Vibration Assisted Extrusion of Polypropylene

Citation: Fang-zhen An, Xue-qin Gao, Jun Lei, Cong Deng, Zhong-ming Li, Kai-zhi Shen. Vibration Assisted Extrusion of Polypropylene[J]. Chinese Journal of Polymer Science, 2015, 33(5): 688-696. doi: 10.1007/s10118-015-1617-z shu

Vibration Assisted Extrusion of Polypropylene

1.
Department of Polymer Science and Materials, State Key Laboratory of Polymer Materials Engineering, Sichuan University, Chengdu 610065, China
2.
Analytical and Testing Center, Sichuan University, Chengdu 610065, China
基金项目:
This work was financially supported by the National Natural Science Foundation of China (Nos. 51033004 and 51121001) and China Postdoctoral Science Foundation (No. 2013M540711).

摘要: A new homemade apparatus, i.e. vibration assisted extrusion equipment, is employed to extrude polypropylene. Vibration assisted extrusion is based on the application of a specific macroscopic shear vibration field. Reduction of apparent melt viscosity as a function of vibration frequency is measured at different screw speeds and die temperatures. The effect of the process is investigated by performing mechanical tests, differential scanning calorimetry studies, polarized light microscopy and wide-angle X-ray diffraction. It is found that, compared with conventional extrusion, vibration assisted extrusion could effectively improve the rheological properties of PP melt by incorporating an extra shear vibration field. Both the tensile strength and elongation at break increased under the shear vibration field. For vibration assisted extrusion samples, both the melting temperature and crystallinity increased, accompanied by remarkable grain refinement. Vibration assisted extrusion induced a significantly enhanced bimodal orientation with a high fraction of a*-oriented a-crystallites, while only a limited improvement in the flow direction orientation. A structural model, i.e. bimodal c-axis and a*-axis orientation of PP macromolecular chains, was adopted to explain the experimental results.

关键词:

English

Vibration Assisted Extrusion of Polypropylene

1.
Department of Polymer Science and Materials, State Key Laboratory of Polymer Materials Engineering, Sichuan University, Chengdu 610065, China
2.
Analytical and Testing Center, Sichuan University, Chengdu 610065, China
Received Date: 17 August 2014
Revised Date: 10 September 2014
Available Online: 05 May 2015
Fund Project:
This work was financially supported by the National Natural Science Foundation of China (Nos. 51033004 and 51121001) and China Postdoctoral Science Foundation (No. 2013M540711).

Abstract: A new homemade apparatus, i.e. vibration assisted extrusion equipment, is employed to extrude polypropylene. Vibration assisted extrusion is based on the application of a specific macroscopic shear vibration field. Reduction of apparent melt viscosity as a function of vibration frequency is measured at different screw speeds and die temperatures. The effect of the process is investigated by performing mechanical tests, differential scanning calorimetry studies, polarized light microscopy and wide-angle X-ray diffraction. It is found that, compared with conventional extrusion, vibration assisted extrusion could effectively improve the rheological properties of PP melt by incorporating an extra shear vibration field. Both the tensile strength and elongation at break increased under the shear vibration field. For vibration assisted extrusion samples, both the melting temperature and crystallinity increased, accompanied by remarkable grain refinement. Vibration assisted extrusion induced a significantly enhanced bimodal orientation with a high fraction of a*-oriented a-crystallites, while only a limited improvement in the flow direction orientation. A structural model, i.e. bimodal c-axis and a*-axis orientation of PP macromolecular chains, was adopted to explain the experimental results.

Key words:

