mater. Sci., 1983, 18(7): 2149
20. [20]
  Chao, L.C. and Chang, E.P., J. Appl. Polym. Sci., 1981, 26(2): 603
21. [21]
  Hao, C., Zhao, Y., Zhou, Y., Zhou, L., Xu, Y., Wang, D. and Xu, D., J. Polym. Sci., Part B: Polym. Phys.,2007, 45(13): 1589
22. [22]
  Moghri, M., Garmabi, H. and Molajavadi, V., J. Vinyl Addit. Technol., 2010, 16(3): 195
23. [23]
  Ashabi, L., Jafari, S.H., Khonakdar, H.A. and Baghaei, B., J. Polym. Res., 2011, 18(2): 197
24. [24]
  Woodward, A.E., Sauer, J.A., Deeley, C.W. and Kline, D.E., J. Colloid Sci., 1957, 12(4): 363
25. [25]
  Habor, J., Zeits. Chemie., 1976, 11: 422
26. [26]
  Yan, D., Wang, W.J. and Zhu, S., Polymer, 1999, 40(7): 1737

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 678
HTML全文浏览量: 21

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

The Influence of Rare Earth Ions on the Rheological Behavior of Polyamide

通讯作者: Yong-mei Ma,

English

The Influence of Rare Earth Ions on the Rheological Behavior of Polyamide

Corresponding author: Yong-mei Ma,

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

The Influence of Rare Earth Ions on the Rheological Behavior of Polyamide

通讯作者: Yong-mei Ma,

English

The Influence of Rare Earth Ions on the Rheological Behavior of Polyamide

Corresponding author: Yong-mei Ma,

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南： 你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

文章相关

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs