Citation: MO Yi-Jie, GUO Rui-Hua, AN Sheng-Li, GUO Le-Le, ZHANG Jie-Yu, ZHOU Guo-Zhi. High Specific Area Cerium Oxide: Synthesis and Effect on Catalytic Performance of Pt-Based Catalysts[J]. Chinese Journal of Inorganic Chemistry, ;2018, 34(11): 1991-1999. doi: 10.11862/CJIC.2018.247 shu

High Specific Area Cerium Oxide: Synthesis and Effect on Catalytic Performance of Pt-Based Catalysts

MO Yi-Jie ^1,2 ,
GUO Rui-Hua ^1,2,3,, ,
AN Sheng-Li ^1,2 ,
GUO Le-Le ^1,2 ,
ZHANG Jie-Yu ³ ,
ZHOU Guo-Zhi ³

1.
School of Material and Metallurgy, Inner Mongolia University of Science & Technology, Baotou, Inner Mongolia 014010, China
2.
Inner Mongolia Key Laboratory of Advanced Ceramic Materials and Devices, Baotou, Inner Mongolia 014010, China
3.
College of Materials Science and Engineering, Shanghai University, Shanghai 200072, China

Corresponding author: GUO Rui-Hua, grh7810@163.com
Received Date: 24 June 2018
Revised Date: 15 August 2018

Figures(11)

A broom-like CeO₂ with a specific surface area of 175 m²·g^-1 and a pore size of 2~4 nm was synthesized by hydrothermal method. The Pt-CeO₂/RGO catalyst was prepared by the microwave-assisted ethylene glycol reduction chloroplatinic acid method, and the effect of the addition of broom-like CeO₂ on the electrocatalytic performance of Pt-based catalysts was investigated. The prepared CeO₂ and catalyst were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), N₂ adsorption-desorption, and X-ray photoelectron spectroscopy (XPS). The electrochemical performance of catalysts was tested by electrochemical workstation. The results showed that the CeO₂ in the catalyst remains in the form of a broom, and the Pt nanoparticles are evenly distributed on the surface of graphene carrier. When the mass ratio of RGO to CeO₂(m_RGO:m_CeO₂) is 1:2, the electrocatalytic performance of the Pt-CeO₂/RGO catalyst with broom-like CeO₂ is the best, the electrochemical active surface area was 102.83 m²·g^-1, the peak current density of ethanol oxidation was 757.17 A·g^-1, the steady-state current density of 1 000 s was 108.17 A·g^-1, the charge transfer resistance of the catalytic oxidation reaction of ethanol is the smallest and the activation energy is the lowest.
- direct ethanol fuel cell,
- anode catalyst,
- broom-like CeO₂,
- catalytic performance,
- stability
1. [1]
  ZHAO Xiao-Lin, HANG Min-Fang. Rare Metal Materials and Engineering, 2007, 36(S2):645-647
2. [2]
  WANG Xu-Hong, ZHU Hui, LIU Fei, et al. Materials Review, 2013, 27(11):128-131
3. [3]
  ZHANG Hai-Yan, CAO Chun-Hui, ZHAO Jian, et al. Chin. J. Catal., 2012, 33(2):222-229
4. [4]
  MA De-Na, CHEN Wei, JIAO Lian-Sheng, et al. Chinese J. Inorg. Chem., 2008, 24(11):1803-1806 doi: 10.3321/j.issn:1001-4861.2008.11.013
5. [5]
  Linares J J, Rocha T A, Zignani S, et al. Int. J. Hydrogen Energy, 2013, 38(1):620-630 doi: 10.1016/j.ijhydene.2012.06.113
6. [6]
  YUAN Shan-Mei, ZHU Yu, NI Hong-Jun, et al. New Chemical Materials, 2011, 39(1):15-18 doi: 10.3969/j.issn.1006-3536.2011.01.006
7. [7]
  Eiji H, Tomonori T, Masanobu C, et al. J. Power Sources, 2014, 263(1):280-287
8. [8]
  WANG Xu-Hong, JI Wang-Jin, RUAN Shi-Dong, et al. Bulletin of the Chinese Ceramic Society, 2015, 34(10):2786-2791
9. [9]
  SUN Hong-Yan, ZHAO Lian-Hua, YU Feng -Chun, et al. Acta Phys.-Chim. Sin., 2013, 29(5):959-965 doi: 10.3866/PKU.WHXB201303042
10. [10]
  ZHANG Xin-Wei, ZHU Hong, GUO Zhi-Jun, et al. Journal of Beijing Jiaotong University, 2010, 34(6):95-99 doi: 10.3969/j.issn.1673-0291.2010.06.021
11. [11]
  Zhu M Y, Sun G Q, Xin Q. Electrochim. Acta, 2009, 54(5):1511-1518 doi: 10.1016/j.electacta.2008.09.035
12. [12]
  Singh R N, Madhu, Awasthi R. New and Future Developments in Catalysis. Netherlands:Elsevier, 2013:459-465
13. [13]
  Lu Q Q, Huang J S, Han C, et al. Electrochim. Acta, 2018, 266(1):305-311
14. [14]
  Kowal A, Li M, Shao M, et al. Nat. Mater., 2009, 8(4):325-330 doi: 10.1038/nmat2359
15. [15]
  Rubén R, María L, Elena P, et al. Molecules, 2016, 21(9):1225-1237 doi: 10.3390/molecules21091225
16. [16]
  Yang P P, Yuan X L, Hu H C, et al. Adv. Funct. Mater., 2017, 28(1):1704774
17. [17]
  Song H Q, Qiu X P, Guo D J, et al. J. Power Sources, 2008, 178(1):97-102 doi: 10.1016/j.jpowsour.2007.11.044
18. [18]
  Ribeiro N F P, Mendes F M T, Perez C A C, et al. Appl. Catal. A, 2008, 347(1):62-71 doi: 10.1016/j.apcata.2008.05.030
19. [19]
  Ioroi T, Akita T, Yamazaki S, et al. Electrochim. Acta, 2006, 52(1):491-498
20. [20]
  Yu S P, Liu Q B, Yang W S, et al. Electrochim. Acta, 2013, 94(1):245-251
21. [21]
  Bai Y X, Wu J J, Qiu X P, et al. Appl. Catal. B, 2007, 73(1/2):144-149
22. [22]
  Gojković S L, Vidaković T R, Durović D R. Electrochim. Acta, 2003, 48(24):3607-3614
23. [23]
  Tapan N A, Mustain W E, Gurau B, et al. J. New Mater. Electrochem. Syst., 2004, 7(4):281-286
24. [24]
  Chen W X, Lee J Y, Liu Z L. Mater. Lett., 2004, 58(25):3166-3169 doi: 10.1016/j.matlet.2004.06.008
25. [25]
  Song S, Wang Y, Shen P K. J. Power Sources, 2007, 170(1):46-49 doi: 10.1016/j.jpowsour.2007.04.012
26. [26]
  Xu B, Zhang Q, Yuan S S, et al. Chem. Eng. J., 2015, 260(1):126-132
27. [27]
  Deivaraj T C, Chen W X, Lee J Y. J. Mater. Chem., 2003, 13(10):2555-2560 doi: 10.1039/b307040a
28. [28]
  Wang G J, Gao Y Z, Wang Z B, et al. J. Power Sources, 2010, 195(1):185-189 doi: 10.1016/j.jpowsour.2009.06.080
29. [29]
  Feng L G, Yang J, Hu Y, et al. Int. J. Hydrogen Energy, 2012, 37(6):4812-4818 doi: 10.1016/j.ijhydene.2011.12.114
30. [30]
  Zhou Y K, Holme T, Berry J, et al. J. Phys. Chem. C, 2010, 114(1):506-515 doi: 10.1021/jp9088386
31. [31]
  Feng L G, Sun X J, Liu C P, et al. Chem. Commun., 2012, 48(3):419-421 doi: 10.1039/C1CC16522D
32. [32]
  Lu L J, Nie Y, Wang Y, et al. J. Mater. Chem. A, 2018, 6(1):104-109 doi: 10.1039/C7TA08343B
33. [33]
  Zhou Y, Gao Y F, Liu Y C, et al. J. Power Sources, 2010, 195(6):1605-1609 doi: 10.1016/j.jpowsour.2009.08.106
34. [34]
  Kim J H, Hac H Y, Oh I H, et al. Electrochim. Acta, 2004, 50(2/3):801-806
35. [35]
  Meli G, Leger J M, Lamy C. J. Appl. Electrochem., 1993, 23(3):197-202
1. [1]
  Siyu HOU , Weiyao LI , Jiadong LIU , Fei WANG , Wensi LIU , Jing YANG , Ying ZHANG . Preparation and catalytic performance of magnetic nano iron oxide by oxidation co-precipitation method. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1577-1582. doi: 10.11862/CJIC.20230469
2. [2]
  Xingyang LI , Tianju LIU , Yang GAO , Dandan ZHANG , Yong ZHOU , Meng PAN . A superior methanol-to-propylene catalyst: Construction via synergistic regulation of pore structure and acidic property of high-silica ZSM-5 zeolite. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1279-1289. doi: 10.11862/CJIC.20240026
3. [3]
  Wen YANG , Didi WANG , Ziyi HUANG , Yaping ZHOU , Yanyan FENG . La promoted hydrotalcite derived Ni-based catalysts: In situ preparation and CO₂ methanation performance. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 561-570. doi: 10.11862/CJIC.20230276
4. [4]
  Zhuo WANG , Junshan ZHANG , Shaoyan YANG , Lingyan ZHOU , Yedi LI , Yuanpei LAN . Preparation and photocatalytic performance of CeO₂-reduced graphene oxide by thermal decomposition. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1708-1718. doi: 10.11862/CJIC.20240067
5. [5]
  Wenlong LI , Xinyu JIA , Jie LING , Mengdan MA , Anning ZHOU . Photothermal catalytic CO₂ hydrogenation over a Mg-doped In₂O_3-x catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 919-929. doi: 10.11862/CJIC.20230421
6. [6]
  Kun WANG , Wenrui LIU , Peng JIANG , Yuhang SONG , Lihua CHEN , Zhao DENG . Hierarchical hollow structured BiOBr-Pt catalysts for photocatalytic CO₂ reduction. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1270-1278. doi: 10.11862/CJIC.20240037
7. [7]
  Yi YANG , Shuang WANG , Wendan WANG , Limiao CHEN . Photocatalytic CO₂ reduction performance of Z-scheme Ag-Cu₂O/BiVO₄ photocatalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 895-906. doi: 10.11862/CJIC.20230434
8. [8]
  Zhanggui DUAN , Yi PEI , Shanshan ZHENG , Zhaoyang WANG , Yongguang WANG , Junjie WANG , Yang HU , Chunxin LÜ , Wei ZHONG . Preparation of UiO-66-NH₂ supported copper catalyst and its catalytic activity on alcohol oxidation. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 496-506. doi: 10.11862/CJIC.20230317
9. [9]
  Ruolin CHENG , Haoran WANG , Jing REN , Yingying MA , Huagen LIANG . Efficient photocatalytic CO₂ cycloaddition over W₁₈O₄₉/NH₂-UiO-66 composite catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 523-532. doi: 10.11862/CJIC.20230349
10. [10]
  Min WANG , Dehua XIN , Yaning SHI , Wenyao ZHU , Yuanqun ZHANG , Wei ZHANG . Construction and full-spectrum catalytic performance of multilevel Ag/Bi/nitrogen vacancy g-C₃N₄/Ti₃C₂T_x Schottky junction. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1123-1134. doi: 10.11862/CJIC.20230477
11. [11]
  Juan WANG , Zhongqiu WANG , Qin SHANG , Guohong WANG , Jinmao LI . NiS and Pt as dual co-catalysts for the enhanced photocatalytic H₂ production activity of BaTiO₃ nanofibers. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1719-1730. doi: 10.11862/CJIC.20240102
12. [12]
  Bing LIU , Huang ZHANG , Hongliang HAN , Changwen HU , Yinglei ZHANG . Visible light degradation of methylene blue from water by triangle Au@TiO₂ mesoporous catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 941-952. doi: 10.11862/CJIC.20230398
13. [13]
  Zhiwen HU , Weixia DONG , Qifu BAO , Ping LI . Low-temperature synthesis of tetragonal BaTiO₃ for piezocatalysis. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 857-866. doi: 10.11862/CJIC.20230462
14. [14]
  Guimin ZHANG , Wenjuan MA , Wenqiang DING , Zhengyi FU . Synthesis and catalytic properties of hollow AgPd bimetallic nanospheres. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 963-971. doi: 10.11862/CJIC.20230293
15. [15]
  Xiutao Xu , Chunfeng Shao , Jinfeng Zhang , Zhongliao Wang , Kai Dai . Rational Design of S-Scheme CeO₂/Bi₂MoO₆ Microsphere Heterojunction for Efficient Photocatalytic CO₂ Reduction. Acta Physico-Chimica Sinica, 2024, 40(10): 2309031-. doi: 10.3866/PKU.WHXB202309031
16. [16]
  Qianqian Liu , Xing Du , Wanfei Li , Wei-Lin Dai , Bo Liu . Synergistic Effects of Internal Electric and Dipole Fields in SnNb₂O₆/Nitrogen-Enriched C₃N₅ S-Scheme Heterojunction for Boosting Photocatalytic Performance. Acta Physico-Chimica Sinica, 2024, 40(10): 2311016-. doi: 10.3866/PKU.WHXB202311016
17. [17]
  Juntao Yan , Liang Wei . 2D S-Scheme Heterojunction Photocatalyst. Acta Physico-Chimica Sinica, 2024, 40(10): 2312024-. doi: 10.3866/PKU.WHXB202312024
18. [18]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
19. [19]
  Xiaoning TANG , Junnan LIU , Xingfu YANG , Jie LEI , Qiuyang LUO , Shu XIA , An XUE . Effect of sodium alginate-sodium carboxymethylcellulose gel layer on the stability of Zn anodes. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1452-1460. doi: 10.11862/CJIC.20240191
20. [20]
  Yufang GAO , Nan HOU , Yaning LIANG , Ning LI , Yanting ZHANG , Zelong LI , Xiaofeng LI . Nano-thin layer MCM-22 zeolite: Synthesis and catalytic properties of trimethylbenzene isomerization reaction. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1079-1087. doi: 10.11862/CJIC.20240036

Get Citation

PDF

XML

Metrics

PDF Downloads(1)
Abstract views(1087)
HTML views(639)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142