1. [1]
  Casulli, J. and Clermont, J.R., Polym. Eng. Sci., 1990, 30: 1551
2. [2]
  Guan, Q., Zhu, X.G., Chiu, D., Shen, K.Z., Lai, F.S. and Mccarthy, S.P., J. Appl. Polym. Sci., 1996, 62: 755
3. [3]
  Kalay, G. and Kalay, C.R., J. Appl. Polym. Sci., 2003, 88: 814
4. [4]
  Chen, G.S., Guo, S.Y. and Li, H.L., J. Appl. Polym. Sci., 2001, 86: 23
5. [5]
  Zhao, L.J., Li, J., Guo, S.Y. and Du, Q., Polymer, 2006, 47: 2460
6. [6]
  Swain, S.K. and Isayev, A.I., Polymer, 2007, 48: 281
7. [7]
  Isayev, A.I., Kumar, R. and Lewis, T.M., Polymer, 2009, 50: 250
8. [8]
  Li, Y.B., Liao, Y.C., Gao, X.Q., Yuan, Y., Ke, W.T. and Shen, K.Z., J. Polym. Sci., Part B: Polym. Phys., 2005, 43: 13
9. [9]
  Zhang, J., Shen, K.Z., Na, S. and Fu, Q., J. Polym. Sci., Part B: Polym. Phys., 2004, 42: 2385
10. [10]
  Jiang, L., Shen, K.Z., Ji, J.L. and Guan, Q., J. Appl. Polym. Sci., 1998, 69: 323
11. [11]
  Nie, M., Bai, S.B. and Wang, Q., Polym. Bull., 2010, 65: 609
12. [12]
  Nie, M. and Wang, Q., J. Appl. Polym. Sci., 2013, 128: 3149
13. [13]
  Wales, J.L.S., Den Otter, J.L. and Janeschitz-Kriegl, H., Rheol. Acta, 1965, 4: 146
14. [14]
  Gao, X.Q., Zhang, J., Chen, C.S. and Shen, K.Z., J. Appl. Polym. Sci., 2007, 106: 552
15. [15]
  van der Wal, A., Mulder, J.J. and Gaymans, R.J., Polymer, 1998, 39: 5477
16. [16]
  Zipper, P., Jnosi, A., Geymayer, W., Ingolic, E. and Fleischmann, E., Polym. Eng. Sci., 1996, 36: 467
17. [17]
  Zhu, P.W. and Edward, G., Macromol. Mater. Eng., 2003, 288: 301
18. [18]
  Costantino, A., Pettarin, V., Viana, J., Pontes, A., Pouzada, A. and Frontini, P., Procedia. Mater. Sci., 2012, 1: 34
19. [19]
  Luo, F., Wang, K., Ning, N.Y., Geng, C.Z., Deng, H., Chen, F., Fu, Q., Qian, Y.Y. and Zheng, D., Polym. Adv. Technol., 2011, 22: 2044
20. [20]
  Tanniru, M., Yuan, Q. and Misra, R.D.K., Polymer, 2006, 47: 2133
21. [21]
  Yuan, Q. and Misra, R.D.K., Polymer, 2006, 47: 4421
22. [22]
  Kalay, G. and Bevis, M.J., J. Polym. Sci. B Polym. Phys., 1997, 35: 265
23. [23]
  Li, Q.T., Zheng, G.Q., Dai, K., Xie, M.C., Liu, C.T., Liu, B.C., Zhang, X.L., Wang, B., Chen, J.B., Shen, C.Y., Li, Q. and Peng, X.F., Mater. Lett., 2011, 65: 2274
24. [24]
  Way, J.L., Atkinson, J.R. and Nutting, J., J. Mater. Sci., 1974, 9: 293
25. [25]
  Campbell, D. and Qayyum, M.M,. J. Mater. Sci., 1977, 12: 2427
26. [26]
  Chan, C.M., Wu, J.S., Li, J.X. and Cheung, Y.K., Polymer, 2002, 43: 2981
27. [27]
  Rybnik?, F., J. Appl. Polym. Sci., 1989, 38: 1479
28. [28]
  Choi, W.J. and Kim, S.C., Polymer, 2004, 45: 2393
29. [29]
  Clark, E.S. and Spruiell, J.E., Polym. Eng. Sci., 1976, 16: 176
30. [30]
  Fujiyama, M., Wakino, T. and Kawasaki, Y., J. Appl. Polym. Sci., 1988, 35: 29

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 1019
HTML全文浏览量: 59

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Vibration Assisted Extrusion of Polypropylene

English

Vibration Assisted Extrusion of Polypropylene

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

Vibration Assisted Extrusion of Polypropylene

English

Vibration Assisted Extrusion of Polypropylene

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南： 你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

文章相关

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs